Abstract

We demonstrate highly flexible and efficient top-emitting organic light-emitting devices (TOLEDs) by using an ultrasmooth Ag anode. A template-stripping process has been employed to create the ultrasmooth Ag anode on a photopolymer substrate. The flexible TOLEDs obtained by this method keep good electroluminescence properties under a small bending radius and after repeated bending. The efficiency of the flexible TOLEDs is improved by 60% compared with the conventional TOLEDs deposited on Si substrate due to the enhanced hole injection from the ultrasmooth anode.

© 2012 Optical Society of America

Full Article  |  PDF Article

References

  • View by:
  • |
  • |
  • |

  1. G. Gustafsson, Y. Cao, G. M. Treacy, F. Klavetter, N. Colaneri, and A. J. Heeger, Nature 357, 477 (1992).
    [CrossRef]
  2. G. Gu, P. E. Burrows, S. Venkatesh, S. R. Forrest, and M. E. Thompson, Opt. Lett. 22, 172 (1997).
    [CrossRef]
  3. A. N. Krasnov, Appl. Phys. Lett. 80, 3853 (2002).
    [CrossRef]
  4. Z. Y. Xie, L. S. Hung, and F. R. Zhu, Chem. Phys. Lett. 381, 691 (2003).
    [CrossRef]
  5. Y. Q. Li, L. W. Tan, X. T. Hao, K. S. Ong, F. R. Zhu, and L. S. Hung, Appl. Phys. Lett. 86, 153508 (2005).
    [CrossRef]
  6. A. R. Schlatmann, D. W. Floet, A. Hilberer, F. Garten, P. J. M. Smulders, T. M. Klapwijk, and G. Hadziioannou, Appl. Phys. Lett. 69, 1764 (1996).
    [CrossRef]
  7. G. F. Wang, X. M. Tao, and R. X. Wang, Nanotechnology 19, 145201 (2008).
    [CrossRef]
  8. H. Cho, C. Yun, J. W. Park, and S. Yoo, Org. Electron. 10, 1163 (2009).
    [CrossRef]
  9. R. Paetzold, K. Heuser, D. Henseler, S. Roeger, G. Wittmann, and A. Winnacker, Appl. Phys. Lett. 82, 3342 (2003).
    [CrossRef]
  10. W. F. Wu and B. S. Chiou, Thin Solid Films 298, 221 (1997).
    [CrossRef]
  11. S. Cheylan, D. S. Ghosh, D. Krautz, T. L. Chen, and V. Pruneri, Org. Electron. 12, 818 (2011).
    [CrossRef]
  12. Y. Y. Yuan, S. Han, D. Grozea, and Z. H. Lu, Appl. Phys. Lett. 88, 093503 (2006).
    [CrossRef]
  13. D. D. Zhang, J. Feng, Y. F. Liu, Y. Q. Zhong, Y. Bai, Y. Jin, G. H. Xie, Q. Xue, Y. Zhao, S. Y. Liu, and H. B. Sun, Appl. Phys. Lett. 94, 223306 (2009).
    [CrossRef]
  14. H. You, Y. F. Dai, Z. Q. Zhang, and D. G. Ma, J. Appl. Phys. 101, 026105 (2007).
    [CrossRef]
  15. M. Hegner, P. Wagner, and G. Semenza, Surf. Sci. 291, 39 (1993).
    [CrossRef]
  16. P. Nagpal, N. C. Lindquist, S. H. Oh, and D. J. Norris, Science 325, 594 (2009).
    [CrossRef]
  17. N. C. Lindquist, T. W. Johnson, D. J. Norris, and S. H. Oh, Nano Lett. 11, 3526 (2011).
    [CrossRef]
  18. J. Cao, X. Y. Jiang, and Z. L. Zhang, Appl. Phys. Lett. 89, 252108 (2006).
    [CrossRef]

2011 (2)

