Abstract

The CdS/SiO2 core/shell nanowires (NWs) with controlled shell thickness were successfully synthesized and subsequently heat-treated at 500 °C. The influences of silica shell coating and annealing processes on their optical properties have been investigated. Compared with original CdS NWs, the annealed CdS/SiO2 NWs exhibited an enhanced band-edge emission with slowed photoluminescence lifetime, while the intensity of defect emission decreased. The results were ascribed to the surface passivation and recrystallization by shell coating and annealing. We believe our finding would help improving the optical properties of semiconductor NWs, and facilitate its applications in various realms, such as nanoscale emitter, sensor, and photoelectric device.

© 2013 OSA

1. Introduction

As a one-dimensional wide band gap (2.42 eV) semiconductor, CdS nanowires (NWs) have received considerable attention owing to their attractive optical properties [120]. Especially, the stimulated emission and lasing of CdS NWs have blossomed increasingly in recent years, attributed to the efforts from a large number of research groups [1016]. For example, optically pumped lasing of CdS NWs at 75 K was reported by Lieber and associates in 2005 [11]. Stimulated emission was observed by Pan et al. for the silica coated CdS NWs under high-intensity excitation at room temperature [12]. Low threshold lasing of CdS NWs at room temperature was further revealed by Geburt’s group [13]. In addition, electrically pumped CdS NWs laser was also reported by Duan and associates [15], which demonstrated their feasibility for producing integrated electrically driven photonic devices. Based on these interesting optical properties, CdS NWs have been regarded as wonderful optical material for various applications, such as telecommunications, solar cells, highly integrated devices [14,1618].

Based on above considerations, great recent efforts have been devoted to synthesize CdS NWs with high crystallinity and efficient photoluminescence (PL) [1926]. Hydrothermal method is the most employed route for the preparation of CdS NWs due to some significant advantages such as cost-effective, controllable particle size, low-temperature, and easy-operation techniques [2427]. However, such as-prepared CdS NWs synthesized by hydrothermal method have defects inevitably owing to the surface absorption of surfactant, ligands, or other groups, which reduce the PL efficiency of the CdS NWs [2527]. In order to further improve the PL efficiency of the as-prepared CdS NWs, the researchers have suggested several processing methods [2832]. The typical strategy included growing silica shells to passivate the surface of CdS NWs [2831]. Annealing is an efficient strategy for surface recrystallization [32,33], however the CdS NWs were often damaged under long-term heating in air due to the surface degradation.

In this paper, we investigated the influences of silica shell coating and annealing processes on the PL of CdS NWs. The CdS/SiO2 core/shell NWs were synthesized, and annealed at 500 °C for 5 h. Compared with the original CdS NWs, such annealed CdS/SiO2 core/shell NWs exhibited highly efficient band-edge emission of CdS.

2. Experimental section

The original CdS NWs were synthesized by the solvothermal method using ethylenediamine as a solvent [12,24]. In brief, 33.5 mL of ethylenediamine was added to a Teflon-lined stainless-steel autoclave of 45 mL capacity, then 0.0025 mol of cadmium nitrate hexahydrate and 0.002 mol of thiacetamide were dissolved in the above solvent. After stirring for about 10 mins, a viscous gel-like solution was obtained. Then, the Teflon-lined stainless-steel autoclave was sealed and heated without stirring at 180 °C for 24 h. The obtained yellow product was centrifuged (5 mins, 4500 rps) and washed with distilled water and ethanol.

Subsequently, the CdS/SiO2 core/shell NWs were prepared by a modified Stöber method. 10 mg of the as-prepared CdS NWs was dispersed in the mixed solution containing 10 mL ethanol, 450 μL distilled water, and 325 μL of 28% ammonia. Then, 35 μL of TEOS was added to the above mixture and sonicated for about 2 h at room temperature. A white-yellow precipitate was obtained by centrifugation at 4000 rpm, and then re-dispersed in ethanol. As thus, the high-yielded and uniform silica coated CdS NWs were successfully synthesized. In this method, the thickness of silica shell could be controlled by the amount of TEOS. In order to study the joint action of silica shell and annealing processes on the optical properties of the CdS NWs, part of the as-prepared sample was annealed at 500 °C in air atmosphere for 5 h.

The transmission electron microscope (TEM) images were obtained with a JEOL 2010 HT transmission electron microscope (operated at 200 kV). The absorption spectra were measured with a Varian Cary 5000 UV-Vis-NIR spectrophotometer. Powder X-ray diffraction (XRD) analyses were performed on a Bruker D8-advance X-ray diffractometer with Cu Kα irradiation (λ = 1.5406 Ǻ). The PL spectra of the samples were recorded using a spectrometer (Spectrapro 2500i, Acton) equipped with a liquid nitrogen cooled CCD (SPEC-10, Princeton). The excitation laser of 400 nm with a pulse width of around 3 ps and a repetition rate of 76 MHz was generated by a mode-locked Ti:sapphire laser (Mira 900, Coherent) equipped with an optical frequency doubling system.

3. Results and discussion

3.1 Controllable synthesis of CdS/SiO2 core/shell NWs

The CdS/SiO2 core/shell NWs with controlled shell thickness were produced in a modified Stöber method which is facile, high-yielded and reproducible. Compared with the typical procedure [12], methanol is replaced by ethanol in our method. Sonic oscillation was used as a stirring method during the synthesizing procedure, which greatly shortens the synthesis period of silica shell. Figure 1 displays the TEM images of the original CdS NWs and CdS/SiO2 core/shell NWs with different shell thickness. Figure 1(a) shows the low and high magnitude TEM images of original CdS NWs. It can be seen that the diameter of CdS NWs is about 70 nm. In addition, the CdS/SiO2 core/shell NWs with different shell thickness could be obtained by changing the amount of TEOS in the synthesis. Typically, when 2.5 μL, 10 μL, and 35 μL of TEOS were used, the shell thickness was 11 nm, 25 nm, and 70 nm, respectively. Their TEM images of the corresponding CdS/SiO2 core/shell NWs are shown in Figs. 1(b)-1(d). From the images, it also can be seen that the silica shells are uniform and precisely controllable.

 

Fig. 1 (a) Low and high magnitude TEM images of CdS NWs. (b-d) CdS/SiO2 core/shell NWs with shell thickness of around (b) 11 nm, (c) 25 nm and (d) 70 nm.

Download Full Size | PPT Slide | PDF

3.2 Thermal stability of CdS/SiO2 core/shell NWs

The XRD patterns of the as-prepared CdS NWs, annealed CdS NWs, CdS/SiO2 core/shell NWs, and annealed CdS/SiO2 core/shell NWs are shown in Fig. 2 . The annealed CdS NWs have a distinct XRD pattern from the others, which can be indexed as the orthorhombic Cd3O2SO4 phase (JCPDS card No.32-0140). It indicated that the structure of CdS NWs is damaged due to the surface degradation (such as oxidation) under long-term heating in air. All the other diffraction peaks in Fig. 2 can be clearly seen and indexed as the hexagonal CdS phase (JCPDS card No.41-1049). Meanwhile, due to the amorphous structure of silica shell, no peaks for silica were detected in the coated sample. The results imply that the silica shell can prevent CdS NWs from being oxidized by oxygen at high temperature, and it offers the feasibility for next optical properties research of CdS NWs under stronger laser excitation.

 

Fig. 2 XRD patterns of (a) CdS NWs, (b) uncoated CdS NWs annealed at 500 °C, (c) CdS/SiO2 core/shell NWs, and (d) CdS/SiO2 core/shell NWs annealed at 500 °C.

Download Full Size | PPT Slide | PDF

3.3 Optical properties of the annealed CdS/SiO2 core/shell NWs

The absorption spectra of the as-prepared CdS NWs, CdS/SiO2 NWs and annealed CdS/SiO2 core/shell NWs are shown in Fig. 3 . All the samples have a pronounced absorption bump at about 486 nm, which is similar with the results obtained by the other groups [26,27]. By comparing the absorption line shape of the CdS NWs, CdS/SiO2 NWs, and annealed CdS/SiO2 NWs, we found that the absorption bump position of CdS NWs is insensitive to the shell coating and annealing processes.

 

Fig. 3 Normalized absorption spectra of CdS NWs, CdS/SiO2 NWs, and annealed CdS/SiO2 core/shell NWs.

Download Full Size | PPT Slide | PDF

The PL spectra of the CdS NWs, CdS/SiO2 NWs and annealed CdS/SiO2 NWs are presented in Fig. 4(a) . The samples show a sharp emission band at around 505 nm with the excitation of a 400 nm laser, which is attributed to the typical band–band transitions of CdS crystal since the spectral position is very near the band gap of CdS at room temperature [31]. Meanwhile, a broad emission band at around 700 nm can also be observed in these samples, which may be ascribed to structural defects such as crystalline surface structure defects, ionized vacancies and/or impurities [26,27].

 

Fig. 4 (a) PL spectra of CdS NWs, CdS/SiO2 NWs and CdS/SiO2 NWs annealed at 500 °C. (b) Time-resolved PL of CdS NWs, CdS/SiO2 NWs and annealed CdS/SiO2 NWs at ~505 nm.

Download Full Size | PPT Slide | PDF

Most interesting, compared with the original CdS NWs, the band-edge emission of the silica coated CdS NWs enhances nearly 4 times, and that of the annealed CdS/SiO2 NWs enhances about 8 times. Here, silica coating could passivate the surface of CdS NWs, which prevent the surface adsorption of surfactant, ligands, or other chemical groups. Therefore, it could reduce the number of nonradiative energy channels so as to improve the band-edge emission efficiency. Furthermore, annealing process could improve the crystal quality of CdS NWs under the protection of silica shell. Then the defect (trap) emission was depressed and the band-edge emission efficiency was further enhanced. It can be seen that the defect emission at about 700 nm was decreased by nearly 50% when the CdS/SiO2 NWs were annealed at 500 °C, which also reveals the improvement of CdS crystal quality. In addition, the full width at half maximum (FWHM) of the band-edge emission peaks for the CdS NWs, CdS/SiO2 NWs, and annealed CdS/SiO2 NWs are 20 nm, 17 nm, and 16 nm, respectively. It demonstrates that both the shell coating and annealing processes induce the decreased FWHM of the band-edge emission, which indicate that the trap density near band edge decreases and the quality factor of band-edge emission increases.

To further investigate the dynamics of the band-edge emission, time-resolved PL experiments were performed. As shown in Fig. 4(b), two decay processes with fast lifetime (τf) and slow lifetime (τs) were observed for the CdS NWs, CdS/SiO2 NWs and annealed CdS/SiO2 NWs. We have fitted the PL decay rate of the samples by double exponential, and the fitted values of τf are 0.86 ns (94%), 0.95 ns (89%) and 0.99 ns (85%) for the CdS NWs, CdS/SiO2 NWs, and annealed CdS/SiO2 NWs, respectively. The decrease of density of trap states was expected to reduce the exciton-trap interaction and thus increase the observed lifetime [34,35]. The increased lifetime of band-edge emission for annealed CdS/SiO2 NWs coincided with their enhanced emission efficiency induced by surface passivation and crystal improvement.

Figure 5(a) displays the excitation power (Pexc) dependence of the PL intensity (IPL) at around 505 nm of the samples. From these data, the slopes (ν = log IPL/ log Pexc) are fitted as 1.56, 1.76 and 1.82 for the original CdS, CdS/SiO2 and annealed CdS/SiO2 NWs, respectively. It can be seen that, with the increasing of excitation power, the PL intensity of CdS/SiO2 NWs and annealed CdS/SiO2 NWs increase nonlinearly. In contrast, as shown in Fig. 5(b), the defect emission at about 700 nm is nearly linear with slopes of 1.10, 1.19 and 1.11 for the original CdS NWs, CdS/SiO2 NWs and annealed CdS/SiO2 NWs, respectively.

 

Fig. 5 Excitation power dependence of PL intensity for CdS NWs, CdS/SiO2 core/shell NWs and annealed CdS/SiO2 core/shell NWs at (a) 505 nm and (b) 700 nm with excitation wavelength of 400 nm.

Download Full Size | PPT Slide | PDF

4. Conclusion

In summary, the thickness-controlled CdS/SiO2 core/shell NWs have been successfully prepared in an improved Stöber method, and the influences of silica shell coating and annealing processes on their optical properties have been investigated. The band-edge emission of the annealed CdS/SiO2 NWs was enhanced with slowed lifetime, and the defect emission was depressed. The results indicated that the joint action of silica coating and annealing processes was beneficial for the band-edge emission efficiency, owing to that silica coating could reduce the nonradiative energy channels by the surface state, and annealing process could improve the crystal quality. We believe our finding would help improving the optical properties of semiconductor NWs, and facilitate its applications in various realms, such as nanoscale emitter, sensor, and photoelectric device.

Acknowledgments

This work was supported in part by NSFC (61008043, 11174229 and 11204221), Specialized Research Fund for the Doctoral Program of Higher Education of China (20100141120041) and the National Program on Key Science Research of China (2011CB922201).

