Abstract

InGaN-based light emitting diodes (LEDs) with a top nano-roughened p-GaN surface are fabricated using self-assembled CsCl nano-islands as etch masks. Following formation of hemispherical GaN nano-island arrays, electroluminescence (EL) spectra of roughened LEDs display an obvious redshift due to partial compression release in quantum wells through Inductively Coupled Plasma (ICP) etching. At a 350-mA current, the enhancement of light output power of LEDs subjected to ICP treatment with durations of 50, 150 and 250 sec compared with conventional LED have been determined to be 9.2, 70.6, and 42.3%, respectively. Additionally, the extraction enhancement factor can be further improved by increasing the size of CsCl nano-island. The economic and rapid method puts forward great potential for high performance lighting devices.

© 2011 Optical Society of America

1. Introduction

III-nitride wide bandgap light-emitting diodes (LEDs) have recently attracted considerable interest due to their various applications, such as traffic signals, back lighting in liquid crystal display, and white-light LED lighting. However, the majority of applications are currently hindered by the low extraction efficiency and Lambertian-like radiation profile caused by the large difference in the refractive index between LED die and external medium [1,2]. In this case, the critical angle for the light generated in the InGaN/GaN multi-quantum well (MQW) layers to escape is approximately 23°, and only a small fraction of light can be extracted from active region. Most photons are trapped inside the LED device by total internal reflection (TIR) and converted to heat, which limits the external quantum efficiency of conventional LEDs to only a few percent [1].

To solve this problem, an intensive study has been made, in order to improve the light output power by increasing the light scattering at the GaN/air interface by using a surface-roughening technique. Typically, surface texturing of p-GaN layer is performed by using maskless wet etching [3,4], electron-beam and nanoimprint lithography [57] as well as a self-assembled cluster of metal drops [8,9]. However, the roughness obtained using wet etching is not uniform, and thus, leads to a variation in the improvement of light extraction efficiency of the LEDs across the sample. There are still problems in applying electron-beam and nanoimprint lithography to commercial products because the nano-fabrication methods are quite expensive and time consuming. Additionally, the self-assembled metal cluster is formed at higher temperature of 800-900 °C, which may impair InGaN/GaN quantum well and reduce the internal quantum efficiency of LEDs. Therefore, developing a novel cost-effective and reproducible approach for surface texturization of LED chips with large-scale area is urgent.

Most recently, several approaches using self-assembled polystyrene (PS) or/and SiO2 nano-spheres have been employed to improve light extraction efficiency of nitride LEDs [1012]. In this letter, we report a new method to roughen p-GaN surface using self-assembled CsCl nano-islands as an etch mask and generation of nano-patterns on the p-GaN surface, resulting in substantial performance improvement of InGaN-based LED. The method is economic, controllable and rapid, and may be extensively applied in the roughened LEDs field in the future. In addition, the fabrication process and optical and electrical properties of the roughened LED will be discussed in detail.

2. Fabrication

The LED samples were grown on c-plane sapphire substrates by means of a Veeco metal-organic chemical vapor deposition (MOCVD) system at a growth pressure of 200 mbar. The LED structures consisted of a 30 nm-thick GaN low-temperature buffer layer, a 1 μm-thick unintentionally doped GaN layer, a 2 μm-thick n-type GaN layer, a 40 nm-thick n-Al0.15Ga0.85N blocking layer, a multiple quantum well (MQW) active layer, a 40 nm-thick p-Al0.15Ga0.85N electron blocking layer, and finally 0.4 μm-thick p-type GaN layer. The MQW active layer consisted of eight periods of 3/12 nm-thick In0.2Ga0.8N/GaN quantum well layers and barrier layers. The LED wafer was thermally treated at 720 °C for 20 min to activate the p-type GaN:Mg layer. A schematic of the roughening p-GaN process was shown in Fig. 1 . First, a CsCl thin layer with a thickness of 80-350 nm was deposited on the p-GaN surface at room temperature by thermal evaporation in vacuum 0.01 Pa using a homemade vacuum equipment. Then, on exposure to water vapor, nanosize hemispherical islands were formed, driven by the size-dependent solubility of CsCl. The average diameter and coverage ratio of CsCl nano-islands can be controlled by varying the CsCl film thickness, relative humidity and developing time. Here, CsCl nano-islands with the size of 150-650 nm were obtained at relative humidity of 40-50% within 20-50 min, following a coverage ratio of 30%. Subsequently, the samples were transported to an ICP chamber and etched with 450 W power, 75 bias power, and 4 mTorr chamber pressure and then dipped into deionized water for 5 min to remove the remaining CsCl islands. Thus, the nanostructures were transferred by ICP dry etching and separate island-shaped p-GaN surface structure was formed, as illustrated in Fig. 1.

 

Fig. 1 Schematic illustration for texturization of the GaN surface using the CsCl nano-islands as an etch mask.

Download Full Size | PPT Slide | PDF

Afterwards, the conventional LED and LEDs with nano-roughened surface were fabricated using the standard process with a mesa of 1 × 1 mm2. An indium tin oxide (ITO) layer was deposited on the p-GaN surface as a transparent contact layer (TCL). Cr-Pt-Au (70/30/145 nm) metal layers were deposited on the p-type GaN and n-type GaN surfaces as the contact electrodes. Surface morphology was inspected by using the scanning electronic microscope (SEM, a Hitachi S-4800 apparatus) and atomic force microscope (AFM, a Nanoscope III apparatus operated in the tapping mode) techniques. The light output power, EL spectra, and current-voltage (I-V) curves were studied with an Everfin-PMS50 optical spectrum analyzer.

3. Results and discussion

Figure 2 shows AFM images illustrating the change of the surface morphology of the p-GaN layer before and after the ICP dry etching. As shown in Fig. 2(a), the uniformly distributed hemispherical CsCl islands with an average size of around 450 nm may be observed on the p-GaN surface. The self-assembled mask height and density are approximately 250 nm and 3.5 × 108 cm−2, respectively. The CsCl island size and density can be easily controlled by tuning processing conditions, such as CsCl film thickness, relative humidity and ripening time. Figure 2(b)2(d) show the topography of nano-roughened surface after ICP etching with time durations of 50, 150 and 250 sec, corresponding to the root mean square (RMS) roughness of 10.8, 22.3 and 26.8 nm, respectively. With the increase of etching time, the diameter of GaN nano-island arrays transferred from CsCl islands is also enlarged due to lateral etching. The provided AFM images confirm that the p-GaN surface is effectively roughened using CsCl islands as the mask. However, when the etching time is increased up to 250 sec responding the GaN etching depth of 150 nm, CsCl islands are almost decomposed, and lots of acicular structures appear on the surface of GaN. Furthermore, the diminished surface roughness of etched p-GaN compared to that of CsCl mask covered also indicates that CsCl has more brittle resistance to ICP etching with respect to p-GaN.

 

Fig. 2 AFM images of the top surface morphology of LED. (a) CsCl islands on p-GaN surface with average size of 450 nm. Nano-roughened p-GaN surface with ICP etching durations of (b) 50, (c) 150 and (d) 250 sec.

Download Full Size | PPT Slide | PDF

The current-voltage (I-V) curves of conventional and roughened LEDs are shown in Fig. 3(a) . The forward voltages of conventional LED and those etched with 50, 150 and 250 sec at the 20 mA operation current are 5.06, 6.42, 4.67 and 4.66 V, respectively. Usually, nano-roughening facilitates p-type contact, resulting in an ohmic contact by the increase in the contact area of the nano-roughened surface [2]. However, it is also noted that the ICP etching of 50 sec results in a Schottky contact with a high specific resistance between the roughened p-GaN and TCL layers. A similar anomalous phenomenon is also observed for the 25 sec-etched sample. The phenomenon indicates that the ICP damage of p-GaN surface dominates the electrical properties of 50 sec-etched sample and increased contact area of 50 sec-etched sample is inadequate to improve the Ohmic contact. The anomalous behavior is also observed in C. C. Yang’s results [13] and further investigation is needed to clarify the reason. Figure 3(b) reveals the enhancement of the reverse leakage current together with the increase in the ICP etching time. Except for the LED with 250 sec etching, the leakage currents of LEDs with 50 and 150 sec ICP etching are acceptable, corresponding to 520 and 940 nA, respectively, at a reverse bias voltage of −10 V. The great leakage current observed for the 250 sec-etched LED should be attributed to the ICP etching-induced damages of p-GaN, as shown in the inset of Fig. 3(b).

 

Fig. 3 (a) I-V forward characteristics and (b) leakage current as a function of reverse bias of conventional and ICP-roughened LEDs. The inset shows a SEM cross-section micrograph of p-GaN etched for 250 sec.