S. Cheylan, D. S. Ghosh, D. Krautz, T. L. Chen, and V. Pruneri, Org. Electron. 12, 818 (2011).
[CrossRef]

N. C. Lindquist, T. W. Johnson, D. J. Norris, and S. H. Oh, Nano Lett. 11, 3526 (2011).
[CrossRef]

2009 (3)

D. D. Zhang, J. Feng, Y. F. Liu, Y. Q. Zhong, Y. Bai, Y. Jin, G. H. Xie, Q. Xue, Y. Zhao, S. Y. Liu, and H. B. Sun, Appl. Phys. Lett. 94, 223306 (2009).
[CrossRef]

P. Nagpal, N. C. Lindquist, S. H. Oh, and D. J. Norris, Science 325, 594 (2009).
[CrossRef]

H. Cho, C. Yun, J. W. Park, and S. Yoo, Org. Electron. 10, 1163 (2009).
[CrossRef]

2008 (1)

G. F. Wang, X. M. Tao, and R. X. Wang, Nanotechnology 19, 145201 (2008).
[CrossRef]

2007 (1)

H. You, Y. F. Dai, Z. Q. Zhang, and D. G. Ma, J. Appl. Phys. 101, 026105 (2007).
[CrossRef]

2006 (2)

J. Cao, X. Y. Jiang, and Z. L. Zhang, Appl. Phys. Lett. 89, 252108 (2006).
[CrossRef]

Y. Y. Yuan, S. Han, D. Grozea, and Z. H. Lu, Appl. Phys. Lett. 88, 093503 (2006).
[CrossRef]

2005 (1)

Y. Q. Li, L. W. Tan, X. T. Hao, K. S. Ong, F. R. Zhu, and L. S. Hung, Appl. Phys. Lett. 86, 153508 (2005).
[CrossRef]

2003 (2)

Z. Y. Xie, L. S. Hung, and F. R. Zhu, Chem. Phys. Lett. 381, 691 (2003).
[CrossRef]

R. Paetzold, K. Heuser, D. Henseler, S. Roeger, G. Wittmann, and A. Winnacker, Appl. Phys. Lett. 82, 3342 (2003).
[CrossRef]

2002 (1)

A. N. Krasnov, Appl. Phys. Lett. 80, 3853 (2002).
[CrossRef]

1997 (2)

1996 (1)

A. R. Schlatmann, D. W. Floet, A. Hilberer, F. Garten, P. J. M. Smulders, T. M. Klapwijk, and G. Hadziioannou, Appl. Phys. Lett. 69, 1764 (1996).
[CrossRef]

1993 (1)

M. Hegner, P. Wagner, and G. Semenza, Surf. Sci. 291, 39 (1993).
[CrossRef]

1992 (1)

G. Gustafsson, Y. Cao, G. M. Treacy, F. Klavetter, N. Colaneri, and A. J. Heeger, Nature 357, 477 (1992).
[CrossRef]

Bai, Y.

D. D. Zhang, J. Feng, Y. F. Liu, Y. Q. Zhong, Y. Bai, Y. Jin, G. H. Xie, Q. Xue, Y. Zhao, S. Y. Liu, and H. B. Sun, Appl. Phys. Lett. 94, 223306 (2009).
[CrossRef]

Burrows, P. E.

Cao, J.

J. Cao, X. Y. Jiang, and Z. L. Zhang, Appl. Phys. Lett. 89, 252108 (2006).
[CrossRef]

Cao, Y.

G. Gustafsson, Y. Cao, G. M. Treacy, F. Klavetter, N. Colaneri, and A. J. Heeger, Nature 357, 477 (1992).
[CrossRef]

Chen, T. L.

S. Cheylan, D. S. Ghosh, D. Krautz, T. L. Chen, and V. Pruneri, Org. Electron. 12, 818 (2011).
[CrossRef]

Cheylan, S.

S. Cheylan, D. S. Ghosh, D. Krautz, T. L. Chen, and V. Pruneri, Org. Electron. 12, 818 (2011).
[CrossRef]

Chiou, B. S.