References and links

1. O. Hayden, R. Agarwal, and C. M. Lieber, “Nanoscale avalanche photodiodes for highly sensitive and spatially resolved photon detection,” Nat. Mater. 5(5), 352–356 (2006). [CrossRef]   [PubMed]  

2. C. J. Barrelet, A. B. Greytak, and C. M. Lieber, “Nanowire photonic circuit elements,” Nano Lett. 4(10), 1981–1985 (2004). [CrossRef]  

3. Z. Li, J. Wei, P. Li, L. Zhang, E. Shi, C. Ji, J. Liu, D. Zhuang, Z. Liu, J. Zhou, Y. Shang, Y. Li, K. Wang, H. Zhu, D. Wu, and A. Cao, “Solution-processed bulk heterojunction solar cells based on interpenetrating CdS nanowires and carbon nanotubes,” Nano Res. 5(9), 595–604 (2012). [CrossRef]  

4. Y. Liu, Q. Yang, Y. Zhang, Z. Yang, and Z. L. Wang, “Nanowire piezo-phototronic photodetector: theory and experimental design,” Adv. Mater. (Deerfield Beach Fla.) 24(11), 1410–1417 (2012). [CrossRef]   [PubMed]  

5. Y. F. Lin, J. Song, Y. Ding, S. Y. Lu, and Z. L. Wang, “Alternating the output of a CdS nanowire nanogenerator by a white-light-stimulated optoelectronic effect,” Adv. Mater. (Deerfield Beach Fla.) 20(16), 3127–3130 (2008). [CrossRef]  

6. J. S. Jie, W. J. Zhang, Y. Jiang, X. M. Meng, Y. Q. Li, and S. T. Lee, “Photoconductive characteristics of single-crystal CdS nanoribbons,” Nano Lett. 6(9), 1887–1892 (2006). [CrossRef]   [PubMed]  

7. C. H. Cho, C. O. Aspetti, M. E. Turk, J. M. Kikkawa, S. W. Nam, and R. Agarwal, “Tailoring hot-exciton emission and lifetimes in semiconducting nanowires via whispering-gallery nanocavity plasmons,” Nat. Mater. 10(9), 669–675 (2011). [CrossRef]   [PubMed]  

8. D. Li, J. Zhang, Q. Zhang, and Q. Xiong, “Electric-field-dependent photoconductivity in CdS nanowires and nanobelts: exciton ionization, franz-keldysh, and stark effects,” Nano Lett. 12(6), 2993–2999 (2012). [CrossRef]   [PubMed]  

9. Q. Zhang, X. Y. Shan, X. Feng, C. X. Wang, Q. Q. Wang, J. F. Jia, and Q. K. Xue, “Modulating resonance modes and Q value of a CdS nanowire cavity by single Ag nanoparticles,” Nano Lett. 11(10), 4270–4274 (2011). [CrossRef]   [PubMed]  

10. J. Puthussery, A. Lan, T. H. Kosel, and M. Kuno, “Band-filling of solution-synthesized CdS nanowires,” ACS Nano 2(2), 357–367 (2008). [CrossRef]   [PubMed]  

11. R. Agarwal, C. J. Barrelet, and C. M. Lieber, “Lasing in single cadmium sulfide nanowire optical cavities,” Nano Lett. 5(5), 917–920 (2005). [CrossRef]   [PubMed]  

12. A. Pan, S. Wang, R. Liu, C. Li, and B. Zou, “Thermal stability and lasing of CdS nanowires coated by amorphous silica,” Small 1(11), 1058–1062 (2005). [CrossRef]   [PubMed]  

13. S. Geburt, A. Thielmann, R. Röder, C. Borschel, A. McDonnell, M. Kozlik, J. Kühnel, K. A. Sunter, F. Capasso, and C. Ronning, “Low threshold room-temperature lasing of CdS nanowires,” Nanotechnology 23(36), 365204 (2012). [CrossRef]   [PubMed]  

14. R. F. Oulton, V. J. Sorger, T. Zentgraf, R. M. Ma, C. Gladden, L. Dai, G. Bartal, and X. Zhang, “Plasmon lasers at deep subwavelength scale,” Nature 461(7264), 629–632 (2009). [CrossRef]   [PubMed]  

15. X. Duan, Y. Huang, R. Agarwal, and C. M. Lieber, “Single-nanowire electrically driven lasers,” Nature 421(6920), 241–245 (2003). [CrossRef]   [PubMed]  

16. H. Lee, K. Heo, J. Park, Y. Park, S. Noh, K. S. Kim, C. Lee, B. H. Hong, J. Jian, and S. Hong, “Graphene–nanowire hybrid structures for high-performance photoconductive devices,” J. Mater. Chem. 22(17), 8372–8376 (2012). [CrossRef]  

17. R. M. Ma, L. Dai, H. B. Huo, W. J. Xu, and G. G. Qin, “High-performance logic circuits constructed on single CdS nanowires,” Nano Lett. 7(11), 3300–3304 (2007). [CrossRef]   [PubMed]  

18. T. Dufaux, M. Burghard, and K. Kern, “Efficient charge extraction out of nanoscale Schottky contacts to CdS nanowires,” Nano Lett. 12(6), 2705–2709 (2012). [CrossRef]   [PubMed]  

19. M. I. Utama, J. Zhang, R. Chen, X. Xu, D. Li, H. Sun, and Q. Xiong, “Synthesis and optical properties of II-VI 1D nanostructures,” Nanoscale 4(5), 1422–1435 (2012). [CrossRef]   [PubMed]  

20. B. Piccione, C. H. Cho, L. K. van Vugt, and R. Agarwal, “All-optical active switching in individual semiconductor nanowires,” Nat. Nanotechnol. 7(10), 640–645 (2012). [CrossRef]   [PubMed]  

21. Z. X. Yang, W. Zhong, P. Zhang, M. H. Xu, Y. Deng, C. T. Au, and Y. W. Du, “Controllable synthesis, characterization and photoluminescence properties of morphology-tunable CdS nanomaterials generated in thermal evaporation processes,” Appl. Surf. Sci. 258(19), 7343–7347 (2012). [CrossRef]  

22. D. Xu, Y. Xu, D. Chen, G. Guo, L. Gui, and Y. Tang, “Preparation and characterization of CdS nanowire arrays by DC electrodeposit in porous anodic aluminum oxide templates,” Chem. Phys. Lett. 325(4), 340–344 (2000). [CrossRef]  

23. H. Gai, Y. Wu, L. Wu, Z. Wang, Y. Shi, M. Jing, and K. Zou, “Solvothermal synthesis of CdS nanowires using L-cysteine as sulfur source and their characterization,” Appl. Phys., A Mater. Sci. Process. 91(1), 69–72 (2008). [CrossRef]  

24. K. B. Tang, Y. T. Qian, J. H. Zeng, and X. G. Yang, “Solvothermal route to semiconductor nanowires,” Adv. Mater. (Deerfield Beach Fla.) 15(5), 448–450 (2003). [CrossRef]  

25. C. C. Kang, C. W. Lai, H. C. Peng, J. J. Shyue, and P. T. Chou, “Surfactant- and temperature-controlled CdS nanowire formation,” Small 3(11), 1882–1885 (2007). [CrossRef]   [PubMed]  

26. Q. Wang, G. Zhao, and G. Han, “Synthesis of single crystalline CdS nanorods by a PVP-assisted solvothermal method,” Mater. Lett. 59(21), 2625–2629 (2005). [CrossRef]  

27. K. Pal, U. N. Maiti, T. P. Majumder, and S. C. Debnath, “A facile strategy for the fabrication of uniform CdS nanowires with high yield and its controlled morphological growth with the assistance of PEG in hydrothermal route,” Appl. Surf. Sci. 258(1), 163–168 (2011). [CrossRef]  

28. M. A. Correa-Duarte, M. Giersig, N. A. Kotov, and L. M. Liz-Marzán, “Control of packing order of self-assembled monolayers of magnetite nanoparticles with and without SiO2 coating by microwave irradiation,” Langmuir 14(22), 6430–6435 (1998). [CrossRef]  

29. X. F. Yu, L. D. Chen, M. Li, M. Y. Xie, L. Zhou, Y. Li, and Q. Q. Wang, “Highly efficient fluorescence of NdF3/SiO2 core/shell nanoparticles and the applications for in vivo NIR detection,” Adv. Mater. (Deerfield Beach Fla.) 20(21), 4118–4123 (2008). [CrossRef]  

30. S. T. Selvan, T. T. Tan, and J. Y. Ying, “Robust, non-cytotoxic, silica-coated CdSe quantum dots with efficient photoluminescence,” Adv. Mater. (Deerfield Beach Fla.) 17(13), 1620–1625 (2005). [CrossRef]  

31. L. K. van Vugt, B. Piccione, C. H. Cho, P. Nukala, and R. Agarwal, “One-dimensional polaritons with size-tunable and enhanced coupling strengths in semiconductor nanowires,” Proc. Natl. Acad. Sci. U.S.A. 108(25), 10050–10055 (2011). [CrossRef]   [PubMed]  

32. A. Pan, X. Lin, R. Liu, C. Li, X. He, H. Gao, and B. Zou, “Surface crystallization effects on the optical and electric properties of CdS nanorods,” Nanotechnology 16(10), 2402–2406 (2005). [CrossRef]   [PubMed]  

33. P. Liu, V. P. Singh, C. A. Jarro, and S. Rajaputra, “Cadmium sulfide nanowires for the window semiconductor layer in thin film CdS-CdTe solar cells,” Nanotechnology 22(14), 145304 (2011). [CrossRef]   [PubMed]  

34. F. Wu, J. Z. Zhang, R. Kho, and R. K. Mehra, “Radiative and nonradiative lifetimes of band edge states and deep trap states of CdS nanoparticles determined by time-correlated single photon counting,” Chem. Phys. Lett. 330(3-4), 237–242 (2000). [CrossRef]  

35. L. Yu, X. F. Yu, Y. Qiu, Y. Chen, and S. Yang, “Nonlinear photoluminescence of ZnO/ZnS nanotetrapods,” Chem. Phys. Lett. 465(4-6), 272–274 (2008). [CrossRef]  

References

  • View by:
  • |
  • |
  • |

  1. O. Hayden, R. Agarwal, and C. M. Lieber, “Nanoscale avalanche photodiodes for highly sensitive and spatially resolved photon detection,” Nat. Mater.5(5), 352–356 (2006).
    [CrossRef] [PubMed]
  2. C. J. Barrelet, A. B. Greytak, and C. M. Lieber, “Nanowire photonic circuit elements,” Nano Lett.4(10), 1981–1985 (2004).
    [CrossRef]
  3. Z. Li, J. Wei, P. Li, L. Zhang, E. Shi, C. Ji, J. Liu, D. Zhuang, Z. Liu, J. Zhou, Y. Shang, Y. Li, K. Wang, H. Zhu, D. Wu, and A. Cao, “Solution-processed bulk heterojunction solar cells based on interpenetrating CdS nanowires and carbon nanotubes,” Nano Res.5(9), 595–604 (2012).
    [CrossRef]
  4. Y. Liu, Q. Yang, Y. Zhang, Z. Yang, and Z. L. Wang, “Nanowire piezo-phototronic photodetector: theory and experimental design,” Adv. Mater. (Deerfield Beach Fla.)24(11), 1410–1417 (2012).
    [CrossRef] [PubMed]
  5. Y. F. Lin, J. Song, Y. Ding, S. Y. Lu, and Z. L. Wang, “Alternating the output of a CdS nanowire nanogenerator by a white-light-stimulated optoelectronic effect,” Adv. Mater. (Deerfield Beach Fla.)20(16), 3127–3130 (2008).
    [CrossRef]
  6. J. S. Jie, W. J. Zhang, Y. Jiang, X. M. Meng, Y. Q. Li, and S. T. Lee, “Photoconductive characteristics of single-crystal CdS nanoribbons,” Nano Lett.6(9), 1887–1892 (2006).
    [CrossRef] [PubMed]
  7. C. H. Cho, C. O. Aspetti, M. E. Turk, J. M. Kikkawa, S. W. Nam, and R. Agarwal, “Tailoring hot-exciton emission and lifetimes in semiconducting nanowires via whispering-gallery nanocavity plasmons,” Nat. Mater.10(9), 669–675 (2011).
    [CrossRef] [PubMed]
  8. D. Li, J. Zhang, Q. Zhang, and Q. Xiong, “Electric-field-dependent photoconductivity in CdS nanowires and nanobelts: exciton ionization, franz-keldysh, and stark effects,” Nano Lett.12(6), 2993–2999 (2012).
    [CrossRef] [PubMed]
  9. Q. Zhang, X. Y. Shan, X. Feng, C. X. Wang, Q. Q. Wang, J. F. Jia, and Q. K. Xue, “Modulating resonance modes and Q value of a CdS nanowire cavity by single Ag nanoparticles,” Nano Lett.11(10), 4270–4274 (2011).
    [CrossRef] [PubMed]
  10. J. Puthussery, A. Lan, T. H. Kosel, and M. Kuno, “Band-filling of solution-synthesized CdS nanowires,” ACS Nano2(2), 357–367 (2008).
    [CrossRef] [PubMed]
  11. R. Agarwal, C. J. Barrelet, and C. M. Lieber, “Lasing in single cadmium sulfide nanowire optical cavities,” Nano Lett.5(5), 917–920 (2005).
    [CrossRef] [PubMed]
  12. A. Pan, S. Wang, R. Liu, C. Li, and B. Zou, “Thermal stability and lasing of CdS nanowires coated by amorphous silica,” Small1(11), 1058–1062 (2005).
    [CrossRef] [PubMed]
  13. S. Geburt, A. Thielmann, R. Röder, C. Borschel, A. McDonnell, M. Kozlik, J. Kühnel, K. A. Sunter, F. Capasso, and C. Ronning, “Low threshold room-temperature lasing of CdS nanowires,” Nanotechnology23(36), 365204 (2012).
    [CrossRef] [PubMed]
  14. R. F. Oulton, V. J. Sorger, T. Zentgraf, R. M. Ma, C. Gladden, L. Dai, G. Bartal, and X. Zhang, “Plasmon lasers at deep subwavelength scale,” Nature461(7264), 629–632 (2009).
    [CrossRef] [PubMed]
  15. X. Duan, Y. Huang, R. Agarwal, and C. M. Lieber, “Single-nanowire electrically driven lasers,” Nature421(6920), 241–245 (2003).
    [CrossRef] [PubMed]
  16. H. Lee, K. Heo, J. Park, Y. Park, S. Noh, K. S. Kim, C. Lee, B. H. Hong, J. Jian, and S. Hong, “Graphene–nanowire hybrid structures for high-performance photoconductive devices,” J. Mater. Chem.22(17), 8372–8376 (2012).
    [CrossRef]
  17. R. M. Ma, L. Dai, H. B. Huo, W. J. Xu, and G. G. Qin, “High-performance logic circuits constructed on single CdS nanowires,” Nano Lett.7(11), 3300–3304 (2007).
    [CrossRef] [PubMed]
  18. T. Dufaux, M. Burghard, and K. Kern, “Efficient charge extraction out of nanoscale Schottky contacts to CdS nanowires,” Nano Lett.12(6), 2705–2709 (2012).
    [CrossRef] [PubMed]
  19. M. I. Utama, J. Zhang, R. Chen, X. Xu, D. Li, H. Sun, and Q. Xiong, “Synthesis and optical properties of II-VI 1D nanostructures,” Nanoscale4(5), 1422–1435 (2012).
    [CrossRef] [PubMed]
  20. B. Piccione, C. H. Cho, L. K. van Vugt, and R. Agarwal, “All-optical active switching in individual semiconductor nanowires,” Nat. Nanotechnol.7(10), 640–645 (2012).
    [CrossRef] [PubMed]
  21. Z. X. Yang, W. Zhong, P. Zhang, M. H. Xu, Y. Deng, C. T. Au, and Y. W. Du, “Controllable synthesis, characterization and photoluminescence properties of morphology-tunable CdS nanomaterials generated in thermal evaporation processes,” Appl. Surf. Sci.258(19), 7343–7347 (2012).
    [CrossRef]
  22. D. Xu, Y. Xu, D. Chen, G. Guo, L. Gui, and Y. Tang, “Preparation and characterization of CdS nanowire arrays by DC electrodeposit in porous anodic aluminum oxide templates,” Chem. Phys. Lett.325(4), 340–344 (2000).
    [CrossRef]
  23. H. Gai, Y. Wu, L. Wu, Z. Wang, Y. Shi, M. Jing, and K. Zou, “Solvothermal synthesis of CdS nanowires using L-cysteine as sulfur source and their characterization,” Appl. Phys., A Mater. Sci. Process.91(1), 69–72 (2008).
    [CrossRef]
  24. K. B. Tang, Y. T. Qian, J. H. Zeng, and X. G. Yang, “Solvothermal route to semiconductor nanowires,” Adv. Mater. (Deerfield Beach Fla.)15(5), 448–450 (2003).
    [CrossRef]
  25. C. C. Kang, C. W. Lai, H. C. Peng, J. J. Shyue, and P. T. Chou, “Surfactant- and temperature-controlled CdS nanowire formation,” Small3(11), 1882–1885 (2007).
    [CrossRef] [PubMed]
  26. Q. Wang, G. Zhao, and G. Han, “Synthesis of single crystalline CdS nanorods by a PVP-assisted solvothermal method,” Mater. Lett.59(21), 2625–2629 (2005).
    [CrossRef]
  27. K. Pal, U. N. Maiti, T. P. Majumder, and S. C. Debnath, “A facile strategy for the fabrication of uniform CdS nanowires with high yield and its controlled morphological growth with the assistance of PEG in hydrothermal route,” Appl. Surf. Sci.258(1), 163–168 (2011).
    [CrossRef]
  28. M. A. Correa-Duarte, M. Giersig, N. A. Kotov, and L. M. Liz-Marzán, “Control of packing order of self-assembled monolayers of magnetite nanoparticles with and without SiO2 coating by microwave irradiation,” Langmuir14(22), 6430–6435 (1998).
    [CrossRef]
  29. X. F. Yu, L. D. Chen, M. Li, M. Y. Xie, L. Zhou, Y. Li, and Q. Q. Wang, “Highly efficient fluorescence of NdF3/SiO2 core/shell nanoparticles and the applications for in vivo NIR detection,” Adv. Mater. (Deerfield Beach Fla.)20(21), 4118–4123 (2008).
    [CrossRef]
  30. S. T. Selvan, T. T. Tan, and J. Y. Ying, “Robust, non-cytotoxic, silica-coated CdSe quantum dots with efficient photoluminescence,” Adv. Mater. (Deerfield Beach Fla.)17(13), 1620–1625 (2005).
    [CrossRef]
  31. L. K. van Vugt, B. Piccione, C. H. Cho, P. Nukala, and R. Agarwal, “One-dimensional polaritons with size-tunable and enhanced coupling strengths in semiconductor nanowires,” Proc. Natl. Acad. Sci. U.S.A.108(25), 10050–10055 (2011).
    [CrossRef] [PubMed]
  32. A. Pan, X. Lin, R. Liu, C. Li, X. He, H. Gao, and B. Zou, “Surface crystallization effects on the optical and electric properties of CdS nanorods,” Nanotechnology16(10), 2402–2406 (2005).
    [CrossRef] [PubMed]
  33. P. Liu, V. P. Singh, C. A. Jarro, and S. Rajaputra, “Cadmium sulfide nanowires for the window semiconductor layer in thin film CdS-CdTe solar cells,” Nanotechnology22(14), 145304 (2011).
    [CrossRef] [PubMed]
  34. F. Wu, J. Z. Zhang, R. Kho, and R. K. Mehra, “Radiative and nonradiative lifetimes of band edge states and deep trap states of CdS nanoparticles determined by time-correlated single photon counting,” Chem. Phys. Lett.330(3-4), 237–242 (2000).
    [CrossRef]
  35. L. Yu, X. F. Yu, Y. Qiu, Y. Chen, and S. Yang, “Nonlinear photoluminescence of ZnO/ZnS nanotetrapods,” Chem. Phys. Lett.465(4-6), 272–274 (2008).
    [CrossRef]

