Abstract

A series of novel yellow persistent luminescence Sr1-xBaxGa2Si2O8:Mn2+ phosphors were synthesized by the solid state method. To investigate the site-selective occupation of Mn2+ in Sr1-xBaxGa2Si2O8, the XRD, emission, and persistent luminescence (PersL) spectra were performed in detail for samples with different Ba2+ concentrations. With increasing Ba2+ concentrations, the Mn2+ showed an occupation preference on the decahedral sites. Furthermore, thermo-luminescence (TL) indicated a broad trap distribution ranging from 0.61 eV to 1.01 eV which endowed SrGa2Si2O8:Mn2+ a bright persistent luminescence at room temperature.

© 2021 Optical Society of America under the terms of the OSA Open Access Publishing Agreement

1. Introduction

Prominent breakthrough in white LED-related devices spurred a wide interest in phosphor research [13]. White LEDs show many advantages over fluorescent tubes and incandescent lamps, as follows: higher power efficiency and brightness; longer life cycle; pollution-free; good stability; environment-friendly characteristics; and saves energy. Now, researchers have proposed various technologies to generate white light by coupling blue/UV LEDs with phosphors. Among various phosphors, silicate-based phosphors have been investigated because of their outstanding thermal chemical, crystal structure diversity, and mechanical stability [47]. Recently, Qiu’s group discovered that novel SrGa2Si2O8:Mn2+ phosphors exhibit a yellow-green multi-band and highly thermal-stable emission, and these kinds of phosphors have a wide trap distribution that can compensate for different luminescence centers in SrGa2Si2O8 [8]. Apart from the charming luminescence property of silicate-based phosphors reported by Qiu’s group, SrGa2Si2O8:Mn2+ has other interesting optical properties. Multiple emission bands that originated from Mn2+ could probably be tailored through the introduction of doping ions owing to the different crystal field environments in SrGa2Si2O8. Moreover, the wide trap distribution in SrGa2Si2O8 may also allow energy storage, which leads to persistent luminescence. However, the report on the persistent luminescence from SrGa2Si2O8 host has not been revealed so far.

Herein, we chose SrGa2Si2O8 as a host to develop a series of Sr1-xBaxGa2Si2O8:Mn2+ phosphors. It is found that the incorporation of Ba2+ drove the site-selective substitution of Mn2+. Furthermore, thermo-luminescence (TL) indicated a broad trap distribution ranging from 0.61 eV to 1.01 eV in SrGa2Si2O8:Mn2+ phosphors. Interestingly, the substitution of Ba2+ did not bring about the change of trapping states in the phosphors. Thus, the phosphors yielded strong yellow the emission and persistent luminescence under UV light excitation.

2. Experiments

Characterization: The phases were determined by XRD on the D8 Advance Bruker Bragg-Brentano diffractometer (Cu Kα radiation) equipped with a Vantec-1 linear detector. The Rietveld refinement of XRD data was performed using TOPAS software. The emission spectra, excitation spectra, PersL spectra, and persistent luminescence decay curves were recorded at room temperature on the FLS1000 spectrophotometer (Edinburgh Instruments) using a 450 W xenon lamp. The TL curves were recorded on the FLS1000 spectrophotometer (Edinburgh Instruments) using a 450 W xenon lamp. The samples were mounted on a thermal stage (FTIR600, Linkam Scientific Instruments). In the TL measurement, the sample was heated at a rate of 1 K·s-1. The digital photographs were captured by using a smartphone (OnePlus 6).

Materials and preparation method: Sr1-xBaxGa2Si2O8: 1%Mn2+ (x = 0-0.4) and Sr1-xBaxGa2Si2O8 (x = 0 and 0.2) samples were synthesized through high-temperature solid-state sintering. Pure ZrCO3 (4N), Ga2O3 (4N), SiO2 (4N), and MnCO3 (4N) were used as raw materials. The powders were finely mixed in an agate mortar to form homogeneous powders for prefiring. After prefiring at 1050 °C for 2 h, the materials were ground again to fine powders. Then, all samples were sintered at 1200 °C for 2 h.

3. Results and discussion

The XRD patterns of Sr1-xBaxGa2Si2O8: 1% Mn2+ (x = 0-0.4) samples are shown in Fig. 1. All the diffraction peaks coincided well with the standard data of SrGa2Si2O8 (ICSD No. 34414), with no appreciable signal from impurities when x < 0.4. With increasing of Ba content, the XRD pattern gradually moved to the lower 2θ side probably due to the lattice expansion induced by Ba replacement (r = 1.38 Å, CN (coordination number) = 7) for Sr (r = 1.21 Å, CN = 7). To further explore the structure variation, XRD refinement analyses (Fig. 2(a)) were performed on both Sr1-xBaxGa2Si2O8 (x = 0 and 0.2) samples. The structural information of SrGa2Si2O8 was used as the refined model. The refinement results are listed in Table 1. The reliability parameters were as follows: Rwp = 9.28% (x = 0) and 8.23% (x = 0.2); Rp = 7% (x = 0) and 6.16% (x = 0.2); and χ2 = 1.79 (x = 0) and 1.49 (x = 0.2). The compound crystallized in a monoclinic phase with space group P121/a (14). The cell parameters were as follows: a = 9.0099 Å, b = 9.4730 Å, c = 8.4039 Å, V = 717.2 Å3 for x = 0. Compared with the refinement result of the x = 0.2 samples (a = 9.0307 Å, b = 9.5239 Å, c = 8.4464 Å, V = 726.4 Å3), the increase in cell parameters indicated that Ba2+ successfully occupied the Sr site by forming a solid solution. Figure 2(b) displays the crystal unit cell of the Sr0.8Ba0.2Ga2Si2O8, which comprised two types of coordination polyhedral; the decahedral site was occupied by Sr2+ and Ba2+, whereas the tetrahedral site was occupied by Ga3+ and Si4+. Such low-dimensional structure is conducive to the formation of traps and enhances the interaction between trap and luminescence centers according to the studies by Long et al [8].

 figure: Fig. 1.

Fig. 1. XRD patterns of Sr1-xBaxGa2Si2O8: 1% Mn2+ (x = 0-0.4) samples and the standard data for the SrGa2Si2O8 phase.

Download Full Size | PPT Slide | PDF

 figure: Fig. 2.

Fig. 2. (a) Rietveld refinement of powder XRD profile of Sr1-xBaxGa2Si2O8 (x = 0 and 0.2) samples. (b) Crystal structure of Sr0.8Ba0.2Ga2Si2O8.

Download Full Size | PPT Slide | PDF

Tables Icon

Table 1. The refined positions of all atoms and the lattice parameters of SrGa2Si2O8 and Sr0.8Ba0.2Ga2Si2O8

Figure 3 shows the excitation and emission spectra of SrGa2Si2O8 matrix. The excitation band was observed at about 270 nm when the emission at 695 nm was monitored. Under excitation at 270 nm, SrGa2Si2O8 matrix exhibited a broad emission band at around 695 nm. The same photoluminescence was observed in β-Ga2O3 single crystals and β-Ga2O3 nanowires [9,10]. The experiment of Víllora et al. indicated that the excitation band at 270 nm was due to the transition from the valence band perturbed by Ga3+ vacancies to the conduction band [11]. The emission band at around 695 nm was due to an electron–hole recombination, which was related to the recombination of electrons trapped by oxygen vacancies and holes captured by deep level acceptor impurity [9].

 figure: Fig. 3.

Fig. 3. Excitation and emission spectra of SrGa2Si2O8 samples.

Download Full Size | PPT Slide | PDF

Figure 4(a) shows the emission spectra of Sr1-xBaxGa2Si2O8: 1% Mn2+ (x = 0-0.3) samples under 270 nm excitation. The broad emission band was obtained from 475 nm to 850 nm, and the broad band can be fitted by three Gaussian peaks. The peak 1 centered at 525 nm and originated from the 4T16A1 transition of the Mn2+ in the tetrahedral site. The peak 2 centered at 585 nm was caused by the 4T16A1 transition of the Mn2+ in the decahedral site [8]. The peak 3 centered at 695 nm was the same as the emission band of SrGa2Si2O8 matrix, which was due to an electron–hole recombination via the donor and acceptor levels. The Mn2+ can replace the Ga3+ in the tetrahedral site, because the ion radius of Ga3+ (r = 0.47 Å, CN = 4) was more similar to Mn2+ (r = 0.66 Å, CN = 4) than Si4+ (r = 0.26 Å, CN = 4). Moreover, Mn2+ (r = 1.04 Å, CN = 7) can also substitute Sr2+ (r = 1.21 Å, CN = 7) in the decahedral site. In addition, the ratios of the peak 2 integrated intensity to the peak 1 integrated intensity increased linearly with x, as shown in Fig. 4(b). This phenomenon indicated that the incorporation of Ba2+ drove the site selection of Mn2+, which transferred from the tetrahedral site to the decahedral site. Figure 4(c) shows the excitation spectrum monitored at 525 nm. The band at 270 nm was the same as the excitation band in the SrGa2Si2O8 matrix, which was attributed to the recombination of electrons trapped by oxygen vacancies and holes captured by deep level acceptor impurity. The other excitation bands ranged from 350 nm to 470 nm and corresponded to the spin-forbidden d–d transitions of Mn2+ from the ground state 6A1(6S) to the excited states, 4E(4D), 4T2(4D), [4A1(4G),4E(G)], and 4T2(4G). The Ba2+ doping did not lead to the excitation band shift, and the incorporation of Ba2+ did not affect the crystal field strength of Mn2+ [12,13].

 figure: Fig. 4.

Fig. 4. (a) Emission spectra of Sr1-xBaxGa2Si2O8: 1% Mn2+ (x = 0-0.3) excited at 270 nm. (b) Intensity ratios of the Peak 2 to Peak 1 as functions of x in the Sr1-xBaxGa2Si2O8: 1% Mn2+ (x = 0-0.3) samples. (c) Excitation spectra of Sr1-xBaxGa2Si2O8: 1% Mn2+ (x = 0, 0.1 and 0.3).

Download Full Size | PPT Slide | PDF

The SrGa2Si2O8: 1% Mn2+ samples emitted yellow fluorescence under 254 nm light, and also exhibited bright yellow afterglow after the removal of 254 nm light, as shown in Figs. 5(a)–(c). Figure 5(d) shows the persistent decay curves of Sr1-xBaxGa2Si2O8: 1% Mn2+ (x = 0-0.3) samples after the irradiation of 270 nm was stopped for 3 min. The persistent luminescence intensity barely varied with increasing Ba2+ concentration. Persistent luminescence intensity and time were determined by the trapping state (such as trap depth and distribution) in persistent phosphors [1417]. Hence, the incorporation of Ba2+ had little impact on the trapping states in the samples. Figure 6(a) shows the PersL spectra of Sr1-xBaxGa2Si2O8: 1% Mn2+ (x = 0-0.3) irradiated by 270 nm light for 5 min. The persistent luminescence bands that ranged from 475 nm to 700 nm can be divided into two Gaussian peaks, namely, peaks 1 and peak 2. These two Gaussian peaks are similar to the emission Gaussian peaks in Fig. 4(a), which corresponded to 4T16A1 transition of the Mn2+ in the tetrahedral and decahedral sites, respectively. The inexistence of the persistent luminesce peak at around 695 nm showed that the recombination via the donors and acceptors did not occur in the persistent luminescence procedure. The ratios of the peak 2 integrated intensity to the peak 1 integrated intensity also increased linearly with x, as shown in Fig. 6(b), which further demonstrated that the incorporation of Ba2+ drove the site selection of Mn2+ from the tetrahedral site to the decahedral site. The ratios of persistent luminescence varied from the ratios of emission, which can be explained by the different energy transfer mechanisms between photoluminescence and persistent luminescence. The higher ratios of persistent luminescence than those of emission implied that defects related to trap states may be located near the Mn2+ in the decahedral site [18,19].

 figure: Fig. 5.

