Abstract

A method has been developed to fabricate organic-inorganic hybrid heterojunction solar cells based on n-type silicon nanowire (SiNW) and poly (3,4-ethylenedioxythiophene):poly (styrenesulfonate) (PEDOT:PSS) hybrid structures by evacuating the PEDOT:PSS solution with dip-dropping on the top of SiNWs before spin-coating (solution-evacuating). The coverage and contact interface between PEDOT:PSS and SiNW arrays can be dramatically enhanced by optimizing the solution-evacuated time. The maximum power conversion efficiency (PCE) reaches 9.22% for a solution-evacuated time of 2 min compared with 5.17% for the untreated pristine device. The improvement photovoltaic performance is mainly attributed to better organic coverage and contact with an n-type SiNW surface.

© 2014 Optical Society of America

Full Article  |  PDF Article

References

  • View by:
  • |
  • |
  • |

  1. R. F. Service, Science 319, 718 (2008).
    [CrossRef]
  2. R. G. Little and M. J. Nowlan, Prog. Photovolt. 5, 309 (1997).
    [CrossRef]
  3. V. M. Fthenakis and H. C. Kim, Sol. Energy 85, 1609 (2011).
    [CrossRef]
  4. M. J. Sailor, E. J. Ginsburg, C. B. Gorman, A. Kumar, R. H. Grubbs, and N. S. Lewis, Science 249, 1146 (1990).
    [CrossRef]
  5. M. Law, L. E. Greene, J. C. Johnson, R. Saykally, and P. D. Yang, Nat. Mater. 4, 455 (2005).
    [CrossRef]
  6. L. Hu and G. Chen, Nano Lett. 7, 3249 (2007).
    [CrossRef]
  7. E. C. Garnett and P. Yang, J. Am. Chem. Soc. 130, 9224 (2008).
    [CrossRef]
  8. L. Tsakalakos, J. Balch, J. Fronheiser, B. A. Korevaar, O. Sulima, and J. Rand, Appl. Phys. Lett. 91, 233117 (2007).
    [CrossRef]
  9. E. Garnett and P. Yang, Nano Lett. 10, 1082 (2010).
    [CrossRef]
  10. S. C. Shiu, J. J. Chao, S. C. Hung, C. L. Yeh, and C. F. Lin, Chem. Mater. 22, 3108 (2010).
    [CrossRef]
  11. J. Ouyang, Q. Xu, C. W. Chu, Y. Yang, G. Li, and J. Shinar, Polymer 45, 8443 (2004).
    [CrossRef]
  12. B. Ozdemir, M. Kulakci, R. Turan, and H. E. Unalan, Appl. Phys. Lett. 99, 113510 (2011).
    [CrossRef]
  13. L. He, Rusli, C. Jiang, H. Wang, and D. Lai, IEEE Electron Device Lett. 32, 1406 (2011).
    [CrossRef]
  14. T.-G. Chen, B.-Y. Huang, E.-C. Chen, P. Yu, and H.-F. Meng, Appl. Phys. Lett. 101, 033301 (2012).
    [CrossRef]
  15. S. Jeong, E. C. Garnett, S. Wang, Z. Yu, S. Fan, M. L. Brongersma, M. D. McGehee, and Y. Cui, Nano Lett. 12, 2971 (2012).
    [CrossRef]
  16. M. Ono, Z. Tang, R. Ishikawa, T. Gotou, K. Ueno, and H. Shirai, Appl. Phys. Express 5, 032301 (2012).
    [CrossRef]
  17. W. H. Lu, Q. Chen, B. Wang, and L. W. Chen, Appl. Phys. Lett. 100, 023112 (2012).
    [CrossRef]
  18. S. A. Moiz, A. M. Nahhas, H.-D. Um, S.-W. Jee, H. K. Cho, S.-W. Kim, and J.-H. Lee, Nanotechnology 23, 145401 (2012).
    [CrossRef]
  19. L. He, C. Jiang, H. Wang, D. Lai, Y. H. Tan, C. S. Tan, and Rusli, Appl. Phys. Lett. 100, 103104 (2012).
    [CrossRef]
  20. J. Zhang, Y. Zhang, F. Zhang, and B. Sun, Appl. Phys. Lett. 102, 013501 (2013).
    [CrossRef]
  21. S. Avasthi, Y. Qi, G. K. Vertelov, J. Schwartz, A. Kahn, and J. C. Sturm, Appl. Phys. Lett. 96, 222109 (2010).
    [CrossRef]
  22. D. Liu, Y. Zhang, X. Fang, F. Zhang, T. Song, and B. Sun, IEEE Electron Device Lett. 34, 345 (2013).
    [CrossRef]
  23. Y. Zhu, T. Song, F. Zhang, S.-T. Lee, and B. Sun, Appl. Phys. Lett. 102, 113504 (2013).
    [CrossRef]
  24. Q. Liu, T. Imamura, T. Hiate, I. Khatri, Z. Tang, R. Ishikawa, K. Ueno, and H. Shirai, Appl. Phys. Lett. 102, 243902 (2013).
    [CrossRef]
  25. P. Yu, C. Y. Tsai, J. K. Chang, C. C. Lai, P. H. Chen, Y. C. Lai, P. T. Tsai, M. C. Li, H. T. Pan, Y. Y. Huang, C. Wu, Y. L. Chueh, S. W. Chen, C. H. Du, S. F. Horng, and H. F. Meng, ACS Nano 7, 10780 (2013).
    [CrossRef]
  26. K. Peng, Y. Xu, Y. Wu, Y. Yan, S.-T. Lee, and J. Zhu, Small 1, 1062 (2005).
    [CrossRef]

2013 (5)

