Abstract

Frequency upconversion (UC) luminescence was investigated in terbium (Tb3+) doped lutetium silicate powders when the samples were irradiated with femtosecond lasers operating either at 800 nm or 1500 nm. The samples with three different Tb3+ concentrations were prepared by the combustion synthesis method. Rietveld analysis of the X-ray powder diffraction data showed the predominance of monoclinic Lu2SiO5 phase. UC luminescence signals induced by three- and four-photon absorption were identified. The mechanisms that originate the anti-Stokes luminescence were discussed.

© 2013 Optical Society of America

1. Introduction

Crystalline powders doped with rare-earth (RE) ions are strong candidates for luminescence based devices such as displays, fluorescent lamps, imaging devices, and scintillators [1]. Among the RE ions, terbium (Tb3+) has attracted significant attention because, along with europium (Eu3+), it presents very large photoluminescence (PL) quantum yield [28]. Although Tb3+ ions are a priori insensitive to near-infrared light at 800 nm some research teams have focused on alternative approaches to obtain infrared-to-visible conversion using short-pulsed lasers. When irradiated with strong near-infrared lasers visible PL is achieved by simultaneous multi-photon absorption, i.e.: electrons in the ground state are promoted to the excited states without intermediate resonances. This process is different from excited-state-absorption, energy-transfer, cooperative upconversion, and photon-avalanche that are more usual processes [9]. For instance, three-photon induced luminescence has been demonstrated in Ce3+-doped YAlO3 crystal [10], Tb3+-doped multicomponent oxide glass [11] and Eu3+-doped LiNbO3 polycrystalline powder [12].

Presently there is large interest in the study of powdered lutetium silicates. Many studies of lutetium silicate doped with RE ions aim their application as luminescent materials motivated by the already proved large efficiency of these compounds as cathode ray phosphors and gamma ray detectors in nuclear medical diagnostic equipment. Lutetium orthosilicate (Lu2SiO5) - LSO - and lutetium pyrosilicate (Lu2Si2O7) – LPS – are the two most stable compounds in the Lu2O3-SiO2 system and powders of cerium (Ce3+) doped LSO and LPS have been studied as scintillators [1315]. However the frequency upconversion (UC) properties of optically excited RE doped lutetium silicate powders were not reported, as far as we know.

There are many synthesis methods to produce RE-doped powders such as citrate-gel [16], solid-state reaction [17] and combustion synthesis (CS) [6, 7, 18, 19]. For instance, CS has been employed to prepare RE-doped low-cost high-yield oxide powders with many advantages over the other methods because it involves simple apparatus, direct crystallization of small particles, low processing temperature and short preparation time. The products obtained by the CS method are generally more homogeneous and have smaller amount of impurities than the powders prepared by conventional methods. However, as it involves a drastic exothermic reaction, it is difficult to control the final product in terms of particle’s sizes and shape, as well as the crystalline phase purity.

In the present work we used the CS technique to prepare Tb3+ doped lutetium silicate powders to study some of their UC properties. One excitation source used was a femtosecond optical parametric amplifier (OPA) operating at 1500 nm. In this case the UC luminescence was due to the absorption of four laser photons. Moreover, aiming to discover new uses of this material, we performed experiments with a femtosecond laser at 800 nm. For biological applications, such as cell imaging, 800 nm is more convenient than 1500 nm due to the large optical absorption of water at this wavelength. Therefore PL induced by absorption of three 800 nm laser photons was also studied.

2. Experimental details

The powders were synthesized using reagent-grade terbium nitrate, Tb(NO3)3-6H2O, lutetium nitrate, Lu(NO3)3-6H2O, silica fumed 0.014 μm and urea, CH4N2O, as the starting materials. To prepare the samples, the metal nitrates and silica fumed were mixed in a proper weight to produce Lu2SiO5 phase. The mixture was put on a small amount of de-ionized water and after that urea was added to the aqueous nitrate solution. The mixed solution was kept under constant stirring until it was transformed into a transparent viscous gel. Afterwards, the resultant gel precursor was placed in a ceramic crucible and introduced in a furnace, preheated at 500 °C, for about 20 minutes. Finally, the as-prepared powders were sintered at 1100 °C for 2 h in air atmosphere with a heating-rate of 200 °C/h. The as-prepared samples have Tb3+ concentrations of 0.5, 1.5 and 3.0% wt.

Surface morphology was investigated using a Hitachi TM-1000 tabletop Scanning Electron Microscope (SEM). The accelerating voltage was preset at 15 kV. Imaging was obtained by a backscattering electron detector with the preset charge-up reduction mode.

Structural analysis was performed by X-ray powder diffraction (XRPD) using a Siemens D-5000 diffractometer with Cu Kα radiation (λ = 0.15406 nm). The diffractometer optics used to collect the data consisted of a fixed divergent slit (1.0 mm), a scattered radiation slit (1.0 mm), a receiving slit (0.2 mm) and a graphite monochromator in front of the detector. The XRPD data was refined following the Rietveld method with the GSAS-II software [20].

Stokes luminescence spectra were obtained using a continuous wave lamp peaked at 255 nm (25 W) as the excitation source. UC luminescence spectra were obtained with a Ti: sapphire amplified system (800 nm, 1.0 kHz, 100 fs) in conjunction with an OPA operating at 1500 nm. Fresh powders were held between two microscope slides with an estimated powder thickness of ≈0.5 mm. The laser power reaching the sample was adjusted using a λ/2 plate followed by a polarizer and focused with a lens (100 mm focal length); the laser spot diameter at the sample was ≈5 mm. The PL was collected by an optical fiber connected to a spectrometer that has resolution of 1 nm. A glass filter (Corning 4-94) was used to block the 800 nm scattered laser light in front of the spectrometer. In the 1500 nm experiments the wavelength rejection of the spectrometer was enough to block the elastic scattered light. The signal was processed using a boxcar (gate delay: 0 ms, gate width: 100 ms; sampling average: 10) coupled to a computer. The luminescence dynamics was obtained by collecting the PL with a multimode fiber connected to a 0.25 m monochromator attached to a H5783 Hamamatsu photomultiplier. The signals were recorded using a digital oscilloscope (load ≈50 Ohms) connected to a personal computer. All measurements were performed at room temperature.

3. Results and discussion

Figure 1 shows the SEM image and the XRPD pattern for one of our prepared samples. The SEM image shows a highly porous material with a complex sponge-like structure containing aggregated particles. This is characteristic of powders prepared by CS where a large amount of gases are released during ignition. The X-ray diffraction peaks are consistent with those of standard monoclinic Lu2SiO5 with space group I2/a (JCPDS card No. 41-0239) and monoclinic Lu2Si2O7 with space group C2/m (JCPDS Card No. 34-0509). The samples do not present the phase Lu2O3 because the heat-treatment temperature was larger than 1000 °C [21]. Rietveld analysis was performed in the XRPD data shown in Fig. 1 and the results are presented in Table 1. As expected, Lu2SiO5 is the predominant phase.

 figure: Fig. 1

Fig. 1 (a) SEM image and (b) XRPD pattern for one of the samples studied in this work. The SEM image full scale bar: 20 μm.

Download Full Size | PPT Slide | PDF

Tables Icon

Table 1. Rietveld refinement results of our lutetium silicate powder prepared by combustion synthesis.

Figure 2 shows the Stokes spectra obtained upon excitation at 255 nm. The PL bands are due to the Tb3+ inner-4f shell electronic transitions from excited states to lower energy states: 5D47FJ (J = 1, 3, 4, 5, 6) and (5D3,5G6) → 7FJ (J = 3, 4, 5, 6) [22]. PL bands in the range 350-450 nm appear only in the sample with low Tb3+ doping concentration (0.5% wt) indicating quenching processes in the samples with larger Tb3+ concentrations, probably due to cross-relaxation involving states 5D3 and 5D4 [4]. Strong emissions in the range 470 - 650 nm are observed for all samples.

 figure: Fig. 2

Fig. 2 Stokes luminescence spectra of the lutetium silicate samples excited at 255 nm.

Download Full Size | PPT Slide | PDF

Figures 3(a) and 3(b) show the UC spectra of samples containing 0.5, 1.5 and 3.0% wt of Tb3+ ions excited at 800 nm and 1500 nm, respectively. Both, Fig. 3(a) and 3(b), show similar results to the ones observed in Fig. 2 with the strongest emission located at ≈549 nm.

 figure: Fig. 3

Fig. 3 Anti-Stokes luminescence spectra of the lutetium silicate samples excited at 800 nm (a) and at 1500 nm (b).

Download Full Size | PPT Slide | PDF

The nonlinear character of the PL under near-infrared excitation is confirmed by determining the number of laser photons involved in the generation of each UC photon. Assuming that the UC process is not saturated we expect that the PL intensity obeys the relationship IUC α ILN where N is the number of laser photons required to populate the UC emitting states and IL is the laser intensity. The value of N may be found determining the slope of the best-fit line in a log-log plot of IUC versus IL. Figure 4 shows the PL signals obtained at 549 nm from one of the samples as a function of excitation intensity. The values determined for N indicate that four and three laser photons contribute for the UC processes for excitation at 1500 and 800 nm, respectively. Similar results were obtained for the other two samples.

 figure: Fig. 4

Fig. 4 Log-log plot of the upconversion intensity at 549 nm as a function of the laser peak power.

