Abstract

We have identified cascading of second-order nonlinear processes as the origin of previously reported, very large nonlinearities measured by self-phase-modulation experiments in organic single-crystal-core fibers of 4-(N, N-dimethylamino)-3-acetamidonitrobenzene.

© 1994 Optical Society of America

Full Article  |  PDF Article

References

  • View by:
  • |
  • |
  • |

  1. J. Zyss, Molecular Nonlinear Optics: Materials, Physics and Devices (Academic, Boston, Mass., 1993).
  2. J.-C. Baumert, R. J. Twieg, G. C. Bjorklund, J. A. Logan, C. W. Dirk, Appl. Phys. Lett. 51, 1484 (1987).
    [CrossRef]
  3. S. Ducharme, W. P. Risk, W. E. Moerner, V. Y. Lee, R. J. Twieg, G. C. Bjorklund, Appl. Phys. Lett. 57, 537 (1990).
    [CrossRef]
  4. K. Sasaki, T. Kinoshita, N. Karasawa, J. Appl. Phys. 45, 333 (1984).
  5. P. V. Vidakovik, M. Coquillay, F. Salin, J. Opt. Soc. Am. B 4, 998 (1987).
    [CrossRef]
  6. T. Uemiya, N. Uenishi, S. Okamoto, K. Chikuma, K. Kumata, T. Kondo, R. Ito, S. Umegaki, Appl. Opt. 31, 7581 (1992).
    [CrossRef] [PubMed]
  7. L. T. Cheng, W. Tam, S. H. Stevenson, G. R. Meredith, G. Rikken, S. R. Marder, J. Phys. Chem. 95, 10631 (1991).
    [CrossRef]
  8. M. Yamashita, K. Torizuka, T. Uemiya, Appl. Phys. Lett. 57, 1301 (1990).
    [CrossRef]
  9. D. Y. Kim, M. Sundheimer, A. Otomo, G. I. Stegeman, W. H. G. Horsthuis, G. R. Möhlmann, Appl. Phys. Lett. 63, 290 (1993).
    [CrossRef]
  10. R. DeSalvo, D. J. Hagan, M. Sheik-Bahae, G. I. Stegeman, E. W. Van Stryland, Opt. Lett. 17, 28 (1992).
    [CrossRef] [PubMed]
  11. G. I. Stegeman, M. Sheik-Bahae, E. Van Stryland, G. Assanto, Opt. Lett. 18, 13 (1993).
    [CrossRef] [PubMed]
  12. M. L. Sundheimer, Ch. Bosshard, E. Van Stryland, G. I. Stegeman, Opt. Lett. 18, 1397 (1993).
    [CrossRef] [PubMed]
  13. I. Ledoux, C. Lepers, A. Perigaud, J. Badan, J. Zyss, Opt. Commun. 80, 149 (1990).
    [CrossRef]

1993

1992

1991

L. T. Cheng, W. Tam, S. H. Stevenson, G. R. Meredith, G. Rikken, S. R. Marder, J. Phys. Chem. 95, 10631 (1991).
[CrossRef]

1990

M. Yamashita, K. Torizuka, T. Uemiya, Appl. Phys. Lett. 57, 1301 (1990).
[CrossRef]

S. Ducharme, W. P. Risk, W. E. Moerner, V. Y. Lee, R. J. Twieg, G. C. Bjorklund, Appl. Phys. Lett. 57, 537 (1990).
[CrossRef]

I. Ledoux, C. Lepers, A. Perigaud, J. Badan, J. Zyss, Opt. Commun. 80, 149 (1990).
[CrossRef]

1987

J.-C. Baumert, R. J. Twieg, G. C. Bjorklund, J. A. Logan, C. W. Dirk, Appl. Phys. Lett. 51, 1484 (1987).
[CrossRef]

P. V. Vidakovik, M. Coquillay, F. Salin, J. Opt. Soc. Am. B 4, 998 (1987).
[CrossRef]

1984

K. Sasaki, T. Kinoshita, N. Karasawa, J. Appl. Phys. 45, 333 (1984).

Assanto, G.

Badan, J.

I. Ledoux, C. Lepers, A. Perigaud, J. Badan, J. Zyss, Opt. Commun. 80, 149 (1990).
[CrossRef]

Baumert, J.-C.

J.-C. Baumert, R. J. Twieg, G. C. Bjorklund, J. A. Logan, C. W. Dirk, Appl. Phys. Lett. 51, 1484 (1987).
[CrossRef]

Bjorklund, G. C.

S. Ducharme, W. P. Risk, W. E. Moerner, V. Y. Lee, R. J. Twieg, G. C. Bjorklund, Appl. Phys. Lett. 57, 537 (1990).
[CrossRef]

J.-C. Baumert, R. J. Twieg, G. C. Bjorklund, J. A. Logan, C. W. Dirk, Appl. Phys. Lett. 51, 1484 (1987).
[CrossRef]

Bosshard, Ch.