D. Liu, Y. Zhang, X. Fang, F. Zhang, T. Song, and B. Sun, IEEE Electron Device Lett. 34, 345 (2013).
[CrossRef]

Y. Zhu, T. Song, F. Zhang, S.-T. Lee, and B. Sun, Appl. Phys. Lett. 102, 113504 (2013).
[CrossRef]

Q. Liu, T. Imamura, T. Hiate, I. Khatri, Z. Tang, R. Ishikawa, K. Ueno, and H. Shirai, Appl. Phys. Lett. 102, 243902 (2013).
[CrossRef]

P. Yu, C. Y. Tsai, J. K. Chang, C. C. Lai, P. H. Chen, Y. C. Lai, P. T. Tsai, M. C. Li, H. T. Pan, Y. Y. Huang, C. Wu, Y. L. Chueh, S. W. Chen, C. H. Du, S. F. Horng, and H. F. Meng, ACS Nano 7, 10780 (2013).
[CrossRef]

J. Zhang, Y. Zhang, F. Zhang, and B. Sun, Appl. Phys. Lett. 102, 013501 (2013).
[CrossRef]

2012 (6)

T.-G. Chen, B.-Y. Huang, E.-C. Chen, P. Yu, and H.-F. Meng, Appl. Phys. Lett. 101, 033301 (2012).
[CrossRef]

S. Jeong, E. C. Garnett, S. Wang, Z. Yu, S. Fan, M. L. Brongersma, M. D. McGehee, and Y. Cui, Nano Lett. 12, 2971 (2012).
[CrossRef]

M. Ono, Z. Tang, R. Ishikawa, T. Gotou, K. Ueno, and H. Shirai, Appl. Phys. Express 5, 032301 (2012).
[CrossRef]

W. H. Lu, Q. Chen, B. Wang, and L. W. Chen, Appl. Phys. Lett. 100, 023112 (2012).
[CrossRef]

S. A. Moiz, A. M. Nahhas, H.-D. Um, S.-W. Jee, H. K. Cho, S.-W. Kim, and J.-H. Lee, Nanotechnology 23, 145401 (2012).
[CrossRef]

L. He, C. Jiang, H. Wang, D. Lai, Y. H. Tan, C. S. Tan, and Rusli, Appl. Phys. Lett. 100, 103104 (2012).
[CrossRef]

2011 (3)

B. Ozdemir, M. Kulakci, R. Turan, and H. E. Unalan, Appl. Phys. Lett. 99, 113510 (2011).
[CrossRef]

L. He, Rusli, C. Jiang, H. Wang, and D. Lai, IEEE Electron Device Lett. 32, 1406 (2011).
[CrossRef]

V. M. Fthenakis and H. C. Kim, Sol. Energy 85, 1609 (2011).
[CrossRef]

2010 (3)

E. Garnett and P. Yang, Nano Lett. 10, 1082 (2010).
[CrossRef]

S. C. Shiu, J. J. Chao, S. C. Hung, C. L. Yeh, and C. F. Lin, Chem. Mater. 22, 3108 (2010).
[CrossRef]

S. Avasthi, Y. Qi, G. K. Vertelov, J. Schwartz, A. Kahn, and J. C. Sturm, Appl. Phys. Lett. 96, 222109 (2010).
[CrossRef]

2008 (2)

R. F. Service, Science 319, 718 (2008).
[CrossRef]

E. C. Garnett and P. Yang, J. Am. Chem. Soc. 130, 9224 (2008).
[CrossRef]

2007 (2)

L. Tsakalakos, J. Balch, J. Fronheiser, B. A. Korevaar, O. Sulima, and J. Rand, Appl. Phys. Lett. 91, 233117 (2007).
[CrossRef]

L. Hu and G. Chen, Nano Lett. 7, 3249 (2007).
[CrossRef]

2005 (2)

M. Law, L. E. Greene, J. C. Johnson, R. Saykally, and P. D. Yang, Nat. Mater. 4, 455 (2005).
[CrossRef]

K. Peng, Y. Xu, Y. Wu, Y. Yan, S.-T. Lee, and J. Zhu, Small 1, 1062 (2005).
[CrossRef]

2004 (1)

J. Ouyang, Q. Xu, C. W. Chu, Y. Yang, G. Li, and J. Shinar, Polymer 45, 8443 (2004).
[CrossRef]

1997 (1)

R. G. Little and M. J. Nowlan, Prog. Photovolt. 5, 309 (1997).
[CrossRef]

1990 (1)

M. J. Sailor, E. J. Ginsburg, C. B. Gorman, A. Kumar, R. H. Grubbs, and N. S. Lewis, Science 249, 1146 (1990).
[CrossRef]

Avasthi, S.

S. Avasthi, Y. Qi, G. K. Vertelov, J. Schwartz, A. Kahn, and J. C. Sturm, Appl. Phys. Lett. 96, 222109 (2010).
[CrossRef]

Balch, J.

L. Tsakalakos, J. Balch, J. Fronheiser, B. A. Korevaar, O. Sulima, and J. Rand, Appl. Phys. Lett. 91, 233117 (2007).
[CrossRef]

Brongersma, M. L.

S. Jeong, E. C. Garnett, S. Wang, Z. Yu, S. Fan, M. L. Brongersma, M. D. McGehee, and Y. Cui, Nano Lett. 12, 2971 (2012).
[CrossRef]

Chang, J. K.

P. Yu, C. Y. Tsai, J. K. Chang, C. C. Lai, P. H. Chen, Y. C. Lai, P. T. Tsai, M. C. Li, H. T. Pan, Y. Y. Huang, C. Wu, Y. L. Chueh, S. W. Chen, C. H. Du, S. F. Horng, and H. F. Meng, ACS Nano 7, 10780 (2013).
[CrossRef]

Chao, J. J.

S. C. Shiu, J. J. Chao, S. C. Hung, C. L. Yeh, and C. F. Lin, Chem. Mater. 22, 3108 (2010).
[CrossRef]

Chen, E.-C.