2012

Z. Li, J. Wei, P. Li, L. Zhang, E. Shi, C. Ji, J. Liu, D. Zhuang, Z. Liu, J. Zhou, Y. Shang, Y. Li, K. Wang, H. Zhu, D. Wu, and A. Cao, “Solution-processed bulk heterojunction solar cells based on interpenetrating CdS nanowires and carbon nanotubes,” Nano Res.5(9), 595–604 (2012).
[CrossRef]

Y. Liu, Q. Yang, Y. Zhang, Z. Yang, and Z. L. Wang, “Nanowire piezo-phototronic photodetector: theory and experimental design,” Adv. Mater. (Deerfield Beach Fla.)24(11), 1410–1417 (2012).
[CrossRef] [PubMed]

D. Li, J. Zhang, Q. Zhang, and Q. Xiong, “Electric-field-dependent photoconductivity in CdS nanowires and nanobelts: exciton ionization, franz-keldysh, and stark effects,” Nano Lett.12(6), 2993–2999 (2012).
[CrossRef] [PubMed]

S. Geburt, A. Thielmann, R. Röder, C. Borschel, A. McDonnell, M. Kozlik, J. Kühnel, K. A. Sunter, F. Capasso, and C. Ronning, “Low threshold room-temperature lasing of CdS nanowires,” Nanotechnology23(36), 365204 (2012).
[CrossRef] [PubMed]

T. Dufaux, M. Burghard, and K. Kern, “Efficient charge extraction out of nanoscale Schottky contacts to CdS nanowires,” Nano Lett.12(6), 2705–2709 (2012).
[CrossRef] [PubMed]

M. I. Utama, J. Zhang, R. Chen, X. Xu, D. Li, H. Sun, and Q. Xiong, “Synthesis and optical properties of II-VI 1D nanostructures,” Nanoscale4(5), 1422–1435 (2012).
[CrossRef] [PubMed]

B. Piccione, C. H. Cho, L. K. van Vugt, and R. Agarwal, “All-optical active switching in individual semiconductor nanowires,” Nat. Nanotechnol.7(10), 640–645 (2012).
[CrossRef] [PubMed]

Z. X. Yang, W. Zhong, P. Zhang, M. H. Xu, Y. Deng, C. T. Au, and Y. W. Du, “Controllable synthesis, characterization and photoluminescence properties of morphology-tunable CdS nanomaterials generated in thermal evaporation processes,” Appl. Surf. Sci.258(19), 7343–7347 (2012).
[CrossRef]

H. Lee, K. Heo, J. Park, Y. Park, S. Noh, K. S. Kim, C. Lee, B. H. Hong, J. Jian, and S. Hong, “Graphene–nanowire hybrid structures for high-performance photoconductive devices,” J. Mater. Chem.22(17), 8372–8376 (2012).
[CrossRef]

2011

K. Pal, U. N. Maiti, T. P. Majumder, and S. C. Debnath, “A facile strategy for the fabrication of uniform CdS nanowires with high yield and its controlled morphological growth with the assistance of PEG in hydrothermal route,” Appl. Surf. Sci.258(1), 163–168 (2011).
[CrossRef]

L. K. van Vugt, B. Piccione, C. H. Cho, P. Nukala, and R. Agarwal, “One-dimensional polaritons with size-tunable and enhanced coupling strengths in semiconductor nanowires,” Proc. Natl. Acad. Sci. U.S.A.108(25), 10050–10055 (2011).
[CrossRef] [PubMed]

P. Liu, V. P. Singh, C. A. Jarro, and S. Rajaputra, “Cadmium sulfide nanowires for the window semiconductor layer in thin film CdS-CdTe solar cells,” Nanotechnology22(14), 145304 (2011).
[CrossRef] [PubMed]

C. H. Cho, C. O. Aspetti, M. E. Turk, J. M. Kikkawa, S. W. Nam, and R. Agarwal, “Tailoring hot-exciton emission and lifetimes in semiconducting nanowires via whispering-gallery nanocavity plasmons,” Nat. Mater.10(9), 669–675 (2011).
[CrossRef] [PubMed]

Q. Zhang, X. Y. Shan, X. Feng, C. X. Wang, Q. Q. Wang, J. F. Jia, and Q. K. Xue, “Modulating resonance modes and Q value of a CdS nanowire cavity by single Ag nanoparticles,” Nano Lett.11(10), 4270–4274 (2011).
[CrossRef] [PubMed]

2009

R. F. Oulton, V. J. Sorger, T. Zentgraf, R. M. Ma, C. Gladden, L. Dai, G. Bartal, and X. Zhang, “Plasmon lasers at deep subwavelength scale,” Nature461(7264), 629–632 (2009).
[CrossRef] [PubMed]

2008

J. Puthussery, A. Lan, T. H. Kosel, and M. Kuno, “Band-filling of solution-synthesized CdS nanowires,” ACS Nano2(2), 357–367 (2008).
[CrossRef] [PubMed]

Y. F. Lin, J. Song, Y. Ding, S. Y. Lu, and Z. L. Wang, “Alternating the output of a CdS nanowire nanogenerator by a white-light-stimulated optoelectronic effect,” Adv. Mater. (Deerfield Beach Fla.)20(16), 3127–3130 (2008).
[CrossRef]

L. Yu, X. F. Yu, Y. Qiu, Y. Chen, and S. Yang, “Nonlinear photoluminescence of ZnO/ZnS nanotetrapods,” Chem. Phys. Lett.465(4-6), 272–274 (2008).
[CrossRef]

X. F. Yu, L. D. Chen, M. Li, M. Y. Xie, L. Zhou, Y. Li, and Q. Q. Wang, “Highly efficient fluorescence of NdF3/SiO2 core/shell nanoparticles and the applications for in vivo NIR detection,” Adv. Mater. (Deerfield Beach Fla.)20(21), 4118–4123 (2008).
[CrossRef]

H. Gai, Y. Wu, L. Wu, Z. Wang, Y. Shi, M. Jing, and K. Zou, “Solvothermal synthesis of CdS nanowires using L-cysteine as sulfur source and their characterization,” Appl. Phys., A Mater. Sci. Process.91(1), 69–72 (2008).
[CrossRef]

2007

R. M. Ma, L. Dai, H. B. Huo, W. J. Xu, and G. G. Qin, “High-performance logic circuits constructed on single CdS nanowires,” Nano Lett.7(11), 3300–3304 (2007).
[CrossRef] [PubMed]

C. C. Kang, C. W. Lai, H. C. Peng, J. J. Shyue, and P. T. Chou, “Surfactant- and temperature-controlled CdS nanowire formation,” Small3(11), 1882–1885 (2007).
[CrossRef] [PubMed]

2006

J. S. Jie, W. J. Zhang, Y. Jiang, X. M. Meng, Y. Q. Li, and S. T. Lee, “Photoconductive characteristics of single-crystal CdS nanoribbons,” Nano Lett.6(9), 1887–1892 (2006).
[CrossRef] [PubMed]

O. Hayden, R. Agarwal, and C. M. Lieber, “Nanoscale avalanche photodiodes for highly sensitive and spatially resolved photon detection,” Nat. Mater.5(5), 352–356 (2006).
[CrossRef] [PubMed]

2005

R. Agarwal, C. J. Barrelet, and C. M. Lieber, “Lasing in single cadmium sulfide nanowire optical cavities,” Nano Lett.5(5), 917–920 (2005).
[CrossRef] [PubMed]

A. Pan, S. Wang, R. Liu, C. Li, and B. Zou, “Thermal stability and lasing of CdS nanowires coated by amorphous silica,” Small1(11), 1058–1062 (2005).
[CrossRef] [PubMed]

Q. Wang, G. Zhao, and G. Han, “Synthesis of single crystalline CdS nanorods by a PVP-assisted solvothermal method,” Mater. Lett.59(21), 2625–2629 (2005).
[CrossRef]

S. T. Selvan, T. T. Tan, and J. Y. Ying, “Robust, non-cytotoxic, silica-coated CdSe quantum dots with efficient photoluminescence,” Adv. Mater. (Deerfield Beach Fla.)17(13), 1620–1625 (2005).
[CrossRef]

A. Pan, X. Lin, R. Liu, C. Li, X. He, H. Gao, and B. Zou, “Surface crystallization effects on the optical and electric properties of CdS nanorods,” Nanotechnology16(10), 2402–2406 (2005).
[CrossRef] [PubMed]

2004

C. J. Barrelet, A. B. Greytak, and C. M. Lieber, “Nanowire photonic circuit elements,” Nano Lett.4(10), 1981–1985 (2004).
[CrossRef]

2003

X. Duan, Y. Huang, R. Agarwal, and C. M. Lieber, “Single-nanowire electrically driven lasers,” Nature421(6920), 241–245 (2003).
[CrossRef] [PubMed]

K. B. Tang, Y. T. Qian, J. H. Zeng, and X. G. Yang, “Solvothermal route to semiconductor nanowires,” Adv. Mater. (Deerfield Beach Fla.)15(5), 448–450 (2003).
[CrossRef]

2000

F. Wu, J. Z. Zhang, R. Kho, and R. K. Mehra, “Radiative and nonradiative lifetimes of band edge states and deep trap states of CdS nanoparticles determined by time-correlated single photon counting,” Chem. Phys. Lett.330(3-4), 237–242 (2000).
[CrossRef]

D. Xu, Y. Xu, D. Chen, G. Guo, L. Gui, and Y. Tang, “Preparation and characterization of CdS nanowire arrays by DC electrodeposit in porous anodic aluminum oxide templates,” Chem. Phys. Lett.325(4), 340–344 (2000).
[CrossRef]

1998

M. A. Correa-Duarte, M. Giersig, N. A. Kotov, and L. M. Liz-Marzán, “Control of packing order of self-assembled monolayers of magnetite nanoparticles with and without SiO2 coating by microwave irradiation,” Langmuir14(22), 6430–6435 (1998).
[CrossRef]

Agarwal, R.