Download Full Size | PPT Slide | PDF

Figure 4(a) shows the light output power versus injection current (L-I) characteristics of the conventional and roughened LEDs. It is found that the output power of all LEDs increases as we increase the injection current. Under 350-mA current injection, the light output intensity of ICP-etched LEDs for 50, 150 and 250 sec is equal to 9.2%, 70.6% and 42.3%, respectively, in magnitude as compared with that of conventional LED with a flat surface. The enhancement can be attributed to the reduction of the photon extraction path length, which is made possible by nano-roughened LED surface according to Snell’s law [14]. The shape of the rough surface is related to the light extraction efficiency, and hemispherical islands formed by ICP etching of 150 sec exhibit the largest enhancement in the light output power, with the appropriate oblique etching facet. The inset of Fig. 4(a) presents an optical microscope photograph of conventional and 150 sec-etched LEDs at an injection current of 1 mA. The images show that the EL emissions from the nano-roughened LED are brighter and more uniform than those of the conventional LED. Additionally, for the LED etched for 50 sec, the light output power firstly decreases at a higher operating current caused by greater thermal heat generated at the non-ohmic contact layer.

 

Fig. 4 (a) Light output powers and (b) peak wavelengths and FWHMs of EL peaks for the LEDs without and with ICP etching treatment as a function of the injection current. The inset in (a) shows photos of conventional and roughened LEDs with 150 sec-etched at an injection current of 1 mA.

Download Full Size | PPT Slide | PDF

Figure 4(b) depicts the dependence of the EL peak wavelength on the current density for the above-discussed LEDs. As illustrated, all samples first exhibit a slight blue-shift trend in the peak emission wavelength and then a red-shift as the injection current increases. The blue-shift behavior is due to the band-filling effect and screening effect in a piezoelectric field quantum well [15]. On the other hand, the red-shift can be attributed to the excess heat generated from the power dissipation that causes the obvious thermal effect and starts to influence the recombination process. Ultimately, LED with 50 sec-etched shows the largest peak shift of 6.3 nm due to poor ohmic contact when the injection current is raised from 10 to 500 mA. Nevertheless, the peak shift is only 1 nm for that for 150 sec etching, attributed to the reduction of heat generation caused by photon self-absorption in MQW. At a same dc current of 20 mA, the peak wavelengths of the LEDs without and with ICP etching for 50, 150, and 250 sec were found to be 457.3, 458.0, 459.0 and 458.5 nm, respectively. Besides, the peak wavelengths of etched LEDs are obviously redshifted compared to that of conventional LED, which is due to the partial relaxation of compressive strain in the MQW layers through the formation of hemispherical islands structure by ICP etching [16]. Further more, the full width at half-maximum (FWHM) of EL peak for these LEDs is plotted as a function of the injection current. With the increase in the current, the FWHM can be seen to increase gradually, for all LEDs. Likewise, the heating reduction effect causes the smaller broadening of EL peak in the case of the 150 sec-etched LED in comparison with the other LEDs. Here, the more pronounced EL peak broadening is observed for the LED with 250 sec etching, originating in the strong leakage current due to ICP damage of p-GaN.

To investigate the influence of surface roughness on light output performance of LED, we also measured the light output radiation patterns of conventional and roughened LEDs at a driving current of 200 mA. Here, the chips were Au-wire bonded and loaded on an aluminium leaded chip carrier without epoxy encapsulation. As shown in Fig. 5 , the emission patterns from the roughened LEDs show omnidirectional enhancement in the overall integrated intensity with almost same view angles of 125-130° compared to conventional LED. Hence, the improvement in light extraction efficiency is considered as a consequence of higher photons scattering efficiency from ICP-etching roughness of p-GaN due to angular randomization or a scrambling of the photons. Especially, the LED etched for 150 sec displays much higher light intensity in the oblique directions at 50° and 120°. The radiation profile should be highly related to the inclined sidewall angle and arrangement of hemispherical nano-islands on the LED surface, similarly to the way the SiO2 microrod array effects on light propagation out from LED MQWs along the specific azimuth angles [17].

 

Fig. 5 Far-field emission patterns of the conventional and ICP-roughened LEDs at an injection current of 200 mA.

Download Full Size | PPT Slide | PDF

Finally, we further investigate the dependence of light extraction efficiency (LEE) on the size of the CsCl nano-islands under the optimum 150 sec ICP etching at an injection current of 350 mA. To be compared, the fill factor of CsCl nano-islands on the surface are constrained as 30% for different sizes islands. As shown in Fig. 6 , the enhancement factor monotonically increases with the size of nano-islands and reaches a value of 77.9% when the island size is about 650 nm. The nano-islands on the p-GaN surface behave as a layer with a gradient index profile, instead of a layer with an effective refractive index [18]. The device behavior, as the nano-islands size increases, implies a gradually changing gradient of the refractive index profile, which is critical to the enhancement of extraction efficiency. In the case, the bigger CsCl hemispherical nano-islands contribute to increase the sidewall area, and then give the photons higher probabilities to escape from the LED structure. The present results strongly suggest that nano-island surface structure controlled precisely the size and depth with CsCl islands plays an important role in improving the electrical properties and the light-extraction efficiency of LED devices. The rapid and economic method is fully comparable to the better report in the literature [10] and illustrates unique advantages and promising potential.

 

Fig. 6 Light extraction enhancements of LEDs as a function of the nano-island size under the optimum 150 sec ICP etching at an injection current of 350 mA. The inset shows the typical rough surface with island average size of 650 nm.

Download Full Size | PPT Slide | PDF

4. Conclusion

In summary, using self-assembled CsCl nano-islands as an ICP etching mask, we present a simple, low-cost and efficient method to improve extraction efficiency of InGaN/GaN LEDs. By optimizing the etching conditions, the electrical performances of roughened LEDs have not been significantly degraded by ICP etching. The hemispherical nanostructure obviously improves the probability of photons to escape from the LEDs due to the angular diffraction, resulting in an increase of nearly 70% in the light extraction efficiency of the LED at 350 mA injection current. With the increase of CsCl nano-island size, the extraction enhancement factor can be further improved, up to 77.9% for 650 nm island. Furthermore, the EL spectra of nano-roughened LEDs show a clear redshift compared with that of conventional LED due to partial release of the compressive strain in the InGaN quantum wells.

Acknowledgment

This work was supported by the National Natural Sciences Foundation of China under Grant No. 60806001 and 50972144, National High Technology Program of China under Grant No. 2009AA03A198 and the Knowledge Innovation Program of the Chinese Academy of Sciences under Grant No. ISCAS2008T03.

References and links

1. E. Fred, Schubert: Light-Emitting Diodes, (Cambridge University Press, 2003) p. 89.

2. C. Huh, K. S. Lee, E. J. Kang, and S. J. Park, “Improved light-output and electrical performance of InGaN-based, light-emitting diode by microroughening of the p-GaN surface,” J. Appl. Phys. 93(11), 9383 (2003). [CrossRef]  

3. S.-I. Na, G.-Y. Ha, D.-S. Han, S.-S. Kim, J.-Y. Kim, J.-H. Lim, D.-J. Kim, K.-I. Min, and S.-J. Park, “Selective wet etching of p-GaN for efficient GaN-based-light-emitting diodes,” IEEE Photon. Technol. Lett. 18(14), 1512–1514 (2006). [CrossRef]  

4. H.-Y. Lee, X. Y. Huang, and C.-T. Lee, “Light output enhancement of GaN-based roughened LEDs using bias-assisted photoelectrochemical etching method,” J. Electrochem. Soc. 155(10), H707 (2008). [CrossRef]  

5. T. David, T. Fujii, B. Moran, S. Nakamura, S. P. DenBaars, C. Weisbuch, and H. Benisty, “Photonic crystal laser lift-off GaN light-emitting diodes,” Appl. Phys. Lett. 88(13), 133514 (2006). [CrossRef]  

6. Y. Sun and S. R. Forrest, “Organic light emitting devices with enhanced outcoupling via microlenses fabricated by imprint lithography,” J. Appl. Phys. 100(7), 073106 (2006). [CrossRef]  

7. H. W. Huang, C. H. Lin, C. C. Yu, B. D. Lee, C. H. Chiu, C. F. Lai, H. C. Kuo, K. M. Leung, T. C. Lu, and S. C. Wang, “Improvement of light output in GaN-based power chip light-emitting diodes with a nano-rough surface by nanoimprint lithography,” Semicond. Sci. Technol. 23(4), 045022 (2008). [CrossRef]  