T.-G. Chen, B.-Y. Huang, E.-C. Chen, P. Yu, and H.-F. Meng, Appl. Phys. Lett. 101, 033301 (2012).
[CrossRef]

Chen, G.

L. Hu and G. Chen, Nano Lett. 7, 3249 (2007).
[CrossRef]

Chen, L. W.

W. H. Lu, Q. Chen, B. Wang, and L. W. Chen, Appl. Phys. Lett. 100, 023112 (2012).
[CrossRef]

Chen, P. H.

P. Yu, C. Y. Tsai, J. K. Chang, C. C. Lai, P. H. Chen, Y. C. Lai, P. T. Tsai, M. C. Li, H. T. Pan, Y. Y. Huang, C. Wu, Y. L. Chueh, S. W. Chen, C. H. Du, S. F. Horng, and H. F. Meng, ACS Nano 7, 10780 (2013).
[CrossRef]

Chen, Q.

W. H. Lu, Q. Chen, B. Wang, and L. W. Chen, Appl. Phys. Lett. 100, 023112 (2012).
[CrossRef]

Chen, S. W.

P. Yu, C. Y. Tsai, J. K. Chang, C. C. Lai, P. H. Chen, Y. C. Lai, P. T. Tsai, M. C. Li, H. T. Pan, Y. Y. Huang, C. Wu, Y. L. Chueh, S. W. Chen, C. H. Du, S. F. Horng, and H. F. Meng, ACS Nano 7, 10780 (2013).
[CrossRef]

Chen, T.-G.

T.-G. Chen, B.-Y. Huang, E.-C. Chen, P. Yu, and H.-F. Meng, Appl. Phys. Lett. 101, 033301 (2012).
[CrossRef]

Cho, H. K.

S. A. Moiz, A. M. Nahhas, H.-D. Um, S.-W. Jee, H. K. Cho, S.-W. Kim, and J.-H. Lee, Nanotechnology 23, 145401 (2012).
[CrossRef]

Chu, C. W.

J. Ouyang, Q. Xu, C. W. Chu, Y. Yang, G. Li, and J. Shinar, Polymer 45, 8443 (2004).
[CrossRef]

Chueh, Y. L.

P. Yu, C. Y. Tsai, J. K. Chang, C. C. Lai, P. H. Chen, Y. C. Lai, P. T. Tsai, M. C. Li, H. T. Pan, Y. Y. Huang, C. Wu, Y. L. Chueh, S. W. Chen, C. H. Du, S. F. Horng, and H. F. Meng, ACS Nano 7, 10780 (2013).
[CrossRef]

Cui, Y.

S. Jeong, E. C. Garnett, S. Wang, Z. Yu, S. Fan, M. L. Brongersma, M. D. McGehee, and Y. Cui, Nano Lett. 12, 2971 (2012).
[CrossRef]

Du, C. H.

P. Yu, C. Y. Tsai, J. K. Chang, C. C. Lai, P. H. Chen, Y. C. Lai, P. T. Tsai, M. C. Li, H. T. Pan, Y. Y. Huang, C. Wu, Y. L. Chueh, S. W. Chen, C. H. Du, S. F. Horng, and H. F. Meng, ACS Nano 7, 10780 (2013).
[CrossRef]

Fan, S.

S. Jeong, E. C. Garnett, S. Wang, Z. Yu, S. Fan, M. L. Brongersma, M. D. McGehee, and Y. Cui, Nano Lett. 12, 2971 (2012).
[CrossRef]

Fang, X.

D. Liu, Y. Zhang, X. Fang, F. Zhang, T. Song, and B. Sun, IEEE Electron Device Lett. 34, 345 (2013).
[CrossRef]

Fronheiser, J.

L. Tsakalakos, J. Balch, J. Fronheiser, B. A. Korevaar, O. Sulima, and J. Rand, Appl. Phys. Lett. 91, 233117 (2007).
[CrossRef]

Fthenakis, V. M.

V. M. Fthenakis and H. C. Kim, Sol. Energy 85, 1609 (2011).
[CrossRef]

Garnett, E.

E. Garnett and P. Yang, Nano Lett. 10, 1082 (2010).
[CrossRef]

Garnett, E. C.

S. Jeong, E. C. Garnett, S. Wang, Z. Yu, S. Fan, M. L. Brongersma, M. D. McGehee, and Y. Cui, Nano Lett. 12, 2971 (2012).
[CrossRef]

E. C. Garnett and P. Yang, J. Am. Chem. Soc. 130, 9224 (2008).
[CrossRef]

Ginsburg, E. J.

M. J. Sailor, E. J. Ginsburg, C. B. Gorman, A. Kumar, R. H. Grubbs, and N. S. Lewis, Science 249, 1146 (1990).
[CrossRef]

Gorman, C. B.

M. J. Sailor, E. J. Ginsburg, C. B. Gorman, A. Kumar, R. H. Grubbs, and N. S. Lewis, Science 249, 1146 (1990).
[CrossRef]

Gotou, T.

M. Ono, Z. Tang, R. Ishikawa, T. Gotou, K. Ueno, and H. Shirai, Appl. Phys. Express 5, 032301 (2012).
[CrossRef]

Greene, L. E.

M. Law, L. E. Greene, J. C. Johnson, R. Saykally, and P. D. Yang, Nat. Mater. 4, 455 (2005).
[CrossRef]

Grubbs, R. H.

M. J. Sailor, E. J. Ginsburg, C. B. Gorman, A. Kumar, R. H. Grubbs, and N. S. Lewis, Science 249, 1146 (1990).
[CrossRef]

He, L.

L. He, C. Jiang, H. Wang, D. Lai, Y. H. Tan, C. S. Tan, and Rusli, Appl. Phys. Lett. 100, 103104 (2012).
[CrossRef]

L. He, Rusli, C. Jiang, H. Wang, and D. Lai, IEEE Electron Device Lett. 32, 1406 (2011).
[CrossRef]

Hiate, T.