W. F. Wu and B. S. Chiou, Thin Solid Films 298, 221 (1997).
[CrossRef]

Cho, H.

H. Cho, C. Yun, J. W. Park, and S. Yoo, Org. Electron. 10, 1163 (2009).
[CrossRef]

Colaneri, N.

G. Gustafsson, Y. Cao, G. M. Treacy, F. Klavetter, N. Colaneri, and A. J. Heeger, Nature 357, 477 (1992).
[CrossRef]

Dai, Y. F.

H. You, Y. F. Dai, Z. Q. Zhang, and D. G. Ma, J. Appl. Phys. 101, 026105 (2007).
[CrossRef]

Feng, J.

D. D. Zhang, J. Feng, Y. F. Liu, Y. Q. Zhong, Y. Bai, Y. Jin, G. H. Xie, Q. Xue, Y. Zhao, S. Y. Liu, and H. B. Sun, Appl. Phys. Lett. 94, 223306 (2009).
[CrossRef]

Floet, D. W.

A. R. Schlatmann, D. W. Floet, A. Hilberer, F. Garten, P. J. M. Smulders, T. M. Klapwijk, and G. Hadziioannou, Appl. Phys. Lett. 69, 1764 (1996).
[CrossRef]

Forrest, S. R.

Garten, F.

A. R. Schlatmann, D. W. Floet, A. Hilberer, F. Garten, P. J. M. Smulders, T. M. Klapwijk, and G. Hadziioannou, Appl. Phys. Lett. 69, 1764 (1996).
[CrossRef]

Ghosh, D. S.

S. Cheylan, D. S. Ghosh, D. Krautz, T. L. Chen, and V. Pruneri, Org. Electron. 12, 818 (2011).
[CrossRef]

Grozea, D.

Y. Y. Yuan, S. Han, D. Grozea, and Z. H. Lu, Appl. Phys. Lett. 88, 093503 (2006).
[CrossRef]

Gu, G.

Gustafsson, G.

G. Gustafsson, Y. Cao, G. M. Treacy, F. Klavetter, N. Colaneri, and A. J. Heeger, Nature 357, 477 (1992).
[CrossRef]

Hadziioannou, G.

A. R. Schlatmann, D. W. Floet, A. Hilberer, F. Garten, P. J. M. Smulders, T. M. Klapwijk, and G. Hadziioannou, Appl. Phys. Lett. 69, 1764 (1996).
[CrossRef]

Han, S.

Y. Y. Yuan, S. Han, D. Grozea, and Z. H. Lu, Appl. Phys. Lett. 88, 093503 (2006).
[CrossRef]

Hao, X. T.

Y. Q. Li, L. W. Tan, X. T. Hao, K. S. Ong, F. R. Zhu, and L. S. Hung, Appl. Phys. Lett. 86, 153508 (2005).
[CrossRef]

Heeger, A. J.

G. Gustafsson, Y. Cao, G. M. Treacy, F. Klavetter, N. Colaneri, and A. J. Heeger, Nature 357, 477 (1992).
[CrossRef]

Hegner, M.

M. Hegner, P. Wagner, and G. Semenza, Surf. Sci. 291, 39 (1993).
[CrossRef]

Henseler, D.

R. Paetzold, K. Heuser, D. Henseler, S. Roeger, G. Wittmann, and A. Winnacker, Appl. Phys. Lett. 82, 3342 (2003).
[CrossRef]

Heuser, K.

R. Paetzold, K. Heuser, D. Henseler, S. Roeger, G. Wittmann, and A. Winnacker, Appl. Phys. Lett. 82, 3342 (2003).
[CrossRef]

Hilberer, A.

A. R. Schlatmann, D. W. Floet, A. Hilberer, F. Garten, P. J. M. Smulders, T. M. Klapwijk, and G. Hadziioannou, Appl. Phys. Lett. 69, 1764 (1996).
[CrossRef]

Hung, L. S.