B. Piccione, C. H. Cho, L. K. van Vugt, and R. Agarwal, “All-optical active switching in individual semiconductor nanowires,” Nat. Nanotechnol.7(10), 640–645 (2012).
[CrossRef] [PubMed]

C. H. Cho, C. O. Aspetti, M. E. Turk, J. M. Kikkawa, S. W. Nam, and R. Agarwal, “Tailoring hot-exciton emission and lifetimes in semiconducting nanowires via whispering-gallery nanocavity plasmons,” Nat. Mater.10(9), 669–675 (2011).
[CrossRef] [PubMed]

L. K. van Vugt, B. Piccione, C. H. Cho, P. Nukala, and R. Agarwal, “One-dimensional polaritons with size-tunable and enhanced coupling strengths in semiconductor nanowires,” Proc. Natl. Acad. Sci. U.S.A.108(25), 10050–10055 (2011).
[CrossRef] [PubMed]

O. Hayden, R. Agarwal, and C. M. Lieber, “Nanoscale avalanche photodiodes for highly sensitive and spatially resolved photon detection,” Nat. Mater.5(5), 352–356 (2006).
[CrossRef] [PubMed]

R. Agarwal, C. J. Barrelet, and C. M. Lieber, “Lasing in single cadmium sulfide nanowire optical cavities,” Nano Lett.5(5), 917–920 (2005).
[CrossRef] [PubMed]

X. Duan, Y. Huang, R. Agarwal, and C. M. Lieber, “Single-nanowire electrically driven lasers,” Nature421(6920), 241–245 (2003).
[CrossRef] [PubMed]

Aspetti, C. O.

C. H. Cho, C. O. Aspetti, M. E. Turk, J. M. Kikkawa, S. W. Nam, and R. Agarwal, “Tailoring hot-exciton emission and lifetimes in semiconducting nanowires via whispering-gallery nanocavity plasmons,” Nat. Mater.10(9), 669–675 (2011).
[CrossRef] [PubMed]

Au, C. T.

Z. X. Yang, W. Zhong, P. Zhang, M. H. Xu, Y. Deng, C. T. Au, and Y. W. Du, “Controllable synthesis, characterization and photoluminescence properties of morphology-tunable CdS nanomaterials generated in thermal evaporation processes,” Appl. Surf. Sci.258(19), 7343–7347 (2012).
[CrossRef]

Barrelet, C. J.

R. Agarwal, C. J. Barrelet, and C. M. Lieber, “Lasing in single cadmium sulfide nanowire optical cavities,” Nano Lett.5(5), 917–920 (2005).
[CrossRef] [PubMed]

C. J. Barrelet, A. B. Greytak, and C. M. Lieber, “Nanowire photonic circuit elements,” Nano Lett.4(10), 1981–1985 (2004).
[CrossRef]

Bartal, G.

R. F. Oulton, V. J. Sorger, T. Zentgraf, R. M. Ma, C. Gladden, L. Dai, G. Bartal, and X. Zhang, “Plasmon lasers at deep subwavelength scale,” Nature461(7264), 629–632 (2009).
[CrossRef] [PubMed]

Borschel, C.

S. Geburt, A. Thielmann, R. Röder, C. Borschel, A. McDonnell, M. Kozlik, J. Kühnel, K. A. Sunter, F. Capasso, and C. Ronning, “Low threshold room-temperature lasing of CdS nanowires,” Nanotechnology23(36), 365204 (2012).
[CrossRef] [PubMed]

Burghard, M.

T. Dufaux, M. Burghard, and K. Kern, “Efficient charge extraction out of nanoscale Schottky contacts to CdS nanowires,” Nano Lett.12(6), 2705–2709 (2012).
[CrossRef] [PubMed]

Cao, A.

Z. Li, J. Wei, P. Li, L. Zhang, E. Shi, C. Ji, J. Liu, D. Zhuang, Z. Liu, J. Zhou, Y. Shang, Y. Li, K. Wang, H. Zhu, D. Wu, and A. Cao, “Solution-processed bulk heterojunction solar cells based on interpenetrating CdS nanowires and carbon nanotubes,” Nano Res.5(9), 595–604 (2012).
[CrossRef]

Capasso, F.

S. Geburt, A. Thielmann, R. Röder, C. Borschel, A. McDonnell, M. Kozlik, J. Kühnel, K. A. Sunter, F. Capasso, and C. Ronning, “Low threshold room-temperature lasing of CdS nanowires,” Nanotechnology23(36), 365204 (2012).
[CrossRef] [PubMed]

Chen, D.

D. Xu, Y. Xu, D. Chen, G. Guo, L. Gui, and Y. Tang, “Preparation and characterization of CdS nanowire arrays by DC electrodeposit in porous anodic aluminum oxide templates,” Chem. Phys. Lett.325(4), 340–344 (2000).
[CrossRef]

Chen, L. D.

X. F. Yu, L. D. Chen, M. Li, M. Y. Xie, L. Zhou, Y. Li, and Q. Q. Wang, “Highly efficient fluorescence of NdF3/SiO2 core/shell nanoparticles and the applications for in vivo NIR detection,” Adv. Mater. (Deerfield Beach Fla.)20(21), 4118–4123 (2008).
[CrossRef]

Chen, R.

M. I. Utama, J. Zhang, R. Chen, X. Xu, D. Li, H. Sun, and Q. Xiong, “Synthesis and optical properties of II-VI 1D nanostructures,” Nanoscale4(5), 1422–1435 (2012).
[CrossRef] [PubMed]

Chen, Y.

L. Yu, X. F. Yu, Y. Qiu, Y. Chen, and S. Yang, “Nonlinear photoluminescence of ZnO/ZnS nanotetrapods,” Chem. Phys. Lett.465(4-6), 272–274 (2008).
[CrossRef]

Cho, C. H.

B. Piccione, C. H. Cho, L. K. van Vugt, and R. Agarwal, “All-optical active switching in individual semiconductor nanowires,” Nat. Nanotechnol.7(10), 640–645 (2012).
[CrossRef] [PubMed]

C. H. Cho, C. O. Aspetti, M. E. Turk, J. M. Kikkawa, S. W. Nam, and R. Agarwal, “Tailoring hot-exciton emission and lifetimes in semiconducting nanowires via whispering-gallery nanocavity plasmons,” Nat. Mater.10(9), 669–675 (2011).
[CrossRef] [PubMed]

L. K. van Vugt, B. Piccione, C. H. Cho, P. Nukala, and R. Agarwal, “One-dimensional polaritons with size-tunable and enhanced coupling strengths in semiconductor nanowires,” Proc. Natl. Acad. Sci. U.S.A.108(25), 10050–10055 (2011).
[CrossRef] [PubMed]

Chou, P. T.

C. C. Kang, C. W. Lai, H. C. Peng, J. J. Shyue, and P. T. Chou, “Surfactant- and temperature-controlled CdS nanowire formation,” Small3(11), 1882–1885 (2007).
[CrossRef] [PubMed]

Correa-Duarte, M. A.

M. A. Correa-Duarte, M. Giersig, N. A. Kotov, and L. M. Liz-Marzán, “Control of packing order of self-assembled monolayers of magnetite nanoparticles with and without SiO2 coating by microwave irradiation,” Langmuir14(22), 6430–6435 (1998).
[CrossRef]

Dai, L.

R. F. Oulton, V. J. Sorger, T. Zentgraf, R. M. Ma, C. Gladden, L. Dai, G. Bartal, and X. Zhang, “Plasmon lasers at deep subwavelength scale,” Nature461(7264), 629–632 (2009).
[CrossRef] [PubMed]

R. M. Ma, L. Dai, H. B. Huo, W. J. Xu, and G. G. Qin, “High-performance logic circuits constructed on single CdS nanowires,” Nano Lett.7(11), 3300–3304 (2007).
[CrossRef] [PubMed]

Debnath, S. C.

K. Pal, U. N. Maiti, T. P. Majumder, and S. C. Debnath, “A facile strategy for the fabrication of uniform CdS nanowires with high yield and its controlled morphological growth with the assistance of PEG in hydrothermal route,” Appl. Surf. Sci.258(1), 163–168 (2011).
[CrossRef]

Deng, Y.

Z. X. Yang, W. Zhong, P. Zhang, M. H. Xu, Y. Deng, C. T. Au, and Y. W. Du, “Controllable synthesis, characterization and photoluminescence properties of morphology-tunable CdS nanomaterials generated in thermal evaporation processes,” Appl. Surf. Sci.258(19), 7343–7347 (2012).
[CrossRef]

Ding, Y.

Y. F. Lin, J. Song, Y. Ding, S. Y. Lu, and Z. L. Wang, “Alternating the output of a CdS nanowire nanogenerator by a white-light-stimulated optoelectronic effect,” Adv. Mater. (Deerfield Beach Fla.)20(16), 3127–3130 (2008).
[CrossRef]

Du, Y. W.

Z. X. Yang, W. Zhong, P. Zhang, M. H. Xu, Y. Deng, C. T. Au, and Y. W. Du, “Controllable synthesis, characterization and photoluminescence properties of morphology-tunable CdS nanomaterials generated in thermal evaporation processes,” Appl. Surf. Sci.258(19), 7343–7347 (2012).
[CrossRef]

Duan, X.

X. Duan, Y. Huang, R. Agarwal, and C. M. Lieber, “Single-nanowire electrically driven lasers,” Nature421(6920), 241–245 (2003).
[CrossRef] [PubMed]

Dufaux, T.

T. Dufaux, M. Burghard, and K. Kern, “Efficient charge extraction out of nanoscale Schottky contacts to CdS nanowires,” Nano Lett.12(6), 2705–2709 (2012).
[CrossRef] [PubMed]

Feng, X.

Q. Zhang, X. Y. Shan, X. Feng, C. X. Wang, Q. Q. Wang, J. F. Jia, and Q. K. Xue, “Modulating resonance modes and Q value of a CdS nanowire cavity by single Ag nanoparticles,” Nano Lett.11(10), 4270–4274 (2011).
[CrossRef] [PubMed]

Gai, H.

H. Gai, Y. Wu, L. Wu, Z. Wang, Y. Shi, M. Jing, and K. Zou, “Solvothermal synthesis of CdS nanowires using L-cysteine as sulfur source and their characterization,” Appl. Phys., A Mater. Sci. Process.91(1), 69–72 (2008).
[CrossRef]

Gao, H.

A. Pan, X. Lin, R. Liu, C. Li, X. He, H. Gao, and B. Zou, “Surface crystallization effects on the optical and electric properties of CdS nanorods,” Nanotechnology16(10), 2402–2406 (2005).
[CrossRef] [PubMed]

Geburt, S.

S. Geburt, A. Thielmann, R. Röder, C. Borschel, A. McDonnell, M. Kozlik, J. Kühnel, K. A. Sunter, F. Capasso, and C. Ronning, “Low threshold room-temperature lasing of CdS nanowires,” Nanotechnology23(36), 365204 (2012).
[CrossRef] [PubMed]

Giersig, M.

M. A. Correa-Duarte, M. Giersig, N. A. Kotov, and L. M. Liz-Marzán, “Control of packing order of self-assembled monolayers of magnetite nanoparticles with and without SiO2 coating by microwave irradiation,” Langmuir14(22), 6430–6435 (1998).
[CrossRef]

Gladden, C.

R. F. Oulton, V. J. Sorger, T. Zentgraf, R. M. Ma, C. Gladden, L. Dai, G. Bartal, and X. Zhang, “Plasmon lasers at deep subwavelength scale,” Nature461(7264), 629–632 (2009).
[CrossRef] [PubMed]

Greytak, A. B.

C. J. Barrelet, A. B. Greytak, and C. M. Lieber, “Nanowire photonic circuit elements,” Nano Lett.4(10), 1981–1985 (2004).
[CrossRef]

Gui, L.

D. Xu, Y. Xu, D. Chen, G. Guo, L. Gui, and Y. Tang, “Preparation and characterization of CdS nanowire arrays by DC electrodeposit in porous anodic aluminum oxide templates,” Chem. Phys. Lett.325(4), 340–344 (2000).
[CrossRef]

Guo, G.

D. Xu, Y. Xu, D. Chen, G. Guo, L. Gui, and Y. Tang, “Preparation and characterization of CdS nanowire arrays by DC electrodeposit in porous anodic aluminum oxide templates,” Chem. Phys. Lett.325(4), 340–344 (2000).
[CrossRef]

Han, G.

Q. Wang, G. Zhao, and G. Han, “Synthesis of single crystalline CdS nanorods by a PVP-assisted solvothermal method,” Mater. Lett.59(21), 2625–2629 (2005).
[CrossRef]

Hayden, O.

O. Hayden, R. Agarwal, and C. M. Lieber, “Nanoscale avalanche photodiodes for highly sensitive and spatially resolved photon detection,” Nat. Mater.5(5), 352–356 (2006).
[CrossRef] [PubMed]

He, X.

A. Pan, X. Lin, R. Liu, C. Li, X. He, H. Gao, and B. Zou, “Surface crystallization effects on the optical and electric properties of CdS nanorods,” Nanotechnology16(10), 2402–2406 (2005).
[CrossRef] [PubMed]

Heo, K.

H. Lee, K. Heo, J. Park, Y. Park, S. Noh, K. S. Kim, C. Lee, B. H. Hong, J. Jian, and S. Hong, “Graphene–nanowire hybrid structures for high-performance photoconductive devices,” J. Mater. Chem.22(17), 8372–8376 (2012).
[CrossRef]

Hong, B. H.

H. Lee, K. Heo, J. Park, Y. Park, S. Noh, K. S. Kim, C. Lee, B. H. Hong, J. Jian, and S. Hong, “Graphene–nanowire hybrid structures for high-performance photoconductive devices,” J. Mater. Chem.22(17), 8372–8376 (2012).
[CrossRef]

Hong, S.

H. Lee, K. Heo, J. Park, Y. Park, S. Noh, K. S. Kim, C. Lee, B. H. Hong, J. Jian, and S. Hong, “Graphene–nanowire hybrid structures for high-performance photoconductive devices,” J. Mater. Chem.22(17), 8372–8376 (2012).
[CrossRef]

Huang, Y.

X. Duan, Y. Huang, R. Agarwal, and C. M. Lieber, “Single-nanowire electrically driven lasers,” Nature421(6920), 241–245 (2003).
[CrossRef] [PubMed]

Huo, H. B.

R. M. Ma, L. Dai, H. B. Huo, W. J. Xu, and G. G. Qin, “High-performance logic circuits constructed on single CdS nanowires,” Nano Lett.7(11), 3300–3304 (2007).
[CrossRef] [PubMed]

Jarro, C. A.