Fig. 5. Image of SrGa2Si2O8: 1% Mn2+ samples (a) under white-LED illumination, (b) under 254 nm light and (c) 1 min after 254 nm light ceased. (d) Persistent luminescence decay curve of the Sr1-xBaxGa2Si2O8: 1% Mn2+ (x = 0-0.3) samples monitoring at 585 nm.

Download Full Size | PPT Slide | PDF

 figure: Fig. 6.

Fig. 6. (a) PersL spectra of Sr1-xBaxGa2Si2O8: 1% Mn2+ (x = 0-0.3). (b) Emission intensity ratios and persistent luminescence intensity ratios of the Peak 2 to Peak 1 as functions of x in the Sr1-xBaxGa2Si2O8: 1% Mn2+ (x = 0-0.3) samples.

Download Full Size | PPT Slide | PDF

The persistent luminescence originated from the energy released from traps. We performed a series of TL experiments on SrGa2Si2O8: 1%Mn2+ at varying excitation temperatures (Fig. 7(a)). The TL peak gradually moved to a higher temperature region at a higher excitation temperature. The initial rise analysis method was used to estimate the trap depths [20,21]. This approach assumed that the concentration of trapped electrons on the low-temperature side of a TL glow curve was relatively constant. Thus, the TL intensity can be written as follows:

$$I(T )= C \times \textrm{exp}\left( { - \frac{E}{{kT}}} \right)$$
where I(T) is the TL intensity, T is the temperature, k is the Boltzmann constant, and C is the fitting constant. Therefore, by plotting the TL curve as ln (T) versus 1/T, the trap depth and the density of energy levels for the trap depth distribution can be estimated from the slope of the straight fitting line on the low-temperature side (Fig. 7(b)). When the excitation temperature increased from 303 K to 478 K, the trap depth gradually extended from 0.61 to ∼1.01 eV, as shown in the inset of Fig. 7(c). Figure 7(c) also revealed high density of energy levels for the trap distribution in Sr1-xBaxGa2Si2O8: 1% Mn2+ (x = 0-0.3). Suitable trap level distribution and high density of energy levels yielded strong persistent luminescence at room temperature as observed in Fig. 5 [22,23]. The above result also provided further evidence that the low-dimensional structure of SrGa2Si2O8 promoted the formation of traps and enhanced the interaction between traps and luminescence center.

 figure: Fig. 7.

Fig. 7. (a) TL curves of SrGa2Si2O8: 1% Mn2+ samples monitoring at 585 nm after initially being excited by 270 nm light for 60 s at various temperatures. (b) Initial rise method used to estimate the trap depths of SrGa2Si2O8: 1% Mn2+ samples. (c) The density of energy levels for the trap distribution in SrGa2Si2O8: 1% Mn2+ samples. Inset: The estimated trap depth in SrGa2Si2O8: 1% Mn2+ as a function of excitation temperature.

Download Full Size | PPT Slide | PDF

4. Conclusions

We successfully developed a series of Sr1-xBaxGa2Si2O8:Mn2+ phosphors with yellow persistent luminescence. The results of XRD and Rietveld refinement indicated that the samples possessed the pure SrGa2Si2O8 phase, and the incorporated Ba2+ occupied the Sr site by forming a solid solution. When the Sr/Ba ratio varied, the emission and persistent luminescence behavior of the sample changed, which was due to the fact that the site selection of Mn2+ changed after the incorporation of Ba2+. Interestingly, the substitution of Ba2+ did not bring about the change of trapping states in the samples. Thus, the samples yielded strong yellow emission and persistent luminescence under UV light excitation.

Funding

Guangdong Basic and Applied Basic Research Foundation (2020A1515010432); Project of Educational Commission of Guangdong Province of China (2019KTSCX096); Special Funds for the Cultivation of Guangdong College Students' Scientific and Technological Innovation (“Climbing Program” Special Funds) (pdjh2020b0377); Hanshan Normal University (XN201918).

Disclosures

The authors declare no conflicts of interest.

Data availability

The data that support the findings of this study are available from the corresponding author upon reasonable request.

References

1. W. Lü, W. Lv, Q. Zhao, M. Jiao, B. Shao, and H. You, “A novel efficient Mn4+ activated Ca14Al10Zn6O35 phosphor: application in red-emitting and white LEDs,” Inorg. Chem. 53(22), 11985–11990 (2014). [CrossRef]  

2. K. Li, D. Geng, M. Shang, Y. Zhang, H. Lian, and J. Lin, “Color-tunable luminescence and energy transfer properties of Ca9Mg(PO4)6F2:Eu2+, Mn2+ phosphors for UV-LEDs,” J. Phys. Chem. C 118(20), 11026–11034 (2014). [CrossRef]  

3. W.-R. Liu, C.-H. Huang, C.-W. Yeh, J.-C. Tsai, Y.-C. Chiu, Y.-T. Yeh, and R.-S. Liu, “A Study on the Luminescence and Energy Transfer of Single-Phase and Color-Tunable KCaY(PO4)2:Eu2+, Mn2+ phosphor for application in white-light LEDs,” Inorg. Chem. 51(18), 9636–9641 (2012). [CrossRef]  

4. S. S. B. Nasir, A. Tanaka, S. Yoshiara, and A. Kato, “Luminescence properties of Li2SrSiO4:Eu2+ silicate yellow phosphors with high thermal stability for high-power efficiency white LED application,” J. Lumin. 207, 22–28 (2019). [CrossRef]  

5. H. Liao, M. Zhao, M. S. Molokeev, Q. Liu, and Z. Xia, “Learning from a mineral structure toward an ultra-narrow-band blue-emitting silicate phosphor RbNa3(Li3SiO4)4:Eu2+,” Angew. Chem. 130(36), 11902–11905 (2018). [CrossRef]  

6. G. Ram Banjare, D. P. Bisen, N. Brahme, and C. Belodhiya, “Studies on structural properties, luminescence behavior and zeta potential of Dy3+ doped alkaline earth ortho-silicate phosphors,” Mater. Sci. Eng., B 263, 114882 (2021). [CrossRef]  

7. T. Sasaki, J. Fukushima, Y. Hayashi, and H. Takizawa, “Synthesis and photoluminescence properties of a novel aluminosilicate Sr3Al10SiO20:Mn4+ red phosphor,” J. Lumin. 188, 101–106 (2017). [CrossRef]  

8. Z. Long, Y. Wen, J. Qiu, J. Wang, D. Zhou, C. Zhu, J. Lai, X. Xu, X. Yu, and Q. Wang, “Crystal structure insight aided design of SrGa2Si2O8:Mn2+ with multi-band and thermally stable emission for high-power LED applications,” Chem. Eng. J. 375, 122016 (2019). [CrossRef]  

9. S. Kumar, C. Tessarek, S. Christiansen, and R. Singh, “A comparative study of β-Ga2O3 nanowires grown on different substrates using CVD technique,” J. Alloys Compd. 587, 812–818 (2014). [CrossRef]  

10. J. Zhang, B. Li, C. Xia, G. Pei, Q. Deng, Z. Yang, W. Xu, H. Shi, F. Wu, Y. Wu, and J. Xu, “Growth and spectral characterization of β-Ga2O3 single crystals,” J. Phys. Chem. Solids 67(12), 2448–2451 (2006). [CrossRef]  

11. E. G. Víllora, M. Yamaga, T. Inoue, S. Yabasi, Y. Masui, T. Sugawara, and T. Fukuda, “Optical spectroscopy study on β-Ga2O3,” Jpn. J. Appl. Phys. 41(Part 2, No. 6A), L622–L625 (2002). [CrossRef]  

12. J. Ueda, P. Dorenbos, A. J. J. Bos, K. Kuroishi, and S. Tanabe, “Control of electron transfer between Ce3+ and Cr3+ in the Y3Al5−xGaxO12 host via conduction band engineering,” J. Mater. Chem. C 3(22), 5642–5651 (2015). [CrossRef]  

13. J. Xu, J. Ueda, and S. Tanabe, “Design of deep-red persistent phosphors of Gd3Al5-xGaxO12:Cr3+ transparent ceramics sensitized by Eu3+ as an electron trap using conduction band engineering,” Opt. Mater. Express 5(5), 963 (2015). [CrossRef]  

14. N. Basavaraju, K. R. Priolkar, D. Gourier, A. Bessière, and B. Viana, “Order and disorder around Cr3+ in chromium doped persistent luminescent AB2O4 spinels,” Phys. Chem. Chem. Phys. 17(16), 10993–10999 (2015). [CrossRef]  

15. Y. Li, Y. Li, R. Chen, K. Sharafudeen, S. Zhou, M. Gecevicius, H. Wang, G. Dong, Y. Wu, X. Qin, and J. Qiu, “Tailoring of the trap distribution and crystal field in Cr3+-doped non-gallate phosphors with near-infrared long-persistence phosphorescence,” NPG Asia Mater. 7(5), e180 (2015). [CrossRef]  

16. Z. Pan, Y.-Y. Lu, and F. Liu, “Sunlight-activated long-persistent luminescence in the near-infrared from Cr3+-doped zinc gallogermanates,” Nat. Mater. 11(1), 58–63 (2011). [CrossRef]  

17. T. Maldiney, A. Lecointre, B. Viana, A. Bessière, M. Bessodes, D. Gourier, C. Richard, and D. Scherman, “Controlling electron trap depth to enhance optical properties of persistent luminescence nanoparticles for in vivo imaging,” J. Am. Chem. Soc. 133(30), 11810–11815 (2011). [CrossRef]  

18. A. Bessière, S. K. Sharma, N. Basavaraju, K. R. Priolkar, L. Binet, B. Viana, A. J. J. Bos, T. Maldiney, C. Richard, D. Scherman, and D. Gourier, “Storage of visible light for long-lasting phosphorescence in chromium-doped zinc gallate,” Chem. Mater. 26(3), 1365–1373 (2014). [CrossRef]  

19. N. Basavaraju, K. R. Priolkar, D. Gourier, S. K. Sharma, A. Bessière, and B. Viana, “The importance of inversion disorder in the visible light induced persistent luminescence in Cr3+ doped AB2O4 (A = Zn or Mg and B = Ga or Al),” Phys. Chem. Chem. Phys. 17(3), 1790–1799 (2015). [CrossRef]  

20. K. Van den Eeckhout, A. J. J. Bos, D. Poelman, and P. F. Smet, “Revealing trap depth distributions in persistent phosphors,” Phys. Rev. B 87(4), 045126 (2013). [CrossRef]  

21. J. Botterman, J. J. Joos, and P. F. Smet, “Trapping and detrapping in SrAl2O4:Eu, Dy persistent phosphors: Influence of excitation wavelength and temperature,” Phys. Rev. B 90(8), 085147 (2014). [CrossRef]  

22. K. Van den Eeckhout, D. Poelman, and P. Smet, “Persistent luminescence in non-Eu2+-doped compounds: a review,” Materials 6(7), 2789–2818 (2013). [CrossRef]  

23. K. Van den Eeckhout, P. F. Smet, and D. Poelman, “Persistent luminescence in Eu2+-doped compounds: a review,” Materials 3(4), 2536–2566 (2010). [CrossRef]  

