Abstract

A systematic study of the effects of poling time and applied voltage on second-harmonic (SH) generation in thermally poled silica glass reveals that the SH signal is proportional to the square of the applied voltage and that the speed of the poling process increases with the applied voltage. Prior treatment of the samples is found to affect the poling process, and the optimum poling conditions are observed to depend on the poling atmosphere. The mechanism of thermal poling is discussed in the light of these new results.

© 1996 Optical Society of America

Full Article  |  PDF Article

References

  • View by:
  • |
  • |
  • |

  1. R. A. Myers, N. Mukherjee, S. R. J. Brueck, Opt. Lett. 15, 1733 (1991).
  2. P. G. Kazansky, L. Dong, P. St. J. Russell, Opt. Lett. 19, 701 (1994).
    [CrossRef] [PubMed]
  3. R. Kashyap, G. J. Veldhuis, D. C. Rogers, P. F. McKee, Appl. Phys. Lett. 64, 1332 (1994).
    [CrossRef]
  4. P. G. Kazansky, V. Pruneri, P. St. J. Russell, Opt. Lett. 20, 843 (1995).
    [CrossRef] [PubMed]
  5. A. C. Liu, M. J. F. Digonnet, G. S. Kino, Opt. Lett. 19, 466 (1994).
    [CrossRef] [PubMed]
  6. X.-C. Long, R. A. Myers, S. R. J. Brueck, Electron. Lett. 30, 2162 (1994).
    [CrossRef]
  7. P. G. Kazansky, P. St. J. Russell, L. Dong, C. N. Pannell, Electron. Lett. 31, 62 (1995).
    [CrossRef]
  8. P. G. Kazansky, L. Dong, P. St. J. Russell, Electron. Lett. 30, 1345 (1994).
    [CrossRef]
  9. T. Fujiwara, D. Wong, Y. Zhao, S. Fleming, S. Poole, M. Sceats, Electron. Lett. 31, 573 (1995).
    [CrossRef]
  10. N. Mukherjee, R. A. Myers, S. R. J. Brueck, J. Opt. Soc. Am. B 11, 665 (1994).
    [CrossRef]
  11. P. G. Kazansky, P. St. J. Russell, Opt. Commun. 110, 611 (1994).
    [CrossRef]
  12. R. A. Myers, S. R. J. Brueck, R. P. Tumminelli, Proc. SPIE 2289, 158 (1994).
    [CrossRef]
  13. R. A. Myers, X.-C. Long, S. R. J. Brueck, Proc. SPIE 2289, 98 (1994).
    [CrossRef]

1995

P. G. Kazansky, V. Pruneri, P. St. J. Russell, Opt. Lett. 20, 843 (1995).
[CrossRef] [PubMed]

T. Fujiwara, D. Wong, Y. Zhao, S. Fleming, S. Poole, M. Sceats, Electron. Lett. 31, 573 (1995).
[CrossRef]

P. G. Kazansky, P. St. J. Russell, L. Dong, C. N. Pannell, Electron. Lett. 31, 62 (1995).
[CrossRef]

1994

P. G. Kazansky, L. Dong, P. St. J. Russell, Electron. Lett. 30, 1345 (1994).
[CrossRef]

N. Mukherjee, R. A. Myers, S. R. J. Brueck, J. Opt. Soc. Am. B 11, 665 (1994).
[CrossRef]

P. G. Kazansky, P. St. J. Russell, Opt. Commun. 110, 611 (1994).
[CrossRef]

R. A. Myers, S. R. J. Brueck, R. P. Tumminelli, Proc. SPIE 2289, 158 (1994).
[CrossRef]

R. A. Myers, X.-C. Long, S. R. J. Brueck, Proc. SPIE 2289, 98 (1994).
[CrossRef]

A. C. Liu, M. J. F. Digonnet, G. S. Kino, Opt. Lett. 19, 466 (1994).
[CrossRef] [PubMed]

X.-C. Long, R. A. Myers, S. R. J. Brueck, Electron. Lett. 30, 2162 (1994).
[CrossRef]

P. G. Kazansky, L. Dong, P. St. J. Russell, Opt. Lett. 19, 701 (1994).
[CrossRef] [PubMed]

R. Kashyap, G. J. Veldhuis, D. C. Rogers, P. F. McKee, Appl. Phys. Lett. 64, 1332 (1994).
[CrossRef]

1991

R. A. Myers, N. Mukherjee, S. R. J. Brueck, Opt. Lett. 15, 1733 (1991).

Brueck, S. R. J.