8. E.-J. Kang, C. Huh, S.-H. Lee, J.-J. Jung, S.-J. Lee, and S.-J. Park, “Improvement in light-output power of InGaN/GaN LED by formation of nanosize cavities on p-GaN surface,” Electrochem. Solid-State Lett. 8(12), G327 (2005). [CrossRef]  

9. C. C. Hung-Wen Huang, C. C. Kao, J. T. Chu, H. C. Kuo, S. C. Wang, and C. C. Yu, “Improvement of InGaN-GaN light-emitting diode performance with a nano-roughened p-GaN surface,” IEEE Photon. Technol. Lett. 17(5), 983–985 (2005). [CrossRef]  

10. M.-A. Tsai, P. Yu, C. H. Chiu, H. C. Kuo, T. C. Lu, and S. H. Lin, “Self-assembled two-dimensional surface structures for beam shaping of GaN-based vertical-injection light-emitting diodes,” IEEE Photon. Technol. Lett. 22(1), 12–14 (2010). [CrossRef]  

11. C.-H. Chan, C.-H. Hou, S.-Z. Tseng, T.-J. Chen, H.-T. Chien, F.-L. Hsiao, C.-C. Lee, Y.-L. Tsai, and C.-C. Chen, “Improved output power of GaN-based light-emitting diodes grown on a nanopatterned sapphire substrate,” Appl. Phys. Lett. 95(1), 011110 (2009). [CrossRef]  

12. Y.-K. Ee, P. Kumnorkaew, R. A. Arif, H. Tong, J. F. Gilchrist, and N. Tansu, “Light extraction efficiency enhancement of InGaN quantum wells light-emitting diodes with polydimethylsiloxane concave microstructures,” Opt. Express 17(16), 13747–13757 (2009). [CrossRef]   [PubMed]  

13. C. C. Yang, C. F. Lin, C. M. Lin, C. C. Chang, K. T. Chen, J. F. Chien, and C. Y. Chang, “Improving light output power of InGaN-based light emitting diodes with pattern-nanoporous p-type GaN:Mg surfaces,” Appl. Phys. Lett. 93(20), 203103 (2008). [CrossRef]  

14. S. M. Huang, Y. Yao, C. Jin, Z. Sun, and Z. J. Dong, “Enhancement of the light output of GaN-based light-emitting diodes using surface-textured indium-tin-oxide transparent ohmic contacts,” Displays 29(3), 254–259 (2008). [CrossRef]  

15. T. Koyama, T. Onuma, H. Masui, A. Chakraborty, B. A. Haskell, S. Keller, U. K. Mishra, H. S. Speck, S. Nakamura, S. P. DenBaars, T. Sota, and S. F. Chichibu, “Prospective emission efficiency and in-plane light polarization of nonpolar m-plane InxGa1-xN/GaN blue light emitting diodes fabricated on freestanding GaN substrates,” Appl. Phys. Lett. 89(9), 091906 (2006). [CrossRef]  

16. M. H. Lo, P. M. Tu, C. H. Wang, C. W. Hung, S. C. Hsu, Y. J. Cheng, H. C. Kuo, H. W. Zan, S. C. Wang, C. Y. Chang, and S. C. Huang, “High efficiency light emitting diode with anisotropically etched GaN-sapphire interface,” Appl. Phys. Lett. 95(4), 041109 (2009). [CrossRef]  

17. C.-C. Kao, Y.-K. Su, C.-L. Lin, and J.-J. Chen, “Efficiency Improvement of GaN-Based LEDs With SiO2 Microrod Array and Textured Sidewalls,” IEEE Electron Device Lett. 31(1), 35–37 (2010). [CrossRef]  

18. C. H. Chiu, P. C. Yu, C. H. Chang, C. S. Yang, M. H. Hsu, H. C. Kuo, and M. A. Tsai, “Oblique electron-beam evaporation of distinctive indium-tin-oxide nanorods for enhanced light extraction from InGaN/GaN light emitting diodes,” Opt. Express 17(23), 21250–21256 (2009). [CrossRef]   [PubMed]  

References

  • View by:
  • |
  • |
  • |

  1. E. Fred, Schubert: Light-Emitting Diodes, (Cambridge University Press, 2003) p. 89.
  2. C. Huh, K. S. Lee, E. J. Kang, and S. J. Park, “Improved light-output and electrical performance of InGaN-based, light-emitting diode by microroughening of the p-GaN surface,” J. Appl. Phys. 93(11), 9383 (2003).
    [Crossref]
  3. S.-I. Na, G.-Y. Ha, D.-S. Han, S.-S. Kim, J.-Y. Kim, J.-H. Lim, D.-J. Kim, K.-I. Min, and S.-J. Park, “Selective wet etching of p-GaN for efficient GaN-based-light-emitting diodes,” IEEE Photon. Technol. Lett. 18(14), 1512–1514 (2006).
    [Crossref]
  4. H.-Y. Lee, X. Y. Huang, and C.-T. Lee, “Light output enhancement of GaN-based roughened LEDs using bias-assisted photoelectrochemical etching method,” J. Electrochem. Soc. 155(10), H707 (2008).
    [Crossref]
  5. T. David, T. Fujii, B. Moran, S. Nakamura, S. P. DenBaars, C. Weisbuch, and H. Benisty, “Photonic crystal laser lift-off GaN light-emitting diodes,” Appl. Phys. Lett. 88(13), 133514 (2006).
    [Crossref]
  6. Y. Sun and S. R. Forrest, “Organic light emitting devices with enhanced outcoupling via microlenses fabricated by imprint lithography,” J. Appl. Phys. 100(7), 073106 (2006).
    [Crossref]
  7. H. W. Huang, C. H. Lin, C. C. Yu, B. D. Lee, C. H. Chiu, C. F. Lai, H. C. Kuo, K. M. Leung, T. C. Lu, and S. C. Wang, “Improvement of light output in GaN-based power chip light-emitting diodes with a nano-rough surface by nanoimprint lithography,” Semicond. Sci. Technol. 23(4), 045022 (2008).
    [Crossref]
  8. E.-J. Kang, C. Huh, S.-H. Lee, J.-J. Jung, S.-J. Lee, and S.-J. Park, “Improvement in light-output power of InGaN/GaN LED by formation of nanosize cavities on p-GaN surface,” Electrochem. Solid-State Lett. 8(12), G327 (2005).
    [Crossref]
  9. C. C. Hung-Wen Huang, C. C. Kao, J. T. Chu, H. C. Kuo, S. C. Wang, and C. C. Yu, “Improvement of InGaN-GaN light-emitting diode performance with a nano-roughened p-GaN surface,” IEEE Photon. Technol. Lett. 17(5), 983–985 (2005).
    [Crossref]
  10. M.-A. Tsai, P. Yu, C. H. Chiu, H. C. Kuo, T. C. Lu, and S. H. Lin, “Self-assembled two-dimensional surface structures for beam shaping of GaN-based vertical-injection light-emitting diodes,” IEEE Photon. Technol. Lett. 22(1), 12–14 (2010).
    [Crossref]
  11. C.-H. Chan, C.-H. Hou, S.-Z. Tseng, T.-J. Chen, H.-T. Chien, F.-L. Hsiao, C.-C. Lee, Y.-L. Tsai, and C.-C. Chen, “Improved output power of GaN-based light-emitting diodes grown on a nanopatterned sapphire substrate,” Appl. Phys. Lett. 95(1), 011110 (2009).
    [Crossref]
  12. Y.-K. Ee, P. Kumnorkaew, R. A. Arif, H. Tong, J. F. Gilchrist, and N. Tansu, “Light extraction efficiency enhancement of InGaN quantum wells light-emitting diodes with polydimethylsiloxane concave microstructures,” Opt. Express 17(16), 13747–13757 (2009).
    [Crossref] [PubMed]
  13. C. C. Yang, C. F. Lin, C. M. Lin, C. C. Chang, K. T. Chen, J. F. Chien, and C. Y. Chang, “Improving light output power of InGaN-based light emitting diodes with pattern-nanoporous p-type GaN:Mg surfaces,” Appl. Phys. Lett. 93(20), 203103 (2008).
    [Crossref]
  14. S. M. Huang, Y. Yao, C. Jin, Z. Sun, and Z. J. Dong, “Enhancement of the light output of GaN-based light-emitting diodes using surface-textured indium-tin-oxide transparent ohmic contacts,” Displays 29(3), 254–259 (2008).
    [Crossref]
  15. T. Koyama, T. Onuma, H. Masui, A. Chakraborty, B. A. Haskell, S. Keller, U. K. Mishra, H. S. Speck, S. Nakamura, S. P. DenBaars, T. Sota, and S. F. Chichibu, “Prospective emission efficiency and in-plane light polarization of nonpolar m-plane InxGa1-xN/GaN blue light emitting diodes fabricated on freestanding GaN substrates,” Appl. Phys. Lett. 89(9), 091906 (2006).
    [Crossref]
  16. M. H. Lo, P. M. Tu, C. H. Wang, C. W. Hung, S. C. Hsu, Y. J. Cheng, H. C. Kuo, H. W. Zan, S. C. Wang, C. Y. Chang, and S. C. Huang, “High efficiency light emitting diode with anisotropically etched GaN-sapphire interface,” Appl. Phys. Lett. 95(4), 041109 (2009).
    [Crossref]
  17. C.-C. Kao, Y.-K. Su, C.-L. Lin, and J.-J. Chen, “Efficiency Improvement of GaN-Based LEDs With SiO2 Microrod Array and Textured Sidewalls,” IEEE Electron Device Lett. 31(1), 35–37 (2010).
    [Crossref]
  18. C. H. Chiu, P. C. Yu, C. H. Chang, C. S. Yang, M. H. Hsu, H. C. Kuo, and M. A. Tsai, “Oblique electron-beam evaporation of distinctive indium-tin-oxide nanorods for enhanced light extraction from InGaN/GaN light emitting diodes,” Opt. Express 17(23), 21250–21256 (2009).
    [Crossref] [PubMed]