Download Full Size | PPT Slide | PDF

In order to understand the anti-Stokes PL process a simplified energy levels diagram of the Tb3+ ions and the UC excitation pathways are represented in Fig. 5. The direct one-photon absorption at 255 nm and three-photon absorption (with laser wavelength at 800 nm) fall into the Tb3+ ion 4f75d1 manifold of states from where, after successive nonradiative relaxation steps, the excited ions decay to the emitting states 5D3 and 5D4. The off-resonance two-photon absorption of transition 7F65D3 excited with the laser at 800 nm is ruled out because the energy mismatch between the two photons energy and the 5D3 level is large (≈1500 cm−1). Accordingly, the results presented in Fig. 4 show that the emission from state 5D4 is due to three-photon absorption at 800 nm. The UC process observed under 1500 nm excitation, also depicted in Fig. 5, is more complex. The proposed scheme considers a resonant one-photon absorption 7F6 → (7F0, 7F1) followed by three-photon absorption to state 5D2, without intermediate resonance. The energy mismatch is compensated by phonons that participate in the process. The results of Fig. 4 show that a four-photon process dominates.

 figure: Fig. 5

Fig. 5 Tb3+ energy level diagram illustrating the single-photon and multi-photon absorption and luminescence.

Download Full Size | PPT Slide | PDF

Further evidence for the energy-transfer process involving Tb3+ ions in the 5D4 state are presented in the semi-logarithmic plot of Fig. 6 showing the luminescence decay of level 5D4 following the excitation at 800 nm. In Lu2SiO5, RE ions occupy two different crystallographic sites of C1-symmetry. It was observed that the RE ions present comparable lifetimes in these two sites [23]. In this case, it was reasonable to estimate the PL decay time in our samples by use of the equation [24]:

τd=t0[I(t)/I(t0)]dt,
where I(t0) is the maximum intensity at the initial time t0. The values found were 1.25, 1.10 and 0.84 ms for 0.5, 1.5 and 3.0 wt %. The shortening in the PL decay time indicates quenching of population as the doping concentration is raised.

 figure: Fig. 6

Fig. 6 Semi-logarithmic plot of the decay signal at 549nm after laser excitation at 800 nm.

Download Full Size | PPT Slide | PDF

4. Summary

In summary, we reported Stokes and anti-Stokes photoluminescence spectra of Tb3+ doped lutetium silicate powders prepared by combustion synthesis. For excitation we used femtosecond lasers at 800 nm and 1500nm and the results show that blue, green and red emissions can be obtained. The multi-photon absorption process that generates infrared-to-visible luminescence upconversion involves three and four incident laser photons. The present results indicate that RE-doped lutetium silicate is a promising infrared-to-visible upconverter material.

Acknowledgments

This work was supported by the National Institute of Photonics (INCT de Fotônica) granted by CNPq (Conselho Nacional de Desenvolvimento Científico e Tecnológico) and by FACEPE (Fundação de Amparo à Ciência e Tecnologia do Estado de Pernambuco).

References and links

1. C. Feldmann, T. Jüstel, C. R. Ronda, and P. J. Schmidt, “Inorganic luminescent materials: 100 years of research and applications,” Adv. Funct. Mater. 13(7), 511–516 (2003). [CrossRef]  

2. R. Martín-Rodríguez, R. Valiente, S. Polizzi, M. Bettinelli, A. Speghini, and F. Piccinelli, “Upconversion luminescence in nanocrystals of Gd3Ga5O12 and Y3Al5O12 doped with Tb3+-Yb3+ and Eu3+-Yb3+,” J. Phys. Chem. C 113(28), 12195–12200 (2009). [CrossRef]  

3. I. R. Martín, A. C. Yanes, J. Méndez-Ramos, M. E. Torres, and V. D. Rodríguez, “Cooperative energy transfer in Yb3+-Tb3+ codoped sílica sol-gel glasses,” J. Appl. Phys. 89(5), 2520–2524 (2001). [CrossRef]  

4. Z. Boruc, B. Fetlinski, M. Kaczkan, S. Turczynski, D. Pawlak, and M. Malinowski, “Temperature and concentration quenching of Tb3+ emissions in Y4Al2O9 crystals,” J. Alloy. Comp. 532, 92–97 (2012). [CrossRef]  

5. D. C. Yeh, R. R. Petrin, W. A. Sibley, V. Madigou, J. L. Adam, and M. J. Suscavage, “Energy transfer between Er3+ and Tm3+ ions in a barium fluoride-thorium fluoride glass,” Phys. Rev. B Condens. Matter 39(1), 80–90 (1989). [CrossRef]   [PubMed]  

6. N. Rakov, G. S. Maciel, W. B. Lozano, and C. B. de Araújo, “Investigation of Eu3+ luminescence intensification in Al2O3 powders codoped with Tb3+ and prepared by low-temperature direct combustion synthesis,” Appl. Phys. Lett. 88, 081908 (2006).

7. N. Rakov and G. S. Maciel, “Enhancement of luminescence efficiency of f-f transitions from Tb3+ due to energy transfer from Ce3+ in Al2O3 crystalline ceramic powders prepared by low temperature direct combustion synthesis,” Chem. Phys. Lett. 400(4-6), 553–557 (2004). [CrossRef]  

8. L. R. P. Kassab, R. de Almeida, D. M. da Silva, and C. B. de Araújo, “Luminescence of Tb3+ doped TeO2-ZnO-Na2O-PbO glasses containing silver nanoparticles,” J. Appl. Phys. 104(9), 093531–093533 (2008). [CrossRef]  

9. F. Auzel, “Upconversion and anti-Stokes processes with f and d ions in solids,” Chem. Rev. 104(1), 139–174 (2004). [CrossRef]   [PubMed]  

10. L. Y. Yang, Y. J. Dong, D. P. Chen, C. Wang, X. Hu, N. Da, G. J. Zhao, J. Xu, X. W. Jiang, C. S. Zhu, and J. R. Qiu, “Three-photon-excited upconversion luminescence of Ce3+ YAP crystal by femtosecond laser irradiation,” Opt. Express 14(1), 243–247 (2006). [CrossRef]   [PubMed]  

11. H. P. Ma, B. W. Zhu, and F. L. Zou, “Three-photon-excited fluorescence of Tb3+-doped CaO-Al2O3-SiO2 glass by femtosecond laser irradiation,” J. Rare Earths 26(6), 928–931 (2008). [CrossRef]  

12. D. Hreniak, W. Strek, A. Speghini, M. Bettinelli, G. Boulon, and Y. Guyot, “Infrared induced red luminescence of Eu3+-doped polycrystalline LiNbO3,” Appl. Phys. Lett. 88(16), 161118 (2006). [CrossRef]  

13. M. Yamaga, Y. Ohsumi, T. Nakayama, and T. P. J. Han, “Persistent phosphorescence in Ce-doped Lu2SiO5,” Opt. Mater. Express 2(4), 413–419 (2012). [CrossRef]  

14. A. J. Wojtowicz, W. Drozdowski, D. Wisniewski, J.-L. Lefaucheur, Z. Galazka, Z. H. Gou, T. Lukasiewicz, and J. Kisielewski, “Scintillation properties of selected oxide monocrystals activated with Ce and Pr,” Opt. Mater. 28(1-2), 85–93 (2006). [CrossRef]  

15. H. Feng, D. Z. Ding, H. Y. Li, F. Yang, S. Lu, S. K. Pan, X. F. Chen, W. D. Zhang, and G. H. Ren, “Scintillation and thermoluminescence properties of a new scintillator YPS:Ce,” J. Inorg. Mater. 25(8), 801–805 (2010). [CrossRef]  

16. Y. H. Zhou, J. Lin, S. B. Wang, and H. J. Zhang, “Preparation of Y3Al5O12:Eu phosphors by citric-gel method and their luminescent properties,” Opt. Mater. 20(1), 13–20 (2002). [CrossRef]  

17. Y. C. Li, Y. H. Chang, Y. F. Lin, Y. S. Chang, and Y. J. Lin, “Synthesis and luminescent properties of Ln3+(Eu3+, Sm3+, Dy3+)-doped lanthanum aluminum germanate LaAlGe2O7 phosphors,” J. Alloy. Comp. 439(1-2), 367–375 (2007). [CrossRef]  

18. L. E. Shea, J. McKittrick, L. A. Lopez, and E. Sluzky, “Synthesis of red-emitting, small particle size luminescent oxides using an optimized combustion process,” J. Am. Ceram. Soc. 79(12), 3257–3265 (1996). [CrossRef]  

19. R. V. Mangalaraja, J. Mouzon, P. Hedström, I. Kero, K. V. S. Ramam, C. P. Camurri, and M. Odén, “Combustion synthesis of Y2O3 and Yb-Y2O3: Part I. Nanopowders and their characterization,” J. Mater. Process. Technol. 208(1-3), 415–422 (2008). [CrossRef]  

20. A. C. Larson, R. B. von Dreele, General Structure Analysis System (GSAS); Los Alamos National Laboratory Report LAUR 86–748, 2004.