References

  • View by:
  • |
  • |
  • |

  1. W. Lü, W. Lv, Q. Zhao, M. Jiao, B. Shao, and H. You, “A novel efficient Mn4+ activated Ca14Al10Zn6O35 phosphor: application in red-emitting and white LEDs,” Inorg. Chem. 53(22), 11985–11990 (2014).
    [Crossref]
  2. K. Li, D. Geng, M. Shang, Y. Zhang, H. Lian, and J. Lin, “Color-tunable luminescence and energy transfer properties of Ca9Mg(PO4)6F2:Eu2+, Mn2+ phosphors for UV-LEDs,” J. Phys. Chem. C 118(20), 11026–11034 (2014).
    [Crossref]
  3. W.-R. Liu, C.-H. Huang, C.-W. Yeh, J.-C. Tsai, Y.-C. Chiu, Y.-T. Yeh, and R.-S. Liu, “A Study on the Luminescence and Energy Transfer of Single-Phase and Color-Tunable KCaY(PO4)2:Eu2+, Mn2+ phosphor for application in white-light LEDs,” Inorg. Chem. 51(18), 9636–9641 (2012).
    [Crossref]
  4. S. S. B. Nasir, A. Tanaka, S. Yoshiara, and A. Kato, “Luminescence properties of Li2SrSiO4:Eu2+ silicate yellow phosphors with high thermal stability for high-power efficiency white LED application,” J. Lumin. 207, 22–28 (2019).
    [Crossref]
  5. H. Liao, M. Zhao, M. S. Molokeev, Q. Liu, and Z. Xia, “Learning from a mineral structure toward an ultra-narrow-band blue-emitting silicate phosphor RbNa3(Li3SiO4)4:Eu2+,” Angew. Chem. 130(36), 11902–11905 (2018).
    [Crossref]
  6. G. Ram Banjare, D. P. Bisen, N. Brahme, and C. Belodhiya, “Studies on structural properties, luminescence behavior and zeta potential of Dy3+ doped alkaline earth ortho-silicate phosphors,” Mater. Sci. Eng., B 263, 114882 (2021).
    [Crossref]
  7. T. Sasaki, J. Fukushima, Y. Hayashi, and H. Takizawa, “Synthesis and photoluminescence properties of a novel aluminosilicate Sr3Al10SiO20:Mn4+ red phosphor,” J. Lumin. 188, 101–106 (2017).
    [Crossref]
  8. Z. Long, Y. Wen, J. Qiu, J. Wang, D. Zhou, C. Zhu, J. Lai, X. Xu, X. Yu, and Q. Wang, “Crystal structure insight aided design of SrGa2Si2O8:Mn2+ with multi-band and thermally stable emission for high-power LED applications,” Chem. Eng. J. 375, 122016 (2019).
    [Crossref]
  9. S. Kumar, C. Tessarek, S. Christiansen, and R. Singh, “A comparative study of β-Ga2O3 nanowires grown on different substrates using CVD technique,” J. Alloys Compd. 587, 812–818 (2014).
    [Crossref]
  10. J. Zhang, B. Li, C. Xia, G. Pei, Q. Deng, Z. Yang, W. Xu, H. Shi, F. Wu, Y. Wu, and J. Xu, “Growth and spectral characterization of β-Ga2O3 single crystals,” J. Phys. Chem. Solids 67(12), 2448–2451 (2006).
    [Crossref]
  11. E. G. Víllora, M. Yamaga, T. Inoue, S. Yabasi, Y. Masui, T. Sugawara, and T. Fukuda, “Optical spectroscopy study on β-Ga2O3,” Jpn. J. Appl. Phys. 41(Part 2, No. 6A), L622–L625 (2002).
    [Crossref]
  12. J. Ueda, P. Dorenbos, A. J. J. Bos, K. Kuroishi, and S. Tanabe, “Control of electron transfer between Ce3+ and Cr3+ in the Y3Al5−xGaxO12 host via conduction band engineering,” J. Mater. Chem. C 3(22), 5642–5651 (2015).
    [Crossref]
  13. J. Xu, J. Ueda, and S. Tanabe, “Design of deep-red persistent phosphors of Gd3Al5-xGaxO12:Cr3+ transparent ceramics sensitized by Eu3+ as an electron trap using conduction band engineering,” Opt. Mater. Express 5(5), 963 (2015).
    [Crossref]
  14. N. Basavaraju, K. R. Priolkar, D. Gourier, A. Bessière, and B. Viana, “Order and disorder around Cr3+ in chromium doped persistent luminescent AB2O4 spinels,” Phys. Chem. Chem. Phys. 17(16), 10993–10999 (2015).
    [Crossref]
  15. Y. Li, Y. Li, R. Chen, K. Sharafudeen, S. Zhou, M. Gecevicius, H. Wang, G. Dong, Y. Wu, X. Qin, and J. Qiu, “Tailoring of the trap distribution and crystal field in Cr3+-doped non-gallate phosphors with near-infrared long-persistence phosphorescence,” NPG Asia Mater. 7(5), e180 (2015).
    [Crossref]
  16. Z. Pan, Y.-Y. Lu, and F. Liu, “Sunlight-activated long-persistent luminescence in the near-infrared from Cr3+-doped zinc gallogermanates,” Nat. Mater. 11(1), 58–63 (2011).
    [Crossref]
  17. T. Maldiney, A. Lecointre, B. Viana, A. Bessière, M. Bessodes, D. Gourier, C. Richard, and D. Scherman, “Controlling electron trap depth to enhance optical properties of persistent luminescence nanoparticles for in vivo imaging,” J. Am. Chem. Soc. 133(30), 11810–11815 (2011).
    [Crossref]
  18. A. Bessière, S. K. Sharma, N. Basavaraju, K. R. Priolkar, L. Binet, B. Viana, A. J. J. Bos, T. Maldiney, C. Richard, D. Scherman, and D. Gourier, “Storage of visible light for long-lasting phosphorescence in chromium-doped zinc gallate,” Chem. Mater. 26(3), 1365–1373 (2014).
    [Crossref]
  19. N. Basavaraju, K. R. Priolkar, D. Gourier, S. K. Sharma, A. Bessière, and B. Viana, “The importance of inversion disorder in the visible light induced persistent luminescence in Cr3+ doped AB2O4 (A = Zn or Mg and B = Ga or Al),” Phys. Chem. Chem. Phys. 17(3), 1790–1799 (2015).
    [Crossref]
  20. K. Van den Eeckhout, A. J. J. Bos, D. Poelman, and P. F. Smet, “Revealing trap depth distributions in persistent phosphors,” Phys. Rev. B 87(4), 045126 (2013).
    [Crossref]
  21. J. Botterman, J. J. Joos, and P. F. Smet, “Trapping and detrapping in SrAl2O4:Eu, Dy persistent phosphors: Influence of excitation wavelength and temperature,” Phys. Rev. B 90(8), 085147 (2014).
    [Crossref]
  22. K. Van den Eeckhout, D. Poelman, and P. Smet, “Persistent luminescence in non-Eu2+-doped compounds: a review,” Materials 6(7), 2789–2818 (2013).
    [Crossref]
  23. K. Van den Eeckhout, P. F. Smet, and D. Poelman, “Persistent luminescence in Eu2+-doped compounds: a review,” Materials 3(4), 2536–2566 (2010).
    [Crossref]

2021 (1)

G. Ram Banjare, D. P. Bisen, N. Brahme, and C. Belodhiya, “Studies on structural properties, luminescence behavior and zeta potential of Dy3+ doped alkaline earth ortho-silicate phosphors,” Mater. Sci. Eng., B 263, 114882 (2021).
[Crossref]

2019 (2)

S. S. B. Nasir, A. Tanaka, S. Yoshiara, and A. Kato, “Luminescence properties of Li2SrSiO4:Eu2+ silicate yellow phosphors with high thermal stability for high-power efficiency white LED application,” J. Lumin. 207, 22–28 (2019).
[Crossref]

Z. Long, Y. Wen, J. Qiu, J. Wang, D. Zhou, C. Zhu, J. Lai, X. Xu, X. Yu, and Q. Wang, “Crystal structure insight aided design of SrGa2Si2O8:Mn2+ with multi-band and thermally stable emission for high-power LED applications,” Chem. Eng. J. 375, 122016 (2019).
[Crossref]

2018 (1)

H. Liao, M. Zhao, M. S. Molokeev, Q. Liu, and Z. Xia, “Learning from a mineral structure toward an ultra-narrow-band blue-emitting silicate phosphor RbNa3(Li3SiO4)4:Eu2+,” Angew. Chem. 130(36), 11902–11905 (2018).
[Crossref]

2017 (1)

T. Sasaki, J. Fukushima, Y. Hayashi, and H. Takizawa, “Synthesis and photoluminescence properties of a novel aluminosilicate Sr3Al10SiO20:Mn4+ red phosphor,” J. Lumin. 188, 101–106 (2017).
[Crossref]

2015 (5)

N. Basavaraju, K. R. Priolkar, D. Gourier, S. K. Sharma, A. Bessière, and B. Viana, “The importance of inversion disorder in the visible light induced persistent luminescence in Cr3+ doped AB2O4 (A = Zn or Mg and B = Ga or Al),” Phys. Chem. Chem. Phys. 17(3), 1790–1799 (2015).
[Crossref]

J. Ueda, P. Dorenbos, A. J. J. Bos, K. Kuroishi, and S. Tanabe, “Control of electron transfer between Ce3+ and Cr3+ in the Y3Al5−xGaxO12 host via conduction band engineering,” J. Mater. Chem. C 3(22), 5642–5651 (2015).
[Crossref]

J. Xu, J. Ueda, and S. Tanabe, “Design of deep-red persistent phosphors of Gd3Al5-xGaxO12:Cr3+ transparent ceramics sensitized by Eu3+ as an electron trap using conduction band engineering,” Opt. Mater. Express 5(5), 963 (2015).
[Crossref]

N. Basavaraju, K. R. Priolkar, D. Gourier, A. Bessière, and B. Viana, “Order and disorder around Cr3+ in chromium doped persistent luminescent AB2O4 spinels,” Phys. Chem. Chem. Phys. 17(16), 10993–10999 (2015).
[Crossref]

Y. Li, Y. Li, R. Chen, K. Sharafudeen, S. Zhou, M. Gecevicius, H. Wang, G. Dong, Y. Wu, X. Qin, and J. Qiu, “Tailoring of the trap distribution and crystal field in Cr3+-doped non-gallate phosphors with near-infrared long-persistence phosphorescence,” NPG Asia Mater. 7(5), e180 (2015).
[Crossref]

2014 (5)

W. Lü, W. Lv, Q. Zhao, M. Jiao, B. Shao, and H. You, “A novel efficient Mn4+ activated Ca14Al10Zn6O35 phosphor: application in red-emitting and white LEDs,” Inorg. Chem. 53(22), 11985–11990 (2014).
[Crossref]

K. Li, D. Geng, M. Shang, Y. Zhang, H. Lian, and J. Lin, “Color-tunable luminescence and energy transfer properties of Ca9Mg(PO4)6F2:Eu2+, Mn2+ phosphors for UV-LEDs,” J. Phys. Chem. C 118(20), 11026–11034 (2014).
[Crossref]

S. Kumar, C. Tessarek, S. Christiansen, and R. Singh, “A comparative study of β-Ga2O3 nanowires grown on different substrates using CVD technique,” J. Alloys Compd. 587, 812–818 (2014).
[Crossref]

J. Botterman, J. J. Joos, and P. F. Smet, “Trapping and detrapping in SrAl2O4:Eu, Dy persistent phosphors: Influence of excitation wavelength and temperature,” Phys. Rev. B 90(8), 085147 (2014).
[Crossref]