Q. Liu, T. Imamura, T. Hiate, I. Khatri, Z. Tang, R. Ishikawa, K. Ueno, and H. Shirai, Appl. Phys. Lett. 102, 243902 (2013).
[CrossRef]

Horng, S. F.

P. Yu, C. Y. Tsai, J. K. Chang, C. C. Lai, P. H. Chen, Y. C. Lai, P. T. Tsai, M. C. Li, H. T. Pan, Y. Y. Huang, C. Wu, Y. L. Chueh, S. W. Chen, C. H. Du, S. F. Horng, and H. F. Meng, ACS Nano 7, 10780 (2013).
[CrossRef]

Hu, L.

L. Hu and G. Chen, Nano Lett. 7, 3249 (2007).
[CrossRef]

Huang, B.-Y.

T.-G. Chen, B.-Y. Huang, E.-C. Chen, P. Yu, and H.-F. Meng, Appl. Phys. Lett. 101, 033301 (2012).
[CrossRef]

Huang, Y. Y.

P. Yu, C. Y. Tsai, J. K. Chang, C. C. Lai, P. H. Chen, Y. C. Lai, P. T. Tsai, M. C. Li, H. T. Pan, Y. Y. Huang, C. Wu, Y. L. Chueh, S. W. Chen, C. H. Du, S. F. Horng, and H. F. Meng, ACS Nano 7, 10780 (2013).
[CrossRef]

Hung, S. C.

S. C. Shiu, J. J. Chao, S. C. Hung, C. L. Yeh, and C. F. Lin, Chem. Mater. 22, 3108 (2010).
[CrossRef]

Imamura, T.

Q. Liu, T. Imamura, T. Hiate, I. Khatri, Z. Tang, R. Ishikawa, K. Ueno, and H. Shirai, Appl. Phys. Lett. 102, 243902 (2013).
[CrossRef]

Ishikawa, R.

Q. Liu, T. Imamura, T. Hiate, I. Khatri, Z. Tang, R. Ishikawa, K. Ueno, and H. Shirai, Appl. Phys. Lett. 102, 243902 (2013).
[CrossRef]

M. Ono, Z. Tang, R. Ishikawa, T. Gotou, K. Ueno, and H. Shirai, Appl. Phys. Express 5, 032301 (2012).
[CrossRef]

Jee, S.-W.

S. A. Moiz, A. M. Nahhas, H.-D. Um, S.-W. Jee, H. K. Cho, S.-W. Kim, and J.-H. Lee, Nanotechnology 23, 145401 (2012).
[CrossRef]

Jeong, S.

S. Jeong, E. C. Garnett, S. Wang, Z. Yu, S. Fan, M. L. Brongersma, M. D. McGehee, and Y. Cui, Nano Lett. 12, 2971 (2012).
[CrossRef]

Jiang, C.

L. He, C. Jiang, H. Wang, D. Lai, Y. H. Tan, C. S. Tan, and Rusli, Appl. Phys. Lett. 100, 103104 (2012).
[CrossRef]

L. He, Rusli, C. Jiang, H. Wang, and D. Lai, IEEE Electron Device Lett. 32, 1406 (2011).
[CrossRef]

Johnson, J. C.

M. Law, L. E. Greene, J. C. Johnson, R. Saykally, and P. D. Yang, Nat. Mater. 4, 455 (2005).
[CrossRef]

Kahn, A.

S. Avasthi, Y. Qi, G. K. Vertelov, J. Schwartz, A. Kahn, and J. C. Sturm, Appl. Phys. Lett. 96, 222109 (2010).
[CrossRef]

Khatri, I.

Q. Liu, T. Imamura, T. Hiate, I. Khatri, Z. Tang, R. Ishikawa, K. Ueno, and H. Shirai, Appl. Phys. Lett. 102, 243902 (2013).
[CrossRef]

Kim, H. C.

V. M. Fthenakis and H. C. Kim, Sol. Energy 85, 1609 (2011).
[CrossRef]

Kim, S.-W.

S. A. Moiz, A. M. Nahhas, H.-D. Um, S.-W. Jee, H. K. Cho, S.-W. Kim, and J.-H. Lee, Nanotechnology 23, 145401 (2012).
[CrossRef]

Korevaar, B. A.

L. Tsakalakos, J. Balch, J. Fronheiser, B. A. Korevaar, O. Sulima, and J. Rand, Appl. Phys. Lett. 91, 233117 (2007).
[CrossRef]

Kulakci, M.

B. Ozdemir, M. Kulakci, R. Turan, and H. E. Unalan, Appl. Phys. Lett. 99, 113510 (2011).
[CrossRef]

Kumar, A.

M. J. Sailor, E. J. Ginsburg, C. B. Gorman, A. Kumar, R. H. Grubbs, and N. S. Lewis, Science 249, 1146 (1990).
[CrossRef]

Lai, C. C.

P. Yu, C. Y. Tsai, J. K. Chang, C. C. Lai, P. H. Chen, Y. C. Lai, P. T. Tsai, M. C. Li, H. T. Pan, Y. Y. Huang, C. Wu, Y. L. Chueh, S. W. Chen, C. H. Du, S. F. Horng, and H. F. Meng, ACS Nano 7, 10780 (2013).
[CrossRef]

Lai, D.

L. He, C. Jiang, H. Wang, D. Lai, Y. H. Tan, C. S. Tan, and Rusli, Appl. Phys. Lett. 100, 103104 (2012).
[CrossRef]

L. He, Rusli, C. Jiang, H. Wang, and D. Lai, IEEE Electron Device Lett. 32, 1406 (2011).
[CrossRef]

Lai, Y. C.

P. Yu, C. Y. Tsai, J. K. Chang, C. C. Lai, P. H. Chen, Y. C. Lai, P. T. Tsai, M. C. Li, H. T. Pan, Y. Y. Huang, C. Wu, Y. L. Chueh, S. W. Chen, C. H. Du, S. F. Horng, and H. F. Meng, ACS Nano 7, 10780 (2013).
[CrossRef]

Law, M.