Cheng, L. T.

L. T. Cheng, W. Tam, S. H. Stevenson, G. R. Meredith, G. Rikken, S. R. Marder, J. Phys. Chem. 95, 10631 (1991).
[CrossRef]

Chikuma, K.

Coquillay, M.

DeSalvo, R.

Dirk, C. W.

J.-C. Baumert, R. J. Twieg, G. C. Bjorklund, J. A. Logan, C. W. Dirk, Appl. Phys. Lett. 51, 1484 (1987).
[CrossRef]

Ducharme, S.

S. Ducharme, W. P. Risk, W. E. Moerner, V. Y. Lee, R. J. Twieg, G. C. Bjorklund, Appl. Phys. Lett. 57, 537 (1990).
[CrossRef]

Hagan, D. J.

Horsthuis, W. H. G.

D. Y. Kim, M. Sundheimer, A. Otomo, G. I. Stegeman, W. H. G. Horsthuis, G. R. Möhlmann, Appl. Phys. Lett. 63, 290 (1993).
[CrossRef]

Ito, R.

Karasawa, N.

K. Sasaki, T. Kinoshita, N. Karasawa, J. Appl. Phys. 45, 333 (1984).

Kim, D. Y.

D. Y. Kim, M. Sundheimer, A. Otomo, G. I. Stegeman, W. H. G. Horsthuis, G. R. Möhlmann, Appl. Phys. Lett. 63, 290 (1993).
[CrossRef]

Kinoshita, T.

K. Sasaki, T. Kinoshita, N. Karasawa, J. Appl. Phys. 45, 333 (1984).

Kondo, T.

Kumata, K.

Ledoux, I.

I. Ledoux, C. Lepers, A. Perigaud, J. Badan, J. Zyss, Opt. Commun. 80, 149 (1990).
[CrossRef]

Lee, V. Y.

S. Ducharme, W. P. Risk, W. E. Moerner, V. Y. Lee, R. J. Twieg, G. C. Bjorklund, Appl. Phys. Lett. 57, 537 (1990).
[CrossRef]

Lepers, C.

I. Ledoux, C. Lepers, A. Perigaud, J. Badan, J. Zyss, Opt. Commun. 80, 149 (1990).
[CrossRef]

Logan, J. A.

J.-C. Baumert, R. J. Twieg, G. C. Bjorklund, J. A. Logan, C. W. Dirk, Appl. Phys. Lett. 51, 1484 (1987).
[CrossRef]

Marder, S. R.

L. T. Cheng, W. Tam, S. H. Stevenson, G. R. Meredith, G. Rikken, S. R. Marder, J. Phys. Chem. 95, 10631 (1991).
[CrossRef]

Meredith, G. R.

L. T. Cheng, W. Tam, S. H. Stevenson, G. R. Meredith, G. Rikken, S. R. Marder, J. Phys. Chem. 95, 10631 (1991).
[CrossRef]

Moerner, W. E.

S. Ducharme, W. P. Risk, W. E. Moerner, V. Y. Lee, R. J. Twieg, G. C. Bjorklund, Appl. Phys. Lett. 57, 537 (1990).
[CrossRef]

Möhlmann, G. R.

D. Y. Kim, M. Sundheimer, A. Otomo, G. I. Stegeman, W. H. G. Horsthuis, G. R. Möhlmann, Appl. Phys. Lett. 63, 290 (1993).
[CrossRef]

Okamoto, S.

Otomo, A.

D. Y. Kim, M. Sundheimer, A. Otomo, G. I. Stegeman, W. H. G. Horsthuis, G. R. Möhlmann, Appl. Phys. Lett. 63, 290 (1993).
[CrossRef]

Perigaud, A.

I. Ledoux, C. Lepers, A. Perigaud, J. Badan, J. Zyss, Opt. Commun. 80, 149 (1990).
[CrossRef]

Rikken, G.

L. T. Cheng, W. Tam, S. H. Stevenson, G. R. Meredith, G. Rikken, S. R. Marder, J. Phys. Chem. 95, 10631 (1991).
[CrossRef]

Risk, W. P.

S. Ducharme, W. P. Risk, W. E. Moerner, V. Y. Lee, R. J. Twieg, G. C. Bjorklund, Appl. Phys. Lett. 57, 537 (1990).
[CrossRef]

Salin, F.

Sasaki, K.

K. Sasaki, T. Kinoshita, N. Karasawa, J. Appl. Phys. 45, 333 (1984).

Sheik-Bahae, M.

Stegeman, G. I.