A. Bessière, S. K. Sharma, N. Basavaraju, K. R. Priolkar, L. Binet, B. Viana, A. J. J. Bos, T. Maldiney, C. Richard, D. Scherman, and D. Gourier, “Storage of visible light for long-lasting phosphorescence in chromium-doped zinc gallate,” Chem. Mater. 26(3), 1365–1373 (2014).
[Crossref]

2013 (2)

K. Van den Eeckhout, D. Poelman, and P. Smet, “Persistent luminescence in non-Eu2+-doped compounds: a review,” Materials 6(7), 2789–2818 (2013).
[Crossref]

K. Van den Eeckhout, A. J. J. Bos, D. Poelman, and P. F. Smet, “Revealing trap depth distributions in persistent phosphors,” Phys. Rev. B 87(4), 045126 (2013).
[Crossref]

2012 (1)

W.-R. Liu, C.-H. Huang, C.-W. Yeh, J.-C. Tsai, Y.-C. Chiu, Y.-T. Yeh, and R.-S. Liu, “A Study on the Luminescence and Energy Transfer of Single-Phase and Color-Tunable KCaY(PO4)2:Eu2+, Mn2+ phosphor for application in white-light LEDs,” Inorg. Chem. 51(18), 9636–9641 (2012).
[Crossref]

2011 (2)

Z. Pan, Y.-Y. Lu, and F. Liu, “Sunlight-activated long-persistent luminescence in the near-infrared from Cr3+-doped zinc gallogermanates,” Nat. Mater. 11(1), 58–63 (2011).
[Crossref]

T. Maldiney, A. Lecointre, B. Viana, A. Bessière, M. Bessodes, D. Gourier, C. Richard, and D. Scherman, “Controlling electron trap depth to enhance optical properties of persistent luminescence nanoparticles for in vivo imaging,” J. Am. Chem. Soc. 133(30), 11810–11815 (2011).
[Crossref]

2010 (1)

K. Van den Eeckhout, P. F. Smet, and D. Poelman, “Persistent luminescence in Eu2+-doped compounds: a review,” Materials 3(4), 2536–2566 (2010).
[Crossref]

2006 (1)

J. Zhang, B. Li, C. Xia, G. Pei, Q. Deng, Z. Yang, W. Xu, H. Shi, F. Wu, Y. Wu, and J. Xu, “Growth and spectral characterization of β-Ga2O3 single crystals,” J. Phys. Chem. Solids 67(12), 2448–2451 (2006).
[Crossref]

2002 (1)

E. G. Víllora, M. Yamaga, T. Inoue, S. Yabasi, Y. Masui, T. Sugawara, and T. Fukuda, “Optical spectroscopy study on β-Ga2O3,” Jpn. J. Appl. Phys. 41(Part 2, No. 6A), L622–L625 (2002).
[Crossref]

Basavaraju, N.

N. Basavaraju, K. R. Priolkar, D. Gourier, A. Bessière, and B. Viana, “Order and disorder around Cr3+ in chromium doped persistent luminescent AB2O4 spinels,” Phys. Chem. Chem. Phys. 17(16), 10993–10999 (2015).
[Crossref]

N. Basavaraju, K. R. Priolkar, D. Gourier, S. K. Sharma, A. Bessière, and B. Viana, “The importance of inversion disorder in the visible light induced persistent luminescence in Cr3+ doped AB2O4 (A = Zn or Mg and B = Ga or Al),” Phys. Chem. Chem. Phys. 17(3), 1790–1799 (2015).
[Crossref]

A. Bessière, S. K. Sharma, N. Basavaraju, K. R. Priolkar, L. Binet, B. Viana, A. J. J. Bos, T. Maldiney, C. Richard, D. Scherman, and D. Gourier, “Storage of visible light for long-lasting phosphorescence in chromium-doped zinc gallate,” Chem. Mater. 26(3), 1365–1373 (2014).
[Crossref]

Belodhiya, C.

G. Ram Banjare, D. P. Bisen, N. Brahme, and C. Belodhiya, “Studies on structural properties, luminescence behavior and zeta potential of Dy3+ doped alkaline earth ortho-silicate phosphors,” Mater. Sci. Eng., B 263, 114882 (2021).
[Crossref]

Bessière, A.

N. Basavaraju, K. R. Priolkar, D. Gourier, A. Bessière, and B. Viana, “Order and disorder around Cr3+ in chromium doped persistent luminescent AB2O4 spinels,” Phys. Chem. Chem. Phys. 17(16), 10993–10999 (2015).
[Crossref]

N. Basavaraju, K. R. Priolkar, D. Gourier, S. K. Sharma, A. Bessière, and B. Viana, “The importance of inversion disorder in the visible light induced persistent luminescence in Cr3+ doped AB2O4 (A = Zn or Mg and B = Ga or Al),” Phys. Chem. Chem. Phys. 17(3), 1790–1799 (2015).
[Crossref]

A. Bessière, S. K. Sharma, N. Basavaraju, K. R. Priolkar, L. Binet, B. Viana, A. J. J. Bos, T. Maldiney, C. Richard, D. Scherman, and D. Gourier, “Storage of visible light for long-lasting phosphorescence in chromium-doped zinc gallate,” Chem. Mater. 26(3), 1365–1373 (2014).
[Crossref]

T. Maldiney, A. Lecointre, B. Viana, A. Bessière, M. Bessodes, D. Gourier, C. Richard, and D. Scherman, “Controlling electron trap depth to enhance optical properties of persistent luminescence nanoparticles for in vivo imaging,” J. Am. Chem. Soc. 133(30), 11810–11815 (2011).
[Crossref]

Bessodes, M.

T. Maldiney, A. Lecointre, B. Viana, A. Bessière, M. Bessodes, D. Gourier, C. Richard, and D. Scherman, “Controlling electron trap depth to enhance optical properties of persistent luminescence nanoparticles for in vivo imaging,” J. Am. Chem. Soc. 133(30), 11810–11815 (2011).
[Crossref]

Binet, L.

A. Bessière, S. K. Sharma, N. Basavaraju, K. R. Priolkar, L. Binet, B. Viana, A. J. J. Bos, T. Maldiney, C. Richard, D. Scherman, and D. Gourier, “Storage of visible light for long-lasting phosphorescence in chromium-doped zinc gallate,” Chem. Mater. 26(3), 1365–1373 (2014).
[Crossref]

Bisen, D. P.

G. Ram Banjare, D. P. Bisen, N. Brahme, and C. Belodhiya, “Studies on structural properties, luminescence behavior and zeta potential of Dy3+ doped alkaline earth ortho-silicate phosphors,” Mater. Sci. Eng., B 263, 114882 (2021).
[Crossref]

Bos, A. J. J.

J. Ueda, P. Dorenbos, A. J. J. Bos, K. Kuroishi, and S. Tanabe, “Control of electron transfer between Ce3+ and Cr3+ in the Y3Al5−xGaxO12 host via conduction band engineering,” J. Mater. Chem. C 3(22), 5642–5651 (2015).
[Crossref]

A. Bessière, S. K. Sharma, N. Basavaraju, K. R. Priolkar, L. Binet, B. Viana, A. J. J. Bos, T. Maldiney, C. Richard, D. Scherman, and D. Gourier, “Storage of visible light for long-lasting phosphorescence in chromium-doped zinc gallate,” Chem. Mater. 26(3), 1365–1373 (2014).
[Crossref]

K. Van den Eeckhout, A. J. J. Bos, D. Poelman, and P. F. Smet, “Revealing trap depth distributions in persistent phosphors,” Phys. Rev. B 87(4), 045126 (2013).
[Crossref]

Botterman, J.

J. Botterman, J. J. Joos, and P. F. Smet, “Trapping and detrapping in SrAl2O4:Eu, Dy persistent phosphors: Influence of excitation wavelength and temperature,” Phys. Rev. B 90(8), 085147 (2014).
[Crossref]

Brahme, N.

G. Ram Banjare, D. P. Bisen, N. Brahme, and C. Belodhiya, “Studies on structural properties, luminescence behavior and zeta potential of Dy3+ doped alkaline earth ortho-silicate phosphors,” Mater. Sci. Eng., B 263, 114882 (2021).
[Crossref]

Chen, R.

Y. Li, Y. Li, R. Chen, K. Sharafudeen, S. Zhou, M. Gecevicius, H. Wang, G. Dong, Y. Wu, X. Qin, and J. Qiu, “Tailoring of the trap distribution and crystal field in Cr3+-doped non-gallate phosphors with near-infrared long-persistence phosphorescence,” NPG Asia Mater. 7(5), e180 (2015).
[Crossref]

Chiu, Y.-C.

W.-R. Liu, C.-H. Huang, C.-W. Yeh, J.-C. Tsai, Y.-C. Chiu, Y.-T. Yeh, and R.-S. Liu, “A Study on the Luminescence and Energy Transfer of Single-Phase and Color-Tunable KCaY(PO4)2:Eu2+, Mn2+ phosphor for application in white-light LEDs,” Inorg. Chem. 51(18), 9636–9641 (2012).
[Crossref]

Christiansen, S.

S. Kumar, C. Tessarek, S. Christiansen, and R. Singh, “A comparative study of β-Ga2O3 nanowires grown on different substrates using CVD technique,” J. Alloys Compd. 587, 812–818 (2014).
[Crossref]

Deng, Q.

J. Zhang, B. Li, C. Xia, G. Pei, Q. Deng, Z. Yang, W. Xu, H. Shi, F. Wu, Y. Wu, and J. Xu, “Growth and spectral characterization of β-Ga2O3 single crystals,” J. Phys. Chem. Solids 67(12), 2448–2451 (2006).
[Crossref]

Dong, G.

Y. Li, Y. Li, R. Chen, K. Sharafudeen, S. Zhou, M. Gecevicius, H. Wang, G. Dong, Y. Wu, X. Qin, and J. Qiu, “Tailoring of the trap distribution and crystal field in Cr3+-doped non-gallate phosphors with near-infrared long-persistence phosphorescence,” NPG Asia Mater. 7(5), e180 (2015).
[Crossref]

Dorenbos, P.

J. Ueda, P. Dorenbos, A. J. J. Bos, K. Kuroishi, and S. Tanabe, “Control of electron transfer between Ce3+ and Cr3+ in the Y3Al5−xGaxO12 host via conduction band engineering,” J. Mater. Chem. C 3(22), 5642–5651 (2015).
[Crossref]

Fukuda, T.

E. G. Víllora, M. Yamaga, T. Inoue, S. Yabasi, Y. Masui, T. Sugawara, and T. Fukuda, “Optical spectroscopy study on β-Ga2O3,” Jpn. J. Appl. Phys. 41(Part 2, No. 6A), L622–L625 (2002).
[Crossref]

Fukushima, J.

T. Sasaki, J. Fukushima, Y. Hayashi, and H. Takizawa, “Synthesis and photoluminescence properties of a novel aluminosilicate Sr3Al10SiO20:Mn4+ red phosphor,” J. Lumin. 188, 101–106 (2017).
[Crossref]

Gecevicius, M.

Y. Li, Y. Li, R. Chen, K. Sharafudeen, S. Zhou, M. Gecevicius, H. Wang, G. Dong, Y. Wu, X. Qin, and J. Qiu, “Tailoring of the trap distribution and crystal field in Cr3+-doped non-gallate phosphors with near-infrared long-persistence phosphorescence,” NPG Asia Mater. 7(5), e180 (2015).
[Crossref]

Geng, D.

K. Li, D. Geng, M. Shang, Y. Zhang, H. Lian, and J. Lin, “Color-tunable luminescence and energy transfer properties of Ca9Mg(PO4)6F2:Eu2+, Mn2+ phosphors for UV-LEDs,” J. Phys. Chem. C 118(20), 11026–11034 (2014).
[Crossref]

Gourier, D.