P. Liu, V. P. Singh, C. A. Jarro, and S. Rajaputra, “Cadmium sulfide nanowires for the window semiconductor layer in thin film CdS-CdTe solar cells,” Nanotechnology22(14), 145304 (2011).
[CrossRef] [PubMed]

Ji, C.

Z. Li, J. Wei, P. Li, L. Zhang, E. Shi, C. Ji, J. Liu, D. Zhuang, Z. Liu, J. Zhou, Y. Shang, Y. Li, K. Wang, H. Zhu, D. Wu, and A. Cao, “Solution-processed bulk heterojunction solar cells based on interpenetrating CdS nanowires and carbon nanotubes,” Nano Res.5(9), 595–604 (2012).
[CrossRef]

Jia, J. F.

Q. Zhang, X. Y. Shan, X. Feng, C. X. Wang, Q. Q. Wang, J. F. Jia, and Q. K. Xue, “Modulating resonance modes and Q value of a CdS nanowire cavity by single Ag nanoparticles,” Nano Lett.11(10), 4270–4274 (2011).
[CrossRef] [PubMed]

Jian, J.

H. Lee, K. Heo, J. Park, Y. Park, S. Noh, K. S. Kim, C. Lee, B. H. Hong, J. Jian, and S. Hong, “Graphene–nanowire hybrid structures for high-performance photoconductive devices,” J. Mater. Chem.22(17), 8372–8376 (2012).
[CrossRef]

Jiang, Y.

J. S. Jie, W. J. Zhang, Y. Jiang, X. M. Meng, Y. Q. Li, and S. T. Lee, “Photoconductive characteristics of single-crystal CdS nanoribbons,” Nano Lett.6(9), 1887–1892 (2006).
[CrossRef] [PubMed]

Jie, J. S.

J. S. Jie, W. J. Zhang, Y. Jiang, X. M. Meng, Y. Q. Li, and S. T. Lee, “Photoconductive characteristics of single-crystal CdS nanoribbons,” Nano Lett.6(9), 1887–1892 (2006).
[CrossRef] [PubMed]

Jing, M.

H. Gai, Y. Wu, L. Wu, Z. Wang, Y. Shi, M. Jing, and K. Zou, “Solvothermal synthesis of CdS nanowires using L-cysteine as sulfur source and their characterization,” Appl. Phys., A Mater. Sci. Process.91(1), 69–72 (2008).
[CrossRef]

Kang, C. C.

C. C. Kang, C. W. Lai, H. C. Peng, J. J. Shyue, and P. T. Chou, “Surfactant- and temperature-controlled CdS nanowire formation,” Small3(11), 1882–1885 (2007).
[CrossRef] [PubMed]

Kern, K.

T. Dufaux, M. Burghard, and K. Kern, “Efficient charge extraction out of nanoscale Schottky contacts to CdS nanowires,” Nano Lett.12(6), 2705–2709 (2012).
[CrossRef] [PubMed]

Kho, R.

F. Wu, J. Z. Zhang, R. Kho, and R. K. Mehra, “Radiative and nonradiative lifetimes of band edge states and deep trap states of CdS nanoparticles determined by time-correlated single photon counting,” Chem. Phys. Lett.330(3-4), 237–242 (2000).
[CrossRef]

Kikkawa, J. M.

C. H. Cho, C. O. Aspetti, M. E. Turk, J. M. Kikkawa, S. W. Nam, and R. Agarwal, “Tailoring hot-exciton emission and lifetimes in semiconducting nanowires via whispering-gallery nanocavity plasmons,” Nat. Mater.10(9), 669–675 (2011).
[CrossRef] [PubMed]

Kim, K. S.

H. Lee, K. Heo, J. Park, Y. Park, S. Noh, K. S. Kim, C. Lee, B. H. Hong, J. Jian, and S. Hong, “Graphene–nanowire hybrid structures for high-performance photoconductive devices,” J. Mater. Chem.22(17), 8372–8376 (2012).
[CrossRef]

Kosel, T. H.

J. Puthussery, A. Lan, T. H. Kosel, and M. Kuno, “Band-filling of solution-synthesized CdS nanowires,” ACS Nano2(2), 357–367 (2008).
[CrossRef] [PubMed]

Kotov, N. A.

M. A. Correa-Duarte, M. Giersig, N. A. Kotov, and L. M. Liz-Marzán, “Control of packing order of self-assembled monolayers of magnetite nanoparticles with and without SiO2 coating by microwave irradiation,” Langmuir14(22), 6430–6435 (1998).
[CrossRef]

Kozlik, M.

S. Geburt, A. Thielmann, R. Röder, C. Borschel, A. McDonnell, M. Kozlik, J. Kühnel, K. A. Sunter, F. Capasso, and C. Ronning, “Low threshold room-temperature lasing of CdS nanowires,” Nanotechnology23(36), 365204 (2012).
[CrossRef] [PubMed]

Kühnel, J.

S. Geburt, A. Thielmann, R. Röder, C. Borschel, A. McDonnell, M. Kozlik, J. Kühnel, K. A. Sunter, F. Capasso, and C. Ronning, “Low threshold room-temperature lasing of CdS nanowires,” Nanotechnology23(36), 365204 (2012).
[CrossRef] [PubMed]

Kuno, M.

J. Puthussery, A. Lan, T. H. Kosel, and M. Kuno, “Band-filling of solution-synthesized CdS nanowires,” ACS Nano2(2), 357–367 (2008).
[CrossRef] [PubMed]

Lai, C. W.

C. C. Kang, C. W. Lai, H. C. Peng, J. J. Shyue, and P. T. Chou, “Surfactant- and temperature-controlled CdS nanowire formation,” Small3(11), 1882–1885 (2007).
[CrossRef] [PubMed]

Lan, A.

J. Puthussery, A. Lan, T. H. Kosel, and M. Kuno, “Band-filling of solution-synthesized CdS nanowires,” ACS Nano2(2), 357–367 (2008).
[CrossRef] [PubMed]

Lee, C.

H. Lee, K. Heo, J. Park, Y. Park, S. Noh, K. S. Kim, C. Lee, B. H. Hong, J. Jian, and S. Hong, “Graphene–nanowire hybrid structures for high-performance photoconductive devices,” J. Mater. Chem.22(17), 8372–8376 (2012).
[CrossRef]

Lee, H.

H. Lee, K. Heo, J. Park, Y. Park, S. Noh, K. S. Kim, C. Lee, B. H. Hong, J. Jian, and S. Hong, “Graphene–nanowire hybrid structures for high-performance photoconductive devices,” J. Mater. Chem.22(17), 8372–8376 (2012).
[CrossRef]

Lee, S. T.

J. S. Jie, W. J. Zhang, Y. Jiang, X. M. Meng, Y. Q. Li, and S. T. Lee, “Photoconductive characteristics of single-crystal CdS nanoribbons,” Nano Lett.6(9), 1887–1892 (2006).
[CrossRef] [PubMed]

Li, C.

A. Pan, S. Wang, R. Liu, C. Li, and B. Zou, “Thermal stability and lasing of CdS nanowires coated by amorphous silica,” Small1(11), 1058–1062 (2005).
[CrossRef] [PubMed]

A. Pan, X. Lin, R. Liu, C. Li, X. He, H. Gao, and B. Zou, “Surface crystallization effects on the optical and electric properties of CdS nanorods,” Nanotechnology16(10), 2402–2406 (2005).
[CrossRef] [PubMed]

Li, D.

D. Li, J. Zhang, Q. Zhang, and Q. Xiong, “Electric-field-dependent photoconductivity in CdS nanowires and nanobelts: exciton ionization, franz-keldysh, and stark effects,” Nano Lett.12(6), 2993–2999 (2012).
[CrossRef] [PubMed]

M. I. Utama, J. Zhang, R. Chen, X. Xu, D. Li, H. Sun, and Q. Xiong, “Synthesis and optical properties of II-VI 1D nanostructures,” Nanoscale4(5), 1422–1435 (2012).
[CrossRef] [PubMed]

Li, M.

X. F. Yu, L. D. Chen, M. Li, M. Y. Xie, L. Zhou, Y. Li, and Q. Q. Wang, “Highly efficient fluorescence of NdF3/SiO2 core/shell nanoparticles and the applications for in vivo NIR detection,” Adv. Mater. (Deerfield Beach Fla.)20(21), 4118–4123 (2008).
[CrossRef]

Li, P.

Z. Li, J. Wei, P. Li, L. Zhang, E. Shi, C. Ji, J. Liu, D. Zhuang, Z. Liu, J. Zhou, Y. Shang, Y. Li, K. Wang, H. Zhu, D. Wu, and A. Cao, “Solution-processed bulk heterojunction solar cells based on interpenetrating CdS nanowires and carbon nanotubes,” Nano Res.5(9), 595–604 (2012).
[CrossRef]

Li, Y.

Z. Li, J. Wei, P. Li, L. Zhang, E. Shi, C. Ji, J. Liu, D. Zhuang, Z. Liu, J. Zhou, Y. Shang, Y. Li, K. Wang, H. Zhu, D. Wu, and A. Cao, “Solution-processed bulk heterojunction solar cells based on interpenetrating CdS nanowires and carbon nanotubes,” Nano Res.5(9), 595–604 (2012).
[CrossRef]

X. F. Yu, L. D. Chen, M. Li, M. Y. Xie, L. Zhou, Y. Li, and Q. Q. Wang, “Highly efficient fluorescence of NdF3/SiO2 core/shell nanoparticles and the applications for in vivo NIR detection,” Adv. Mater. (Deerfield Beach Fla.)20(21), 4118–4123 (2008).
[CrossRef]

Li, Y. Q.

J. S. Jie, W. J. Zhang, Y. Jiang, X. M. Meng, Y. Q. Li, and S. T. Lee, “Photoconductive characteristics of single-crystal CdS nanoribbons,” Nano Lett.6(9), 1887–1892 (2006).
[CrossRef] [PubMed]

Li, Z.

Z. Li, J. Wei, P. Li, L. Zhang, E. Shi, C. Ji, J. Liu, D. Zhuang, Z. Liu, J. Zhou, Y. Shang, Y. Li, K. Wang, H. Zhu, D. Wu, and A. Cao, “Solution-processed bulk heterojunction solar cells based on interpenetrating CdS nanowires and carbon nanotubes,” Nano Res.5(9), 595–604 (2012).
[CrossRef]

Lieber, C. M.

O. Hayden, R. Agarwal, and C. M. Lieber, “Nanoscale avalanche photodiodes for highly sensitive and spatially resolved photon detection,” Nat. Mater.5(5), 352–356 (2006).
[CrossRef] [PubMed]

R. Agarwal, C. J. Barrelet, and C. M. Lieber, “Lasing in single cadmium sulfide nanowire optical cavities,” Nano Lett.5(5), 917–920 (2005).
[CrossRef] [PubMed]

C. J. Barrelet, A. B. Greytak, and C. M. Lieber, “Nanowire photonic circuit elements,” Nano Lett.4(10), 1981–1985 (2004).
[CrossRef]

X. Duan, Y. Huang, R. Agarwal, and C. M. Lieber, “Single-nanowire electrically driven lasers,” Nature421(6920), 241–245 (2003).
[CrossRef] [PubMed]

Lin, X.

A. Pan, X. Lin, R. Liu, C. Li, X. He, H. Gao, and B. Zou, “Surface crystallization effects on the optical and electric properties of CdS nanorods,” Nanotechnology16(10), 2402–2406 (2005).
[CrossRef] [PubMed]

Lin, Y. F.

Y. F. Lin, J. Song, Y. Ding, S. Y. Lu, and Z. L. Wang, “Alternating the output of a CdS nanowire nanogenerator by a white-light-stimulated optoelectronic effect,” Adv. Mater. (Deerfield Beach Fla.)20(16), 3127–3130 (2008).
[CrossRef]

Liu, J.

Z. Li, J. Wei, P. Li, L. Zhang, E. Shi, C. Ji, J. Liu, D. Zhuang, Z. Liu, J. Zhou, Y. Shang, Y. Li, K. Wang, H. Zhu, D. Wu, and A. Cao, “Solution-processed bulk heterojunction solar cells based on interpenetrating CdS nanowires and carbon nanotubes,” Nano Res.5(9), 595–604 (2012).
[CrossRef]

Liu, P.

P. Liu, V. P. Singh, C. A. Jarro, and S. Rajaputra, “Cadmium sulfide nanowires for the window semiconductor layer in thin film CdS-CdTe solar cells,” Nanotechnology22(14), 145304 (2011).
[CrossRef] [PubMed]

Liu, R.

A. Pan, X. Lin, R. Liu, C. Li, X. He, H. Gao, and B. Zou, “Surface crystallization effects on the optical and electric properties of CdS nanorods,” Nanotechnology16(10), 2402–2406 (2005).
[CrossRef] [PubMed]

A. Pan, S. Wang, R. Liu, C. Li, and B. Zou, “Thermal stability and lasing of CdS nanowires coated by amorphous silica,” Small1(11), 1058–1062 (2005).
[CrossRef] [PubMed]

Liu, Y.

Y. Liu, Q. Yang, Y. Zhang, Z. Yang, and Z. L. Wang, “Nanowire piezo-phototronic photodetector: theory and experimental design,” Adv. Mater. (Deerfield Beach Fla.)24(11), 1410–1417 (2012).
[CrossRef] [PubMed]

Liu, Z.

Z. Li, J. Wei, P. Li, L. Zhang, E. Shi, C. Ji, J. Liu, D. Zhuang, Z. Liu, J. Zhou, Y. Shang, Y. Li, K. Wang, H. Zhu, D. Wu, and A. Cao, “Solution-processed bulk heterojunction solar cells based on interpenetrating CdS nanowires and carbon nanotubes,” Nano Res.5(9), 595–604 (2012).
[CrossRef]

Liz-Marzán, L. M.

M. A. Correa-Duarte, M. Giersig, N. A. Kotov, and L. M. Liz-Marzán, “Control of packing order of self-assembled monolayers of magnetite nanoparticles with and without SiO2 coating by microwave irradiation,” Langmuir14(22), 6430–6435 (1998).
[CrossRef]

Lu, S. Y.

Y. F. Lin, J. Song, Y. Ding, S. Y. Lu, and Z. L. Wang, “Alternating the output of a CdS nanowire nanogenerator by a white-light-stimulated optoelectronic effect,” Adv. Mater. (Deerfield Beach Fla.)20(16), 3127–3130 (2008).
[CrossRef]

Ma, R. M.