21. M. Gu, L. Jia, X. L. Liu, S. Huang, B. Liu, and C. Ni, “Luminescent properties of Na-codoped Lu2SiO5:Ce phosphor,” J. Alloy. Comp. 502(1), 190–194 (2010). [CrossRef]  

22. H. Huang and B. Yan, “Luminescence of nanophoshors Lu2SiO5 doped with different concentration of Tb3+ by in situ composition of hybrid precursors,” Mater. Sci. Eng. B 117(3), 261–264 (2005). [CrossRef]  

23. C. Mansuy, F. Leroux, R. Mahiou, and J. M. Nedelec, “Preferential site substitution in sol-gel derived Eu3+ doped Lu2SiO5: a combined study by X-ray absorption and luminescence spectroscopies,” J. Mater. Chem. 15(38), 4129–4135 (2005). [CrossRef]  

24. S. Ye, B. Zhu, J. Chen, J. Luo, and J. R. Qiu, “Infrared quantum cutting in Tb3+,Yb3+ codoped transparent glass ceramics containing CaF2 nanocrystals,” Appl. Phys. Lett. 92(14), 141112 (2008). [CrossRef]  

References

  • View by:
  • |
  • |
  • |

  1. C. Feldmann, T. Jüstel, C. R. Ronda, and P. J. Schmidt, “Inorganic luminescent materials: 100 years of research and applications,” Adv. Funct. Mater. 13(7), 511–516 (2003).
    [Crossref]
  2. R. Martín-Rodríguez, R. Valiente, S. Polizzi, M. Bettinelli, A. Speghini, and F. Piccinelli, “Upconversion luminescence in nanocrystals of Gd3Ga5O12 and Y3Al5O12 doped with Tb3+-Yb3+ and Eu3+-Yb3+,” J. Phys. Chem. C 113(28), 12195–12200 (2009).
    [Crossref]
  3. I. R. Martín, A. C. Yanes, J. Méndez-Ramos, M. E. Torres, and V. D. Rodríguez, “Cooperative energy transfer in Yb3+-Tb3+ codoped sílica sol-gel glasses,” J. Appl. Phys. 89(5), 2520–2524 (2001).
    [Crossref]
  4. Z. Boruc, B. Fetlinski, M. Kaczkan, S. Turczynski, D. Pawlak, and M. Malinowski, “Temperature and concentration quenching of Tb3+ emissions in Y4Al2O9 crystals,” J. Alloy. Comp. 532, 92–97 (2012).
    [Crossref]
  5. D. C. Yeh, R. R. Petrin, W. A. Sibley, V. Madigou, J. L. Adam, and M. J. Suscavage, “Energy transfer between Er3+ and Tm3+ ions in a barium fluoride-thorium fluoride glass,” Phys. Rev. B Condens. Matter 39(1), 80–90 (1989).
    [Crossref] [PubMed]
  6. N. Rakov, G. S. Maciel, W. B. Lozano, and C. B. de Araújo, “Investigation of Eu3+ luminescence intensification in Al2O3 powders codoped with Tb3+ and prepared by low-temperature direct combustion synthesis,” Appl. Phys. Lett. 88, 081908 (2006).
  7. N. Rakov and G. S. Maciel, “Enhancement of luminescence efficiency of f-f transitions from Tb3+ due to energy transfer from Ce3+ in Al2O3 crystalline ceramic powders prepared by low temperature direct combustion synthesis,” Chem. Phys. Lett. 400(4-6), 553–557 (2004).
    [Crossref]
  8. L. R. P. Kassab, R. de Almeida, D. M. da Silva, and C. B. de Araújo, “Luminescence of Tb3+ doped TeO2-ZnO-Na2O-PbO glasses containing silver nanoparticles,” J. Appl. Phys. 104(9), 093531–093533 (2008).
    [Crossref]
  9. F. Auzel, “Upconversion and anti-Stokes processes with f and d ions in solids,” Chem. Rev. 104(1), 139–174 (2004).
    [Crossref] [PubMed]
  10. L. Y. Yang, Y. J. Dong, D. P. Chen, C. Wang, X. Hu, N. Da, G. J. Zhao, J. Xu, X. W. Jiang, C. S. Zhu, and J. R. Qiu, “Three-photon-excited upconversion luminescence of Ce3+ YAP crystal by femtosecond laser irradiation,” Opt. Express 14(1), 243–247 (2006).
    [Crossref] [PubMed]
  11. H. P. Ma, B. W. Zhu, and F. L. Zou, “Three-photon-excited fluorescence of Tb3+-doped CaO-Al2O3-SiO2 glass by femtosecond laser irradiation,” J. Rare Earths 26(6), 928–931 (2008).
    [Crossref]
  12. D. Hreniak, W. Strek, A. Speghini, M. Bettinelli, G. Boulon, and Y. Guyot, “Infrared induced red luminescence of Eu3+-doped polycrystalline LiNbO3,” Appl. Phys. Lett. 88(16), 161118 (2006).
    [Crossref]
  13. M. Yamaga, Y. Ohsumi, T. Nakayama, and T. P. J. Han, “Persistent phosphorescence in Ce-doped Lu2SiO5,” Opt. Mater. Express 2(4), 413–419 (2012).
    [Crossref]
  14. A. J. Wojtowicz, W. Drozdowski, D. Wisniewski, J.-L. Lefaucheur, Z. Galazka, Z. H. Gou, T. Lukasiewicz, and J. Kisielewski, “Scintillation properties of selected oxide monocrystals activated with Ce and Pr,” Opt. Mater. 28(1-2), 85–93 (2006).
    [Crossref]
  15. H. Feng, D. Z. Ding, H. Y. Li, F. Yang, S. Lu, S. K. Pan, X. F. Chen, W. D. Zhang, and G. H. Ren, “Scintillation and thermoluminescence properties of a new scintillator YPS:Ce,” J. Inorg. Mater. 25(8), 801–805 (2010).
    [Crossref]
  16. Y. H. Zhou, J. Lin, S. B. Wang, and H. J. Zhang, “Preparation of Y3Al5O12:Eu phosphors by citric-gel method and their luminescent properties,” Opt. Mater. 20(1), 13–20 (2002).
    [Crossref]
  17. Y. C. Li, Y. H. Chang, Y. F. Lin, Y. S. Chang, and Y. J. Lin, “Synthesis and luminescent properties of Ln3+(Eu3+, Sm3+, Dy3+)-doped lanthanum aluminum germanate LaAlGe2O7 phosphors,” J. Alloy. Comp. 439(1-2), 367–375 (2007).
    [Crossref]
  18. L. E. Shea, J. McKittrick, L. A. Lopez, and E. Sluzky, “Synthesis of red-emitting, small particle size luminescent oxides using an optimized combustion process,” J. Am. Ceram. Soc. 79(12), 3257–3265 (1996).
    [Crossref]
  19. R. V. Mangalaraja, J. Mouzon, P. Hedström, I. Kero, K. V. S. Ramam, C. P. Camurri, and M. Odén, “Combustion synthesis of Y2O3 and Yb-Y2O3: Part I. Nanopowders and their characterization,” J. Mater. Process. Technol. 208(1-3), 415–422 (2008).
    [Crossref]
  20. A. C. Larson, R. B. von Dreele, General Structure Analysis System (GSAS); Los Alamos National Laboratory Report LAUR 86–748, 2004.
  21. M. Gu, L. Jia, X. L. Liu, S. Huang, B. Liu, and C. Ni, “Luminescent properties of Na-codoped Lu2SiO5:Ce phosphor,” J. Alloy. Comp. 502(1), 190–194 (2010).
    [Crossref]
  22. H. Huang and B. Yan, “Luminescence of nanophoshors Lu2SiO5 doped with different concentration of Tb3+ by in situ composition of hybrid precursors,” Mater. Sci. Eng. B 117(3), 261–264 (2005).
    [Crossref]
  23. C. Mansuy, F. Leroux, R. Mahiou, and J. M. Nedelec, “Preferential site substitution in sol-gel derived Eu3+ doped Lu2SiO5: a combined study by X-ray absorption and luminescence spectroscopies,” J. Mater. Chem. 15(38), 4129–4135 (2005).
    [Crossref]
  24. S. Ye, B. Zhu, J. Chen, J. Luo, and J. R. Qiu, “Infrared quantum cutting in Tb3+,Yb3+ codoped transparent glass ceramics containing CaF2 nanocrystals,” Appl. Phys. Lett. 92(14), 141112 (2008).
    [Crossref]

2012 (2)

Z. Boruc, B. Fetlinski, M. Kaczkan, S. Turczynski, D. Pawlak, and M. Malinowski, “Temperature and concentration quenching of Tb3+ emissions in Y4Al2O9 crystals,” J. Alloy. Comp. 532, 92–97 (2012).
[Crossref]

M. Yamaga, Y. Ohsumi, T. Nakayama, and T. P. J. Han, “Persistent phosphorescence in Ce-doped Lu2SiO5,” Opt. Mater. Express 2(4), 413–419 (2012).
[Crossref]

2010 (2)

H. Feng, D. Z. Ding, H. Y. Li, F. Yang, S. Lu, S. K. Pan, X. F. Chen, W. D. Zhang, and G. H. Ren, “Scintillation and thermoluminescence properties of a new scintillator YPS:Ce,” J. Inorg. Mater. 25(8), 801–805 (2010).
[Crossref]

M. Gu, L. Jia, X. L. Liu, S. Huang, B. Liu, and C. Ni, “Luminescent properties of Na-codoped Lu2SiO5:Ce phosphor,” J. Alloy. Comp. 502(1), 190–194 (2010).
[Crossref]

2009 (1)

R. Martín-Rodríguez, R. Valiente, S. Polizzi, M. Bettinelli, A. Speghini, and F. Piccinelli, “Upconversion luminescence in nanocrystals of Gd3Ga5O12 and Y3Al5O12 doped with Tb3+-Yb3+ and Eu3+-Yb3+,” J. Phys. Chem. C 113(28), 12195–12200 (2009).
[Crossref]

2008 (4)

L. R. P. Kassab, R. de Almeida, D. M. da Silva, and C. B. de Araújo, “Luminescence of Tb3+ doped TeO2-ZnO-Na2O-PbO glasses containing silver nanoparticles,” J. Appl. Phys. 104(9), 093531–093533 (2008).
[Crossref]