Y. Q. Li, L. W. Tan, X. T. Hao, K. S. Ong, F. R. Zhu, and L. S. Hung, Appl. Phys. Lett. 86, 153508 (2005).
[CrossRef]

Z. Y. Xie, L. S. Hung, and F. R. Zhu, Chem. Phys. Lett. 381, 691 (2003).
[CrossRef]

Jiang, X. Y.

J. Cao, X. Y. Jiang, and Z. L. Zhang, Appl. Phys. Lett. 89, 252108 (2006).
[CrossRef]

Jin, Y.

D. D. Zhang, J. Feng, Y. F. Liu, Y. Q. Zhong, Y. Bai, Y. Jin, G. H. Xie, Q. Xue, Y. Zhao, S. Y. Liu, and H. B. Sun, Appl. Phys. Lett. 94, 223306 (2009).
[CrossRef]

Johnson, T. W.

N. C. Lindquist, T. W. Johnson, D. J. Norris, and S. H. Oh, Nano Lett. 11, 3526 (2011).
[CrossRef]

Klapwijk, T. M.

A. R. Schlatmann, D. W. Floet, A. Hilberer, F. Garten, P. J. M. Smulders, T. M. Klapwijk, and G. Hadziioannou, Appl. Phys. Lett. 69, 1764 (1996).
[CrossRef]

Klavetter, F.

G. Gustafsson, Y. Cao, G. M. Treacy, F. Klavetter, N. Colaneri, and A. J. Heeger, Nature 357, 477 (1992).
[CrossRef]

Krasnov, A. N.

A. N. Krasnov, Appl. Phys. Lett. 80, 3853 (2002).
[CrossRef]

Krautz, D.

S. Cheylan, D. S. Ghosh, D. Krautz, T. L. Chen, and V. Pruneri, Org. Electron. 12, 818 (2011).
[CrossRef]

Li, Y. Q.

Y. Q. Li, L. W. Tan, X. T. Hao, K. S. Ong, F. R. Zhu, and L. S. Hung, Appl. Phys. Lett. 86, 153508 (2005).
[CrossRef]

Lindquist, N. C.

N. C. Lindquist, T. W. Johnson, D. J. Norris, and S. H. Oh, Nano Lett. 11, 3526 (2011).
[CrossRef]

P. Nagpal, N. C. Lindquist, S. H. Oh, and D. J. Norris, Science 325, 594 (2009).
[CrossRef]

Liu, S. Y.

D. D. Zhang, J. Feng, Y. F. Liu, Y. Q. Zhong, Y. Bai, Y. Jin, G. H. Xie, Q. Xue, Y. Zhao, S. Y. Liu, and H. B. Sun, Appl. Phys. Lett. 94, 223306 (2009).
[CrossRef]

Liu, Y. F.

D. D. Zhang, J. Feng, Y. F. Liu, Y. Q. Zhong, Y. Bai, Y. Jin, G. H. Xie, Q. Xue, Y. Zhao, S. Y. Liu, and H. B. Sun, Appl. Phys. Lett. 94, 223306 (2009).
[CrossRef]

Lu, Z. H.

Y. Y. Yuan, S. Han, D. Grozea, and Z. H. Lu, Appl. Phys. Lett. 88, 093503 (2006).
[CrossRef]

Ma, D. G.

H. You, Y. F. Dai, Z. Q. Zhang, and D. G. Ma, J. Appl. Phys. 101, 026105 (2007).
[CrossRef]

Nagpal, P.

P. Nagpal, N. C. Lindquist, S. H. Oh, and D. J. Norris, Science 325, 594 (2009).
[CrossRef]

Norris, D. J.

N. C. Lindquist, T. W. Johnson, D. J. Norris, and S. H. Oh, Nano Lett. 11, 3526 (2011).
[CrossRef]

P. Nagpal, N. C. Lindquist, S. H. Oh, and D. J. Norris, Science 325, 594 (2009).
[CrossRef]

Oh, S. H.