R. F. Oulton, V. J. Sorger, T. Zentgraf, R. M. Ma, C. Gladden, L. Dai, G. Bartal, and X. Zhang, “Plasmon lasers at deep subwavelength scale,” Nature461(7264), 629–632 (2009).
[CrossRef] [PubMed]

R. M. Ma, L. Dai, H. B. Huo, W. J. Xu, and G. G. Qin, “High-performance logic circuits constructed on single CdS nanowires,” Nano Lett.7(11), 3300–3304 (2007).
[CrossRef] [PubMed]

Maiti, U. N.

K. Pal, U. N. Maiti, T. P. Majumder, and S. C. Debnath, “A facile strategy for the fabrication of uniform CdS nanowires with high yield and its controlled morphological growth with the assistance of PEG in hydrothermal route,” Appl. Surf. Sci.258(1), 163–168 (2011).
[CrossRef]

Majumder, T. P.

K. Pal, U. N. Maiti, T. P. Majumder, and S. C. Debnath, “A facile strategy for the fabrication of uniform CdS nanowires with high yield and its controlled morphological growth with the assistance of PEG in hydrothermal route,” Appl. Surf. Sci.258(1), 163–168 (2011).
[CrossRef]

McDonnell, A.

S. Geburt, A. Thielmann, R. Röder, C. Borschel, A. McDonnell, M. Kozlik, J. Kühnel, K. A. Sunter, F. Capasso, and C. Ronning, “Low threshold room-temperature lasing of CdS nanowires,” Nanotechnology23(36), 365204 (2012).
[CrossRef] [PubMed]

Mehra, R. K.

F. Wu, J. Z. Zhang, R. Kho, and R. K. Mehra, “Radiative and nonradiative lifetimes of band edge states and deep trap states of CdS nanoparticles determined by time-correlated single photon counting,” Chem. Phys. Lett.330(3-4), 237–242 (2000).
[CrossRef]

Meng, X. M.

J. S. Jie, W. J. Zhang, Y. Jiang, X. M. Meng, Y. Q. Li, and S. T. Lee, “Photoconductive characteristics of single-crystal CdS nanoribbons,” Nano Lett.6(9), 1887–1892 (2006).
[CrossRef] [PubMed]

Nam, S. W.

C. H. Cho, C. O. Aspetti, M. E. Turk, J. M. Kikkawa, S. W. Nam, and R. Agarwal, “Tailoring hot-exciton emission and lifetimes in semiconducting nanowires via whispering-gallery nanocavity plasmons,” Nat. Mater.10(9), 669–675 (2011).
[CrossRef] [PubMed]

Noh, S.

H. Lee, K. Heo, J. Park, Y. Park, S. Noh, K. S. Kim, C. Lee, B. H. Hong, J. Jian, and S. Hong, “Graphene–nanowire hybrid structures for high-performance photoconductive devices,” J. Mater. Chem.22(17), 8372–8376 (2012).
[CrossRef]

Nukala, P.

L. K. van Vugt, B. Piccione, C. H. Cho, P. Nukala, and R. Agarwal, “One-dimensional polaritons with size-tunable and enhanced coupling strengths in semiconductor nanowires,” Proc. Natl. Acad. Sci. U.S.A.108(25), 10050–10055 (2011).
[CrossRef] [PubMed]

Oulton, R. F.

R. F. Oulton, V. J. Sorger, T. Zentgraf, R. M. Ma, C. Gladden, L. Dai, G. Bartal, and X. Zhang, “Plasmon lasers at deep subwavelength scale,” Nature461(7264), 629–632 (2009).
[CrossRef] [PubMed]

Pal, K.

K. Pal, U. N. Maiti, T. P. Majumder, and S. C. Debnath, “A facile strategy for the fabrication of uniform CdS nanowires with high yield and its controlled morphological growth with the assistance of PEG in hydrothermal route,” Appl. Surf. Sci.258(1), 163–168 (2011).
[CrossRef]

Pan, A.

A. Pan, X. Lin, R. Liu, C. Li, X. He, H. Gao, and B. Zou, “Surface crystallization effects on the optical and electric properties of CdS nanorods,” Nanotechnology16(10), 2402–2406 (2005).
[CrossRef] [PubMed]

A. Pan, S. Wang, R. Liu, C. Li, and B. Zou, “Thermal stability and lasing of CdS nanowires coated by amorphous silica,” Small1(11), 1058–1062 (2005).
[CrossRef] [PubMed]

Park, J.

H. Lee, K. Heo, J. Park, Y. Park, S. Noh, K. S. Kim, C. Lee, B. H. Hong, J. Jian, and S. Hong, “Graphene–nanowire hybrid structures for high-performance photoconductive devices,” J. Mater. Chem.22(17), 8372–8376 (2012).
[CrossRef]

Park, Y.

H. Lee, K. Heo, J. Park, Y. Park, S. Noh, K. S. Kim, C. Lee, B. H. Hong, J. Jian, and S. Hong, “Graphene–nanowire hybrid structures for high-performance photoconductive devices,” J. Mater. Chem.22(17), 8372–8376 (2012).
[CrossRef]

Peng, H. C.

C. C. Kang, C. W. Lai, H. C. Peng, J. J. Shyue, and P. T. Chou, “Surfactant- and temperature-controlled CdS nanowire formation,” Small3(11), 1882–1885 (2007).
[CrossRef] [PubMed]

Piccione, B.

B. Piccione, C. H. Cho, L. K. van Vugt, and R. Agarwal, “All-optical active switching in individual semiconductor nanowires,” Nat. Nanotechnol.7(10), 640–645 (2012).
[CrossRef] [PubMed]

L. K. van Vugt, B. Piccione, C. H. Cho, P. Nukala, and R. Agarwal, “One-dimensional polaritons with size-tunable and enhanced coupling strengths in semiconductor nanowires,” Proc. Natl. Acad. Sci. U.S.A.108(25), 10050–10055 (2011).
[CrossRef] [PubMed]

Puthussery, J.

J. Puthussery, A. Lan, T. H. Kosel, and M. Kuno, “Band-filling of solution-synthesized CdS nanowires,” ACS Nano2(2), 357–367 (2008).
[CrossRef] [PubMed]

Qian, Y. T.

K. B. Tang, Y. T. Qian, J. H. Zeng, and X. G. Yang, “Solvothermal route to semiconductor nanowires,” Adv. Mater. (Deerfield Beach Fla.)15(5), 448–450 (2003).
[CrossRef]

Qin, G. G.

R. M. Ma, L. Dai, H. B. Huo, W. J. Xu, and G. G. Qin, “High-performance logic circuits constructed on single CdS nanowires,” Nano Lett.7(11), 3300–3304 (2007).
[CrossRef] [PubMed]

Qiu, Y.

L. Yu, X. F. Yu, Y. Qiu, Y. Chen, and S. Yang, “Nonlinear photoluminescence of ZnO/ZnS nanotetrapods,” Chem. Phys. Lett.465(4-6), 272–274 (2008).
[CrossRef]

Rajaputra, S.

P. Liu, V. P. Singh, C. A. Jarro, and S. Rajaputra, “Cadmium sulfide nanowires for the window semiconductor layer in thin film CdS-CdTe solar cells,” Nanotechnology22(14), 145304 (2011).
[CrossRef] [PubMed]

Röder, R.

S. Geburt, A. Thielmann, R. Röder, C. Borschel, A. McDonnell, M. Kozlik, J. Kühnel, K. A. Sunter, F. Capasso, and C. Ronning, “Low threshold room-temperature lasing of CdS nanowires,” Nanotechnology23(36), 365204 (2012).
[CrossRef] [PubMed]

Ronning, C.

S. Geburt, A. Thielmann, R. Röder, C. Borschel, A. McDonnell, M. Kozlik, J. Kühnel, K. A. Sunter, F. Capasso, and C. Ronning, “Low threshold room-temperature lasing of CdS nanowires,” Nanotechnology23(36), 365204 (2012).
[CrossRef] [PubMed]

Selvan, S. T.

S. T. Selvan, T. T. Tan, and J. Y. Ying, “Robust, non-cytotoxic, silica-coated CdSe quantum dots with efficient photoluminescence,” Adv. Mater. (Deerfield Beach Fla.)17(13), 1620–1625 (2005).
[CrossRef]

Shan, X. Y.

Q. Zhang, X. Y. Shan, X. Feng, C. X. Wang, Q. Q. Wang, J. F. Jia, and Q. K. Xue, “Modulating resonance modes and Q value of a CdS nanowire cavity by single Ag nanoparticles,” Nano Lett.11(10), 4270–4274 (2011).
[CrossRef] [PubMed]

Shang, Y.

Z. Li, J. Wei, P. Li, L. Zhang, E. Shi, C. Ji, J. Liu, D. Zhuang, Z. Liu, J. Zhou, Y. Shang, Y. Li, K. Wang, H. Zhu, D. Wu, and A. Cao, “Solution-processed bulk heterojunction solar cells based on interpenetrating CdS nanowires and carbon nanotubes,” Nano Res.5(9), 595–604 (2012).
[CrossRef]

Shi, E.

Z. Li, J. Wei, P. Li, L. Zhang, E. Shi, C. Ji, J. Liu, D. Zhuang, Z. Liu, J. Zhou, Y. Shang, Y. Li, K. Wang, H. Zhu, D. Wu, and A. Cao, “Solution-processed bulk heterojunction solar cells based on interpenetrating CdS nanowires and carbon nanotubes,” Nano Res.5(9), 595–604 (2012).
[CrossRef]

Shi, Y.

H. Gai, Y. Wu, L. Wu, Z. Wang, Y. Shi, M. Jing, and K. Zou, “Solvothermal synthesis of CdS nanowires using L-cysteine as sulfur source and their characterization,” Appl. Phys., A Mater. Sci. Process.91(1), 69–72 (2008).
[CrossRef]

Shyue, J. J.

C. C. Kang, C. W. Lai, H. C. Peng, J. J. Shyue, and P. T. Chou, “Surfactant- and temperature-controlled CdS nanowire formation,” Small3(11), 1882–1885 (2007).
[CrossRef] [PubMed]

Singh, V. P.

P. Liu, V. P. Singh, C. A. Jarro, and S. Rajaputra, “Cadmium sulfide nanowires for the window semiconductor layer in thin film CdS-CdTe solar cells,” Nanotechnology22(14), 145304 (2011).
[CrossRef] [PubMed]

Song, J.

Y. F. Lin, J. Song, Y. Ding, S. Y. Lu, and Z. L. Wang, “Alternating the output of a CdS nanowire nanogenerator by a white-light-stimulated optoelectronic effect,” Adv. Mater. (Deerfield Beach Fla.)20(16), 3127–3130 (2008).
[CrossRef]

Sorger, V. J.

R. F. Oulton, V. J. Sorger, T. Zentgraf, R. M. Ma, C. Gladden, L. Dai, G. Bartal, and X. Zhang, “Plasmon lasers at deep subwavelength scale,” Nature461(7264), 629–632 (2009).
[CrossRef] [PubMed]

Sun, H.

M. I. Utama, J. Zhang, R. Chen, X. Xu, D. Li, H. Sun, and Q. Xiong, “Synthesis and optical properties of II-VI 1D nanostructures,” Nanoscale4(5), 1422–1435 (2012).
[CrossRef] [PubMed]

Sunter, K. A.

S. Geburt, A. Thielmann, R. Röder, C. Borschel, A. McDonnell, M. Kozlik, J. Kühnel, K. A. Sunter, F. Capasso, and C. Ronning, “Low threshold room-temperature lasing of CdS nanowires,” Nanotechnology23(36), 365204 (2012).
[CrossRef] [PubMed]

Tan, T. T.

S. T. Selvan, T. T. Tan, and J. Y. Ying, “Robust, non-cytotoxic, silica-coated CdSe quantum dots with efficient photoluminescence,” Adv. Mater. (Deerfield Beach Fla.)17(13), 1620–1625 (2005).
[CrossRef]

Tang, K. B.

K. B. Tang, Y. T. Qian, J. H. Zeng, and X. G. Yang, “Solvothermal route to semiconductor nanowires,” Adv. Mater. (Deerfield Beach Fla.)15(5), 448–450 (2003).
[CrossRef]

Tang, Y.

D. Xu, Y. Xu, D. Chen, G. Guo, L. Gui, and Y. Tang, “Preparation and characterization of CdS nanowire arrays by DC electrodeposit in porous anodic aluminum oxide templates,” Chem. Phys. Lett.325(4), 340–344 (2000).
[CrossRef]

Thielmann, A.

S. Geburt, A. Thielmann, R. Röder, C. Borschel, A. McDonnell, M. Kozlik, J. Kühnel, K. A. Sunter, F. Capasso, and C. Ronning, “Low threshold room-temperature lasing of CdS nanowires,” Nanotechnology23(36), 365204 (2012).
[CrossRef] [PubMed]

Turk, M. E.

C. H. Cho, C. O. Aspetti, M. E. Turk, J. M. Kikkawa, S. W. Nam, and R. Agarwal, “Tailoring hot-exciton emission and lifetimes in semiconducting nanowires via whispering-gallery nanocavity plasmons,” Nat. Mater.10(9), 669–675 (2011).
[CrossRef] [PubMed]

Utama, M. I.

M. I. Utama, J. Zhang, R. Chen, X. Xu, D. Li, H. Sun, and Q. Xiong, “Synthesis and optical properties of II-VI 1D nanostructures,” Nanoscale4(5), 1422–1435 (2012).
[CrossRef] [PubMed]

van Vugt, L. K.

B. Piccione, C. H. Cho, L. K. van Vugt, and R. Agarwal, “All-optical active switching in individual semiconductor nanowires,” Nat. Nanotechnol.7(10), 640–645 (2012).
[CrossRef] [PubMed]

L. K. van Vugt, B. Piccione, C. H. Cho, P. Nukala, and R. Agarwal, “One-dimensional polaritons with size-tunable and enhanced coupling strengths in semiconductor nanowires,” Proc. Natl. Acad. Sci. U.S.A.108(25), 10050–10055 (2011).
[CrossRef] [PubMed]

Wang, C. X.

Q. Zhang, X. Y. Shan, X. Feng, C. X. Wang, Q. Q. Wang, J. F. Jia, and Q. K. Xue, “Modulating resonance modes and Q value of a CdS nanowire cavity by single Ag nanoparticles,” Nano Lett.11(10), 4270–4274 (2011).
[CrossRef] [PubMed]

Wang, K.