H. P. Ma, B. W. Zhu, and F. L. Zou, “Three-photon-excited fluorescence of Tb3+-doped CaO-Al2O3-SiO2 glass by femtosecond laser irradiation,” J. Rare Earths 26(6), 928–931 (2008).
[Crossref]

R. V. Mangalaraja, J. Mouzon, P. Hedström, I. Kero, K. V. S. Ramam, C. P. Camurri, and M. Odén, “Combustion synthesis of Y2O3 and Yb-Y2O3: Part I. Nanopowders and their characterization,” J. Mater. Process. Technol. 208(1-3), 415–422 (2008).
[Crossref]

S. Ye, B. Zhu, J. Chen, J. Luo, and J. R. Qiu, “Infrared quantum cutting in Tb3+,Yb3+ codoped transparent glass ceramics containing CaF2 nanocrystals,” Appl. Phys. Lett. 92(14), 141112 (2008).
[Crossref]

2007 (1)

Y. C. Li, Y. H. Chang, Y. F. Lin, Y. S. Chang, and Y. J. Lin, “Synthesis and luminescent properties of Ln3+(Eu3+, Sm3+, Dy3+)-doped lanthanum aluminum germanate LaAlGe2O7 phosphors,” J. Alloy. Comp. 439(1-2), 367–375 (2007).
[Crossref]

2006 (4)

D. Hreniak, W. Strek, A. Speghini, M. Bettinelli, G. Boulon, and Y. Guyot, “Infrared induced red luminescence of Eu3+-doped polycrystalline LiNbO3,” Appl. Phys. Lett. 88(16), 161118 (2006).
[Crossref]

L. Y. Yang, Y. J. Dong, D. P. Chen, C. Wang, X. Hu, N. Da, G. J. Zhao, J. Xu, X. W. Jiang, C. S. Zhu, and J. R. Qiu, “Three-photon-excited upconversion luminescence of Ce3+ YAP crystal by femtosecond laser irradiation,” Opt. Express 14(1), 243–247 (2006).
[Crossref] [PubMed]

A. J. Wojtowicz, W. Drozdowski, D. Wisniewski, J.-L. Lefaucheur, Z. Galazka, Z. H. Gou, T. Lukasiewicz, and J. Kisielewski, “Scintillation properties of selected oxide monocrystals activated with Ce and Pr,” Opt. Mater. 28(1-2), 85–93 (2006).
[Crossref]

N. Rakov, G. S. Maciel, W. B. Lozano, and C. B. de Araújo, “Investigation of Eu3+ luminescence intensification in Al2O3 powders codoped with Tb3+ and prepared by low-temperature direct combustion synthesis,” Appl. Phys. Lett. 88, 081908 (2006).

2005 (2)

H. Huang and B. Yan, “Luminescence of nanophoshors Lu2SiO5 doped with different concentration of Tb3+ by in situ composition of hybrid precursors,” Mater. Sci. Eng. B 117(3), 261–264 (2005).
[Crossref]

C. Mansuy, F. Leroux, R. Mahiou, and J. M. Nedelec, “Preferential site substitution in sol-gel derived Eu3+ doped Lu2SiO5: a combined study by X-ray absorption and luminescence spectroscopies,” J. Mater. Chem. 15(38), 4129–4135 (2005).
[Crossref]

2004 (2)

N. Rakov and G. S. Maciel, “Enhancement of luminescence efficiency of f-f transitions from Tb3+ due to energy transfer from Ce3+ in Al2O3 crystalline ceramic powders prepared by low temperature direct combustion synthesis,” Chem. Phys. Lett. 400(4-6), 553–557 (2004).
[Crossref]

F. Auzel, “Upconversion and anti-Stokes processes with f and d ions in solids,” Chem. Rev. 104(1), 139–174 (2004).
[Crossref] [PubMed]

2003 (1)

C. Feldmann, T. Jüstel, C. R. Ronda, and P. J. Schmidt, “Inorganic luminescent materials: 100 years of research and applications,” Adv. Funct. Mater. 13(7), 511–516 (2003).
[Crossref]

2002 (1)

Y. H. Zhou, J. Lin, S. B. Wang, and H. J. Zhang, “Preparation of Y3Al5O12:Eu phosphors by citric-gel method and their luminescent properties,” Opt. Mater. 20(1), 13–20 (2002).
[Crossref]

2001 (1)

I. R. Martín, A. C. Yanes, J. Méndez-Ramos, M. E. Torres, and V. D. Rodríguez, “Cooperative energy transfer in Yb3+-Tb3+ codoped sílica sol-gel glasses,” J. Appl. Phys. 89(5), 2520–2524 (2001).
[Crossref]

1996 (1)

L. E. Shea, J. McKittrick, L. A. Lopez, and E. Sluzky, “Synthesis of red-emitting, small particle size luminescent oxides using an optimized combustion process,” J. Am. Ceram. Soc. 79(12), 3257–3265 (1996).
[Crossref]

1989 (1)

D. C. Yeh, R. R. Petrin, W. A. Sibley, V. Madigou, J. L. Adam, and M. J. Suscavage, “Energy transfer between Er3+ and Tm3+ ions in a barium fluoride-thorium fluoride glass,” Phys. Rev. B Condens. Matter 39(1), 80–90 (1989).
[Crossref] [PubMed]

Adam, J. L.

D. C. Yeh, R. R. Petrin, W. A. Sibley, V. Madigou, J. L. Adam, and M. J. Suscavage, “Energy transfer between Er3+ and Tm3+ ions in a barium fluoride-thorium fluoride glass,” Phys. Rev. B Condens. Matter 39(1), 80–90 (1989).
[Crossref] [PubMed]

Auzel, F.

F. Auzel, “Upconversion and anti-Stokes processes with f and d ions in solids,” Chem. Rev. 104(1), 139–174 (2004).
[Crossref] [PubMed]

Bettinelli, M.

R. Martín-Rodríguez, R. Valiente, S. Polizzi, M. Bettinelli, A. Speghini, and F. Piccinelli, “Upconversion luminescence in nanocrystals of Gd3Ga5O12 and Y3Al5O12 doped with Tb3+-Yb3+ and Eu3+-Yb3+,” J. Phys. Chem. C 113(28), 12195–12200 (2009).
[Crossref]

D. Hreniak, W. Strek, A. Speghini, M. Bettinelli, G. Boulon, and Y. Guyot, “Infrared induced red luminescence of Eu3+-doped polycrystalline LiNbO3,” Appl. Phys. Lett. 88(16), 161118 (2006).
[Crossref]

Boruc, Z.

Z. Boruc, B. Fetlinski, M. Kaczkan, S. Turczynski, D. Pawlak, and M. Malinowski, “Temperature and concentration quenching of Tb3+ emissions in Y4Al2O9 crystals,” J. Alloy. Comp. 532, 92–97 (2012).
[Crossref]

Boulon, G.

D. Hreniak, W. Strek, A. Speghini, M. Bettinelli, G. Boulon, and Y. Guyot, “Infrared induced red luminescence of Eu3+-doped polycrystalline LiNbO3,” Appl. Phys. Lett. 88(16), 161118 (2006).
[Crossref]

Camurri, C. P.

R. V. Mangalaraja, J. Mouzon, P. Hedström, I. Kero, K. V. S. Ramam, C. P. Camurri, and M. Odén, “Combustion synthesis of Y2O3 and Yb-Y2O3: Part I. Nanopowders and their characterization,” J. Mater. Process. Technol. 208(1-3), 415–422 (2008).
[Crossref]

Chang, Y. H.

Y. C. Li, Y. H. Chang, Y. F. Lin, Y. S. Chang, and Y. J. Lin, “Synthesis and luminescent properties of Ln3+(Eu3+, Sm3+, Dy3+)-doped lanthanum aluminum germanate LaAlGe2O7 phosphors,” J. Alloy. Comp. 439(1-2), 367–375 (2007).
[Crossref]

Chang, Y. S.

Y. C. Li, Y. H. Chang, Y. F. Lin, Y. S. Chang, and Y. J. Lin, “Synthesis and luminescent properties of Ln3+(Eu3+, Sm3+, Dy3+)-doped lanthanum aluminum germanate LaAlGe2O7 phosphors,” J. Alloy. Comp. 439(1-2), 367–375 (2007).
[Crossref]

Chen, D. P.

Chen, J.

S. Ye, B. Zhu, J. Chen, J. Luo, and J. R. Qiu, “Infrared quantum cutting in Tb3+,Yb3+ codoped transparent glass ceramics containing CaF2 nanocrystals,” Appl. Phys. Lett. 92(14), 141112 (2008).
[Crossref]

Chen, X. F.

H. Feng, D. Z. Ding, H. Y. Li, F. Yang, S. Lu, S. K. Pan, X. F. Chen, W. D. Zhang, and G. H. Ren, “Scintillation and thermoluminescence properties of a new scintillator YPS:Ce,” J. Inorg. Mater. 25(8), 801–805 (2010).
[Crossref]

Da, N.

da Silva, D. M.

L. R. P. Kassab, R. de Almeida, D. M. da Silva, and C. B. de Araújo, “Luminescence of Tb3+ doped TeO2-ZnO-Na2O-PbO glasses containing silver nanoparticles,” J. Appl. Phys. 104(9), 093531–093533 (2008).
[Crossref]

de Almeida, R.

L. R. P. Kassab, R. de Almeida, D. M. da Silva, and C. B. de Araújo, “Luminescence of Tb3+ doped TeO2-ZnO-Na2O-PbO glasses containing silver nanoparticles,” J. Appl. Phys. 104(9), 093531–093533 (2008).
[Crossref]

de Araújo, C. B.