M. Law, L. E. Greene, J. C. Johnson, R. Saykally, and P. D. Yang, Nat. Mater. 4, 455 (2005).
[CrossRef]

Lee, J.-H.

S. A. Moiz, A. M. Nahhas, H.-D. Um, S.-W. Jee, H. K. Cho, S.-W. Kim, and J.-H. Lee, Nanotechnology 23, 145401 (2012).
[CrossRef]

Lee, S.-T.

Y. Zhu, T. Song, F. Zhang, S.-T. Lee, and B. Sun, Appl. Phys. Lett. 102, 113504 (2013).
[CrossRef]

K. Peng, Y. Xu, Y. Wu, Y. Yan, S.-T. Lee, and J. Zhu, Small 1, 1062 (2005).
[CrossRef]

Lewis, N. S.

M. J. Sailor, E. J. Ginsburg, C. B. Gorman, A. Kumar, R. H. Grubbs, and N. S. Lewis, Science 249, 1146 (1990).
[CrossRef]

Li, G.

J. Ouyang, Q. Xu, C. W. Chu, Y. Yang, G. Li, and J. Shinar, Polymer 45, 8443 (2004).
[CrossRef]

Li, M. C.

P. Yu, C. Y. Tsai, J. K. Chang, C. C. Lai, P. H. Chen, Y. C. Lai, P. T. Tsai, M. C. Li, H. T. Pan, Y. Y. Huang, C. Wu, Y. L. Chueh, S. W. Chen, C. H. Du, S. F. Horng, and H. F. Meng, ACS Nano 7, 10780 (2013).
[CrossRef]

Lin, C. F.

S. C. Shiu, J. J. Chao, S. C. Hung, C. L. Yeh, and C. F. Lin, Chem. Mater. 22, 3108 (2010).
[CrossRef]

Little, R. G.

R. G. Little and M. J. Nowlan, Prog. Photovolt. 5, 309 (1997).
[CrossRef]

Liu, D.

D. Liu, Y. Zhang, X. Fang, F. Zhang, T. Song, and B. Sun, IEEE Electron Device Lett. 34, 345 (2013).
[CrossRef]

Liu, Q.

Q. Liu, T. Imamura, T. Hiate, I. Khatri, Z. Tang, R. Ishikawa, K. Ueno, and H. Shirai, Appl. Phys. Lett. 102, 243902 (2013).
[CrossRef]

Lu, W. H.

W. H. Lu, Q. Chen, B. Wang, and L. W. Chen, Appl. Phys. Lett. 100, 023112 (2012).
[CrossRef]

McGehee, M. D.

S. Jeong, E. C. Garnett, S. Wang, Z. Yu, S. Fan, M. L. Brongersma, M. D. McGehee, and Y. Cui, Nano Lett. 12, 2971 (2012).
[CrossRef]

Meng, H. F.

P. Yu, C. Y. Tsai, J. K. Chang, C. C. Lai, P. H. Chen, Y. C. Lai, P. T. Tsai, M. C. Li, H. T. Pan, Y. Y. Huang, C. Wu, Y. L. Chueh, S. W. Chen, C. H. Du, S. F. Horng, and H. F. Meng, ACS Nano 7, 10780 (2013).
[CrossRef]

Meng, H.-F.

T.-G. Chen, B.-Y. Huang, E.-C. Chen, P. Yu, and H.-F. Meng, Appl. Phys. Lett. 101, 033301 (2012).
[CrossRef]

Moiz, S. A.

S. A. Moiz, A. M. Nahhas, H.-D. Um, S.-W. Jee, H. K. Cho, S.-W. Kim, and J.-H. Lee, Nanotechnology 23, 145401 (2012).
[CrossRef]

Nahhas, A. M.

S. A. Moiz, A. M. Nahhas, H.-D. Um, S.-W. Jee, H. K. Cho, S.-W. Kim, and J.-H. Lee, Nanotechnology 23, 145401 (2012).
[CrossRef]

Nowlan, M. J.

R. G. Little and M. J. Nowlan, Prog. Photovolt. 5, 309 (1997).
[CrossRef]

Ono, M.

M. Ono, Z. Tang, R. Ishikawa, T. Gotou, K. Ueno, and H. Shirai, Appl. Phys. Express 5, 032301 (2012).
[CrossRef]

Ouyang, J.

J. Ouyang, Q. Xu, C. W. Chu, Y. Yang, G. Li, and J. Shinar, Polymer 45, 8443 (2004).
[CrossRef]

Ozdemir, B.

B. Ozdemir, M. Kulakci, R. Turan, and H. E. Unalan, Appl. Phys. Lett. 99, 113510 (2011).
[CrossRef]

Pan, H. T.

P. Yu, C. Y. Tsai, J. K. Chang, C. C. Lai, P. H. Chen, Y. C. Lai, P. T. Tsai, M. C. Li, H. T. Pan, Y. Y. Huang, C. Wu, Y. L. Chueh, S. W. Chen, C. H. Du, S. F. Horng, and H. F. Meng, ACS Nano 7, 10780 (2013).
[CrossRef]

Peng, K.

K. Peng, Y. Xu, Y. Wu, Y. Yan, S.-T. Lee, and J. Zhu, Small 1, 1062 (2005).
[CrossRef]

Qi, Y.

S. Avasthi, Y. Qi, G. K. Vertelov, J. Schwartz, A. Kahn, and J. C. Sturm, Appl. Phys. Lett. 96, 222109 (2010).
[CrossRef]

Rand, J.