N. Basavaraju, K. R. Priolkar, D. Gourier, A. Bessière, and B. Viana, “Order and disorder around Cr3+ in chromium doped persistent luminescent AB2O4 spinels,” Phys. Chem. Chem. Phys. 17(16), 10993–10999 (2015).
[Crossref]

N. Basavaraju, K. R. Priolkar, D. Gourier, S. K. Sharma, A. Bessière, and B. Viana, “The importance of inversion disorder in the visible light induced persistent luminescence in Cr3+ doped AB2O4 (A = Zn or Mg and B = Ga or Al),” Phys. Chem. Chem. Phys. 17(3), 1790–1799 (2015).
[Crossref]

A. Bessière, S. K. Sharma, N. Basavaraju, K. R. Priolkar, L. Binet, B. Viana, A. J. J. Bos, T. Maldiney, C. Richard, D. Scherman, and D. Gourier, “Storage of visible light for long-lasting phosphorescence in chromium-doped zinc gallate,” Chem. Mater. 26(3), 1365–1373 (2014).
[Crossref]

T. Maldiney, A. Lecointre, B. Viana, A. Bessière, M. Bessodes, D. Gourier, C. Richard, and D. Scherman, “Controlling electron trap depth to enhance optical properties of persistent luminescence nanoparticles for in vivo imaging,” J. Am. Chem. Soc. 133(30), 11810–11815 (2011).
[Crossref]

Hayashi, Y.

T. Sasaki, J. Fukushima, Y. Hayashi, and H. Takizawa, “Synthesis and photoluminescence properties of a novel aluminosilicate Sr3Al10SiO20:Mn4+ red phosphor,” J. Lumin. 188, 101–106 (2017).
[Crossref]

Huang, C.-H.

W.-R. Liu, C.-H. Huang, C.-W. Yeh, J.-C. Tsai, Y.-C. Chiu, Y.-T. Yeh, and R.-S. Liu, “A Study on the Luminescence and Energy Transfer of Single-Phase and Color-Tunable KCaY(PO4)2:Eu2+, Mn2+ phosphor for application in white-light LEDs,” Inorg. Chem. 51(18), 9636–9641 (2012).
[Crossref]

Inoue, T.

E. G. Víllora, M. Yamaga, T. Inoue, S. Yabasi, Y. Masui, T. Sugawara, and T. Fukuda, “Optical spectroscopy study on β-Ga2O3,” Jpn. J. Appl. Phys. 41(Part 2, No. 6A), L622–L625 (2002).
[Crossref]

Jiao, M.

W. Lü, W. Lv, Q. Zhao, M. Jiao, B. Shao, and H. You, “A novel efficient Mn4+ activated Ca14Al10Zn6O35 phosphor: application in red-emitting and white LEDs,” Inorg. Chem. 53(22), 11985–11990 (2014).
[Crossref]

Joos, J. J.

J. Botterman, J. J. Joos, and P. F. Smet, “Trapping and detrapping in SrAl2O4:Eu, Dy persistent phosphors: Influence of excitation wavelength and temperature,” Phys. Rev. B 90(8), 085147 (2014).
[Crossref]

Kato, A.

S. S. B. Nasir, A. Tanaka, S. Yoshiara, and A. Kato, “Luminescence properties of Li2SrSiO4:Eu2+ silicate yellow phosphors with high thermal stability for high-power efficiency white LED application,” J. Lumin. 207, 22–28 (2019).
[Crossref]

Kumar, S.

S. Kumar, C. Tessarek, S. Christiansen, and R. Singh, “A comparative study of β-Ga2O3 nanowires grown on different substrates using CVD technique,” J. Alloys Compd. 587, 812–818 (2014).
[Crossref]

Kuroishi, K.

J. Ueda, P. Dorenbos, A. J. J. Bos, K. Kuroishi, and S. Tanabe, “Control of electron transfer between Ce3+ and Cr3+ in the Y3Al5−xGaxO12 host via conduction band engineering,” J. Mater. Chem. C 3(22), 5642–5651 (2015).
[Crossref]

Lai, J.

Z. Long, Y. Wen, J. Qiu, J. Wang, D. Zhou, C. Zhu, J. Lai, X. Xu, X. Yu, and Q. Wang, “Crystal structure insight aided design of SrGa2Si2O8:Mn2+ with multi-band and thermally stable emission for high-power LED applications,” Chem. Eng. J. 375, 122016 (2019).
[Crossref]

Lecointre, A.

T. Maldiney, A. Lecointre, B. Viana, A. Bessière, M. Bessodes, D. Gourier, C. Richard, and D. Scherman, “Controlling electron trap depth to enhance optical properties of persistent luminescence nanoparticles for in vivo imaging,” J. Am. Chem. Soc. 133(30), 11810–11815 (2011).
[Crossref]

Li, B.

J. Zhang, B. Li, C. Xia, G. Pei, Q. Deng, Z. Yang, W. Xu, H. Shi, F. Wu, Y. Wu, and J. Xu, “Growth and spectral characterization of β-Ga2O3 single crystals,” J. Phys. Chem. Solids 67(12), 2448–2451 (2006).
[Crossref]

Li, K.

K. Li, D. Geng, M. Shang, Y. Zhang, H. Lian, and J. Lin, “Color-tunable luminescence and energy transfer properties of Ca9Mg(PO4)6F2:Eu2+, Mn2+ phosphors for UV-LEDs,” J. Phys. Chem. C 118(20), 11026–11034 (2014).
[Crossref]

Li, Y.

Y. Li, Y. Li, R. Chen, K. Sharafudeen, S. Zhou, M. Gecevicius, H. Wang, G. Dong, Y. Wu, X. Qin, and J. Qiu, “Tailoring of the trap distribution and crystal field in Cr3+-doped non-gallate phosphors with near-infrared long-persistence phosphorescence,” NPG Asia Mater. 7(5), e180 (2015).
[Crossref]

Y. Li, Y. Li, R. Chen, K. Sharafudeen, S. Zhou, M. Gecevicius, H. Wang, G. Dong, Y. Wu, X. Qin, and J. Qiu, “Tailoring of the trap distribution and crystal field in Cr3+-doped non-gallate phosphors with near-infrared long-persistence phosphorescence,” NPG Asia Mater. 7(5), e180 (2015).
[Crossref]

Lian, H.

K. Li, D. Geng, M. Shang, Y. Zhang, H. Lian, and J. Lin, “Color-tunable luminescence and energy transfer properties of Ca9Mg(PO4)6F2:Eu2+, Mn2+ phosphors for UV-LEDs,” J. Phys. Chem. C 118(20), 11026–11034 (2014).
[Crossref]

Liao, H.

H. Liao, M. Zhao, M. S. Molokeev, Q. Liu, and Z. Xia, “Learning from a mineral structure toward an ultra-narrow-band blue-emitting silicate phosphor RbNa3(Li3SiO4)4:Eu2+,” Angew. Chem. 130(36), 11902–11905 (2018).
[Crossref]

Lin, J.

K. Li, D. Geng, M. Shang, Y. Zhang, H. Lian, and J. Lin, “Color-tunable luminescence and energy transfer properties of Ca9Mg(PO4)6F2:Eu2+, Mn2+ phosphors for UV-LEDs,” J. Phys. Chem. C 118(20), 11026–11034 (2014).
[Crossref]

Liu, F.

Z. Pan, Y.-Y. Lu, and F. Liu, “Sunlight-activated long-persistent luminescence in the near-infrared from Cr3+-doped zinc gallogermanates,” Nat. Mater. 11(1), 58–63 (2011).
[Crossref]

Liu, Q.

H. Liao, M. Zhao, M. S. Molokeev, Q. Liu, and Z. Xia, “Learning from a mineral structure toward an ultra-narrow-band blue-emitting silicate phosphor RbNa3(Li3SiO4)4:Eu2+,” Angew. Chem. 130(36), 11902–11905 (2018).
[Crossref]

Liu, R.-S.

W.-R. Liu, C.-H. Huang, C.-W. Yeh, J.-C. Tsai, Y.-C. Chiu, Y.-T. Yeh, and R.-S. Liu, “A Study on the Luminescence and Energy Transfer of Single-Phase and Color-Tunable KCaY(PO4)2:Eu2+, Mn2+ phosphor for application in white-light LEDs,” Inorg. Chem. 51(18), 9636–9641 (2012).
[Crossref]

Liu, W.-R.

W.-R. Liu, C.-H. Huang, C.-W. Yeh, J.-C. Tsai, Y.-C. Chiu, Y.-T. Yeh, and R.-S. Liu, “A Study on the Luminescence and Energy Transfer of Single-Phase and Color-Tunable KCaY(PO4)2:Eu2+, Mn2+ phosphor for application in white-light LEDs,” Inorg. Chem. 51(18), 9636–9641 (2012).
[Crossref]

Long, Z.

Z. Long, Y. Wen, J. Qiu, J. Wang, D. Zhou, C. Zhu, J. Lai, X. Xu, X. Yu, and Q. Wang, “Crystal structure insight aided design of SrGa2Si2O8:Mn2+ with multi-band and thermally stable emission for high-power LED applications,” Chem. Eng. J. 375, 122016 (2019).
[Crossref]

Lu, Y.-Y.

Z. Pan, Y.-Y. Lu, and F. Liu, “Sunlight-activated long-persistent luminescence in the near-infrared from Cr3+-doped zinc gallogermanates,” Nat. Mater. 11(1), 58–63 (2011).
[Crossref]

Lü, W.

W. Lü, W. Lv, Q. Zhao, M. Jiao, B. Shao, and H. You, “A novel efficient Mn4+ activated Ca14Al10Zn6O35 phosphor: application in red-emitting and white LEDs,” Inorg. Chem. 53(22), 11985–11990 (2014).
[Crossref]

Lv, W.

W. Lü, W. Lv, Q. Zhao, M. Jiao, B. Shao, and H. You, “A novel efficient Mn4+ activated Ca14Al10Zn6O35 phosphor: application in red-emitting and white LEDs,” Inorg. Chem. 53(22), 11985–11990 (2014).
[Crossref]

Maldiney, T.

A. Bessière, S. K. Sharma, N. Basavaraju, K. R. Priolkar, L. Binet, B. Viana, A. J. J. Bos, T. Maldiney, C. Richard, D. Scherman, and D. Gourier, “Storage of visible light for long-lasting phosphorescence in chromium-doped zinc gallate,” Chem. Mater. 26(3), 1365–1373 (2014).
[Crossref]

T. Maldiney, A. Lecointre, B. Viana, A. Bessière, M. Bessodes, D. Gourier, C. Richard, and D. Scherman, “Controlling electron trap depth to enhance optical properties of persistent luminescence nanoparticles for in vivo imaging,” J. Am. Chem. Soc. 133(30), 11810–11815 (2011).
[Crossref]

Masui, Y.

E. G. Víllora, M. Yamaga, T. Inoue, S. Yabasi, Y. Masui, T. Sugawara, and T. Fukuda, “Optical spectroscopy study on β-Ga2O3,” Jpn. J. Appl. Phys. 41(Part 2, No. 6A), L622–L625 (2002).
[Crossref]

Molokeev, M. S.

H. Liao, M. Zhao, M. S. Molokeev, Q. Liu, and Z. Xia, “Learning from a mineral structure toward an ultra-narrow-band blue-emitting silicate phosphor RbNa3(Li3SiO4)4:Eu2+,” Angew. Chem. 130(36), 11902–11905 (2018).
[Crossref]

Nasir, S. S. B.