N. C. Lindquist, T. W. Johnson, D. J. Norris, and S. H. Oh, Nano Lett. 11, 3526 (2011).
[CrossRef]

P. Nagpal, N. C. Lindquist, S. H. Oh, and D. J. Norris, Science 325, 594 (2009).
[CrossRef]

Ong, K. S.

Y. Q. Li, L. W. Tan, X. T. Hao, K. S. Ong, F. R. Zhu, and L. S. Hung, Appl. Phys. Lett. 86, 153508 (2005).
[CrossRef]

Paetzold, R.

R. Paetzold, K. Heuser, D. Henseler, S. Roeger, G. Wittmann, and A. Winnacker, Appl. Phys. Lett. 82, 3342 (2003).
[CrossRef]

Park, J. W.

H. Cho, C. Yun, J. W. Park, and S. Yoo, Org. Electron. 10, 1163 (2009).
[CrossRef]

Pruneri, V.

S. Cheylan, D. S. Ghosh, D. Krautz, T. L. Chen, and V. Pruneri, Org. Electron. 12, 818 (2011).
[CrossRef]

Roeger, S.

R. Paetzold, K. Heuser, D. Henseler, S. Roeger, G. Wittmann, and A. Winnacker, Appl. Phys. Lett. 82, 3342 (2003).
[CrossRef]

Schlatmann, A. R.

A. R. Schlatmann, D. W. Floet, A. Hilberer, F. Garten, P. J. M. Smulders, T. M. Klapwijk, and G. Hadziioannou, Appl. Phys. Lett. 69, 1764 (1996).
[CrossRef]

Semenza, G.

M. Hegner, P. Wagner, and G. Semenza, Surf. Sci. 291, 39 (1993).
[CrossRef]

Smulders, P. J. M.

A. R. Schlatmann, D. W. Floet, A. Hilberer, F. Garten, P. J. M. Smulders, T. M. Klapwijk, and G. Hadziioannou, Appl. Phys. Lett. 69, 1764 (1996).
[CrossRef]

Sun, H. B.

D. D. Zhang, J. Feng, Y. F. Liu, Y. Q. Zhong, Y. Bai, Y. Jin, G. H. Xie, Q. Xue, Y. Zhao, S. Y. Liu, and H. B. Sun, Appl. Phys. Lett. 94, 223306 (2009).
[CrossRef]

Tan, L. W.

Y. Q. Li, L. W. Tan, X. T. Hao, K. S. Ong, F. R. Zhu, and L. S. Hung, Appl. Phys. Lett. 86, 153508 (2005).
[CrossRef]

Tao, X. M.

G. F. Wang, X. M. Tao, and R. X. Wang, Nanotechnology 19, 145201 (2008).
[CrossRef]

Thompson, M. E.

Treacy, G. M.

G. Gustafsson, Y. Cao, G. M. Treacy, F. Klavetter, N. Colaneri, and A. J. Heeger, Nature 357, 477 (1992).
[CrossRef]

Venkatesh, S.

Wagner, P.

M. Hegner, P. Wagner, and G. Semenza, Surf. Sci. 291, 39 (1993).
[CrossRef]

Wang, G. F.

G. F. Wang, X. M. Tao, and R. X. Wang, Nanotechnology 19, 145201 (2008).
[CrossRef]

Wang, R. X.

G. F. Wang, X. M. Tao, and R. X. Wang, Nanotechnology 19, 145201 (2008).
[CrossRef]

Winnacker, A.

R. Paetzold, K. Heuser, D. Henseler, S. Roeger, G. Wittmann, and A. Winnacker, Appl. Phys. Lett. 82, 3342 (2003).
[CrossRef]

Wittmann, G.

R. Paetzold, K. Heuser, D. Henseler, S. Roeger, G. Wittmann, and A. Winnacker, Appl. Phys. Lett. 82, 3342 (2003).
[CrossRef]

Wu, W. F.