2010 (2)

M.-A. Tsai, P. Yu, C. H. Chiu, H. C. Kuo, T. C. Lu, and S. H. Lin, “Self-assembled two-dimensional surface structures for beam shaping of GaN-based vertical-injection light-emitting diodes,” IEEE Photon. Technol. Lett. 22(1), 12–14 (2010).
[Crossref]

C.-C. Kao, Y.-K. Su, C.-L. Lin, and J.-J. Chen, “Efficiency Improvement of GaN-Based LEDs With SiO2 Microrod Array and Textured Sidewalls,” IEEE Electron Device Lett. 31(1), 35–37 (2010).
[Crossref]

2009 (4)

C. H. Chiu, P. C. Yu, C. H. Chang, C. S. Yang, M. H. Hsu, H. C. Kuo, and M. A. Tsai, “Oblique electron-beam evaporation of distinctive indium-tin-oxide nanorods for enhanced light extraction from InGaN/GaN light emitting diodes,” Opt. Express 17(23), 21250–21256 (2009).
[Crossref] [PubMed]

M. H. Lo, P. M. Tu, C. H. Wang, C. W. Hung, S. C. Hsu, Y. J. Cheng, H. C. Kuo, H. W. Zan, S. C. Wang, C. Y. Chang, and S. C. Huang, “High efficiency light emitting diode with anisotropically etched GaN-sapphire interface,” Appl. Phys. Lett. 95(4), 041109 (2009).
[Crossref]

C.-H. Chan, C.-H. Hou, S.-Z. Tseng, T.-J. Chen, H.-T. Chien, F.-L. Hsiao, C.-C. Lee, Y.-L. Tsai, and C.-C. Chen, “Improved output power of GaN-based light-emitting diodes grown on a nanopatterned sapphire substrate,” Appl. Phys. Lett. 95(1), 011110 (2009).
[Crossref]

Y.-K. Ee, P. Kumnorkaew, R. A. Arif, H. Tong, J. F. Gilchrist, and N. Tansu, “Light extraction efficiency enhancement of InGaN quantum wells light-emitting diodes with polydimethylsiloxane concave microstructures,” Opt. Express 17(16), 13747–13757 (2009).
[Crossref] [PubMed]

2008 (4)

C. C. Yang, C. F. Lin, C. M. Lin, C. C. Chang, K. T. Chen, J. F. Chien, and C. Y. Chang, “Improving light output power of InGaN-based light emitting diodes with pattern-nanoporous p-type GaN:Mg surfaces,” Appl. Phys. Lett. 93(20), 203103 (2008).
[Crossref]

S. M. Huang, Y. Yao, C. Jin, Z. Sun, and Z. J. Dong, “Enhancement of the light output of GaN-based light-emitting diodes using surface-textured indium-tin-oxide transparent ohmic contacts,” Displays 29(3), 254–259 (2008).
[Crossref]

H.-Y. Lee, X. Y. Huang, and C.-T. Lee, “Light output enhancement of GaN-based roughened LEDs using bias-assisted photoelectrochemical etching method,” J. Electrochem. Soc. 155(10), H707 (2008).
[Crossref]

H. W. Huang, C. H. Lin, C. C. Yu, B. D. Lee, C. H. Chiu, C. F. Lai, H. C. Kuo, K. M. Leung, T. C. Lu, and S. C. Wang, “Improvement of light output in GaN-based power chip light-emitting diodes with a nano-rough surface by nanoimprint lithography,” Semicond. Sci. Technol. 23(4), 045022 (2008).
[Crossref]

2006 (4)

T. David, T. Fujii, B. Moran, S. Nakamura, S. P. DenBaars, C. Weisbuch, and H. Benisty, “Photonic crystal laser lift-off GaN light-emitting diodes,” Appl. Phys. Lett. 88(13), 133514 (2006).
[Crossref]

Y. Sun and S. R. Forrest, “Organic light emitting devices with enhanced outcoupling via microlenses fabricated by imprint lithography,” J. Appl. Phys. 100(7), 073106 (2006).
[Crossref]

S.-I. Na, G.-Y. Ha, D.-S. Han, S.-S. Kim, J.-Y. Kim, J.-H. Lim, D.-J. Kim, K.-I. Min, and S.-J. Park, “Selective wet etching of p-GaN for efficient GaN-based-light-emitting diodes,” IEEE Photon. Technol. Lett. 18(14), 1512–1514 (2006).
[Crossref]

T. Koyama, T. Onuma, H. Masui, A. Chakraborty, B. A. Haskell, S. Keller, U. K. Mishra, H. S. Speck, S. Nakamura, S. P. DenBaars, T. Sota, and S. F. Chichibu, “Prospective emission efficiency and in-plane light polarization of nonpolar m-plane InxGa1-xN/GaN blue light emitting diodes fabricated on freestanding GaN substrates,” Appl. Phys. Lett. 89(9), 091906 (2006).
[Crossref]

2005 (2)

E.-J. Kang, C. Huh, S.-H. Lee, J.-J. Jung, S.-J. Lee, and S.-J. Park, “Improvement in light-output power of InGaN/GaN LED by formation of nanosize cavities on p-GaN surface,” Electrochem. Solid-State Lett. 8(12), G327 (2005).
[Crossref]

C. C. Hung-Wen Huang, C. C. Kao, J. T. Chu, H. C. Kuo, S. C. Wang, and C. C. Yu, “Improvement of InGaN-GaN light-emitting diode performance with a nano-roughened p-GaN surface,” IEEE Photon. Technol. Lett. 17(5), 983–985 (2005).
[Crossref]

2003 (1)

C. Huh, K. S. Lee, E. J. Kang, and S. J. Park, “Improved light-output and electrical performance of InGaN-based, light-emitting diode by microroughening of the p-GaN surface,” J. Appl. Phys. 93(11), 9383 (2003).
[Crossref]

Arif, R. A.

Benisty, H.

T. David, T. Fujii, B. Moran, S. Nakamura, S. P. DenBaars, C. Weisbuch, and H. Benisty, “Photonic crystal laser lift-off GaN light-emitting diodes,” Appl. Phys. Lett. 88(13), 133514 (2006).
[Crossref]

Chakraborty, A.

T. Koyama, T. Onuma, H. Masui, A. Chakraborty, B. A. Haskell, S. Keller, U. K. Mishra, H. S. Speck, S. Nakamura, S. P. DenBaars, T. Sota, and S. F. Chichibu, “Prospective emission efficiency and in-plane light polarization of nonpolar m-plane InxGa1-xN/GaN blue light emitting diodes fabricated on freestanding GaN substrates,” Appl. Phys. Lett. 89(9), 091906 (2006).
[Crossref]

Chan, C.-H.

C.-H. Chan, C.-H. Hou, S.-Z. Tseng, T.-J. Chen, H.-T. Chien, F.-L. Hsiao, C.-C. Lee, Y.-L. Tsai, and C.-C. Chen, “Improved output power of GaN-based light-emitting diodes grown on a nanopatterned sapphire substrate,” Appl. Phys. Lett. 95(1), 011110 (2009).
[Crossref]

Chang, C. C.