L. Tsakalakos, J. Balch, J. Fronheiser, B. A. Korevaar, O. Sulima, and J. Rand, Appl. Phys. Lett. 91, 233117 (2007).
[CrossRef]

Rusli,

L. He, C. Jiang, H. Wang, D. Lai, Y. H. Tan, C. S. Tan, and Rusli, Appl. Phys. Lett. 100, 103104 (2012).
[CrossRef]

L. He, Rusli, C. Jiang, H. Wang, and D. Lai, IEEE Electron Device Lett. 32, 1406 (2011).
[CrossRef]

Sailor, M. J.

M. J. Sailor, E. J. Ginsburg, C. B. Gorman, A. Kumar, R. H. Grubbs, and N. S. Lewis, Science 249, 1146 (1990).
[CrossRef]

Saykally, R.

M. Law, L. E. Greene, J. C. Johnson, R. Saykally, and P. D. Yang, Nat. Mater. 4, 455 (2005).
[CrossRef]

Schwartz, J.

S. Avasthi, Y. Qi, G. K. Vertelov, J. Schwartz, A. Kahn, and J. C. Sturm, Appl. Phys. Lett. 96, 222109 (2010).
[CrossRef]

Service, R. F.

R. F. Service, Science 319, 718 (2008).
[CrossRef]

Shinar, J.

J. Ouyang, Q. Xu, C. W. Chu, Y. Yang, G. Li, and J. Shinar, Polymer 45, 8443 (2004).
[CrossRef]

Shirai, H.

Q. Liu, T. Imamura, T. Hiate, I. Khatri, Z. Tang, R. Ishikawa, K. Ueno, and H. Shirai, Appl. Phys. Lett. 102, 243902 (2013).
[CrossRef]

M. Ono, Z. Tang, R. Ishikawa, T. Gotou, K. Ueno, and H. Shirai, Appl. Phys. Express 5, 032301 (2012).
[CrossRef]

Shiu, S. C.

S. C. Shiu, J. J. Chao, S. C. Hung, C. L. Yeh, and C. F. Lin, Chem. Mater. 22, 3108 (2010).
[CrossRef]

Song, T.

Y. Zhu, T. Song, F. Zhang, S.-T. Lee, and B. Sun, Appl. Phys. Lett. 102, 113504 (2013).
[CrossRef]

D. Liu, Y. Zhang, X. Fang, F. Zhang, T. Song, and B. Sun, IEEE Electron Device Lett. 34, 345 (2013).
[CrossRef]

Sturm, J. C.

S. Avasthi, Y. Qi, G. K. Vertelov, J. Schwartz, A. Kahn, and J. C. Sturm, Appl. Phys. Lett. 96, 222109 (2010).
[CrossRef]

Sulima, O.

L. Tsakalakos, J. Balch, J. Fronheiser, B. A. Korevaar, O. Sulima, and J. Rand, Appl. Phys. Lett. 91, 233117 (2007).
[CrossRef]

Sun, B.

D. Liu, Y. Zhang, X. Fang, F. Zhang, T. Song, and B. Sun, IEEE Electron Device Lett. 34, 345 (2013).
[CrossRef]

Y. Zhu, T. Song, F. Zhang, S.-T. Lee, and B. Sun, Appl. Phys. Lett. 102, 113504 (2013).
[CrossRef]

J. Zhang, Y. Zhang, F. Zhang, and B. Sun, Appl. Phys. Lett. 102, 013501 (2013).
[CrossRef]

Tan, C. S.

L. He, C. Jiang, H. Wang, D. Lai, Y. H. Tan, C. S. Tan, and Rusli, Appl. Phys. Lett. 100, 103104 (2012).
[CrossRef]

Tan, Y. H.

L. He, C. Jiang, H. Wang, D. Lai, Y. H. Tan, C. S. Tan, and Rusli, Appl. Phys. Lett. 100, 103104 (2012).
[CrossRef]

Tang, Z.

Q. Liu, T. Imamura, T. Hiate, I. Khatri, Z. Tang, R. Ishikawa, K. Ueno, and H. Shirai, Appl. Phys. Lett. 102, 243902 (2013).
[CrossRef]

M. Ono, Z. Tang, R. Ishikawa, T. Gotou, K. Ueno, and H. Shirai, Appl. Phys. Express 5, 032301 (2012).
[CrossRef]

Tsai, C. Y.

P. Yu, C. Y. Tsai, J. K. Chang, C. C. Lai, P. H. Chen, Y. C. Lai, P. T. Tsai, M. C. Li, H. T. Pan, Y. Y. Huang, C. Wu, Y. L. Chueh, S. W. Chen, C. H. Du, S. F. Horng, and H. F. Meng, ACS Nano 7, 10780 (2013).
[CrossRef]

Tsai, P. T.

P. Yu, C. Y. Tsai, J. K. Chang, C. C. Lai, P. H. Chen, Y. C. Lai, P. T. Tsai, M. C. Li, H. T. Pan, Y. Y. Huang, C. Wu, Y. L. Chueh, S. W. Chen, C. H. Du, S. F. Horng, and H. F. Meng, ACS Nano 7, 10780 (2013).
[CrossRef]

Tsakalakos, L.

L. Tsakalakos, J. Balch, J. Fronheiser, B. A. Korevaar, O. Sulima, and J. Rand, Appl. Phys. Lett. 91, 233117 (2007).
[CrossRef]

Turan, R.

B. Ozdemir, M. Kulakci, R. Turan, and H. E. Unalan, Appl. Phys. Lett. 99, 113510 (2011).
[CrossRef]

Ueno, K.

Q. Liu, T. Imamura, T. Hiate, I. Khatri, Z. Tang, R. Ishikawa, K. Ueno, and H. Shirai, Appl. Phys. Lett. 102, 243902 (2013).
[CrossRef]

M. Ono, Z. Tang, R. Ishikawa, T. Gotou, K. Ueno, and H. Shirai, Appl. Phys. Express 5, 032301 (2012).
[CrossRef]

Um, H.-D.