S. S. B. Nasir, A. Tanaka, S. Yoshiara, and A. Kato, “Luminescence properties of Li2SrSiO4:Eu2+ silicate yellow phosphors with high thermal stability for high-power efficiency white LED application,” J. Lumin. 207, 22–28 (2019).
[Crossref]

Pan, Z.

Z. Pan, Y.-Y. Lu, and F. Liu, “Sunlight-activated long-persistent luminescence in the near-infrared from Cr3+-doped zinc gallogermanates,” Nat. Mater. 11(1), 58–63 (2011).
[Crossref]

Pei, G.

J. Zhang, B. Li, C. Xia, G. Pei, Q. Deng, Z. Yang, W. Xu, H. Shi, F. Wu, Y. Wu, and J. Xu, “Growth and spectral characterization of β-Ga2O3 single crystals,” J. Phys. Chem. Solids 67(12), 2448–2451 (2006).
[Crossref]

Poelman, D.

K. Van den Eeckhout, A. J. J. Bos, D. Poelman, and P. F. Smet, “Revealing trap depth distributions in persistent phosphors,” Phys. Rev. B 87(4), 045126 (2013).
[Crossref]

K. Van den Eeckhout, D. Poelman, and P. Smet, “Persistent luminescence in non-Eu2+-doped compounds: a review,” Materials 6(7), 2789–2818 (2013).
[Crossref]

K. Van den Eeckhout, P. F. Smet, and D. Poelman, “Persistent luminescence in Eu2+-doped compounds: a review,” Materials 3(4), 2536–2566 (2010).
[Crossref]

Priolkar, K. R.

N. Basavaraju, K. R. Priolkar, D. Gourier, S. K. Sharma, A. Bessière, and B. Viana, “The importance of inversion disorder in the visible light induced persistent luminescence in Cr3+ doped AB2O4 (A = Zn or Mg and B = Ga or Al),” Phys. Chem. Chem. Phys. 17(3), 1790–1799 (2015).
[Crossref]

N. Basavaraju, K. R. Priolkar, D. Gourier, A. Bessière, and B. Viana, “Order and disorder around Cr3+ in chromium doped persistent luminescent AB2O4 spinels,” Phys. Chem. Chem. Phys. 17(16), 10993–10999 (2015).
[Crossref]

A. Bessière, S. K. Sharma, N. Basavaraju, K. R. Priolkar, L. Binet, B. Viana, A. J. J. Bos, T. Maldiney, C. Richard, D. Scherman, and D. Gourier, “Storage of visible light for long-lasting phosphorescence in chromium-doped zinc gallate,” Chem. Mater. 26(3), 1365–1373 (2014).
[Crossref]

Qin, X.

Y. Li, Y. Li, R. Chen, K. Sharafudeen, S. Zhou, M. Gecevicius, H. Wang, G. Dong, Y. Wu, X. Qin, and J. Qiu, “Tailoring of the trap distribution and crystal field in Cr3+-doped non-gallate phosphors with near-infrared long-persistence phosphorescence,” NPG Asia Mater. 7(5), e180 (2015).
[Crossref]

Qiu, J.

Z. Long, Y. Wen, J. Qiu, J. Wang, D. Zhou, C. Zhu, J. Lai, X. Xu, X. Yu, and Q. Wang, “Crystal structure insight aided design of SrGa2Si2O8:Mn2+ with multi-band and thermally stable emission for high-power LED applications,” Chem. Eng. J. 375, 122016 (2019).
[Crossref]

Y. Li, Y. Li, R. Chen, K. Sharafudeen, S. Zhou, M. Gecevicius, H. Wang, G. Dong, Y. Wu, X. Qin, and J. Qiu, “Tailoring of the trap distribution and crystal field in Cr3+-doped non-gallate phosphors with near-infrared long-persistence phosphorescence,” NPG Asia Mater. 7(5), e180 (2015).
[Crossref]

Ram Banjare, G.

G. Ram Banjare, D. P. Bisen, N. Brahme, and C. Belodhiya, “Studies on structural properties, luminescence behavior and zeta potential of Dy3+ doped alkaline earth ortho-silicate phosphors,” Mater. Sci. Eng., B 263, 114882 (2021).
[Crossref]

Richard, C.

A. Bessière, S. K. Sharma, N. Basavaraju, K. R. Priolkar, L. Binet, B. Viana, A. J. J. Bos, T. Maldiney, C. Richard, D. Scherman, and D. Gourier, “Storage of visible light for long-lasting phosphorescence in chromium-doped zinc gallate,” Chem. Mater. 26(3), 1365–1373 (2014).
[Crossref]

T. Maldiney, A. Lecointre, B. Viana, A. Bessière, M. Bessodes, D. Gourier, C. Richard, and D. Scherman, “Controlling electron trap depth to enhance optical properties of persistent luminescence nanoparticles for in vivo imaging,” J. Am. Chem. Soc. 133(30), 11810–11815 (2011).
[Crossref]

Sasaki, T.

T. Sasaki, J. Fukushima, Y. Hayashi, and H. Takizawa, “Synthesis and photoluminescence properties of a novel aluminosilicate Sr3Al10SiO20:Mn4+ red phosphor,” J. Lumin. 188, 101–106 (2017).
[Crossref]

Scherman, D.

A. Bessière, S. K. Sharma, N. Basavaraju, K. R. Priolkar, L. Binet, B. Viana, A. J. J. Bos, T. Maldiney, C. Richard, D. Scherman, and D. Gourier, “Storage of visible light for long-lasting phosphorescence in chromium-doped zinc gallate,” Chem. Mater. 26(3), 1365–1373 (2014).
[Crossref]

T. Maldiney, A. Lecointre, B. Viana, A. Bessière, M. Bessodes, D. Gourier, C. Richard, and D. Scherman, “Controlling electron trap depth to enhance optical properties of persistent luminescence nanoparticles for in vivo imaging,” J. Am. Chem. Soc. 133(30), 11810–11815 (2011).
[Crossref]

Shang, M.

K. Li, D. Geng, M. Shang, Y. Zhang, H. Lian, and J. Lin, “Color-tunable luminescence and energy transfer properties of Ca9Mg(PO4)6F2:Eu2+, Mn2+ phosphors for UV-LEDs,” J. Phys. Chem. C 118(20), 11026–11034 (2014).
[Crossref]

Shao, B.

W. Lü, W. Lv, Q. Zhao, M. Jiao, B. Shao, and H. You, “A novel efficient Mn4+ activated Ca14Al10Zn6O35 phosphor: application in red-emitting and white LEDs,” Inorg. Chem. 53(22), 11985–11990 (2014).
[Crossref]

Sharafudeen, K.

Y. Li, Y. Li, R. Chen, K. Sharafudeen, S. Zhou, M. Gecevicius, H. Wang, G. Dong, Y. Wu, X. Qin, and J. Qiu, “Tailoring of the trap distribution and crystal field in Cr3+-doped non-gallate phosphors with near-infrared long-persistence phosphorescence,” NPG Asia Mater. 7(5), e180 (2015).
[Crossref]

Sharma, S. K.

N. Basavaraju, K. R. Priolkar, D. Gourier, S. K. Sharma, A. Bessière, and B. Viana, “The importance of inversion disorder in the visible light induced persistent luminescence in Cr3+ doped AB2O4 (A = Zn or Mg and B = Ga or Al),” Phys. Chem. Chem. Phys. 17(3), 1790–1799 (2015).
[Crossref]

A. Bessière, S. K. Sharma, N. Basavaraju, K. R. Priolkar, L. Binet, B. Viana, A. J. J. Bos, T. Maldiney, C. Richard, D. Scherman, and D. Gourier, “Storage of visible light for long-lasting phosphorescence in chromium-doped zinc gallate,” Chem. Mater. 26(3), 1365–1373 (2014).
[Crossref]

Shi, H.

J. Zhang, B. Li, C. Xia, G. Pei, Q. Deng, Z. Yang, W. Xu, H. Shi, F. Wu, Y. Wu, and J. Xu, “Growth and spectral characterization of β-Ga2O3 single crystals,” J. Phys. Chem. Solids 67(12), 2448–2451 (2006).
[Crossref]

Singh, R.

S. Kumar, C. Tessarek, S. Christiansen, and R. Singh, “A comparative study of β-Ga2O3 nanowires grown on different substrates using CVD technique,” J. Alloys Compd. 587, 812–818 (2014).
[Crossref]

Smet, P.

K. Van den Eeckhout, D. Poelman, and P. Smet, “Persistent luminescence in non-Eu2+-doped compounds: a review,” Materials 6(7), 2789–2818 (2013).
[Crossref]

Smet, P. F.

J. Botterman, J. J. Joos, and P. F. Smet, “Trapping and detrapping in SrAl2O4:Eu, Dy persistent phosphors: Influence of excitation wavelength and temperature,” Phys. Rev. B 90(8), 085147 (2014).
[Crossref]

K. Van den Eeckhout, A. J. J. Bos, D. Poelman, and P. F. Smet, “Revealing trap depth distributions in persistent phosphors,” Phys. Rev. B 87(4), 045126 (2013).
[Crossref]

K. Van den Eeckhout, P. F. Smet, and D. Poelman, “Persistent luminescence in Eu2+-doped compounds: a review,” Materials 3(4), 2536–2566 (2010).
[Crossref]

Sugawara, T.

E. G. Víllora, M. Yamaga, T. Inoue, S. Yabasi, Y. Masui, T. Sugawara, and T. Fukuda, “Optical spectroscopy study on β-Ga2O3,” Jpn. J. Appl. Phys. 41(Part 2, No. 6A), L622–L625 (2002).
[Crossref]

Takizawa, H.

T. Sasaki, J. Fukushima, Y. Hayashi, and H. Takizawa, “Synthesis and photoluminescence properties of a novel aluminosilicate Sr3Al10SiO20:Mn4+ red phosphor,” J. Lumin. 188, 101–106 (2017).
[Crossref]

Tanabe, S.

J. Ueda, P. Dorenbos, A. J. J. Bos, K. Kuroishi, and S. Tanabe, “Control of electron transfer between Ce3+ and Cr3+ in the Y3Al5−xGaxO12 host via conduction band engineering,” J. Mater. Chem. C 3(22), 5642–5651 (2015).
[Crossref]

J. Xu, J. Ueda, and S. Tanabe, “Design of deep-red persistent phosphors of Gd3Al5-xGaxO12:Cr3+ transparent ceramics sensitized by Eu3+ as an electron trap using conduction band engineering,” Opt. Mater. Express 5(5), 963 (2015).
[Crossref]

Tanaka, A.

S. S. B. Nasir, A. Tanaka, S. Yoshiara, and A. Kato, “Luminescence properties of Li2SrSiO4:Eu2+ silicate yellow phosphors with high thermal stability for high-power efficiency white LED application,” J. Lumin. 207, 22–28 (2019).
[Crossref]

Tessarek, C.

S. Kumar, C. Tessarek, S. Christiansen, and R. Singh, “A comparative study of β-Ga2O3 nanowires grown on different substrates using CVD technique,” J. Alloys Compd. 587, 812–818 (2014).
[Crossref]

Tsai, J.-C.

W.-R. Liu, C.-H. Huang, C.-W. Yeh, J.-C. Tsai, Y.-C. Chiu, Y.-T. Yeh, and R.-S. Liu, “A Study on the Luminescence and Energy Transfer of Single-Phase and Color-Tunable KCaY(PO4)2:Eu2+, Mn2+ phosphor for application in white-light LEDs,” Inorg. Chem. 51(18), 9636–9641 (2012).
[Crossref]

Ueda, J.