Z. Li, J. Wei, P. Li, L. Zhang, E. Shi, C. Ji, J. Liu, D. Zhuang, Z. Liu, J. Zhou, Y. Shang, Y. Li, K. Wang, H. Zhu, D. Wu, and A. Cao, “Solution-processed bulk heterojunction solar cells based on interpenetrating CdS nanowires and carbon nanotubes,” Nano Res.5(9), 595–604 (2012).
[CrossRef]

Wang, Q.

Q. Wang, G. Zhao, and G. Han, “Synthesis of single crystalline CdS nanorods by a PVP-assisted solvothermal method,” Mater. Lett.59(21), 2625–2629 (2005).
[CrossRef]

Wang, Q. Q.

Q. Zhang, X. Y. Shan, X. Feng, C. X. Wang, Q. Q. Wang, J. F. Jia, and Q. K. Xue, “Modulating resonance modes and Q value of a CdS nanowire cavity by single Ag nanoparticles,” Nano Lett.11(10), 4270–4274 (2011).
[CrossRef] [PubMed]

X. F. Yu, L. D. Chen, M. Li, M. Y. Xie, L. Zhou, Y. Li, and Q. Q. Wang, “Highly efficient fluorescence of NdF3/SiO2 core/shell nanoparticles and the applications for in vivo NIR detection,” Adv. Mater. (Deerfield Beach Fla.)20(21), 4118–4123 (2008).
[CrossRef]

Wang, S.

A. Pan, S. Wang, R. Liu, C. Li, and B. Zou, “Thermal stability and lasing of CdS nanowires coated by amorphous silica,” Small1(11), 1058–1062 (2005).
[CrossRef] [PubMed]

Wang, Z.

H. Gai, Y. Wu, L. Wu, Z. Wang, Y. Shi, M. Jing, and K. Zou, “Solvothermal synthesis of CdS nanowires using L-cysteine as sulfur source and their characterization,” Appl. Phys., A Mater. Sci. Process.91(1), 69–72 (2008).
[CrossRef]

Wang, Z. L.

Y. Liu, Q. Yang, Y. Zhang, Z. Yang, and Z. L. Wang, “Nanowire piezo-phototronic photodetector: theory and experimental design,” Adv. Mater. (Deerfield Beach Fla.)24(11), 1410–1417 (2012).
[CrossRef] [PubMed]

Y. F. Lin, J. Song, Y. Ding, S. Y. Lu, and Z. L. Wang, “Alternating the output of a CdS nanowire nanogenerator by a white-light-stimulated optoelectronic effect,” Adv. Mater. (Deerfield Beach Fla.)20(16), 3127–3130 (2008).
[CrossRef]

Wei, J.

Z. Li, J. Wei, P. Li, L. Zhang, E. Shi, C. Ji, J. Liu, D. Zhuang, Z. Liu, J. Zhou, Y. Shang, Y. Li, K. Wang, H. Zhu, D. Wu, and A. Cao, “Solution-processed bulk heterojunction solar cells based on interpenetrating CdS nanowires and carbon nanotubes,” Nano Res.5(9), 595–604 (2012).
[CrossRef]

Wu, D.

Z. Li, J. Wei, P. Li, L. Zhang, E. Shi, C. Ji, J. Liu, D. Zhuang, Z. Liu, J. Zhou, Y. Shang, Y. Li, K. Wang, H. Zhu, D. Wu, and A. Cao, “Solution-processed bulk heterojunction solar cells based on interpenetrating CdS nanowires and carbon nanotubes,” Nano Res.5(9), 595–604 (2012).
[CrossRef]

Wu, F.

F. Wu, J. Z. Zhang, R. Kho, and R. K. Mehra, “Radiative and nonradiative lifetimes of band edge states and deep trap states of CdS nanoparticles determined by time-correlated single photon counting,” Chem. Phys. Lett.330(3-4), 237–242 (2000).
[CrossRef]

Wu, L.

H. Gai, Y. Wu, L. Wu, Z. Wang, Y. Shi, M. Jing, and K. Zou, “Solvothermal synthesis of CdS nanowires using L-cysteine as sulfur source and their characterization,” Appl. Phys., A Mater. Sci. Process.91(1), 69–72 (2008).
[CrossRef]

Wu, Y.

H. Gai, Y. Wu, L. Wu, Z. Wang, Y. Shi, M. Jing, and K. Zou, “Solvothermal synthesis of CdS nanowires using L-cysteine as sulfur source and their characterization,” Appl. Phys., A Mater. Sci. Process.91(1), 69–72 (2008).
[CrossRef]

Xie, M. Y.

X. F. Yu, L. D. Chen, M. Li, M. Y. Xie, L. Zhou, Y. Li, and Q. Q. Wang, “Highly efficient fluorescence of NdF3/SiO2 core/shell nanoparticles and the applications for in vivo NIR detection,” Adv. Mater. (Deerfield Beach Fla.)20(21), 4118–4123 (2008).
[CrossRef]

Xiong, Q.

M. I. Utama, J. Zhang, R. Chen, X. Xu, D. Li, H. Sun, and Q. Xiong, “Synthesis and optical properties of II-VI 1D nanostructures,” Nanoscale4(5), 1422–1435 (2012).
[CrossRef] [PubMed]

D. Li, J. Zhang, Q. Zhang, and Q. Xiong, “Electric-field-dependent photoconductivity in CdS nanowires and nanobelts: exciton ionization, franz-keldysh, and stark effects,” Nano Lett.12(6), 2993–2999 (2012).
[CrossRef] [PubMed]

Xu, D.

D. Xu, Y. Xu, D. Chen, G. Guo, L. Gui, and Y. Tang, “Preparation and characterization of CdS nanowire arrays by DC electrodeposit in porous anodic aluminum oxide templates,” Chem. Phys. Lett.325(4), 340–344 (2000).
[CrossRef]

Xu, M. H.

Z. X. Yang, W. Zhong, P. Zhang, M. H. Xu, Y. Deng, C. T. Au, and Y. W. Du, “Controllable synthesis, characterization and photoluminescence properties of morphology-tunable CdS nanomaterials generated in thermal evaporation processes,” Appl. Surf. Sci.258(19), 7343–7347 (2012).
[CrossRef]

Xu, W. J.

R. M. Ma, L. Dai, H. B. Huo, W. J. Xu, and G. G. Qin, “High-performance logic circuits constructed on single CdS nanowires,” Nano Lett.7(11), 3300–3304 (2007).
[CrossRef] [PubMed]

Xu, X.

M. I. Utama, J. Zhang, R. Chen, X. Xu, D. Li, H. Sun, and Q. Xiong, “Synthesis and optical properties of II-VI 1D nanostructures,” Nanoscale4(5), 1422–1435 (2012).
[CrossRef] [PubMed]

Xu, Y.

D. Xu, Y. Xu, D. Chen, G. Guo, L. Gui, and Y. Tang, “Preparation and characterization of CdS nanowire arrays by DC electrodeposit in porous anodic aluminum oxide templates,” Chem. Phys. Lett.325(4), 340–344 (2000).
[CrossRef]

Xue, Q. K.

Q. Zhang, X. Y. Shan, X. Feng, C. X. Wang, Q. Q. Wang, J. F. Jia, and Q. K. Xue, “Modulating resonance modes and Q value of a CdS nanowire cavity by single Ag nanoparticles,” Nano Lett.11(10), 4270–4274 (2011).
[CrossRef] [PubMed]

Yang, Q.

Y. Liu, Q. Yang, Y. Zhang, Z. Yang, and Z. L. Wang, “Nanowire piezo-phototronic photodetector: theory and experimental design,” Adv. Mater. (Deerfield Beach Fla.)24(11), 1410–1417 (2012).
[CrossRef] [PubMed]

Yang, S.

L. Yu, X. F. Yu, Y. Qiu, Y. Chen, and S. Yang, “Nonlinear photoluminescence of ZnO/ZnS nanotetrapods,” Chem. Phys. Lett.465(4-6), 272–274 (2008).
[CrossRef]

Yang, X. G.

K. B. Tang, Y. T. Qian, J. H. Zeng, and X. G. Yang, “Solvothermal route to semiconductor nanowires,” Adv. Mater. (Deerfield Beach Fla.)15(5), 448–450 (2003).
[CrossRef]

Yang, Z.

Y. Liu, Q. Yang, Y. Zhang, Z. Yang, and Z. L. Wang, “Nanowire piezo-phototronic photodetector: theory and experimental design,” Adv. Mater. (Deerfield Beach Fla.)24(11), 1410–1417 (2012).
[CrossRef] [PubMed]

Yang, Z. X.

Z. X. Yang, W. Zhong, P. Zhang, M. H. Xu, Y. Deng, C. T. Au, and Y. W. Du, “Controllable synthesis, characterization and photoluminescence properties of morphology-tunable CdS nanomaterials generated in thermal evaporation processes,” Appl. Surf. Sci.258(19), 7343–7347 (2012).
[CrossRef]

Ying, J. Y.

S. T. Selvan, T. T. Tan, and J. Y. Ying, “Robust, non-cytotoxic, silica-coated CdSe quantum dots with efficient photoluminescence,” Adv. Mater. (Deerfield Beach Fla.)17(13), 1620–1625 (2005).
[CrossRef]

Yu, L.

L. Yu, X. F. Yu, Y. Qiu, Y. Chen, and S. Yang, “Nonlinear photoluminescence of ZnO/ZnS nanotetrapods,” Chem. Phys. Lett.465(4-6), 272–274 (2008).
[CrossRef]

Yu, X. F.

L. Yu, X. F. Yu, Y. Qiu, Y. Chen, and S. Yang, “Nonlinear photoluminescence of ZnO/ZnS nanotetrapods,” Chem. Phys. Lett.465(4-6), 272–274 (2008).
[CrossRef]

X. F. Yu, L. D. Chen, M. Li, M. Y. Xie, L. Zhou, Y. Li, and Q. Q. Wang, “Highly efficient fluorescence of NdF3/SiO2 core/shell nanoparticles and the applications for in vivo NIR detection,” Adv. Mater. (Deerfield Beach Fla.)20(21), 4118–4123 (2008).
[CrossRef]

Zeng, J. H.

K. B. Tang, Y. T. Qian, J. H. Zeng, and X. G. Yang, “Solvothermal route to semiconductor nanowires,” Adv. Mater. (Deerfield Beach Fla.)15(5), 448–450 (2003).
[CrossRef]

Zentgraf, T.

R. F. Oulton, V. J. Sorger, T. Zentgraf, R. M. Ma, C. Gladden, L. Dai, G. Bartal, and X. Zhang, “Plasmon lasers at deep subwavelength scale,” Nature461(7264), 629–632 (2009).
[CrossRef] [PubMed]

Zhang, J.

M. I. Utama, J. Zhang, R. Chen, X. Xu, D. Li, H. Sun, and Q. Xiong, “Synthesis and optical properties of II-VI 1D nanostructures,” Nanoscale4(5), 1422–1435 (2012).
[CrossRef] [PubMed]

D. Li, J. Zhang, Q. Zhang, and Q. Xiong, “Electric-field-dependent photoconductivity in CdS nanowires and nanobelts: exciton ionization, franz-keldysh, and stark effects,” Nano Lett.12(6), 2993–2999 (2012).
[CrossRef] [PubMed]

Zhang, J. Z.

F. Wu, J. Z. Zhang, R. Kho, and R. K. Mehra, “Radiative and nonradiative lifetimes of band edge states and deep trap states of CdS nanoparticles determined by time-correlated single photon counting,” Chem. Phys. Lett.330(3-4), 237–242 (2000).
[CrossRef]

Zhang, L.

Z. Li, J. Wei, P. Li, L. Zhang, E. Shi, C. Ji, J. Liu, D. Zhuang, Z. Liu, J. Zhou, Y. Shang, Y. Li, K. Wang, H. Zhu, D. Wu, and A. Cao, “Solution-processed bulk heterojunction solar cells based on interpenetrating CdS nanowires and carbon nanotubes,” Nano Res.5(9), 595–604 (2012).
[CrossRef]

Zhang, P.

Z. X. Yang, W. Zhong, P. Zhang, M. H. Xu, Y. Deng, C. T. Au, and Y. W. Du, “Controllable synthesis, characterization and photoluminescence properties of morphology-tunable CdS nanomaterials generated in thermal evaporation processes,” Appl. Surf. Sci.258(19), 7343–7347 (2012).
[CrossRef]

Zhang, Q.

D. Li, J. Zhang, Q. Zhang, and Q. Xiong, “Electric-field-dependent photoconductivity in CdS nanowires and nanobelts: exciton ionization, franz-keldysh, and stark effects,” Nano Lett.12(6), 2993–2999 (2012).
[CrossRef] [PubMed]

Q. Zhang, X. Y. Shan, X. Feng, C. X. Wang, Q. Q. Wang, J. F. Jia, and Q. K. Xue, “Modulating resonance modes and Q value of a CdS nanowire cavity by single Ag nanoparticles,” Nano Lett.11(10), 4270–4274 (2011).
[CrossRef] [PubMed]

Zhang, W. J.

J. S. Jie, W. J. Zhang, Y. Jiang, X. M. Meng, Y. Q. Li, and S. T. Lee, “Photoconductive characteristics of single-crystal CdS nanoribbons,” Nano Lett.6(9), 1887–1892 (2006).
[CrossRef] [PubMed]

Zhang, X.

R. F. Oulton, V. J. Sorger, T. Zentgraf, R. M. Ma, C. Gladden, L. Dai, G. Bartal, and X. Zhang, “Plasmon lasers at deep subwavelength scale,” Nature461(7264), 629–632 (2009).
[CrossRef] [PubMed]

Zhang, Y.

Y. Liu, Q. Yang, Y. Zhang, Z. Yang, and Z. L. Wang, “Nanowire piezo-phototronic photodetector: theory and experimental design,” Adv. Mater. (Deerfield Beach Fla.)24(11), 1410–1417 (2012).
[CrossRef] [PubMed]

Zhao, G.

Q. Wang, G. Zhao, and G. Han, “Synthesis of single crystalline CdS nanorods by a PVP-assisted solvothermal method,” Mater. Lett.59(21), 2625–2629 (2005).
[CrossRef]

Zhong, W.