C. C. Yang, C. F. Lin, C. M. Lin, C. C. Chang, K. T. Chen, J. F. Chien, and C. Y. Chang, “Improving light output power of InGaN-based light emitting diodes with pattern-nanoporous p-type GaN:Mg surfaces,” Appl. Phys. Lett. 93(20), 203103 (2008).
[Crossref]

Chang, C. H.

Chang, C. Y.

M. H. Lo, P. M. Tu, C. H. Wang, C. W. Hung, S. C. Hsu, Y. J. Cheng, H. C. Kuo, H. W. Zan, S. C. Wang, C. Y. Chang, and S. C. Huang, “High efficiency light emitting diode with anisotropically etched GaN-sapphire interface,” Appl. Phys. Lett. 95(4), 041109 (2009).
[Crossref]

C. C. Yang, C. F. Lin, C. M. Lin, C. C. Chang, K. T. Chen, J. F. Chien, and C. Y. Chang, “Improving light output power of InGaN-based light emitting diodes with pattern-nanoporous p-type GaN:Mg surfaces,” Appl. Phys. Lett. 93(20), 203103 (2008).
[Crossref]

Chen, C.-C.

C.-H. Chan, C.-H. Hou, S.-Z. Tseng, T.-J. Chen, H.-T. Chien, F.-L. Hsiao, C.-C. Lee, Y.-L. Tsai, and C.-C. Chen, “Improved output power of GaN-based light-emitting diodes grown on a nanopatterned sapphire substrate,” Appl. Phys. Lett. 95(1), 011110 (2009).
[Crossref]

Chen, J.-J.

C.-C. Kao, Y.-K. Su, C.-L. Lin, and J.-J. Chen, “Efficiency Improvement of GaN-Based LEDs With SiO2 Microrod Array and Textured Sidewalls,” IEEE Electron Device Lett. 31(1), 35–37 (2010).
[Crossref]

Chen, K. T.

C. C. Yang, C. F. Lin, C. M. Lin, C. C. Chang, K. T. Chen, J. F. Chien, and C. Y. Chang, “Improving light output power of InGaN-based light emitting diodes with pattern-nanoporous p-type GaN:Mg surfaces,” Appl. Phys. Lett. 93(20), 203103 (2008).
[Crossref]

Chen, T.-J.

C.-H. Chan, C.-H. Hou, S.-Z. Tseng, T.-J. Chen, H.-T. Chien, F.-L. Hsiao, C.-C. Lee, Y.-L. Tsai, and C.-C. Chen, “Improved output power of GaN-based light-emitting diodes grown on a nanopatterned sapphire substrate,” Appl. Phys. Lett. 95(1), 011110 (2009).
[Crossref]

Cheng, Y. J.

M. H. Lo, P. M. Tu, C. H. Wang, C. W. Hung, S. C. Hsu, Y. J. Cheng, H. C. Kuo, H. W. Zan, S. C. Wang, C. Y. Chang, and S. C. Huang, “High efficiency light emitting diode with anisotropically etched GaN-sapphire interface,” Appl. Phys. Lett. 95(4), 041109 (2009).
[Crossref]

Chichibu, S. F.

T. Koyama, T. Onuma, H. Masui, A. Chakraborty, B. A. Haskell, S. Keller, U. K. Mishra, H. S. Speck, S. Nakamura, S. P. DenBaars, T. Sota, and S. F. Chichibu, “Prospective emission efficiency and in-plane light polarization of nonpolar m-plane InxGa1-xN/GaN blue light emitting diodes fabricated on freestanding GaN substrates,” Appl. Phys. Lett. 89(9), 091906 (2006).
[Crossref]

Chien, H.-T.

C.-H. Chan, C.-H. Hou, S.-Z. Tseng, T.-J. Chen, H.-T. Chien, F.-L. Hsiao, C.-C. Lee, Y.-L. Tsai, and C.-C. Chen, “Improved output power of GaN-based light-emitting diodes grown on a nanopatterned sapphire substrate,” Appl. Phys. Lett. 95(1), 011110 (2009).
[Crossref]

Chien, J. F.

C. C. Yang, C. F. Lin, C. M. Lin, C. C. Chang, K. T. Chen, J. F. Chien, and C. Y. Chang, “Improving light output power of InGaN-based light emitting diodes with pattern-nanoporous p-type GaN:Mg surfaces,” Appl. Phys. Lett. 93(20), 203103 (2008).
[Crossref]

Chiu, C. H.

M.-A. Tsai, P. Yu, C. H. Chiu, H. C. Kuo, T. C. Lu, and S. H. Lin, “Self-assembled two-dimensional surface structures for beam shaping of GaN-based vertical-injection light-emitting diodes,” IEEE Photon. Technol. Lett. 22(1), 12–14 (2010).
[Crossref]

C. H. Chiu, P. C. Yu, C. H. Chang, C. S. Yang, M. H. Hsu, H. C. Kuo, and M. A. Tsai, “Oblique electron-beam evaporation of distinctive indium-tin-oxide nanorods for enhanced light extraction from InGaN/GaN light emitting diodes,” Opt. Express 17(23), 21250–21256 (2009).
[Crossref] [PubMed]

H. W. Huang, C. H. Lin, C. C. Yu, B. D. Lee, C. H. Chiu, C. F. Lai, H. C. Kuo, K. M. Leung, T. C. Lu, and S. C. Wang, “Improvement of light output in GaN-based power chip light-emitting diodes with a nano-rough surface by nanoimprint lithography,” Semicond. Sci. Technol. 23(4), 045022 (2008).
[Crossref]

Chu, J. T.

C. C. Hung-Wen Huang, C. C. Kao, J. T. Chu, H. C. Kuo, S. C. Wang, and C. C. Yu, “Improvement of InGaN-GaN light-emitting diode performance with a nano-roughened p-GaN surface,” IEEE Photon. Technol. Lett. 17(5), 983–985 (2005).
[Crossref]

David, T.

T. David, T. Fujii, B. Moran, S. Nakamura, S. P. DenBaars, C. Weisbuch, and H. Benisty, “Photonic crystal laser lift-off GaN light-emitting diodes,” Appl. Phys. Lett. 88(13), 133514 (2006).
[Crossref]

DenBaars, S. P.

T. David, T. Fujii, B. Moran, S. Nakamura, S. P. DenBaars, C. Weisbuch, and H. Benisty, “Photonic crystal laser lift-off GaN light-emitting diodes,” Appl. Phys. Lett. 88(13), 133514 (2006).
[Crossref]

T. Koyama, T. Onuma, H. Masui, A. Chakraborty, B. A. Haskell, S. Keller, U. K. Mishra, H. S. Speck, S. Nakamura, S. P. DenBaars, T. Sota, and S. F. Chichibu, “Prospective emission efficiency and in-plane light polarization of nonpolar m-plane InxGa1-xN/GaN blue light emitting diodes fabricated on freestanding GaN substrates,” Appl. Phys. Lett. 89(9), 091906 (2006).
[Crossref]

Dong, Z. J.

S. M. Huang, Y. Yao, C. Jin, Z. Sun, and Z. J. Dong, “Enhancement of the light output of GaN-based light-emitting diodes using surface-textured indium-tin-oxide transparent ohmic contacts,” Displays 29(3), 254–259 (2008).
[Crossref]

Ee, Y.-K.

Forrest, S. R.

Y. Sun and S. R. Forrest, “Organic light emitting devices with enhanced outcoupling via microlenses fabricated by imprint lithography,” J. Appl. Phys. 100(7), 073106 (2006).
[Crossref]

Fujii, T.

T. David, T. Fujii, B. Moran, S. Nakamura, S. P. DenBaars, C. Weisbuch, and H. Benisty, “Photonic crystal laser lift-off GaN light-emitting diodes,” Appl. Phys. Lett. 88(13), 133514 (2006).
[Crossref]

Gilchrist, J. F.

Ha, G.-Y.

S.-I. Na, G.-Y. Ha, D.-S. Han, S.-S. Kim, J.-Y. Kim, J.-H. Lim, D.-J. Kim, K.-I. Min, and S.-J. Park, “Selective wet etching of p-GaN for efficient GaN-based-light-emitting diodes,” IEEE Photon. Technol. Lett. 18(14), 1512–1514 (2006).
[Crossref]

Han, D.-S.

S.-I. Na, G.-Y. Ha, D.-S. Han, S.-S. Kim, J.-Y. Kim, J.-H. Lim, D.-J. Kim, K.-I. Min, and S.-J. Park, “Selective wet etching of p-GaN for efficient GaN-based-light-emitting diodes,” IEEE Photon. Technol. Lett. 18(14), 1512–1514 (2006).
[Crossref]

Haskell, B. A.