J. Ueda, P. Dorenbos, A. J. J. Bos, K. Kuroishi, and S. Tanabe, “Control of electron transfer between Ce3+ and Cr3+ in the Y3Al5−xGaxO12 host via conduction band engineering,” J. Mater. Chem. C 3(22), 5642–5651 (2015).
[Crossref]

J. Xu, J. Ueda, and S. Tanabe, “Design of deep-red persistent phosphors of Gd3Al5-xGaxO12:Cr3+ transparent ceramics sensitized by Eu3+ as an electron trap using conduction band engineering,” Opt. Mater. Express 5(5), 963 (2015).
[Crossref]

Van den Eeckhout, K.

K. Van den Eeckhout, A. J. J. Bos, D. Poelman, and P. F. Smet, “Revealing trap depth distributions in persistent phosphors,” Phys. Rev. B 87(4), 045126 (2013).
[Crossref]

K. Van den Eeckhout, D. Poelman, and P. Smet, “Persistent luminescence in non-Eu2+-doped compounds: a review,” Materials 6(7), 2789–2818 (2013).
[Crossref]

K. Van den Eeckhout, P. F. Smet, and D. Poelman, “Persistent luminescence in Eu2+-doped compounds: a review,” Materials 3(4), 2536–2566 (2010).
[Crossref]

Viana, B.

N. Basavaraju, K. R. Priolkar, D. Gourier, S. K. Sharma, A. Bessière, and B. Viana, “The importance of inversion disorder in the visible light induced persistent luminescence in Cr3+ doped AB2O4 (A = Zn or Mg and B = Ga or Al),” Phys. Chem. Chem. Phys. 17(3), 1790–1799 (2015).
[Crossref]

N. Basavaraju, K. R. Priolkar, D. Gourier, A. Bessière, and B. Viana, “Order and disorder around Cr3+ in chromium doped persistent luminescent AB2O4 spinels,” Phys. Chem. Chem. Phys. 17(16), 10993–10999 (2015).
[Crossref]

A. Bessière, S. K. Sharma, N. Basavaraju, K. R. Priolkar, L. Binet, B. Viana, A. J. J. Bos, T. Maldiney, C. Richard, D. Scherman, and D. Gourier, “Storage of visible light for long-lasting phosphorescence in chromium-doped zinc gallate,” Chem. Mater. 26(3), 1365–1373 (2014).
[Crossref]

T. Maldiney, A. Lecointre, B. Viana, A. Bessière, M. Bessodes, D. Gourier, C. Richard, and D. Scherman, “Controlling electron trap depth to enhance optical properties of persistent luminescence nanoparticles for in vivo imaging,” J. Am. Chem. Soc. 133(30), 11810–11815 (2011).
[Crossref]

Víllora, E. G.

E. G. Víllora, M. Yamaga, T. Inoue, S. Yabasi, Y. Masui, T. Sugawara, and T. Fukuda, “Optical spectroscopy study on β-Ga2O3,” Jpn. J. Appl. Phys. 41(Part 2, No. 6A), L622–L625 (2002).
[Crossref]

Wang, H.

Y. Li, Y. Li, R. Chen, K. Sharafudeen, S. Zhou, M. Gecevicius, H. Wang, G. Dong, Y. Wu, X. Qin, and J. Qiu, “Tailoring of the trap distribution and crystal field in Cr3+-doped non-gallate phosphors with near-infrared long-persistence phosphorescence,” NPG Asia Mater. 7(5), e180 (2015).
[Crossref]

Wang, J.

Z. Long, Y. Wen, J. Qiu, J. Wang, D. Zhou, C. Zhu, J. Lai, X. Xu, X. Yu, and Q. Wang, “Crystal structure insight aided design of SrGa2Si2O8:Mn2+ with multi-band and thermally stable emission for high-power LED applications,” Chem. Eng. J. 375, 122016 (2019).
[Crossref]

Wang, Q.

Z. Long, Y. Wen, J. Qiu, J. Wang, D. Zhou, C. Zhu, J. Lai, X. Xu, X. Yu, and Q. Wang, “Crystal structure insight aided design of SrGa2Si2O8:Mn2+ with multi-band and thermally stable emission for high-power LED applications,” Chem. Eng. J. 375, 122016 (2019).
[Crossref]

Wen, Y.

Z. Long, Y. Wen, J. Qiu, J. Wang, D. Zhou, C. Zhu, J. Lai, X. Xu, X. Yu, and Q. Wang, “Crystal structure insight aided design of SrGa2Si2O8:Mn2+ with multi-band and thermally stable emission for high-power LED applications,” Chem. Eng. J. 375, 122016 (2019).
[Crossref]

Wu, F.

J. Zhang, B. Li, C. Xia, G. Pei, Q. Deng, Z. Yang, W. Xu, H. Shi, F. Wu, Y. Wu, and J. Xu, “Growth and spectral characterization of β-Ga2O3 single crystals,” J. Phys. Chem. Solids 67(12), 2448–2451 (2006).
[Crossref]

Wu, Y.

Y. Li, Y. Li, R. Chen, K. Sharafudeen, S. Zhou, M. Gecevicius, H. Wang, G. Dong, Y. Wu, X. Qin, and J. Qiu, “Tailoring of the trap distribution and crystal field in Cr3+-doped non-gallate phosphors with near-infrared long-persistence phosphorescence,” NPG Asia Mater. 7(5), e180 (2015).
[Crossref]

J. Zhang, B. Li, C. Xia, G. Pei, Q. Deng, Z. Yang, W. Xu, H. Shi, F. Wu, Y. Wu, and J. Xu, “Growth and spectral characterization of β-Ga2O3 single crystals,” J. Phys. Chem. Solids 67(12), 2448–2451 (2006).
[Crossref]

Xia, C.

J. Zhang, B. Li, C. Xia, G. Pei, Q. Deng, Z. Yang, W. Xu, H. Shi, F. Wu, Y. Wu, and J. Xu, “Growth and spectral characterization of β-Ga2O3 single crystals,” J. Phys. Chem. Solids 67(12), 2448–2451 (2006).
[Crossref]

Xia, Z.

H. Liao, M. Zhao, M. S. Molokeev, Q. Liu, and Z. Xia, “Learning from a mineral structure toward an ultra-narrow-band blue-emitting silicate phosphor RbNa3(Li3SiO4)4:Eu2+,” Angew. Chem. 130(36), 11902–11905 (2018).
[Crossref]

Xu, J.

J. Xu, J. Ueda, and S. Tanabe, “Design of deep-red persistent phosphors of Gd3Al5-xGaxO12:Cr3+ transparent ceramics sensitized by Eu3+ as an electron trap using conduction band engineering,” Opt. Mater. Express 5(5), 963 (2015).
[Crossref]

J. Zhang, B. Li, C. Xia, G. Pei, Q. Deng, Z. Yang, W. Xu, H. Shi, F. Wu, Y. Wu, and J. Xu, “Growth and spectral characterization of β-Ga2O3 single crystals,” J. Phys. Chem. Solids 67(12), 2448–2451 (2006).
[Crossref]

Xu, W.

J. Zhang, B. Li, C. Xia, G. Pei, Q. Deng, Z. Yang, W. Xu, H. Shi, F. Wu, Y. Wu, and J. Xu, “Growth and spectral characterization of β-Ga2O3 single crystals,” J. Phys. Chem. Solids 67(12), 2448–2451 (2006).
[Crossref]

Xu, X.

Z. Long, Y. Wen, J. Qiu, J. Wang, D. Zhou, C. Zhu, J. Lai, X. Xu, X. Yu, and Q. Wang, “Crystal structure insight aided design of SrGa2Si2O8:Mn2+ with multi-band and thermally stable emission for high-power LED applications,” Chem. Eng. J. 375, 122016 (2019).
[Crossref]

Yabasi, S.

E. G. Víllora, M. Yamaga, T. Inoue, S. Yabasi, Y. Masui, T. Sugawara, and T. Fukuda, “Optical spectroscopy study on β-Ga2O3,” Jpn. J. Appl. Phys. 41(Part 2, No. 6A), L622–L625 (2002).
[Crossref]

Yamaga, M.

E. G. Víllora, M. Yamaga, T. Inoue, S. Yabasi, Y. Masui, T. Sugawara, and T. Fukuda, “Optical spectroscopy study on β-Ga2O3,” Jpn. J. Appl. Phys. 41(Part 2, No. 6A), L622–L625 (2002).
[Crossref]

Yang, Z.

J. Zhang, B. Li, C. Xia, G. Pei, Q. Deng, Z. Yang, W. Xu, H. Shi, F. Wu, Y. Wu, and J. Xu, “Growth and spectral characterization of β-Ga2O3 single crystals,” J. Phys. Chem. Solids 67(12), 2448–2451 (2006).
[Crossref]

Yeh, C.-W.

W.-R. Liu, C.-H. Huang, C.-W. Yeh, J.-C. Tsai, Y.-C. Chiu, Y.-T. Yeh, and R.-S. Liu, “A Study on the Luminescence and Energy Transfer of Single-Phase and Color-Tunable KCaY(PO4)2:Eu2+, Mn2+ phosphor for application in white-light LEDs,” Inorg. Chem. 51(18), 9636–9641 (2012).
[Crossref]

Yeh, Y.-T.

W.-R. Liu, C.-H. Huang, C.-W. Yeh, J.-C. Tsai, Y.-C. Chiu, Y.-T. Yeh, and R.-S. Liu, “A Study on the Luminescence and Energy Transfer of Single-Phase and Color-Tunable KCaY(PO4)2:Eu2+, Mn2+ phosphor for application in white-light LEDs,” Inorg. Chem. 51(18), 9636–9641 (2012).
[Crossref]

Yoshiara, S.

S. S. B. Nasir, A. Tanaka, S. Yoshiara, and A. Kato, “Luminescence properties of Li2SrSiO4:Eu2+ silicate yellow phosphors with high thermal stability for high-power efficiency white LED application,” J. Lumin. 207, 22–28 (2019).
[Crossref]

You, H.

W. Lü, W. Lv, Q. Zhao, M. Jiao, B. Shao, and H. You, “A novel efficient Mn4+ activated Ca14Al10Zn6O35 phosphor: application in red-emitting and white LEDs,” Inorg. Chem. 53(22), 11985–11990 (2014).
[Crossref]

Yu, X.

Z. Long, Y. Wen, J. Qiu, J. Wang, D. Zhou, C. Zhu, J. Lai, X. Xu, X. Yu, and Q. Wang, “Crystal structure insight aided design of SrGa2Si2O8:Mn2+ with multi-band and thermally stable emission for high-power LED applications,” Chem. Eng. J. 375, 122016 (2019).
[Crossref]

Zhang, J.

J. Zhang, B. Li, C. Xia, G. Pei, Q. Deng, Z. Yang, W. Xu, H. Shi, F. Wu, Y. Wu, and J. Xu, “Growth and spectral characterization of β-Ga2O3 single crystals,” J. Phys. Chem. Solids 67(12), 2448–2451 (2006).
[Crossref]

Zhang, Y.

K. Li, D. Geng, M. Shang, Y. Zhang, H. Lian, and J. Lin, “Color-tunable luminescence and energy transfer properties of Ca9Mg(PO4)6F2:Eu2+, Mn2+ phosphors for UV-LEDs,” J. Phys. Chem. C 118(20), 11026–11034 (2014).
[Crossref]

Zhao, M.

H. Liao, M. Zhao, M. S. Molokeev, Q. Liu, and Z. Xia, “Learning from a mineral structure toward an ultra-narrow-band blue-emitting silicate phosphor RbNa3(Li3SiO4)4:Eu2+,” Angew. Chem. 130(36), 11902–11905 (2018).
[Crossref]

Zhao, Q.