S. A. Moiz, A. M. Nahhas, H.-D. Um, S.-W. Jee, H. K. Cho, S.-W. Kim, and J.-H. Lee, Nanotechnology 23, 145401 (2012).
[CrossRef]

Unalan, H. E.

B. Ozdemir, M. Kulakci, R. Turan, and H. E. Unalan, Appl. Phys. Lett. 99, 113510 (2011).
[CrossRef]

Vertelov, G. K.

S. Avasthi, Y. Qi, G. K. Vertelov, J. Schwartz, A. Kahn, and J. C. Sturm, Appl. Phys. Lett. 96, 222109 (2010).
[CrossRef]

Wang, B.

W. H. Lu, Q. Chen, B. Wang, and L. W. Chen, Appl. Phys. Lett. 100, 023112 (2012).
[CrossRef]

Wang, H.

L. He, C. Jiang, H. Wang, D. Lai, Y. H. Tan, C. S. Tan, and Rusli, Appl. Phys. Lett. 100, 103104 (2012).
[CrossRef]

L. He, Rusli, C. Jiang, H. Wang, and D. Lai, IEEE Electron Device Lett. 32, 1406 (2011).
[CrossRef]

Wang, S.

S. Jeong, E. C. Garnett, S. Wang, Z. Yu, S. Fan, M. L. Brongersma, M. D. McGehee, and Y. Cui, Nano Lett. 12, 2971 (2012).
[CrossRef]

Wu, C.

P. Yu, C. Y. Tsai, J. K. Chang, C. C. Lai, P. H. Chen, Y. C. Lai, P. T. Tsai, M. C. Li, H. T. Pan, Y. Y. Huang, C. Wu, Y. L. Chueh, S. W. Chen, C. H. Du, S. F. Horng, and H. F. Meng, ACS Nano 7, 10780 (2013).
[CrossRef]

Wu, Y.

K. Peng, Y. Xu, Y. Wu, Y. Yan, S.-T. Lee, and J. Zhu, Small 1, 1062 (2005).
[CrossRef]

Xu, Q.

J. Ouyang, Q. Xu, C. W. Chu, Y. Yang, G. Li, and J. Shinar, Polymer 45, 8443 (2004).
[CrossRef]

Xu, Y.

K. Peng, Y. Xu, Y. Wu, Y. Yan, S.-T. Lee, and J. Zhu, Small 1, 1062 (2005).
[CrossRef]

Yan, Y.

K. Peng, Y. Xu, Y. Wu, Y. Yan, S.-T. Lee, and J. Zhu, Small 1, 1062 (2005).
[CrossRef]

Yang, P.

E. Garnett and P. Yang, Nano Lett. 10, 1082 (2010).
[CrossRef]

E. C. Garnett and P. Yang, J. Am. Chem. Soc. 130, 9224 (2008).
[CrossRef]

Yang, P. D.

M. Law, L. E. Greene, J. C. Johnson, R. Saykally, and P. D. Yang, Nat. Mater. 4, 455 (2005).
[CrossRef]

Yang, Y.

J. Ouyang, Q. Xu, C. W. Chu, Y. Yang, G. Li, and J. Shinar, Polymer 45, 8443 (2004).
[CrossRef]

Yeh, C. L.

S. C. Shiu, J. J. Chao, S. C. Hung, C. L. Yeh, and C. F. Lin, Chem. Mater. 22, 3108 (2010).
[CrossRef]

Yu, P.

P. Yu, C. Y. Tsai, J. K. Chang, C. C. Lai, P. H. Chen, Y. C. Lai, P. T. Tsai, M. C. Li, H. T. Pan, Y. Y. Huang, C. Wu, Y. L. Chueh, S. W. Chen, C. H. Du, S. F. Horng, and H. F. Meng, ACS Nano 7, 10780 (2013).
[CrossRef]

T.-G. Chen, B.-Y. Huang, E.-C. Chen, P. Yu, and H.-F. Meng, Appl. Phys. Lett. 101, 033301 (2012).
[CrossRef]

Yu, Z.

S. Jeong, E. C. Garnett, S. Wang, Z. Yu, S. Fan, M. L. Brongersma, M. D. McGehee, and Y. Cui, Nano Lett. 12, 2971 (2012).
[CrossRef]

Zhang, F.

D. Liu, Y. Zhang, X. Fang, F. Zhang, T. Song, and B. Sun, IEEE Electron Device Lett. 34, 345 (2013).
[CrossRef]

Y. Zhu, T. Song, F. Zhang, S.-T. Lee, and B. Sun, Appl. Phys. Lett. 102, 113504 (2013).
[CrossRef]

J. Zhang, Y. Zhang, F. Zhang, and B. Sun, Appl. Phys. Lett. 102, 013501 (2013).
[CrossRef]

Zhang, J.

J. Zhang, Y. Zhang, F. Zhang, and B. Sun, Appl. Phys. Lett. 102, 013501 (2013).
[CrossRef]

Zhang, Y.

J. Zhang, Y. Zhang, F. Zhang, and B. Sun, Appl. Phys. Lett. 102, 013501 (2013).
[CrossRef]

D. Liu, Y. Zhang, X. Fang, F. Zhang, T. Song, and B. Sun, IEEE Electron Device Lett. 34, 345 (2013).
[CrossRef]

Zhu, J.

K. Peng, Y. Xu, Y. Wu, Y. Yan, S.-T. Lee, and J. Zhu, Small 1, 1062 (2005).
[CrossRef]

Zhu, Y.