Stevenson, S. H.

L. T. Cheng, W. Tam, S. H. Stevenson, G. R. Meredith, G. Rikken, S. R. Marder, J. Phys. Chem. 95, 10631 (1991).
[CrossRef]

Sundheimer, M.

D. Y. Kim, M. Sundheimer, A. Otomo, G. I. Stegeman, W. H. G. Horsthuis, G. R. Möhlmann, Appl. Phys. Lett. 63, 290 (1993).
[CrossRef]

Sundheimer, M. L.

Tam, W.

L. T. Cheng, W. Tam, S. H. Stevenson, G. R. Meredith, G. Rikken, S. R. Marder, J. Phys. Chem. 95, 10631 (1991).
[CrossRef]

Torizuka, K.

M. Yamashita, K. Torizuka, T. Uemiya, Appl. Phys. Lett. 57, 1301 (1990).
[CrossRef]

Twieg, R. J.

S. Ducharme, W. P. Risk, W. E. Moerner, V. Y. Lee, R. J. Twieg, G. C. Bjorklund, Appl. Phys. Lett. 57, 537 (1990).
[CrossRef]

J.-C. Baumert, R. J. Twieg, G. C. Bjorklund, J. A. Logan, C. W. Dirk, Appl. Phys. Lett. 51, 1484 (1987).
[CrossRef]

Uemiya, T.

Uenishi, N.

Umegaki, S.

Van Stryland, E.

Van Stryland, E. W.

Vidakovik, P. V.

Yamashita, M.

M. Yamashita, K. Torizuka, T. Uemiya, Appl. Phys. Lett. 57, 1301 (1990).
[CrossRef]

Zyss, J.

I. Ledoux, C. Lepers, A. Perigaud, J. Badan, J. Zyss, Opt. Commun. 80, 149 (1990).
[CrossRef]

Appl. Opt.

Appl. Phys. Lett.

J.-C. Baumert, R. J. Twieg, G. C. Bjorklund, J. A. Logan, C. W. Dirk, Appl. Phys. Lett. 51, 1484 (1987).
[CrossRef]

S. Ducharme, W. P. Risk, W. E. Moerner, V. Y. Lee, R. J. Twieg, G. C. Bjorklund, Appl. Phys. Lett. 57, 537 (1990).
[CrossRef]

M. Yamashita, K. Torizuka, T. Uemiya, Appl. Phys. Lett. 57, 1301 (1990).
[CrossRef]

D. Y. Kim, M. Sundheimer, A. Otomo, G. I. Stegeman, W. H. G. Horsthuis, G. R. Möhlmann, Appl. Phys. Lett. 63, 290 (1993).
[CrossRef]

J. Appl. Phys.

K. Sasaki, T. Kinoshita, N. Karasawa, J. Appl. Phys. 45, 333 (1984).

J. Opt. Soc. Am. B

J. Phys. Chem.

L. T. Cheng, W. Tam, S. H. Stevenson, G. R. Meredith, G. Rikken, S. R. Marder, J. Phys. Chem. 95, 10631 (1991).
[CrossRef]

Opt. Commun.

I. Ledoux, C. Lepers, A. Perigaud, J. Badan, J. Zyss, Opt. Commun. 80, 149 (1990).
[CrossRef]

Opt. Lett.

Other

J. Zyss, Molecular Nonlinear Optics: Materials, Physics and Devices (Academic, Boston, Mass., 1993).

Cited By

OSA participates in CrossRef's Cited-By Linking service. Citing articles from OSA journals and other participating publishers are listed here.

Alert me when this article is cited.


Figures (2)

Fig. 1
Fig. 1

Mode patterns at 1.32 μm for the DAN/SF1 sample with crystal orientation of DAN in the fiber core.4

Fig. 2
Fig. 2

Pump depletion and SHG efficiency at 1.064 μm. and 2-GW/cm2 pump peak intensity. Pump depletions near 70% were observed at 8 GW/cm2; no damage was observed below 10 GW/cm2. The measured external phase-matching angle was approximately 44°. The dashed curves are theoretical predictions for a Gaussian beam in time and space. (b) Experimentally determined (symbols) effective nonlinear refractive index versus detuning for a DAN single-crystal phase matched in the XZ plane for 2-GW/cm2 intensity (the dashed curve is only a guide to the eye). The solid curve shows the results of a theoretical calculation for a Gaussian pulse in time and space. Walk-off between the pump and SHG beams was neglected, as was diffraction of the beams.

Equations (1)

Equations on this page are rendered with MathJax. Learn more.

n 2 eff = 4 π c 0 L λ d eff 2 n 2 ω n ω 2 1 Δ k L = 1 2 π L λ I ω Γ 2 L 2 Δ k L ,

Metrics