Z. X. Yang, W. Zhong, P. Zhang, M. H. Xu, Y. Deng, C. T. Au, and Y. W. Du, “Controllable synthesis, characterization and photoluminescence properties of morphology-tunable CdS nanomaterials generated in thermal evaporation processes,” Appl. Surf. Sci.258(19), 7343–7347 (2012).
[CrossRef]

Zhou, J.

Z. Li, J. Wei, P. Li, L. Zhang, E. Shi, C. Ji, J. Liu, D. Zhuang, Z. Liu, J. Zhou, Y. Shang, Y. Li, K. Wang, H. Zhu, D. Wu, and A. Cao, “Solution-processed bulk heterojunction solar cells based on interpenetrating CdS nanowires and carbon nanotubes,” Nano Res.5(9), 595–604 (2012).
[CrossRef]

Zhou, L.

X. F. Yu, L. D. Chen, M. Li, M. Y. Xie, L. Zhou, Y. Li, and Q. Q. Wang, “Highly efficient fluorescence of NdF3/SiO2 core/shell nanoparticles and the applications for in vivo NIR detection,” Adv. Mater. (Deerfield Beach Fla.)20(21), 4118–4123 (2008).
[CrossRef]

Zhu, H.

Z. Li, J. Wei, P. Li, L. Zhang, E. Shi, C. Ji, J. Liu, D. Zhuang, Z. Liu, J. Zhou, Y. Shang, Y. Li, K. Wang, H. Zhu, D. Wu, and A. Cao, “Solution-processed bulk heterojunction solar cells based on interpenetrating CdS nanowires and carbon nanotubes,” Nano Res.5(9), 595–604 (2012).
[CrossRef]

Zhuang, D.

Z. Li, J. Wei, P. Li, L. Zhang, E. Shi, C. Ji, J. Liu, D. Zhuang, Z. Liu, J. Zhou, Y. Shang, Y. Li, K. Wang, H. Zhu, D. Wu, and A. Cao, “Solution-processed bulk heterojunction solar cells based on interpenetrating CdS nanowires and carbon nanotubes,” Nano Res.5(9), 595–604 (2012).
[CrossRef]

Zou, B.

A. Pan, S. Wang, R. Liu, C. Li, and B. Zou, “Thermal stability and lasing of CdS nanowires coated by amorphous silica,” Small1(11), 1058–1062 (2005).
[CrossRef] [PubMed]

A. Pan, X. Lin, R. Liu, C. Li, X. He, H. Gao, and B. Zou, “Surface crystallization effects on the optical and electric properties of CdS nanorods,” Nanotechnology16(10), 2402–2406 (2005).
[CrossRef] [PubMed]

Zou, K.

H. Gai, Y. Wu, L. Wu, Z. Wang, Y. Shi, M. Jing, and K. Zou, “Solvothermal synthesis of CdS nanowires using L-cysteine as sulfur source and their characterization,” Appl. Phys., A Mater. Sci. Process.91(1), 69–72 (2008).
[CrossRef]

ACS Nano

J. Puthussery, A. Lan, T. H. Kosel, and M. Kuno, “Band-filling of solution-synthesized CdS nanowires,” ACS Nano2(2), 357–367 (2008).
[CrossRef] [PubMed]

Adv. Mater. (Deerfield Beach Fla.)

Y. Liu, Q. Yang, Y. Zhang, Z. Yang, and Z. L. Wang, “Nanowire piezo-phototronic photodetector: theory and experimental design,” Adv. Mater. (Deerfield Beach Fla.)24(11), 1410–1417 (2012).
[CrossRef] [PubMed]

Y. F. Lin, J. Song, Y. Ding, S. Y. Lu, and Z. L. Wang, “Alternating the output of a CdS nanowire nanogenerator by a white-light-stimulated optoelectronic effect,” Adv. Mater. (Deerfield Beach Fla.)20(16), 3127–3130 (2008).
[CrossRef]

K. B. Tang, Y. T. Qian, J. H. Zeng, and X. G. Yang, “Solvothermal route to semiconductor nanowires,” Adv. Mater. (Deerfield Beach Fla.)15(5), 448–450 (2003).
[CrossRef]

X. F. Yu, L. D. Chen, M. Li, M. Y. Xie, L. Zhou, Y. Li, and Q. Q. Wang, “Highly efficient fluorescence of NdF3/SiO2 core/shell nanoparticles and the applications for in vivo NIR detection,” Adv. Mater. (Deerfield Beach Fla.)20(21), 4118–4123 (2008).
[CrossRef]

S. T. Selvan, T. T. Tan, and J. Y. Ying, “Robust, non-cytotoxic, silica-coated CdSe quantum dots with efficient photoluminescence,” Adv. Mater. (Deerfield Beach Fla.)17(13), 1620–1625 (2005).
[CrossRef]

Appl. Phys., A Mater. Sci. Process.

H. Gai, Y. Wu, L. Wu, Z. Wang, Y. Shi, M. Jing, and K. Zou, “Solvothermal synthesis of CdS nanowires using L-cysteine as sulfur source and their characterization,” Appl. Phys., A Mater. Sci. Process.91(1), 69–72 (2008).
[CrossRef]

Appl. Surf. Sci.

Z. X. Yang, W. Zhong, P. Zhang, M. H. Xu, Y. Deng, C. T. Au, and Y. W. Du, “Controllable synthesis, characterization and photoluminescence properties of morphology-tunable CdS nanomaterials generated in thermal evaporation processes,” Appl. Surf. Sci.258(19), 7343–7347 (2012).
[CrossRef]

K. Pal, U. N. Maiti, T. P. Majumder, and S. C. Debnath, “A facile strategy for the fabrication of uniform CdS nanowires with high yield and its controlled morphological growth with the assistance of PEG in hydrothermal route,” Appl. Surf. Sci.258(1), 163–168 (2011).
[CrossRef]

Chem. Phys. Lett.

D. Xu, Y. Xu, D. Chen, G. Guo, L. Gui, and Y. Tang, “Preparation and characterization of CdS nanowire arrays by DC electrodeposit in porous anodic aluminum oxide templates,” Chem. Phys. Lett.325(4), 340–344 (2000).
[CrossRef]

F. Wu, J. Z. Zhang, R. Kho, and R. K. Mehra, “Radiative and nonradiative lifetimes of band edge states and deep trap states of CdS nanoparticles determined by time-correlated single photon counting,” Chem. Phys. Lett.330(3-4), 237–242 (2000).
[CrossRef]

L. Yu, X. F. Yu, Y. Qiu, Y. Chen, and S. Yang, “Nonlinear photoluminescence of ZnO/ZnS nanotetrapods,” Chem. Phys. Lett.465(4-6), 272–274 (2008).
[CrossRef]

J. Mater. Chem.

H. Lee, K. Heo, J. Park, Y. Park, S. Noh, K. S. Kim, C. Lee, B. H. Hong, J. Jian, and S. Hong, “Graphene–nanowire hybrid structures for high-performance photoconductive devices,” J. Mater. Chem.22(17), 8372–8376 (2012).
[CrossRef]

Langmuir

M. A. Correa-Duarte, M. Giersig, N. A. Kotov, and L. M. Liz-Marzán, “Control of packing order of self-assembled monolayers of magnetite nanoparticles with and without SiO2 coating by microwave irradiation,” Langmuir14(22), 6430–6435 (1998).
[CrossRef]

Mater. Lett.

Q. Wang, G. Zhao, and G. Han, “Synthesis of single crystalline CdS nanorods by a PVP-assisted solvothermal method,” Mater. Lett.59(21), 2625–2629 (2005).
[CrossRef]

Nano Lett.

R. M. Ma, L. Dai, H. B. Huo, W. J. Xu, and G. G. Qin, “High-performance logic circuits constructed on single CdS nanowires,” Nano Lett.7(11), 3300–3304 (2007).
[CrossRef] [PubMed]

T. Dufaux, M. Burghard, and K. Kern, “Efficient charge extraction out of nanoscale Schottky contacts to CdS nanowires,” Nano Lett.12(6), 2705–2709 (2012).
[CrossRef] [PubMed]

R. Agarwal, C. J. Barrelet, and C. M. Lieber, “Lasing in single cadmium sulfide nanowire optical cavities,” Nano Lett.5(5), 917–920 (2005).
[CrossRef] [PubMed]

J. S. Jie, W. J. Zhang, Y. Jiang, X. M. Meng, Y. Q. Li, and S. T. Lee, “Photoconductive characteristics of single-crystal CdS nanoribbons,” Nano Lett.6(9), 1887–1892 (2006).
[CrossRef] [PubMed]

C. J. Barrelet, A. B. Greytak, and C. M. Lieber, “Nanowire photonic circuit elements,” Nano Lett.4(10), 1981–1985 (2004).
[CrossRef]

D. Li, J. Zhang, Q. Zhang, and Q. Xiong, “Electric-field-dependent photoconductivity in CdS nanowires and nanobelts: exciton ionization, franz-keldysh, and stark effects,” Nano Lett.12(6), 2993–2999 (2012).
[CrossRef] [PubMed]

Q. Zhang, X. Y. Shan, X. Feng, C. X. Wang, Q. Q. Wang, J. F. Jia, and Q. K. Xue, “Modulating resonance modes and Q value of a CdS nanowire cavity by single Ag nanoparticles,” Nano Lett.11(10), 4270–4274 (2011).
[CrossRef] [PubMed]

Nano Res.

Z. Li, J. Wei, P. Li, L. Zhang, E. Shi, C. Ji, J. Liu, D. Zhuang, Z. Liu, J. Zhou, Y. Shang, Y. Li, K. Wang, H. Zhu, D. Wu, and A. Cao, “Solution-processed bulk heterojunction solar cells based on interpenetrating CdS nanowires and carbon nanotubes,” Nano Res.5(9), 595–604 (2012).
[CrossRef]

Nanoscale

M. I. Utama, J. Zhang, R. Chen, X. Xu, D. Li, H. Sun, and Q. Xiong, “Synthesis and optical properties of II-VI 1D nanostructures,” Nanoscale4(5), 1422–1435 (2012).
[CrossRef] [PubMed]

Nanotechnology

S. Geburt, A. Thielmann, R. Röder, C. Borschel, A. McDonnell, M. Kozlik, J. Kühnel, K. A. Sunter, F. Capasso, and C. Ronning, “Low threshold room-temperature lasing of CdS nanowires,” Nanotechnology23(36), 365204 (2012).
[CrossRef] [PubMed]

A. Pan, X. Lin, R. Liu, C. Li, X. He, H. Gao, and B. Zou, “Surface crystallization effects on the optical and electric properties of CdS nanorods,” Nanotechnology16(10), 2402–2406 (2005).
[CrossRef] [PubMed]

P. Liu, V. P. Singh, C. A. Jarro, and S. Rajaputra, “Cadmium sulfide nanowires for the window semiconductor layer in thin film CdS-CdTe solar cells,” Nanotechnology22(14), 145304 (2011).
[CrossRef] [PubMed]

Nat. Mater.

O. Hayden, R. Agarwal, and C. M. Lieber, “Nanoscale avalanche photodiodes for highly sensitive and spatially resolved photon detection,” Nat. Mater.5(5), 352–356 (2006).
[CrossRef] [PubMed]

C. H. Cho, C. O. Aspetti, M. E. Turk, J. M. Kikkawa, S. W. Nam, and R. Agarwal, “Tailoring hot-exciton emission and lifetimes in semiconducting nanowires via whispering-gallery nanocavity plasmons,” Nat. Mater.10(9), 669–675 (2011).
[CrossRef] [PubMed]

Nat. Nanotechnol.

B. Piccione, C. H. Cho, L. K. van Vugt, and R. Agarwal, “All-optical active switching in individual semiconductor nanowires,” Nat. Nanotechnol.7(10), 640–645 (2012).
[CrossRef] [PubMed]

Nature

R. F. Oulton, V. J. Sorger, T. Zentgraf, R. M. Ma, C. Gladden, L. Dai, G. Bartal, and X. Zhang, “Plasmon lasers at deep subwavelength scale,” Nature461(7264), 629–632 (2009).
[CrossRef] [PubMed]

X. Duan, Y. Huang, R. Agarwal, and C. M. Lieber, “Single-nanowire electrically driven lasers,” Nature421(6920), 241–245 (2003).
[CrossRef] [PubMed]

Proc. Natl. Acad. Sci. U.S.A.

L. K. van Vugt, B. Piccione, C. H. Cho, P. Nukala, and R. Agarwal, “One-dimensional polaritons with size-tunable and enhanced coupling strengths in semiconductor nanowires,” Proc. Natl. Acad. Sci. U.S.A.108(25), 10050–10055 (2011).
[CrossRef] [PubMed]

Small

C. C. Kang, C. W. Lai, H. C. Peng, J. J. Shyue, and P. T. Chou, “Surfactant- and temperature-controlled CdS nanowire formation,” Small3(11), 1882–1885 (2007).
[CrossRef] [PubMed]

A. Pan, S. Wang, R. Liu, C. Li, and B. Zou, “Thermal stability and lasing of CdS nanowires coated by amorphous silica,” Small1(11), 1058–1062 (2005).
[CrossRef] [PubMed]

Cited By

OSA participates in CrossRef's Cited-By Linking service. Citing articles from OSA journals and other participating publishers are listed here.

Alert me when this article is cited.


Figures (5)

Fig. 1
Fig. 1

(a) Low and high magnitude TEM images of CdS NWs. (b-d) CdS/SiO2 core/shell NWs with shell thickness of around (b) 11 nm, (c) 25 nm and (d) 70 nm.

Fig. 2
Fig. 2

XRD patterns of (a) CdS NWs, (b) uncoated CdS NWs annealed at 500 °C, (c) CdS/SiO2 core/shell NWs, and (d) CdS/SiO2 core/shell NWs annealed at 500 °C.

Fig. 3
Fig. 3

Normalized absorption spectra of CdS NWs, CdS/SiO2 NWs, and annealed CdS/SiO2 core/shell NWs.

Fig. 4
Fig. 4

(a) PL spectra of CdS NWs, CdS/SiO2 NWs and CdS/SiO2 NWs annealed at 500 °C. (b) Time-resolved PL of CdS NWs, CdS/SiO2 NWs and annealed CdS/SiO2 NWs at ~505 nm.

Fig. 5
Fig. 5

Excitation power dependence of PL intensity for CdS NWs, CdS/SiO2 core/shell NWs and annealed CdS/SiO2 core/shell NWs at (a) 505 nm and (b) 700 nm with excitation wavelength of 400 nm.

Metrics