X.-C. Long, R. A. Myers, S. R. J. Brueck, Electron. Lett. 30, 2162 (1994).
[CrossRef]

N. Mukherjee, R. A. Myers, S. R. J. Brueck, J. Opt. Soc. Am. B 11, 665 (1994).
[CrossRef]

R. A. Myers, S. R. J. Brueck, R. P. Tumminelli, Proc. SPIE 2289, 158 (1994).
[CrossRef]

R. A. Myers, X.-C. Long, S. R. J. Brueck, Proc. SPIE 2289, 98 (1994).
[CrossRef]

R. A. Myers, N. Mukherjee, S. R. J. Brueck, Opt. Lett. 15, 1733 (1991).

Digonnet, M. J. F.

Dong, L.

P. G. Kazansky, P. St. J. Russell, L. Dong, C. N. Pannell, Electron. Lett. 31, 62 (1995).
[CrossRef]

P. G. Kazansky, L. Dong, P. St. J. Russell, Electron. Lett. 30, 1345 (1994).
[CrossRef]

P. G. Kazansky, L. Dong, P. St. J. Russell, Opt. Lett. 19, 701 (1994).
[CrossRef] [PubMed]

Fleming, S.

T. Fujiwara, D. Wong, Y. Zhao, S. Fleming, S. Poole, M. Sceats, Electron. Lett. 31, 573 (1995).
[CrossRef]

Fujiwara, T.

T. Fujiwara, D. Wong, Y. Zhao, S. Fleming, S. Poole, M. Sceats, Electron. Lett. 31, 573 (1995).
[CrossRef]

Kashyap, R.

R. Kashyap, G. J. Veldhuis, D. C. Rogers, P. F. McKee, Appl. Phys. Lett. 64, 1332 (1994).
[CrossRef]

Kazansky, P. G.

P. G. Kazansky, V. Pruneri, P. St. J. Russell, Opt. Lett. 20, 843 (1995).
[CrossRef] [PubMed]

P. G. Kazansky, P. St. J. Russell, L. Dong, C. N. Pannell, Electron. Lett. 31, 62 (1995).
[CrossRef]

P. G. Kazansky, L. Dong, P. St. J. Russell, Electron. Lett. 30, 1345 (1994).
[CrossRef]

P. G. Kazansky, P. St. J. Russell, Opt. Commun. 110, 611 (1994).
[CrossRef]

P. G. Kazansky, L. Dong, P. St. J. Russell, Opt. Lett. 19, 701 (1994).
[CrossRef] [PubMed]

Kino, G. S.

Liu, A. C.

Long, X.-C.

X.-C. Long, R. A. Myers, S. R. J. Brueck, Electron. Lett. 30, 2162 (1994).
[CrossRef]

R. A. Myers, X.-C. Long, S. R. J. Brueck, Proc. SPIE 2289, 98 (1994).
[CrossRef]

McKee, P. F.

R. Kashyap, G. J. Veldhuis, D. C. Rogers, P. F. McKee, Appl. Phys. Lett. 64, 1332 (1994).
[CrossRef]

Mukherjee, N.

N. Mukherjee, R. A. Myers, S. R. J. Brueck, J. Opt. Soc. Am. B 11, 665 (1994).
[CrossRef]

R. A. Myers, N. Mukherjee, S. R. J. Brueck, Opt. Lett. 15, 1733 (1991).

Myers, R. A.

X.-C. Long, R. A. Myers, S. R. J. Brueck, Electron. Lett. 30, 2162 (1994).
[CrossRef]

N. Mukherjee, R. A. Myers, S. R. J. Brueck, J. Opt. Soc. Am. B 11, 665 (1994).
[CrossRef]

R. A. Myers, S. R. J. Brueck, R. P. Tumminelli, Proc. SPIE 2289, 158 (1994).
[CrossRef]

R. A. Myers, X.-C. Long, S. R. J. Brueck, Proc. SPIE 2289, 98 (1994).
[CrossRef]

R. A. Myers, N. Mukherjee, S. R. J. Brueck, Opt. Lett. 15, 1733 (1991).

Pannell, C. N.

P. G. Kazansky, P. St. J. Russell, L. Dong, C. N. Pannell, Electron. Lett. 31, 62 (1995).
[CrossRef]

Poole, S.

T. Fujiwara, D. Wong, Y. Zhao, S. Fleming, S. Poole, M. Sceats, Electron. Lett. 31, 573 (1995).
[CrossRef]

Pruneri, V.