W. F. Wu and B. S. Chiou, Thin Solid Films 298, 221 (1997).
[CrossRef]

Xie, G. H.

D. D. Zhang, J. Feng, Y. F. Liu, Y. Q. Zhong, Y. Bai, Y. Jin, G. H. Xie, Q. Xue, Y. Zhao, S. Y. Liu, and H. B. Sun, Appl. Phys. Lett. 94, 223306 (2009).
[CrossRef]

Xie, Z. Y.

Z. Y. Xie, L. S. Hung, and F. R. Zhu, Chem. Phys. Lett. 381, 691 (2003).
[CrossRef]

Xue, Q.

D. D. Zhang, J. Feng, Y. F. Liu, Y. Q. Zhong, Y. Bai, Y. Jin, G. H. Xie, Q. Xue, Y. Zhao, S. Y. Liu, and H. B. Sun, Appl. Phys. Lett. 94, 223306 (2009).
[CrossRef]

Yoo, S.

H. Cho, C. Yun, J. W. Park, and S. Yoo, Org. Electron. 10, 1163 (2009).
[CrossRef]

You, H.

H. You, Y. F. Dai, Z. Q. Zhang, and D. G. Ma, J. Appl. Phys. 101, 026105 (2007).
[CrossRef]

Yuan, Y. Y.

Y. Y. Yuan, S. Han, D. Grozea, and Z. H. Lu, Appl. Phys. Lett. 88, 093503 (2006).
[CrossRef]

Yun, C.

H. Cho, C. Yun, J. W. Park, and S. Yoo, Org. Electron. 10, 1163 (2009).
[CrossRef]

Zhang, D. D.

D. D. Zhang, J. Feng, Y. F. Liu, Y. Q. Zhong, Y. Bai, Y. Jin, G. H. Xie, Q. Xue, Y. Zhao, S. Y. Liu, and H. B. Sun, Appl. Phys. Lett. 94, 223306 (2009).
[CrossRef]

Zhang, Z. L.

J. Cao, X. Y. Jiang, and Z. L. Zhang, Appl. Phys. Lett. 89, 252108 (2006).
[CrossRef]

Zhang, Z. Q.

H. You, Y. F. Dai, Z. Q. Zhang, and D. G. Ma, J. Appl. Phys. 101, 026105 (2007).
[CrossRef]

Zhao, Y.

D. D. Zhang, J. Feng, Y. F. Liu, Y. Q. Zhong, Y. Bai, Y. Jin, G. H. Xie, Q. Xue, Y. Zhao, S. Y. Liu, and H. B. Sun, Appl. Phys. Lett. 94, 223306 (2009).
[CrossRef]

Zhong, Y. Q.

D. D. Zhang, J. Feng, Y. F. Liu, Y. Q. Zhong, Y. Bai, Y. Jin, G. H. Xie, Q. Xue, Y. Zhao, S. Y. Liu, and H. B. Sun, Appl. Phys. Lett. 94, 223306 (2009).
[CrossRef]

Zhu, F. R.

Y. Q. Li, L. W. Tan, X. T. Hao, K. S. Ong, F. R. Zhu, and L. S. Hung, Appl. Phys. Lett. 86, 153508 (2005).
[CrossRef]

Z. Y. Xie, L. S. Hung, and F. R. Zhu, Chem. Phys. Lett. 381, 691 (2003).
[CrossRef]

Appl. Phys. Lett. (7)

Y. Q. Li, L. W. Tan, X. T. Hao, K. S. Ong, F. R. Zhu, and L. S. Hung, Appl. Phys. Lett. 86, 153508 (2005).
[CrossRef]

A. R. Schlatmann, D. W. Floet, A. Hilberer, F. Garten, P. J. M. Smulders, T. M. Klapwijk, and G. Hadziioannou, Appl. Phys. Lett. 69, 1764 (1996).
[CrossRef]