L. R. P. Kassab, R. de Almeida, D. M. da Silva, and C. B. de Araújo, “Luminescence of Tb3+ doped TeO2-ZnO-Na2O-PbO glasses containing silver nanoparticles,” J. Appl. Phys. 104(9), 093531–093533 (2008).
[Crossref]

N. Rakov, G. S. Maciel, W. B. Lozano, and C. B. de Araújo, “Investigation of Eu3+ luminescence intensification in Al2O3 powders codoped with Tb3+ and prepared by low-temperature direct combustion synthesis,” Appl. Phys. Lett. 88, 081908 (2006).

Ding, D. Z.

H. Feng, D. Z. Ding, H. Y. Li, F. Yang, S. Lu, S. K. Pan, X. F. Chen, W. D. Zhang, and G. H. Ren, “Scintillation and thermoluminescence properties of a new scintillator YPS:Ce,” J. Inorg. Mater. 25(8), 801–805 (2010).
[Crossref]

Dong, Y. J.

Drozdowski, W.

A. J. Wojtowicz, W. Drozdowski, D. Wisniewski, J.-L. Lefaucheur, Z. Galazka, Z. H. Gou, T. Lukasiewicz, and J. Kisielewski, “Scintillation properties of selected oxide monocrystals activated with Ce and Pr,” Opt. Mater. 28(1-2), 85–93 (2006).
[Crossref]

Feldmann, C.

C. Feldmann, T. Jüstel, C. R. Ronda, and P. J. Schmidt, “Inorganic luminescent materials: 100 years of research and applications,” Adv. Funct. Mater. 13(7), 511–516 (2003).
[Crossref]

Feng, H.

H. Feng, D. Z. Ding, H. Y. Li, F. Yang, S. Lu, S. K. Pan, X. F. Chen, W. D. Zhang, and G. H. Ren, “Scintillation and thermoluminescence properties of a new scintillator YPS:Ce,” J. Inorg. Mater. 25(8), 801–805 (2010).
[Crossref]

Fetlinski, B.

Z. Boruc, B. Fetlinski, M. Kaczkan, S. Turczynski, D. Pawlak, and M. Malinowski, “Temperature and concentration quenching of Tb3+ emissions in Y4Al2O9 crystals,” J. Alloy. Comp. 532, 92–97 (2012).
[Crossref]

Galazka, Z.

A. J. Wojtowicz, W. Drozdowski, D. Wisniewski, J.-L. Lefaucheur, Z. Galazka, Z. H. Gou, T. Lukasiewicz, and J. Kisielewski, “Scintillation properties of selected oxide monocrystals activated with Ce and Pr,” Opt. Mater. 28(1-2), 85–93 (2006).
[Crossref]

Gou, Z. H.

A. J. Wojtowicz, W. Drozdowski, D. Wisniewski, J.-L. Lefaucheur, Z. Galazka, Z. H. Gou, T. Lukasiewicz, and J. Kisielewski, “Scintillation properties of selected oxide monocrystals activated with Ce and Pr,” Opt. Mater. 28(1-2), 85–93 (2006).
[Crossref]

Gu, M.

M. Gu, L. Jia, X. L. Liu, S. Huang, B. Liu, and C. Ni, “Luminescent properties of Na-codoped Lu2SiO5:Ce phosphor,” J. Alloy. Comp. 502(1), 190–194 (2010).
[Crossref]

Guyot, Y.

D. Hreniak, W. Strek, A. Speghini, M. Bettinelli, G. Boulon, and Y. Guyot, “Infrared induced red luminescence of Eu3+-doped polycrystalline LiNbO3,” Appl. Phys. Lett. 88(16), 161118 (2006).
[Crossref]

Han, T. P. J.

Hedström, P.

R. V. Mangalaraja, J. Mouzon, P. Hedström, I. Kero, K. V. S. Ramam, C. P. Camurri, and M. Odén, “Combustion synthesis of Y2O3 and Yb-Y2O3: Part I. Nanopowders and their characterization,” J. Mater. Process. Technol. 208(1-3), 415–422 (2008).
[Crossref]

Hreniak, D.

D. Hreniak, W. Strek, A. Speghini, M. Bettinelli, G. Boulon, and Y. Guyot, “Infrared induced red luminescence of Eu3+-doped polycrystalline LiNbO3,” Appl. Phys. Lett. 88(16), 161118 (2006).
[Crossref]

Hu, X.

Huang, H.

H. Huang and B. Yan, “Luminescence of nanophoshors Lu2SiO5 doped with different concentration of Tb3+ by in situ composition of hybrid precursors,” Mater. Sci. Eng. B 117(3), 261–264 (2005).
[Crossref]

Huang, S.

M. Gu, L. Jia, X. L. Liu, S. Huang, B. Liu, and C. Ni, “Luminescent properties of Na-codoped Lu2SiO5:Ce phosphor,” J. Alloy. Comp. 502(1), 190–194 (2010).
[Crossref]

Jia, L.

M. Gu, L. Jia, X. L. Liu, S. Huang, B. Liu, and C. Ni, “Luminescent properties of Na-codoped Lu2SiO5:Ce phosphor,” J. Alloy. Comp. 502(1), 190–194 (2010).
[Crossref]

Jiang, X. W.

Jüstel, T.

C. Feldmann, T. Jüstel, C. R. Ronda, and P. J. Schmidt, “Inorganic luminescent materials: 100 years of research and applications,” Adv. Funct. Mater. 13(7), 511–516 (2003).
[Crossref]

Kaczkan, M.

Z. Boruc, B. Fetlinski, M. Kaczkan, S. Turczynski, D. Pawlak, and M. Malinowski, “Temperature and concentration quenching of Tb3+ emissions in Y4Al2O9 crystals,” J. Alloy. Comp. 532, 92–97 (2012).
[Crossref]

Kassab, L. R. P.

L. R. P. Kassab, R. de Almeida, D. M. da Silva, and C. B. de Araújo, “Luminescence of Tb3+ doped TeO2-ZnO-Na2O-PbO glasses containing silver nanoparticles,” J. Appl. Phys. 104(9), 093531–093533 (2008).
[Crossref]

Kero, I.

R. V. Mangalaraja, J. Mouzon, P. Hedström, I. Kero, K. V. S. Ramam, C. P. Camurri, and M. Odén, “Combustion synthesis of Y2O3 and Yb-Y2O3: Part I. Nanopowders and their characterization,” J. Mater. Process. Technol. 208(1-3), 415–422 (2008).
[Crossref]

Kisielewski, J.

A. J. Wojtowicz, W. Drozdowski, D. Wisniewski, J.-L. Lefaucheur, Z. Galazka, Z. H. Gou, T. Lukasiewicz, and J. Kisielewski, “Scintillation properties of selected oxide monocrystals activated with Ce and Pr,” Opt. Mater. 28(1-2), 85–93 (2006).
[Crossref]

Lefaucheur, J.-L.

A. J. Wojtowicz, W. Drozdowski, D. Wisniewski, J.-L. Lefaucheur, Z. Galazka, Z. H. Gou, T. Lukasiewicz, and J. Kisielewski, “Scintillation properties of selected oxide monocrystals activated with Ce and Pr,” Opt. Mater. 28(1-2), 85–93 (2006).
[Crossref]

Leroux, F.

C. Mansuy, F. Leroux, R. Mahiou, and J. M. Nedelec, “Preferential site substitution in sol-gel derived Eu3+ doped Lu2SiO5: a combined study by X-ray absorption and luminescence spectroscopies,” J. Mater. Chem. 15(38), 4129–4135 (2005).
[Crossref]

Li, H. Y.

H. Feng, D. Z. Ding, H. Y. Li, F. Yang, S. Lu, S. K. Pan, X. F. Chen, W. D. Zhang, and G. H. Ren, “Scintillation and thermoluminescence properties of a new scintillator YPS:Ce,” J. Inorg. Mater. 25(8), 801–805 (2010).
[Crossref]

Li, Y. C.

Y. C. Li, Y. H. Chang, Y. F. Lin, Y. S. Chang, and Y. J. Lin, “Synthesis and luminescent properties of Ln3+(Eu3+, Sm3+, Dy3+)-doped lanthanum aluminum germanate LaAlGe2O7 phosphors,” J. Alloy. Comp. 439(1-2), 367–375 (2007).
[Crossref]

Lin, J.

Y. H. Zhou, J. Lin, S. B. Wang, and H. J. Zhang, “Preparation of Y3Al5O12:Eu phosphors by citric-gel method and their luminescent properties,” Opt. Mater. 20(1), 13–20 (2002).
[Crossref]

Lin, Y. F.

Y. C. Li, Y. H. Chang, Y. F. Lin, Y. S. Chang, and Y. J. Lin, “Synthesis and luminescent properties of Ln3+(Eu3+, Sm3+, Dy3+)-doped lanthanum aluminum germanate LaAlGe2O7 phosphors,” J. Alloy. Comp. 439(1-2), 367–375 (2007).
[Crossref]

Lin, Y. J.

Y. C. Li, Y. H. Chang, Y. F. Lin, Y. S. Chang, and Y. J. Lin, “Synthesis and luminescent properties of Ln3+(Eu3+, Sm3+, Dy3+)-doped lanthanum aluminum germanate LaAlGe2O7 phosphors,” J. Alloy. Comp. 439(1-2), 367–375 (2007).
[Crossref]

Liu, B.