T. Koyama, T. Onuma, H. Masui, A. Chakraborty, B. A. Haskell, S. Keller, U. K. Mishra, H. S. Speck, S. Nakamura, S. P. DenBaars, T. Sota, and S. F. Chichibu, “Prospective emission efficiency and in-plane light polarization of nonpolar m-plane InxGa1-xN/GaN blue light emitting diodes fabricated on freestanding GaN substrates,” Appl. Phys. Lett. 89(9), 091906 (2006).
[Crossref]

Hou, C.-H.

C.-H. Chan, C.-H. Hou, S.-Z. Tseng, T.-J. Chen, H.-T. Chien, F.-L. Hsiao, C.-C. Lee, Y.-L. Tsai, and C.-C. Chen, “Improved output power of GaN-based light-emitting diodes grown on a nanopatterned sapphire substrate,” Appl. Phys. Lett. 95(1), 011110 (2009).
[Crossref]

Hsiao, F.-L.

C.-H. Chan, C.-H. Hou, S.-Z. Tseng, T.-J. Chen, H.-T. Chien, F.-L. Hsiao, C.-C. Lee, Y.-L. Tsai, and C.-C. Chen, “Improved output power of GaN-based light-emitting diodes grown on a nanopatterned sapphire substrate,” Appl. Phys. Lett. 95(1), 011110 (2009).
[Crossref]

Hsu, M. H.

Hsu, S. C.

M. H. Lo, P. M. Tu, C. H. Wang, C. W. Hung, S. C. Hsu, Y. J. Cheng, H. C. Kuo, H. W. Zan, S. C. Wang, C. Y. Chang, and S. C. Huang, “High efficiency light emitting diode with anisotropically etched GaN-sapphire interface,” Appl. Phys. Lett. 95(4), 041109 (2009).
[Crossref]

Huang, H. W.

H. W. Huang, C. H. Lin, C. C. Yu, B. D. Lee, C. H. Chiu, C. F. Lai, H. C. Kuo, K. M. Leung, T. C. Lu, and S. C. Wang, “Improvement of light output in GaN-based power chip light-emitting diodes with a nano-rough surface by nanoimprint lithography,” Semicond. Sci. Technol. 23(4), 045022 (2008).
[Crossref]

Huang, S. C.

M. H. Lo, P. M. Tu, C. H. Wang, C. W. Hung, S. C. Hsu, Y. J. Cheng, H. C. Kuo, H. W. Zan, S. C. Wang, C. Y. Chang, and S. C. Huang, “High efficiency light emitting diode with anisotropically etched GaN-sapphire interface,” Appl. Phys. Lett. 95(4), 041109 (2009).
[Crossref]

Huang, S. M.

S. M. Huang, Y. Yao, C. Jin, Z. Sun, and Z. J. Dong, “Enhancement of the light output of GaN-based light-emitting diodes using surface-textured indium-tin-oxide transparent ohmic contacts,” Displays 29(3), 254–259 (2008).
[Crossref]

Huang, X. Y.

H.-Y. Lee, X. Y. Huang, and C.-T. Lee, “Light output enhancement of GaN-based roughened LEDs using bias-assisted photoelectrochemical etching method,” J. Electrochem. Soc. 155(10), H707 (2008).
[Crossref]

Huh, C.

E.-J. Kang, C. Huh, S.-H. Lee, J.-J. Jung, S.-J. Lee, and S.-J. Park, “Improvement in light-output power of InGaN/GaN LED by formation of nanosize cavities on p-GaN surface,” Electrochem. Solid-State Lett. 8(12), G327 (2005).
[Crossref]

C. Huh, K. S. Lee, E. J. Kang, and S. J. Park, “Improved light-output and electrical performance of InGaN-based, light-emitting diode by microroughening of the p-GaN surface,” J. Appl. Phys. 93(11), 9383 (2003).
[Crossref]

Hung, C. W.

M. H. Lo, P. M. Tu, C. H. Wang, C. W. Hung, S. C. Hsu, Y. J. Cheng, H. C. Kuo, H. W. Zan, S. C. Wang, C. Y. Chang, and S. C. Huang, “High efficiency light emitting diode with anisotropically etched GaN-sapphire interface,” Appl. Phys. Lett. 95(4), 041109 (2009).
[Crossref]

Hung-Wen Huang, C. C.

C. C. Hung-Wen Huang, C. C. Kao, J. T. Chu, H. C. Kuo, S. C. Wang, and C. C. Yu, “Improvement of InGaN-GaN light-emitting diode performance with a nano-roughened p-GaN surface,” IEEE Photon. Technol. Lett. 17(5), 983–985 (2005).
[Crossref]

Jin, C.

S. M. Huang, Y. Yao, C. Jin, Z. Sun, and Z. J. Dong, “Enhancement of the light output of GaN-based light-emitting diodes using surface-textured indium-tin-oxide transparent ohmic contacts,” Displays 29(3), 254–259 (2008).
[Crossref]

Jung, J.-J.

E.-J. Kang, C. Huh, S.-H. Lee, J.-J. Jung, S.-J. Lee, and S.-J. Park, “Improvement in light-output power of InGaN/GaN LED by formation of nanosize cavities on p-GaN surface,” Electrochem. Solid-State Lett. 8(12), G327 (2005).
[Crossref]

Kang, E. J.

C. Huh, K. S. Lee, E. J. Kang, and S. J. Park, “Improved light-output and electrical performance of InGaN-based, light-emitting diode by microroughening of the p-GaN surface,” J. Appl. Phys. 93(11), 9383 (2003).
[Crossref]

Kang, E.-J.

E.-J. Kang, C. Huh, S.-H. Lee, J.-J. Jung, S.-J. Lee, and S.-J. Park, “Improvement in light-output power of InGaN/GaN LED by formation of nanosize cavities on p-GaN surface,” Electrochem. Solid-State Lett. 8(12), G327 (2005).
[Crossref]

Kao, C. C.

C. C. Hung-Wen Huang, C. C. Kao, J. T. Chu, H. C. Kuo, S. C. Wang, and C. C. Yu, “Improvement of InGaN-GaN light-emitting diode performance with a nano-roughened p-GaN surface,” IEEE Photon. Technol. Lett. 17(5), 983–985 (2005).
[Crossref]

Kao, C.-C.

C.-C. Kao, Y.-K. Su, C.-L. Lin, and J.-J. Chen, “Efficiency Improvement of GaN-Based LEDs With SiO2 Microrod Array and Textured Sidewalls,” IEEE Electron Device Lett. 31(1), 35–37 (2010).
[Crossref]

Keller, S.

T. Koyama, T. Onuma, H. Masui, A. Chakraborty, B. A. Haskell, S. Keller, U. K. Mishra, H. S. Speck, S. Nakamura, S. P. DenBaars, T. Sota, and S. F. Chichibu, “Prospective emission efficiency and in-plane light polarization of nonpolar m-plane InxGa1-xN/GaN blue light emitting diodes fabricated on freestanding GaN substrates,” Appl. Phys. Lett. 89(9), 091906 (2006).
[Crossref]

Kim, D.-J.

S.-I. Na, G.-Y. Ha, D.-S. Han, S.-S. Kim, J.-Y. Kim, J.-H. Lim, D.-J. Kim, K.-I. Min, and S.-J. Park, “Selective wet etching of p-GaN for efficient GaN-based-light-emitting diodes,” IEEE Photon. Technol. Lett. 18(14), 1512–1514 (2006).
[Crossref]

Kim, J.-Y.

S.-I. Na, G.-Y. Ha, D.-S. Han, S.-S. Kim, J.-Y. Kim, J.-H. Lim, D.-J. Kim, K.-I. Min, and S.-J. Park, “Selective wet etching of p-GaN for efficient GaN-based-light-emitting diodes,” IEEE Photon. Technol. Lett. 18(14), 1512–1514 (2006).
[Crossref]

Kim, S.-S.

S.-I. Na, G.-Y. Ha, D.-S. Han, S.-S. Kim, J.-Y. Kim, J.-H. Lim, D.-J. Kim, K.-I. Min, and S.-J. Park, “Selective wet etching of p-GaN for efficient GaN-based-light-emitting diodes,” IEEE Photon. Technol. Lett. 18(14), 1512–1514 (2006).
[Crossref]

Koyama, T.