A. N. Krasnov, Appl. Phys. Lett. 80, 3853 (2002).
[CrossRef]

R. Paetzold, K. Heuser, D. Henseler, S. Roeger, G. Wittmann, and A. Winnacker, Appl. Phys. Lett. 82, 3342 (2003).
[CrossRef]

Y. Y. Yuan, S. Han, D. Grozea, and Z. H. Lu, Appl. Phys. Lett. 88, 093503 (2006).
[CrossRef]

D. D. Zhang, J. Feng, Y. F. Liu, Y. Q. Zhong, Y. Bai, Y. Jin, G. H. Xie, Q. Xue, Y. Zhao, S. Y. Liu, and H. B. Sun, Appl. Phys. Lett. 94, 223306 (2009).
[CrossRef]

J. Cao, X. Y. Jiang, and Z. L. Zhang, Appl. Phys. Lett. 89, 252108 (2006).
[CrossRef]

Chem. Phys. Lett. (1)

Z. Y. Xie, L. S. Hung, and F. R. Zhu, Chem. Phys. Lett. 381, 691 (2003).
[CrossRef]

J. Appl. Phys. (1)

H. You, Y. F. Dai, Z. Q. Zhang, and D. G. Ma, J. Appl. Phys. 101, 026105 (2007).
[CrossRef]

Nano Lett. (1)

N. C. Lindquist, T. W. Johnson, D. J. Norris, and S. H. Oh, Nano Lett. 11, 3526 (2011).
[CrossRef]

Nanotechnology (1)

G. F. Wang, X. M. Tao, and R. X. Wang, Nanotechnology 19, 145201 (2008).
[CrossRef]

Nature (1)

G. Gustafsson, Y. Cao, G. M. Treacy, F. Klavetter, N. Colaneri, and A. J. Heeger, Nature 357, 477 (1992).
[CrossRef]

Opt. Lett. (1)

Org. Electron. (2)

S. Cheylan, D. S. Ghosh, D. Krautz, T. L. Chen, and V. Pruneri, Org. Electron. 12, 818 (2011).
[CrossRef]

H. Cho, C. Yun, J. W. Park, and S. Yoo, Org. Electron. 10, 1163 (2009).
[CrossRef]

Science (1)

P. Nagpal, N. C. Lindquist, S. H. Oh, and D. J. Norris, Science 325, 594 (2009).
[CrossRef]

Surf. Sci. (1)

M. Hegner, P. Wagner, and G. Semenza, Surf. Sci. 291, 39 (1993).
[CrossRef]

Thin Solid Films (1)

W. F. Wu and B. S. Chiou, Thin Solid Films 298, 221 (1997).
[CrossRef]

Cited By

OSA participates in CrossRef's Cited-By Linking service. Citing articles from OSA journals and other participating publishers are listed here.

Alert me when this article is cited.


Figures (4)

Fig. 1.
Fig. 1.

Scheme of fabricating ultrasmooth Ag film by template stripping. (a) A cleaned Si substrate is prepared as the template. (b) Ag film is deposited onto the Si template by thermal evaporation. (c) Photopolymer is spin-coated as a backing film. (d) The Ag film adhered to the cured photopolymer film is stripped.

Fig. 2.
Fig. 2.

AFM images of (a) Si surface, (b) template-stripped Ag surface, and (c) as-evaporated Ag surface. (d) Current density-voltage characteristics of hole-only devices on Si and stripped photopolymer substrates.

Fig. 3.
Fig. 3.

EL performance of TOLEDs on Si and peeled-off photopolymer substrates. (a) Current density-voltage and (b) luminance-current density-efficiency characteristics.

Fig. 4.
Fig. 4.

Flexibility and mechanical robustness of the flexible TOLEDs. (a)–(g) Photographs of the flexible TOLEDs at different bending radius. (h) Luminance and efficiency at 5 V as a function of the number of bending cycles. Inset in (h): Comparison of EL spectra and J-V characteristics before and after repeated bending.

Metrics