M. Gu, L. Jia, X. L. Liu, S. Huang, B. Liu, and C. Ni, “Luminescent properties of Na-codoped Lu2SiO5:Ce phosphor,” J. Alloy. Comp. 502(1), 190–194 (2010).
[Crossref]

Liu, X. L.

M. Gu, L. Jia, X. L. Liu, S. Huang, B. Liu, and C. Ni, “Luminescent properties of Na-codoped Lu2SiO5:Ce phosphor,” J. Alloy. Comp. 502(1), 190–194 (2010).
[Crossref]

Lopez, L. A.

L. E. Shea, J. McKittrick, L. A. Lopez, and E. Sluzky, “Synthesis of red-emitting, small particle size luminescent oxides using an optimized combustion process,” J. Am. Ceram. Soc. 79(12), 3257–3265 (1996).
[Crossref]

Lozano, W. B.

N. Rakov, G. S. Maciel, W. B. Lozano, and C. B. de Araújo, “Investigation of Eu3+ luminescence intensification in Al2O3 powders codoped with Tb3+ and prepared by low-temperature direct combustion synthesis,” Appl. Phys. Lett. 88, 081908 (2006).

Lu, S.

H. Feng, D. Z. Ding, H. Y. Li, F. Yang, S. Lu, S. K. Pan, X. F. Chen, W. D. Zhang, and G. H. Ren, “Scintillation and thermoluminescence properties of a new scintillator YPS:Ce,” J. Inorg. Mater. 25(8), 801–805 (2010).
[Crossref]

Lukasiewicz, T.

A. J. Wojtowicz, W. Drozdowski, D. Wisniewski, J.-L. Lefaucheur, Z. Galazka, Z. H. Gou, T. Lukasiewicz, and J. Kisielewski, “Scintillation properties of selected oxide monocrystals activated with Ce and Pr,” Opt. Mater. 28(1-2), 85–93 (2006).
[Crossref]

Luo, J.

S. Ye, B. Zhu, J. Chen, J. Luo, and J. R. Qiu, “Infrared quantum cutting in Tb3+,Yb3+ codoped transparent glass ceramics containing CaF2 nanocrystals,” Appl. Phys. Lett. 92(14), 141112 (2008).
[Crossref]

Ma, H. P.

H. P. Ma, B. W. Zhu, and F. L. Zou, “Three-photon-excited fluorescence of Tb3+-doped CaO-Al2O3-SiO2 glass by femtosecond laser irradiation,” J. Rare Earths 26(6), 928–931 (2008).
[Crossref]

Maciel, G. S.

N. Rakov, G. S. Maciel, W. B. Lozano, and C. B. de Araújo, “Investigation of Eu3+ luminescence intensification in Al2O3 powders codoped with Tb3+ and prepared by low-temperature direct combustion synthesis,” Appl. Phys. Lett. 88, 081908 (2006).

N. Rakov and G. S. Maciel, “Enhancement of luminescence efficiency of f-f transitions from Tb3+ due to energy transfer from Ce3+ in Al2O3 crystalline ceramic powders prepared by low temperature direct combustion synthesis,” Chem. Phys. Lett. 400(4-6), 553–557 (2004).
[Crossref]

Madigou, V.

D. C. Yeh, R. R. Petrin, W. A. Sibley, V. Madigou, J. L. Adam, and M. J. Suscavage, “Energy transfer between Er3+ and Tm3+ ions in a barium fluoride-thorium fluoride glass,” Phys. Rev. B Condens. Matter 39(1), 80–90 (1989).
[Crossref] [PubMed]

Mahiou, R.

C. Mansuy, F. Leroux, R. Mahiou, and J. M. Nedelec, “Preferential site substitution in sol-gel derived Eu3+ doped Lu2SiO5: a combined study by X-ray absorption and luminescence spectroscopies,” J. Mater. Chem. 15(38), 4129–4135 (2005).
[Crossref]

Malinowski, M.

Z. Boruc, B. Fetlinski, M. Kaczkan, S. Turczynski, D. Pawlak, and M. Malinowski, “Temperature and concentration quenching of Tb3+ emissions in Y4Al2O9 crystals,” J. Alloy. Comp. 532, 92–97 (2012).
[Crossref]

Mangalaraja, R. V.

R. V. Mangalaraja, J. Mouzon, P. Hedström, I. Kero, K. V. S. Ramam, C. P. Camurri, and M. Odén, “Combustion synthesis of Y2O3 and Yb-Y2O3: Part I. Nanopowders and their characterization,” J. Mater. Process. Technol. 208(1-3), 415–422 (2008).
[Crossref]

Mansuy, C.

C. Mansuy, F. Leroux, R. Mahiou, and J. M. Nedelec, “Preferential site substitution in sol-gel derived Eu3+ doped Lu2SiO5: a combined study by X-ray absorption and luminescence spectroscopies,” J. Mater. Chem. 15(38), 4129–4135 (2005).
[Crossref]

Martín, I. R.

I. R. Martín, A. C. Yanes, J. Méndez-Ramos, M. E. Torres, and V. D. Rodríguez, “Cooperative energy transfer in Yb3+-Tb3+ codoped sílica sol-gel glasses,” J. Appl. Phys. 89(5), 2520–2524 (2001).
[Crossref]

Martín-Rodríguez, R.

R. Martín-Rodríguez, R. Valiente, S. Polizzi, M. Bettinelli, A. Speghini, and F. Piccinelli, “Upconversion luminescence in nanocrystals of Gd3Ga5O12 and Y3Al5O12 doped with Tb3+-Yb3+ and Eu3+-Yb3+,” J. Phys. Chem. C 113(28), 12195–12200 (2009).
[Crossref]

McKittrick, J.

L. E. Shea, J. McKittrick, L. A. Lopez, and E. Sluzky, “Synthesis of red-emitting, small particle size luminescent oxides using an optimized combustion process,” J. Am. Ceram. Soc. 79(12), 3257–3265 (1996).
[Crossref]

Méndez-Ramos, J.

I. R. Martín, A. C. Yanes, J. Méndez-Ramos, M. E. Torres, and V. D. Rodríguez, “Cooperative energy transfer in Yb3+-Tb3+ codoped sílica sol-gel glasses,” J. Appl. Phys. 89(5), 2520–2524 (2001).
[Crossref]

Mouzon, J.

R. V. Mangalaraja, J. Mouzon, P. Hedström, I. Kero, K. V. S. Ramam, C. P. Camurri, and M. Odén, “Combustion synthesis of Y2O3 and Yb-Y2O3: Part I. Nanopowders and their characterization,” J. Mater. Process. Technol. 208(1-3), 415–422 (2008).
[Crossref]

Nakayama, T.

Nedelec, J. M.

C. Mansuy, F. Leroux, R. Mahiou, and J. M. Nedelec, “Preferential site substitution in sol-gel derived Eu3+ doped Lu2SiO5: a combined study by X-ray absorption and luminescence spectroscopies,” J. Mater. Chem. 15(38), 4129–4135 (2005).
[Crossref]

Ni, C.

M. Gu, L. Jia, X. L. Liu, S. Huang, B. Liu, and C. Ni, “Luminescent properties of Na-codoped Lu2SiO5:Ce phosphor,” J. Alloy. Comp. 502(1), 190–194 (2010).
[Crossref]

Odén, M.

R. V. Mangalaraja, J. Mouzon, P. Hedström, I. Kero, K. V. S. Ramam, C. P. Camurri, and M. Odén, “Combustion synthesis of Y2O3 and Yb-Y2O3: Part I. Nanopowders and their characterization,” J. Mater. Process. Technol. 208(1-3), 415–422 (2008).
[Crossref]

Ohsumi, Y.

Pan, S. K.

H. Feng, D. Z. Ding, H. Y. Li, F. Yang, S. Lu, S. K. Pan, X. F. Chen, W. D. Zhang, and G. H. Ren, “Scintillation and thermoluminescence properties of a new scintillator YPS:Ce,” J. Inorg. Mater. 25(8), 801–805 (2010).
[Crossref]

Pawlak, D.

Z. Boruc, B. Fetlinski, M. Kaczkan, S. Turczynski, D. Pawlak, and M. Malinowski, “Temperature and concentration quenching of Tb3+ emissions in Y4Al2O9 crystals,” J. Alloy. Comp. 532, 92–97 (2012).
[Crossref]

Petrin, R. R.

D. C. Yeh, R. R. Petrin, W. A. Sibley, V. Madigou, J. L. Adam, and M. J. Suscavage, “Energy transfer between Er3+ and Tm3+ ions in a barium fluoride-thorium fluoride glass,” Phys. Rev. B Condens. Matter 39(1), 80–90 (1989).
[Crossref] [PubMed]

Piccinelli, F.

R. Martín-Rodríguez, R. Valiente, S. Polizzi, M. Bettinelli, A. Speghini, and F. Piccinelli, “Upconversion luminescence in nanocrystals of Gd3Ga5O12 and Y3Al5O12 doped with Tb3+-Yb3+ and Eu3+-Yb3+,” J. Phys. Chem. C 113(28), 12195–12200 (2009).
[Crossref]

Polizzi, S.

R. Martín-Rodríguez, R. Valiente, S. Polizzi, M. Bettinelli, A. Speghini, and F. Piccinelli, “Upconversion luminescence in nanocrystals of Gd3Ga5O12 and Y3Al5O12 doped with Tb3+-Yb3+ and Eu3+-Yb3+,” J. Phys. Chem. C 113(28), 12195–12200 (2009).
[Crossref]

Qiu, J. R.