T. Koyama, T. Onuma, H. Masui, A. Chakraborty, B. A. Haskell, S. Keller, U. K. Mishra, H. S. Speck, S. Nakamura, S. P. DenBaars, T. Sota, and S. F. Chichibu, “Prospective emission efficiency and in-plane light polarization of nonpolar m-plane InxGa1-xN/GaN blue light emitting diodes fabricated on freestanding GaN substrates,” Appl. Phys. Lett. 89(9), 091906 (2006).
[Crossref]

Kumnorkaew, P.

Kuo, H. C.

M.-A. Tsai, P. Yu, C. H. Chiu, H. C. Kuo, T. C. Lu, and S. H. Lin, “Self-assembled two-dimensional surface structures for beam shaping of GaN-based vertical-injection light-emitting diodes,” IEEE Photon. Technol. Lett. 22(1), 12–14 (2010).
[Crossref]

M. H. Lo, P. M. Tu, C. H. Wang, C. W. Hung, S. C. Hsu, Y. J. Cheng, H. C. Kuo, H. W. Zan, S. C. Wang, C. Y. Chang, and S. C. Huang, “High efficiency light emitting diode with anisotropically etched GaN-sapphire interface,” Appl. Phys. Lett. 95(4), 041109 (2009).
[Crossref]

C. H. Chiu, P. C. Yu, C. H. Chang, C. S. Yang, M. H. Hsu, H. C. Kuo, and M. A. Tsai, “Oblique electron-beam evaporation of distinctive indium-tin-oxide nanorods for enhanced light extraction from InGaN/GaN light emitting diodes,” Opt. Express 17(23), 21250–21256 (2009).
[Crossref] [PubMed]

H. W. Huang, C. H. Lin, C. C. Yu, B. D. Lee, C. H. Chiu, C. F. Lai, H. C. Kuo, K. M. Leung, T. C. Lu, and S. C. Wang, “Improvement of light output in GaN-based power chip light-emitting diodes with a nano-rough surface by nanoimprint lithography,” Semicond. Sci. Technol. 23(4), 045022 (2008).
[Crossref]

C. C. Hung-Wen Huang, C. C. Kao, J. T. Chu, H. C. Kuo, S. C. Wang, and C. C. Yu, “Improvement of InGaN-GaN light-emitting diode performance with a nano-roughened p-GaN surface,” IEEE Photon. Technol. Lett. 17(5), 983–985 (2005).
[Crossref]

Lai, C. F.

H. W. Huang, C. H. Lin, C. C. Yu, B. D. Lee, C. H. Chiu, C. F. Lai, H. C. Kuo, K. M. Leung, T. C. Lu, and S. C. Wang, “Improvement of light output in GaN-based power chip light-emitting diodes with a nano-rough surface by nanoimprint lithography,” Semicond. Sci. Technol. 23(4), 045022 (2008).
[Crossref]

Lee, B. D.

H. W. Huang, C. H. Lin, C. C. Yu, B. D. Lee, C. H. Chiu, C. F. Lai, H. C. Kuo, K. M. Leung, T. C. Lu, and S. C. Wang, “Improvement of light output in GaN-based power chip light-emitting diodes with a nano-rough surface by nanoimprint lithography,” Semicond. Sci. Technol. 23(4), 045022 (2008).
[Crossref]

Lee, C.-C.

C.-H. Chan, C.-H. Hou, S.-Z. Tseng, T.-J. Chen, H.-T. Chien, F.-L. Hsiao, C.-C. Lee, Y.-L. Tsai, and C.-C. Chen, “Improved output power of GaN-based light-emitting diodes grown on a nanopatterned sapphire substrate,” Appl. Phys. Lett. 95(1), 011110 (2009).
[Crossref]

Lee, C.-T.

H.-Y. Lee, X. Y. Huang, and C.-T. Lee, “Light output enhancement of GaN-based roughened LEDs using bias-assisted photoelectrochemical etching method,” J. Electrochem. Soc. 155(10), H707 (2008).
[Crossref]

Lee, H.-Y.

H.-Y. Lee, X. Y. Huang, and C.-T. Lee, “Light output enhancement of GaN-based roughened LEDs using bias-assisted photoelectrochemical etching method,” J. Electrochem. Soc. 155(10), H707 (2008).
[Crossref]

Lee, K. S.

C. Huh, K. S. Lee, E. J. Kang, and S. J. Park, “Improved light-output and electrical performance of InGaN-based, light-emitting diode by microroughening of the p-GaN surface,” J. Appl. Phys. 93(11), 9383 (2003).
[Crossref]

Lee, S.-H.

E.-J. Kang, C. Huh, S.-H. Lee, J.-J. Jung, S.-J. Lee, and S.-J. Park, “Improvement in light-output power of InGaN/GaN LED by formation of nanosize cavities on p-GaN surface,” Electrochem. Solid-State Lett. 8(12), G327 (2005).
[Crossref]

Lee, S.-J.

E.-J. Kang, C. Huh, S.-H. Lee, J.-J. Jung, S.-J. Lee, and S.-J. Park, “Improvement in light-output power of InGaN/GaN LED by formation of nanosize cavities on p-GaN surface,” Electrochem. Solid-State Lett. 8(12), G327 (2005).
[Crossref]

Leung, K. M.

H. W. Huang, C. H. Lin, C. C. Yu, B. D. Lee, C. H. Chiu, C. F. Lai, H. C. Kuo, K. M. Leung, T. C. Lu, and S. C. Wang, “Improvement of light output in GaN-based power chip light-emitting diodes with a nano-rough surface by nanoimprint lithography,” Semicond. Sci. Technol. 23(4), 045022 (2008).
[Crossref]

Lim, J.-H.

S.-I. Na, G.-Y. Ha, D.-S. Han, S.-S. Kim, J.-Y. Kim, J.-H. Lim, D.-J. Kim, K.-I. Min, and S.-J. Park, “Selective wet etching of p-GaN for efficient GaN-based-light-emitting diodes,” IEEE Photon. Technol. Lett. 18(14), 1512–1514 (2006).
[Crossref]

Lin, C. F.

C. C. Yang, C. F. Lin, C. M. Lin, C. C. Chang, K. T. Chen, J. F. Chien, and C. Y. Chang, “Improving light output power of InGaN-based light emitting diodes with pattern-nanoporous p-type GaN:Mg surfaces,” Appl. Phys. Lett. 93(20), 203103 (2008).
[Crossref]

Lin, C. H.

H. W. Huang, C. H. Lin, C. C. Yu, B. D. Lee, C. H. Chiu, C. F. Lai, H. C. Kuo, K. M. Leung, T. C. Lu, and S. C. Wang, “Improvement of light output in GaN-based power chip light-emitting diodes with a nano-rough surface by nanoimprint lithography,” Semicond. Sci. Technol. 23(4), 045022 (2008).
[Crossref]

Lin, C. M.

C. C. Yang, C. F. Lin, C. M. Lin, C. C. Chang, K. T. Chen, J. F. Chien, and C. Y. Chang, “Improving light output power of InGaN-based light emitting diodes with pattern-nanoporous p-type GaN:Mg surfaces,” Appl. Phys. Lett. 93(20), 203103 (2008).
[Crossref]

Lin, C.-L.

C.-C. Kao, Y.-K. Su, C.-L. Lin, and J.-J. Chen, “Efficiency Improvement of GaN-Based LEDs With SiO2 Microrod Array and Textured Sidewalls,” IEEE Electron Device Lett. 31(1), 35–37 (2010).
[Crossref]

Lin, S. H.

M.-A. Tsai, P. Yu, C. H. Chiu, H. C. Kuo, T. C. Lu, and S. H. Lin, “Self-assembled two-dimensional surface structures for beam shaping of GaN-based vertical-injection light-emitting diodes,” IEEE Photon. Technol. Lett. 22(1), 12–14 (2010).
[Crossref]

Lo, M. H.

M. H. Lo, P. M. Tu, C. H. Wang, C. W. Hung, S. C. Hsu, Y. J. Cheng, H. C. Kuo, H. W. Zan, S. C. Wang, C. Y. Chang, and S. C. Huang, “High efficiency light emitting diode with anisotropically etched GaN-sapphire interface,” Appl. Phys. Lett. 95(4), 041109 (2009).
[Crossref]

Lu, T. C.

M.-A. Tsai, P. Yu, C. H. Chiu, H. C. Kuo, T. C. Lu, and S. H. Lin, “Self-assembled two-dimensional surface structures for beam shaping of GaN-based vertical-injection light-emitting diodes,” IEEE Photon. Technol. Lett. 22(1), 12–14 (2010).
[Crossref]

H. W. Huang, C. H. Lin, C. C. Yu, B. D. Lee, C. H. Chiu, C. F. Lai, H. C. Kuo, K. M. Leung, T. C. Lu, and S. C. Wang, “Improvement of light output in GaN-based power chip light-emitting diodes with a nano-rough surface by nanoimprint lithography,” Semicond. Sci. Technol. 23(4), 045022 (2008).
[Crossref]

Masui, H.