W. Lü, W. Lv, Q. Zhao, M. Jiao, B. Shao, and H. You, “A novel efficient Mn4+ activated Ca14Al10Zn6O35 phosphor: application in red-emitting and white LEDs,” Inorg. Chem. 53(22), 11985–11990 (2014).
[Crossref]

Zhou, D.

Z. Long, Y. Wen, J. Qiu, J. Wang, D. Zhou, C. Zhu, J. Lai, X. Xu, X. Yu, and Q. Wang, “Crystal structure insight aided design of SrGa2Si2O8:Mn2+ with multi-band and thermally stable emission for high-power LED applications,” Chem. Eng. J. 375, 122016 (2019).
[Crossref]

Zhou, S.

Y. Li, Y. Li, R. Chen, K. Sharafudeen, S. Zhou, M. Gecevicius, H. Wang, G. Dong, Y. Wu, X. Qin, and J. Qiu, “Tailoring of the trap distribution and crystal field in Cr3+-doped non-gallate phosphors with near-infrared long-persistence phosphorescence,” NPG Asia Mater. 7(5), e180 (2015).
[Crossref]

Zhu, C.

Z. Long, Y. Wen, J. Qiu, J. Wang, D. Zhou, C. Zhu, J. Lai, X. Xu, X. Yu, and Q. Wang, “Crystal structure insight aided design of SrGa2Si2O8:Mn2+ with multi-band and thermally stable emission for high-power LED applications,” Chem. Eng. J. 375, 122016 (2019).
[Crossref]

Angew. Chem. (1)

H. Liao, M. Zhao, M. S. Molokeev, Q. Liu, and Z. Xia, “Learning from a mineral structure toward an ultra-narrow-band blue-emitting silicate phosphor RbNa3(Li3SiO4)4:Eu2+,” Angew. Chem. 130(36), 11902–11905 (2018).
[Crossref]

Chem. Eng. J. (1)

Z. Long, Y. Wen, J. Qiu, J. Wang, D. Zhou, C. Zhu, J. Lai, X. Xu, X. Yu, and Q. Wang, “Crystal structure insight aided design of SrGa2Si2O8:Mn2+ with multi-band and thermally stable emission for high-power LED applications,” Chem. Eng. J. 375, 122016 (2019).
[Crossref]

Chem. Mater. (1)

A. Bessière, S. K. Sharma, N. Basavaraju, K. R. Priolkar, L. Binet, B. Viana, A. J. J. Bos, T. Maldiney, C. Richard, D. Scherman, and D. Gourier, “Storage of visible light for long-lasting phosphorescence in chromium-doped zinc gallate,” Chem. Mater. 26(3), 1365–1373 (2014).
[Crossref]

Inorg. Chem. (2)

W. Lü, W. Lv, Q. Zhao, M. Jiao, B. Shao, and H. You, “A novel efficient Mn4+ activated Ca14Al10Zn6O35 phosphor: application in red-emitting and white LEDs,” Inorg. Chem. 53(22), 11985–11990 (2014).
[Crossref]

W.-R. Liu, C.-H. Huang, C.-W. Yeh, J.-C. Tsai, Y.-C. Chiu, Y.-T. Yeh, and R.-S. Liu, “A Study on the Luminescence and Energy Transfer of Single-Phase and Color-Tunable KCaY(PO4)2:Eu2+, Mn2+ phosphor for application in white-light LEDs,” Inorg. Chem. 51(18), 9636–9641 (2012).
[Crossref]

J. Alloys Compd. (1)

S. Kumar, C. Tessarek, S. Christiansen, and R. Singh, “A comparative study of β-Ga2O3 nanowires grown on different substrates using CVD technique,” J. Alloys Compd. 587, 812–818 (2014).
[Crossref]

J. Am. Chem. Soc. (1)

T. Maldiney, A. Lecointre, B. Viana, A. Bessière, M. Bessodes, D. Gourier, C. Richard, and D. Scherman, “Controlling electron trap depth to enhance optical properties of persistent luminescence nanoparticles for in vivo imaging,” J. Am. Chem. Soc. 133(30), 11810–11815 (2011).
[Crossref]

J. Lumin. (2)

T. Sasaki, J. Fukushima, Y. Hayashi, and H. Takizawa, “Synthesis and photoluminescence properties of a novel aluminosilicate Sr3Al10SiO20:Mn4+ red phosphor,” J. Lumin. 188, 101–106 (2017).
[Crossref]

S. S. B. Nasir, A. Tanaka, S. Yoshiara, and A. Kato, “Luminescence properties of Li2SrSiO4:Eu2+ silicate yellow phosphors with high thermal stability for high-power efficiency white LED application,” J. Lumin. 207, 22–28 (2019).
[Crossref]

J. Mater. Chem. C (1)

J. Ueda, P. Dorenbos, A. J. J. Bos, K. Kuroishi, and S. Tanabe, “Control of electron transfer between Ce3+ and Cr3+ in the Y3Al5−xGaxO12 host via conduction band engineering,” J. Mater. Chem. C 3(22), 5642–5651 (2015).
[Crossref]

J. Phys. Chem. C (1)

K. Li, D. Geng, M. Shang, Y. Zhang, H. Lian, and J. Lin, “Color-tunable luminescence and energy transfer properties of Ca9Mg(PO4)6F2:Eu2+, Mn2+ phosphors for UV-LEDs,” J. Phys. Chem. C 118(20), 11026–11034 (2014).
[Crossref]

J. Phys. Chem. Solids (1)

J. Zhang, B. Li, C. Xia, G. Pei, Q. Deng, Z. Yang, W. Xu, H. Shi, F. Wu, Y. Wu, and J. Xu, “Growth and spectral characterization of β-Ga2O3 single crystals,” J. Phys. Chem. Solids 67(12), 2448–2451 (2006).
[Crossref]

Jpn. J. Appl. Phys. (1)

E. G. Víllora, M. Yamaga, T. Inoue, S. Yabasi, Y. Masui, T. Sugawara, and T. Fukuda, “Optical spectroscopy study on β-Ga2O3,” Jpn. J. Appl. Phys. 41(Part 2, No. 6A), L622–L625 (2002).
[Crossref]

Mater. Sci. Eng., B (1)

G. Ram Banjare, D. P. Bisen, N. Brahme, and C. Belodhiya, “Studies on structural properties, luminescence behavior and zeta potential of Dy3+ doped alkaline earth ortho-silicate phosphors,” Mater. Sci. Eng., B 263, 114882 (2021).
[Crossref]

Materials (2)

K. Van den Eeckhout, D. Poelman, and P. Smet, “Persistent luminescence in non-Eu2+-doped compounds: a review,” Materials 6(7), 2789–2818 (2013).
[Crossref]

K. Van den Eeckhout, P. F. Smet, and D. Poelman, “Persistent luminescence in Eu2+-doped compounds: a review,” Materials 3(4), 2536–2566 (2010).
[Crossref]

Nat. Mater. (1)

Z. Pan, Y.-Y. Lu, and F. Liu, “Sunlight-activated long-persistent luminescence in the near-infrared from Cr3+-doped zinc gallogermanates,” Nat. Mater. 11(1), 58–63 (2011).
[Crossref]

NPG Asia Mater. (1)

Y. Li, Y. Li, R. Chen, K. Sharafudeen, S. Zhou, M. Gecevicius, H. Wang, G. Dong, Y. Wu, X. Qin, and J. Qiu, “Tailoring of the trap distribution and crystal field in Cr3+-doped non-gallate phosphors with near-infrared long-persistence phosphorescence,” NPG Asia Mater. 7(5), e180 (2015).
[Crossref]

Opt. Mater. Express (1)

Phys. Chem. Chem. Phys. (2)

N. Basavaraju, K. R. Priolkar, D. Gourier, A. Bessière, and B. Viana, “Order and disorder around Cr3+ in chromium doped persistent luminescent AB2O4 spinels,” Phys. Chem. Chem. Phys. 17(16), 10993–10999 (2015).
[Crossref]

N. Basavaraju, K. R. Priolkar, D. Gourier, S. K. Sharma, A. Bessière, and B. Viana, “The importance of inversion disorder in the visible light induced persistent luminescence in Cr3+ doped AB2O4 (A = Zn or Mg and B = Ga or Al),” Phys. Chem. Chem. Phys. 17(3), 1790–1799 (2015).
[Crossref]

Phys. Rev. B (2)

K. Van den Eeckhout, A. J. J. Bos, D. Poelman, and P. F. Smet, “Revealing trap depth distributions in persistent phosphors,” Phys. Rev. B 87(4), 045126 (2013).
[Crossref]

J. Botterman, J. J. Joos, and P. F. Smet, “Trapping and detrapping in SrAl2O4:Eu, Dy persistent phosphors: Influence of excitation wavelength and temperature,” Phys. Rev. B 90(8), 085147 (2014).
[Crossref]

Data availability

The data that support the findings of this study are available from the corresponding author upon reasonable request.

Cited By

OSA participates in Crossref's Cited-By Linking service. Citing articles from OSA journals and other participating publishers are listed here.

Alert me when this article is cited.


Figures (7)

Fig. 1.
Fig. 1. XRD patterns of Sr1-xBaxGa2Si2O8: 1% Mn2+ (x = 0-0.4) samples and the standard data for the SrGa2Si2O8 phase.
Fig. 2.
Fig. 2. (a) Rietveld refinement of powder XRD profile of Sr1-xBaxGa2Si2O8 (x = 0 and 0.2) samples. (b) Crystal structure of Sr0.8Ba0.2Ga2Si2O8.
Fig. 3.
Fig. 3. Excitation and emission spectra of SrGa2Si2O8 samples.
Fig. 4.
Fig. 4. (a) Emission spectra of Sr1-xBaxGa2Si2O8: 1% Mn2+ (x = 0-0.3) excited at 270 nm. (b) Intensity ratios of the Peak 2 to Peak 1 as functions of x in the Sr1-xBaxGa2Si2O8: 1% Mn2+ (x = 0-0.3) samples. (c) Excitation spectra of Sr1-xBaxGa2Si2O8: 1% Mn2+ (x = 0, 0.1 and 0.3).
Fig. 5.
Fig. 5. Image of SrGa2Si2O8: 1% Mn2+ samples (a) under white-LED illumination, (b) under 254 nm light and (c) 1 min after 254 nm light ceased. (d) Persistent luminescence decay curve of the Sr1-xBaxGa2Si2O8: 1% Mn2+ (x = 0-0.3) samples monitoring at 585 nm.
Fig. 6.
Fig. 6. (a) PersL spectra of Sr1-xBaxGa2Si2O8: 1% Mn2+ (x = 0-0.3). (b) Emission intensity ratios and persistent luminescence intensity ratios of the Peak 2 to Peak 1 as functions of x in the Sr1-xBaxGa2Si2O8: 1% Mn2+ (x = 0-0.3) samples.
Fig. 7.
Fig. 7. (a) TL curves of SrGa2Si2O8: 1% Mn2+ samples monitoring at 585 nm after initially being excited by 270 nm light for 60 s at various temperatures. (b) Initial rise method used to estimate the trap depths of SrGa2Si2O8: 1% Mn2+ samples. (c) The density of energy levels for the trap distribution in SrGa2Si2O8: 1% Mn2+ samples. Inset: The estimated trap depth in SrGa2Si2O8: 1% Mn2+ as a function of excitation temperature.

Tables (1)

Tables Icon

Table 1. The refined positions of all atoms and the lattice parameters of SrGa2Si2O8 and Sr0.8Ba0.2Ga2Si2O8

Equations (1)

Equations on this page are rendered with MathJax. Learn more.

I ( T ) = C × exp ( E k T )