S. Ye, B. Zhu, J. Chen, J. Luo, and J. R. Qiu, “Infrared quantum cutting in Tb3+,Yb3+ codoped transparent glass ceramics containing CaF2 nanocrystals,” Appl. Phys. Lett. 92(14), 141112 (2008).
[Crossref]

L. Y. Yang, Y. J. Dong, D. P. Chen, C. Wang, X. Hu, N. Da, G. J. Zhao, J. Xu, X. W. Jiang, C. S. Zhu, and J. R. Qiu, “Three-photon-excited upconversion luminescence of Ce3+ YAP crystal by femtosecond laser irradiation,” Opt. Express 14(1), 243–247 (2006).
[Crossref] [PubMed]

Rakov, N.

N. Rakov, G. S. Maciel, W. B. Lozano, and C. B. de Araújo, “Investigation of Eu3+ luminescence intensification in Al2O3 powders codoped with Tb3+ and prepared by low-temperature direct combustion synthesis,” Appl. Phys. Lett. 88, 081908 (2006).

N. Rakov and G. S. Maciel, “Enhancement of luminescence efficiency of f-f transitions from Tb3+ due to energy transfer from Ce3+ in Al2O3 crystalline ceramic powders prepared by low temperature direct combustion synthesis,” Chem. Phys. Lett. 400(4-6), 553–557 (2004).
[Crossref]

Ramam, K. V. S.

R. V. Mangalaraja, J. Mouzon, P. Hedström, I. Kero, K. V. S. Ramam, C. P. Camurri, and M. Odén, “Combustion synthesis of Y2O3 and Yb-Y2O3: Part I. Nanopowders and their characterization,” J. Mater. Process. Technol. 208(1-3), 415–422 (2008).
[Crossref]

Ren, G. H.

H. Feng, D. Z. Ding, H. Y. Li, F. Yang, S. Lu, S. K. Pan, X. F. Chen, W. D. Zhang, and G. H. Ren, “Scintillation and thermoluminescence properties of a new scintillator YPS:Ce,” J. Inorg. Mater. 25(8), 801–805 (2010).
[Crossref]

Rodríguez, V. D.

I. R. Martín, A. C. Yanes, J. Méndez-Ramos, M. E. Torres, and V. D. Rodríguez, “Cooperative energy transfer in Yb3+-Tb3+ codoped sílica sol-gel glasses,” J. Appl. Phys. 89(5), 2520–2524 (2001).
[Crossref]

Ronda, C. R.

C. Feldmann, T. Jüstel, C. R. Ronda, and P. J. Schmidt, “Inorganic luminescent materials: 100 years of research and applications,” Adv. Funct. Mater. 13(7), 511–516 (2003).
[Crossref]

Schmidt, P. J.

C. Feldmann, T. Jüstel, C. R. Ronda, and P. J. Schmidt, “Inorganic luminescent materials: 100 years of research and applications,” Adv. Funct. Mater. 13(7), 511–516 (2003).
[Crossref]

Shea, L. E.

L. E. Shea, J. McKittrick, L. A. Lopez, and E. Sluzky, “Synthesis of red-emitting, small particle size luminescent oxides using an optimized combustion process,” J. Am. Ceram. Soc. 79(12), 3257–3265 (1996).
[Crossref]

Sibley, W. A.

D. C. Yeh, R. R. Petrin, W. A. Sibley, V. Madigou, J. L. Adam, and M. J. Suscavage, “Energy transfer between Er3+ and Tm3+ ions in a barium fluoride-thorium fluoride glass,” Phys. Rev. B Condens. Matter 39(1), 80–90 (1989).
[Crossref] [PubMed]

Sluzky, E.

L. E. Shea, J. McKittrick, L. A. Lopez, and E. Sluzky, “Synthesis of red-emitting, small particle size luminescent oxides using an optimized combustion process,” J. Am. Ceram. Soc. 79(12), 3257–3265 (1996).
[Crossref]

Speghini, A.

R. Martín-Rodríguez, R. Valiente, S. Polizzi, M. Bettinelli, A. Speghini, and F. Piccinelli, “Upconversion luminescence in nanocrystals of Gd3Ga5O12 and Y3Al5O12 doped with Tb3+-Yb3+ and Eu3+-Yb3+,” J. Phys. Chem. C 113(28), 12195–12200 (2009).
[Crossref]

D. Hreniak, W. Strek, A. Speghini, M. Bettinelli, G. Boulon, and Y. Guyot, “Infrared induced red luminescence of Eu3+-doped polycrystalline LiNbO3,” Appl. Phys. Lett. 88(16), 161118 (2006).
[Crossref]

Strek, W.

D. Hreniak, W. Strek, A. Speghini, M. Bettinelli, G. Boulon, and Y. Guyot, “Infrared induced red luminescence of Eu3+-doped polycrystalline LiNbO3,” Appl. Phys. Lett. 88(16), 161118 (2006).
[Crossref]

Suscavage, M. J.

D. C. Yeh, R. R. Petrin, W. A. Sibley, V. Madigou, J. L. Adam, and M. J. Suscavage, “Energy transfer between Er3+ and Tm3+ ions in a barium fluoride-thorium fluoride glass,” Phys. Rev. B Condens. Matter 39(1), 80–90 (1989).
[Crossref] [PubMed]

Torres, M. E.

I. R. Martín, A. C. Yanes, J. Méndez-Ramos, M. E. Torres, and V. D. Rodríguez, “Cooperative energy transfer in Yb3+-Tb3+ codoped sílica sol-gel glasses,” J. Appl. Phys. 89(5), 2520–2524 (2001).
[Crossref]

Turczynski, S.

Z. Boruc, B. Fetlinski, M. Kaczkan, S. Turczynski, D. Pawlak, and M. Malinowski, “Temperature and concentration quenching of Tb3+ emissions in Y4Al2O9 crystals,” J. Alloy. Comp. 532, 92–97 (2012).
[Crossref]

Valiente, R.

R. Martín-Rodríguez, R. Valiente, S. Polizzi, M. Bettinelli, A. Speghini, and F. Piccinelli, “Upconversion luminescence in nanocrystals of Gd3Ga5O12 and Y3Al5O12 doped with Tb3+-Yb3+ and Eu3+-Yb3+,” J. Phys. Chem. C 113(28), 12195–12200 (2009).
[Crossref]

Wang, C.

Wang, S. B.

Y. H. Zhou, J. Lin, S. B. Wang, and H. J. Zhang, “Preparation of Y3Al5O12:Eu phosphors by citric-gel method and their luminescent properties,” Opt. Mater. 20(1), 13–20 (2002).
[Crossref]

Wisniewski, D.

A. J. Wojtowicz, W. Drozdowski, D. Wisniewski, J.-L. Lefaucheur, Z. Galazka, Z. H. Gou, T. Lukasiewicz, and J. Kisielewski, “Scintillation properties of selected oxide monocrystals activated with Ce and Pr,” Opt. Mater. 28(1-2), 85–93 (2006).
[Crossref]

Wojtowicz, A. J.

A. J. Wojtowicz, W. Drozdowski, D. Wisniewski, J.-L. Lefaucheur, Z. Galazka, Z. H. Gou, T. Lukasiewicz, and J. Kisielewski, “Scintillation properties of selected oxide monocrystals activated with Ce and Pr,” Opt. Mater. 28(1-2), 85–93 (2006).
[Crossref]

Xu, J.

Yamaga, M.

Yan, B.

H. Huang and B. Yan, “Luminescence of nanophoshors Lu2SiO5 doped with different concentration of Tb3+ by in situ composition of hybrid precursors,” Mater. Sci. Eng. B 117(3), 261–264 (2005).
[Crossref]

Yanes, A. C.

I. R. Martín, A. C. Yanes, J. Méndez-Ramos, M. E. Torres, and V. D. Rodríguez, “Cooperative energy transfer in Yb3+-Tb3+ codoped sílica sol-gel glasses,” J. Appl. Phys. 89(5), 2520–2524 (2001).
[Crossref]

Yang, F.

H. Feng, D. Z. Ding, H. Y. Li, F. Yang, S. Lu, S. K. Pan, X. F. Chen, W. D. Zhang, and G. H. Ren, “Scintillation and thermoluminescence properties of a new scintillator YPS:Ce,” J. Inorg. Mater. 25(8), 801–805 (2010).
[Crossref]

Yang, L. Y.

Ye, S.

S. Ye, B. Zhu, J. Chen, J. Luo, and J. R. Qiu, “Infrared quantum cutting in Tb3+,Yb3+ codoped transparent glass ceramics containing CaF2 nanocrystals,” Appl. Phys. Lett. 92(14), 141112 (2008).
[Crossref]

Yeh, D. C.

D. C. Yeh, R. R. Petrin, W. A. Sibley, V. Madigou, J. L. Adam, and M. J. Suscavage, “Energy transfer between Er3+ and Tm3+ ions in a barium fluoride-thorium fluoride glass,” Phys. Rev. B Condens. Matter 39(1), 80–90 (1989).
[Crossref] [PubMed]

Zhang, H. J.

Y. H. Zhou, J. Lin, S. B. Wang, and H. J. Zhang, “Preparation of Y3Al5O12:Eu phosphors by citric-gel method and their luminescent properties,” Opt. Mater. 20(1), 13–20 (2002).
[Crossref]

Zhang, W. D.

H. Feng, D. Z. Ding, H. Y. Li, F. Yang, S. Lu, S. K. Pan, X. F. Chen, W. D. Zhang, and G. H. Ren, “Scintillation and thermoluminescence properties of a new scintillator YPS:Ce,” J. Inorg. Mater. 25(8), 801–805 (2010).
[Crossref]

Zhao, G. J.