Rogers, D. C.

R. Kashyap, G. J. Veldhuis, D. C. Rogers, P. F. McKee, Appl. Phys. Lett. 64, 1332 (1994).
[CrossRef]

Russell, P. St. J.

P. G. Kazansky, V. Pruneri, P. St. J. Russell, Opt. Lett. 20, 843 (1995).
[CrossRef] [PubMed]

P. G. Kazansky, P. St. J. Russell, L. Dong, C. N. Pannell, Electron. Lett. 31, 62 (1995).
[CrossRef]

P. G. Kazansky, L. Dong, P. St. J. Russell, Electron. Lett. 30, 1345 (1994).
[CrossRef]

P. G. Kazansky, P. St. J. Russell, Opt. Commun. 110, 611 (1994).
[CrossRef]

P. G. Kazansky, L. Dong, P. St. J. Russell, Opt. Lett. 19, 701 (1994).
[CrossRef] [PubMed]

Sceats, M.

T. Fujiwara, D. Wong, Y. Zhao, S. Fleming, S. Poole, M. Sceats, Electron. Lett. 31, 573 (1995).
[CrossRef]

Tumminelli, R. P.

R. A. Myers, S. R. J. Brueck, R. P. Tumminelli, Proc. SPIE 2289, 158 (1994).
[CrossRef]

Veldhuis, G. J.

R. Kashyap, G. J. Veldhuis, D. C. Rogers, P. F. McKee, Appl. Phys. Lett. 64, 1332 (1994).
[CrossRef]

Wong, D.

T. Fujiwara, D. Wong, Y. Zhao, S. Fleming, S. Poole, M. Sceats, Electron. Lett. 31, 573 (1995).
[CrossRef]

Zhao, Y.

T. Fujiwara, D. Wong, Y. Zhao, S. Fleming, S. Poole, M. Sceats, Electron. Lett. 31, 573 (1995).
[CrossRef]

Appl. Phys. Lett.

R. Kashyap, G. J. Veldhuis, D. C. Rogers, P. F. McKee, Appl. Phys. Lett. 64, 1332 (1994).
[CrossRef]

Electron. Lett.

X.-C. Long, R. A. Myers, S. R. J. Brueck, Electron. Lett. 30, 2162 (1994).
[CrossRef]

P. G. Kazansky, P. St. J. Russell, L. Dong, C. N. Pannell, Electron. Lett. 31, 62 (1995).
[CrossRef]

P. G. Kazansky, L. Dong, P. St. J. Russell, Electron. Lett. 30, 1345 (1994).
[CrossRef]

T. Fujiwara, D. Wong, Y. Zhao, S. Fleming, S. Poole, M. Sceats, Electron. Lett. 31, 573 (1995).
[CrossRef]

J. Opt. Soc. Am. B

Opt. Commun.

P. G. Kazansky, P. St. J. Russell, Opt. Commun. 110, 611 (1994).
[CrossRef]

Opt. Lett.

Proc. SPIE

R. A. Myers, S. R. J. Brueck, R. P. Tumminelli, Proc. SPIE 2289, 158 (1994).
[CrossRef]

R. A. Myers, X.-C. Long, S. R. J. Brueck, Proc. SPIE 2289, 98 (1994).
[CrossRef]

Cited By

OSA participates in CrossRef's Cited-By Linking service. Citing articles from OSA journals and other participating publishers are listed here.

Alert me when this article is cited.


Figures (3)

Fig. 1
Fig. 1

SH signal versus poling time (a) in air and (b) in vacuum for the 3-mm-thick, as-received Hersil 1 samples. SH signals are normalized to the SH signal in a reference sample poled at 280 °C and 4 kV for 15 min in air.

Fig. 2
Fig. 2

Log SH versus log dc voltage for (a) the as-received Herasil 1 samples and for (b) repeatedly poled and annealed (for 1 h at 350 °C before poling) samples. Samples were poled at 280 °C. The poling time of the sample is optimum for a maximum SH signal for each dc voltage. Line (a) is fitted to as-received samples poled in air (the slope of the line is 1.98). Line (b) is fitted to all the repeatedly poled and annealed samples (the slope of the line is 1.92).

Fig. 3
Fig. 3

SH signal versus poling time in air and vacuum for 1-mm-thick, repeatedly poled and annealed Herasil 1 samples poled at 280 °C.

Metrics