Y. Zhu, T. Song, F. Zhang, S.-T. Lee, and B. Sun, Appl. Phys. Lett. 102, 113504 (2013).
[CrossRef]

ACS Nano (1)

P. Yu, C. Y. Tsai, J. K. Chang, C. C. Lai, P. H. Chen, Y. C. Lai, P. T. Tsai, M. C. Li, H. T. Pan, Y. Y. Huang, C. Wu, Y. L. Chueh, S. W. Chen, C. H. Du, S. F. Horng, and H. F. Meng, ACS Nano 7, 10780 (2013).
[CrossRef]

Appl. Phys. Express (1)

M. Ono, Z. Tang, R. Ishikawa, T. Gotou, K. Ueno, and H. Shirai, Appl. Phys. Express 5, 032301 (2012).
[CrossRef]

Appl. Phys. Lett. (9)

W. H. Lu, Q. Chen, B. Wang, and L. W. Chen, Appl. Phys. Lett. 100, 023112 (2012).
[CrossRef]

T.-G. Chen, B.-Y. Huang, E.-C. Chen, P. Yu, and H.-F. Meng, Appl. Phys. Lett. 101, 033301 (2012).
[CrossRef]

B. Ozdemir, M. Kulakci, R. Turan, and H. E. Unalan, Appl. Phys. Lett. 99, 113510 (2011).
[CrossRef]

L. Tsakalakos, J. Balch, J. Fronheiser, B. A. Korevaar, O. Sulima, and J. Rand, Appl. Phys. Lett. 91, 233117 (2007).
[CrossRef]

Y. Zhu, T. Song, F. Zhang, S.-T. Lee, and B. Sun, Appl. Phys. Lett. 102, 113504 (2013).
[CrossRef]

Q. Liu, T. Imamura, T. Hiate, I. Khatri, Z. Tang, R. Ishikawa, K. Ueno, and H. Shirai, Appl. Phys. Lett. 102, 243902 (2013).
[CrossRef]

L. He, C. Jiang, H. Wang, D. Lai, Y. H. Tan, C. S. Tan, and Rusli, Appl. Phys. Lett. 100, 103104 (2012).
[CrossRef]

J. Zhang, Y. Zhang, F. Zhang, and B. Sun, Appl. Phys. Lett. 102, 013501 (2013).
[CrossRef]

S. Avasthi, Y. Qi, G. K. Vertelov, J. Schwartz, A. Kahn, and J. C. Sturm, Appl. Phys. Lett. 96, 222109 (2010).
[CrossRef]

Chem. Mater. (1)

S. C. Shiu, J. J. Chao, S. C. Hung, C. L. Yeh, and C. F. Lin, Chem. Mater. 22, 3108 (2010).
[CrossRef]

IEEE Electron Device Lett. (2)

L. He, Rusli, C. Jiang, H. Wang, and D. Lai, IEEE Electron Device Lett. 32, 1406 (2011).
[CrossRef]

D. Liu, Y. Zhang, X. Fang, F. Zhang, T. Song, and B. Sun, IEEE Electron Device Lett. 34, 345 (2013).
[CrossRef]

J. Am. Chem. Soc. (1)

E. C. Garnett and P. Yang, J. Am. Chem. Soc. 130, 9224 (2008).
[CrossRef]

Nano Lett. (3)

S. Jeong, E. C. Garnett, S. Wang, Z. Yu, S. Fan, M. L. Brongersma, M. D. McGehee, and Y. Cui, Nano Lett. 12, 2971 (2012).
[CrossRef]

E. Garnett and P. Yang, Nano Lett. 10, 1082 (2010).
[CrossRef]

L. Hu and G. Chen, Nano Lett. 7, 3249 (2007).
[CrossRef]

Nanotechnology (1)

S. A. Moiz, A. M. Nahhas, H.-D. Um, S.-W. Jee, H. K. Cho, S.-W. Kim, and J.-H. Lee, Nanotechnology 23, 145401 (2012).
[CrossRef]

Nat. Mater. (1)

M. Law, L. E. Greene, J. C. Johnson, R. Saykally, and P. D. Yang, Nat. Mater. 4, 455 (2005).
[CrossRef]

Polymer (1)

J. Ouyang, Q. Xu, C. W. Chu, Y. Yang, G. Li, and J. Shinar, Polymer 45, 8443 (2004).
[CrossRef]

Prog. Photovolt. (1)

R. G. Little and M. J. Nowlan, Prog. Photovolt. 5, 309 (1997).
[CrossRef]

Science (2)

R. F. Service, Science 319, 718 (2008).
[CrossRef]

M. J. Sailor, E. J. Ginsburg, C. B. Gorman, A. Kumar, R. H. Grubbs, and N. S. Lewis, Science 249, 1146 (1990).
[CrossRef]

Small (1)

K. Peng, Y. Xu, Y. Wu, Y. Yan, S.-T. Lee, and J. Zhu, Small 1, 1062 (2005).
[CrossRef]

Sol. Energy (1)

V. M. Fthenakis and H. C. Kim, Sol. Energy 85, 1609 (2011).
[CrossRef]

Cited By

OSA participates in CrossRef's Cited-By Linking service. Citing articles from OSA journals and other participating publishers are listed here.

Alert me when this article is cited.


Figures (5)

Fig. 1.
Fig. 1.

(a) Schematic structure of the hybrid solar cells. (b) SEM images of top view and cross-section of SiNW arrays. (c) Schematic of the solution-evacuated process for the hybrid active layer.

Fig. 2.
Fig. 2.

SEM cross-section of the hybrid active layers with the different solution-evacuated times. A corresponds to top area of the hybrid active layer profile while B corresponds to bottom area of the hybrid active layer profile.

Fig. 3.
Fig. 3.

Variation of the relative profile atomic concentrations that were averaged from three-spots test results for the cross-section area of the corresponding Fig. 2.

Fig. 4.
Fig. 4.

Current density and voltage (J-V) characteristics of the hybrid solar cells by the different solution-evacuated times.

Fig. 5.
Fig. 5.

Reflectance and external quantum efficiency spectra of the hybrid solar cells by the different solution-evacuated times.

Tables (1)

Tables Icon

Table 1. Summary of Photovoltaic Characteristics of the Hybrid Solar Cells by the Different Solution-Evacuated Times

Metrics