Zhou, Y. H.

Y. H. Zhou, J. Lin, S. B. Wang, and H. J. Zhang, “Preparation of Y3Al5O12:Eu phosphors by citric-gel method and their luminescent properties,” Opt. Mater. 20(1), 13–20 (2002).
[Crossref]

Zhu, B.

S. Ye, B. Zhu, J. Chen, J. Luo, and J. R. Qiu, “Infrared quantum cutting in Tb3+,Yb3+ codoped transparent glass ceramics containing CaF2 nanocrystals,” Appl. Phys. Lett. 92(14), 141112 (2008).
[Crossref]

Zhu, B. W.

H. P. Ma, B. W. Zhu, and F. L. Zou, “Three-photon-excited fluorescence of Tb3+-doped CaO-Al2O3-SiO2 glass by femtosecond laser irradiation,” J. Rare Earths 26(6), 928–931 (2008).
[Crossref]

Zhu, C. S.

Zou, F. L.

H. P. Ma, B. W. Zhu, and F. L. Zou, “Three-photon-excited fluorescence of Tb3+-doped CaO-Al2O3-SiO2 glass by femtosecond laser irradiation,” J. Rare Earths 26(6), 928–931 (2008).
[Crossref]

Adv. Funct. Mater. (1)

C. Feldmann, T. Jüstel, C. R. Ronda, and P. J. Schmidt, “Inorganic luminescent materials: 100 years of research and applications,” Adv. Funct. Mater. 13(7), 511–516 (2003).
[Crossref]

Appl. Phys. Lett. (3)

N. Rakov, G. S. Maciel, W. B. Lozano, and C. B. de Araújo, “Investigation of Eu3+ luminescence intensification in Al2O3 powders codoped with Tb3+ and prepared by low-temperature direct combustion synthesis,” Appl. Phys. Lett. 88, 081908 (2006).

D. Hreniak, W. Strek, A. Speghini, M. Bettinelli, G. Boulon, and Y. Guyot, “Infrared induced red luminescence of Eu3+-doped polycrystalline LiNbO3,” Appl. Phys. Lett. 88(16), 161118 (2006).
[Crossref]

S. Ye, B. Zhu, J. Chen, J. Luo, and J. R. Qiu, “Infrared quantum cutting in Tb3+,Yb3+ codoped transparent glass ceramics containing CaF2 nanocrystals,” Appl. Phys. Lett. 92(14), 141112 (2008).
[Crossref]

Chem. Phys. Lett. (1)

N. Rakov and G. S. Maciel, “Enhancement of luminescence efficiency of f-f transitions from Tb3+ due to energy transfer from Ce3+ in Al2O3 crystalline ceramic powders prepared by low temperature direct combustion synthesis,” Chem. Phys. Lett. 400(4-6), 553–557 (2004).
[Crossref]

Chem. Rev. (1)

F. Auzel, “Upconversion and anti-Stokes processes with f and d ions in solids,” Chem. Rev. 104(1), 139–174 (2004).
[Crossref] [PubMed]

J. Alloy. Comp. (3)

Z. Boruc, B. Fetlinski, M. Kaczkan, S. Turczynski, D. Pawlak, and M. Malinowski, “Temperature and concentration quenching of Tb3+ emissions in Y4Al2O9 crystals,” J. Alloy. Comp. 532, 92–97 (2012).
[Crossref]

Y. C. Li, Y. H. Chang, Y. F. Lin, Y. S. Chang, and Y. J. Lin, “Synthesis and luminescent properties of Ln3+(Eu3+, Sm3+, Dy3+)-doped lanthanum aluminum germanate LaAlGe2O7 phosphors,” J. Alloy. Comp. 439(1-2), 367–375 (2007).
[Crossref]

M. Gu, L. Jia, X. L. Liu, S. Huang, B. Liu, and C. Ni, “Luminescent properties of Na-codoped Lu2SiO5:Ce phosphor,” J. Alloy. Comp. 502(1), 190–194 (2010).
[Crossref]

J. Am. Ceram. Soc. (1)

L. E. Shea, J. McKittrick, L. A. Lopez, and E. Sluzky, “Synthesis of red-emitting, small particle size luminescent oxides using an optimized combustion process,” J. Am. Ceram. Soc. 79(12), 3257–3265 (1996).
[Crossref]

J. Appl. Phys. (2)

I. R. Martín, A. C. Yanes, J. Méndez-Ramos, M. E. Torres, and V. D. Rodríguez, “Cooperative energy transfer in Yb3+-Tb3+ codoped sílica sol-gel glasses,” J. Appl. Phys. 89(5), 2520–2524 (2001).
[Crossref]

L. R. P. Kassab, R. de Almeida, D. M. da Silva, and C. B. de Araújo, “Luminescence of Tb3+ doped TeO2-ZnO-Na2O-PbO glasses containing silver nanoparticles,” J. Appl. Phys. 104(9), 093531–093533 (2008).
[Crossref]

J. Inorg. Mater. (1)

H. Feng, D. Z. Ding, H. Y. Li, F. Yang, S. Lu, S. K. Pan, X. F. Chen, W. D. Zhang, and G. H. Ren, “Scintillation and thermoluminescence properties of a new scintillator YPS:Ce,” J. Inorg. Mater. 25(8), 801–805 (2010).
[Crossref]

J. Mater. Chem. (1)

C. Mansuy, F. Leroux, R. Mahiou, and J. M. Nedelec, “Preferential site substitution in sol-gel derived Eu3+ doped Lu2SiO5: a combined study by X-ray absorption and luminescence spectroscopies,” J. Mater. Chem. 15(38), 4129–4135 (2005).
[Crossref]

J. Mater. Process. Technol. (1)

R. V. Mangalaraja, J. Mouzon, P. Hedström, I. Kero, K. V. S. Ramam, C. P. Camurri, and M. Odén, “Combustion synthesis of Y2O3 and Yb-Y2O3: Part I. Nanopowders and their characterization,” J. Mater. Process. Technol. 208(1-3), 415–422 (2008).
[Crossref]

J. Phys. Chem. C (1)

R. Martín-Rodríguez, R. Valiente, S. Polizzi, M. Bettinelli, A. Speghini, and F. Piccinelli, “Upconversion luminescence in nanocrystals of Gd3Ga5O12 and Y3Al5O12 doped with Tb3+-Yb3+ and Eu3+-Yb3+,” J. Phys. Chem. C 113(28), 12195–12200 (2009).
[Crossref]

J. Rare Earths (1)

H. P. Ma, B. W. Zhu, and F. L. Zou, “Three-photon-excited fluorescence of Tb3+-doped CaO-Al2O3-SiO2 glass by femtosecond laser irradiation,” J. Rare Earths 26(6), 928–931 (2008).
[Crossref]

Mater. Sci. Eng. B (1)

H. Huang and B. Yan, “Luminescence of nanophoshors Lu2SiO5 doped with different concentration of Tb3+ by in situ composition of hybrid precursors,” Mater. Sci. Eng. B 117(3), 261–264 (2005).
[Crossref]

Opt. Express (1)

Opt. Mater. (2)

Y. H. Zhou, J. Lin, S. B. Wang, and H. J. Zhang, “Preparation of Y3Al5O12:Eu phosphors by citric-gel method and their luminescent properties,” Opt. Mater. 20(1), 13–20 (2002).
[Crossref]

A. J. Wojtowicz, W. Drozdowski, D. Wisniewski, J.-L. Lefaucheur, Z. Galazka, Z. H. Gou, T. Lukasiewicz, and J. Kisielewski, “Scintillation properties of selected oxide monocrystals activated with Ce and Pr,” Opt. Mater. 28(1-2), 85–93 (2006).
[Crossref]

Opt. Mater. Express (1)

Phys. Rev. B Condens. Matter (1)

D. C. Yeh, R. R. Petrin, W. A. Sibley, V. Madigou, J. L. Adam, and M. J. Suscavage, “Energy transfer between Er3+ and Tm3+ ions in a barium fluoride-thorium fluoride glass,” Phys. Rev. B Condens. Matter 39(1), 80–90 (1989).
[Crossref] [PubMed]

Other (1)

A. C. Larson, R. B. von Dreele, General Structure Analysis System (GSAS); Los Alamos National Laboratory Report LAUR 86–748, 2004.

Cited By

OSA participates in Crossref's Cited-By Linking service. Citing articles from OSA journals and other participating publishers are listed here.

Alert me when this article is cited.


Figures (6)

Fig. 1
Fig. 1 (a) SEM image and (b) XRPD pattern for one of the samples studied in this work. The SEM image full scale bar: 20 μm.
Fig. 2
Fig. 2 Stokes luminescence spectra of the lutetium silicate samples excited at 255 nm.
Fig. 3
Fig. 3 Anti-Stokes luminescence spectra of the lutetium silicate samples excited at 800 nm (a) and at 1500 nm (b).
Fig. 4
Fig. 4 Log-log plot of the upconversion intensity at 549 nm as a function of the laser peak power.
Fig. 5
Fig. 5 Tb3+ energy level diagram illustrating the single-photon and multi-photon absorption and luminescence.
Fig. 6
Fig. 6 Semi-logarithmic plot of the decay signal at 549nm after laser excitation at 800 nm.

Tables (1)

Tables Icon

Table 1 Rietveld refinement results of our lutetium silicate powder prepared by combustion synthesis.

Equations (1)

Equations on this page are rendered with MathJax. Learn more.

τ d = t 0 [ I( t ) / I( t 0 ) ]dt ,

Metrics