T. Koyama, T. Onuma, H. Masui, A. Chakraborty, B. A. Haskell, S. Keller, U. K. Mishra, H. S. Speck, S. Nakamura, S. P. DenBaars, T. Sota, and S. F. Chichibu, “Prospective emission efficiency and in-plane light polarization of nonpolar m-plane InxGa1-xN/GaN blue light emitting diodes fabricated on freestanding GaN substrates,” Appl. Phys. Lett. 89(9), 091906 (2006).
[Crossref]

Min, K.-I.

S.-I. Na, G.-Y. Ha, D.-S. Han, S.-S. Kim, J.-Y. Kim, J.-H. Lim, D.-J. Kim, K.-I. Min, and S.-J. Park, “Selective wet etching of p-GaN for efficient GaN-based-light-emitting diodes,” IEEE Photon. Technol. Lett. 18(14), 1512–1514 (2006).
[Crossref]

Mishra, U. K.

T. Koyama, T. Onuma, H. Masui, A. Chakraborty, B. A. Haskell, S. Keller, U. K. Mishra, H. S. Speck, S. Nakamura, S. P. DenBaars, T. Sota, and S. F. Chichibu, “Prospective emission efficiency and in-plane light polarization of nonpolar m-plane InxGa1-xN/GaN blue light emitting diodes fabricated on freestanding GaN substrates,” Appl. Phys. Lett. 89(9), 091906 (2006).
[Crossref]

Moran, B.

T. David, T. Fujii, B. Moran, S. Nakamura, S. P. DenBaars, C. Weisbuch, and H. Benisty, “Photonic crystal laser lift-off GaN light-emitting diodes,” Appl. Phys. Lett. 88(13), 133514 (2006).
[Crossref]

Na, S.-I.

S.-I. Na, G.-Y. Ha, D.-S. Han, S.-S. Kim, J.-Y. Kim, J.-H. Lim, D.-J. Kim, K.-I. Min, and S.-J. Park, “Selective wet etching of p-GaN for efficient GaN-based-light-emitting diodes,” IEEE Photon. Technol. Lett. 18(14), 1512–1514 (2006).
[Crossref]

Nakamura, S.

T. David, T. Fujii, B. Moran, S. Nakamura, S. P. DenBaars, C. Weisbuch, and H. Benisty, “Photonic crystal laser lift-off GaN light-emitting diodes,” Appl. Phys. Lett. 88(13), 133514 (2006).
[Crossref]

T. Koyama, T. Onuma, H. Masui, A. Chakraborty, B. A. Haskell, S. Keller, U. K. Mishra, H. S. Speck, S. Nakamura, S. P. DenBaars, T. Sota, and S. F. Chichibu, “Prospective emission efficiency and in-plane light polarization of nonpolar m-plane InxGa1-xN/GaN blue light emitting diodes fabricated on freestanding GaN substrates,” Appl. Phys. Lett. 89(9), 091906 (2006).
[Crossref]

Onuma, T.

T. Koyama, T. Onuma, H. Masui, A. Chakraborty, B. A. Haskell, S. Keller, U. K. Mishra, H. S. Speck, S. Nakamura, S. P. DenBaars, T. Sota, and S. F. Chichibu, “Prospective emission efficiency and in-plane light polarization of nonpolar m-plane InxGa1-xN/GaN blue light emitting diodes fabricated on freestanding GaN substrates,” Appl. Phys. Lett. 89(9), 091906 (2006).
[Crossref]

Park, S. J.

C. Huh, K. S. Lee, E. J. Kang, and S. J. Park, “Improved light-output and electrical performance of InGaN-based, light-emitting diode by microroughening of the p-GaN surface,” J. Appl. Phys. 93(11), 9383 (2003).
[Crossref]

Park, S.-J.

S.-I. Na, G.-Y. Ha, D.-S. Han, S.-S. Kim, J.-Y. Kim, J.-H. Lim, D.-J. Kim, K.-I. Min, and S.-J. Park, “Selective wet etching of p-GaN for efficient GaN-based-light-emitting diodes,” IEEE Photon. Technol. Lett. 18(14), 1512–1514 (2006).
[Crossref]

E.-J. Kang, C. Huh, S.-H. Lee, J.-J. Jung, S.-J. Lee, and S.-J. Park, “Improvement in light-output power of InGaN/GaN LED by formation of nanosize cavities on p-GaN surface,” Electrochem. Solid-State Lett. 8(12), G327 (2005).
[Crossref]

Sota, T.

T. Koyama, T. Onuma, H. Masui, A. Chakraborty, B. A. Haskell, S. Keller, U. K. Mishra, H. S. Speck, S. Nakamura, S. P. DenBaars, T. Sota, and S. F. Chichibu, “Prospective emission efficiency and in-plane light polarization of nonpolar m-plane InxGa1-xN/GaN blue light emitting diodes fabricated on freestanding GaN substrates,” Appl. Phys. Lett. 89(9), 091906 (2006).
[Crossref]

Speck, H. S.

T. Koyama, T. Onuma, H. Masui, A. Chakraborty, B. A. Haskell, S. Keller, U. K. Mishra, H. S. Speck, S. Nakamura, S. P. DenBaars, T. Sota, and S. F. Chichibu, “Prospective emission efficiency and in-plane light polarization of nonpolar m-plane InxGa1-xN/GaN blue light emitting diodes fabricated on freestanding GaN substrates,” Appl. Phys. Lett. 89(9), 091906 (2006).
[Crossref]

Su, Y.-K.

C.-C. Kao, Y.-K. Su, C.-L. Lin, and J.-J. Chen, “Efficiency Improvement of GaN-Based LEDs With SiO2 Microrod Array and Textured Sidewalls,” IEEE Electron Device Lett. 31(1), 35–37 (2010).
[Crossref]

Sun, Y.

Y. Sun and S. R. Forrest, “Organic light emitting devices with enhanced outcoupling via microlenses fabricated by imprint lithography,” J. Appl. Phys. 100(7), 073106 (2006).
[Crossref]

Sun, Z.

S. M. Huang, Y. Yao, C. Jin, Z. Sun, and Z. J. Dong, “Enhancement of the light output of GaN-based light-emitting diodes using surface-textured indium-tin-oxide transparent ohmic contacts,” Displays 29(3), 254–259 (2008).
[Crossref]

Tansu, N.

Tong, H.

Tsai, M. A.

Tsai, M.-A.

M.-A. Tsai, P. Yu, C. H. Chiu, H. C. Kuo, T. C. Lu, and S. H. Lin, “Self-assembled two-dimensional surface structures for beam shaping of GaN-based vertical-injection light-emitting diodes,” IEEE Photon. Technol. Lett. 22(1), 12–14 (2010).
[Crossref]

Tsai, Y.-L.

C.-H. Chan, C.-H. Hou, S.-Z. Tseng, T.-J. Chen, H.-T. Chien, F.-L. Hsiao, C.-C. Lee, Y.-L. Tsai, and C.-C. Chen, “Improved output power of GaN-based light-emitting diodes grown on a nanopatterned sapphire substrate,” Appl. Phys. Lett. 95(1), 011110 (2009).
[Crossref]

Tseng, S.-Z.

C.-H. Chan, C.-H. Hou, S.-Z. Tseng, T.-J. Chen, H.-T. Chien, F.-L. Hsiao, C.-C. Lee, Y.-L. Tsai, and C.-C. Chen, “Improved output power of GaN-based light-emitting diodes grown on a nanopatterned sapphire substrate,” Appl. Phys. Lett. 95(1), 011110 (2009).
[Crossref]

Tu, P. M.

M. H. Lo, P. M. Tu, C. H. Wang, C. W. Hung, S. C. Hsu, Y. J. Cheng, H. C. Kuo, H. W. Zan, S. C. Wang, C. Y. Chang, and S. C. Huang, “High efficiency light emitting diode with anisotropically etched GaN-sapphire interface,” Appl. Phys. Lett. 95(4), 041109 (2009).
[Crossref]

Wang, C. H.

M. H. Lo, P. M. Tu, C. H. Wang, C. W. Hung, S. C. Hsu, Y. J. Cheng, H. C. Kuo, H. W. Zan, S. C. Wang, C. Y. Chang, and S. C. Huang, “High efficiency light emitting diode with anisotropically etched GaN-sapphire interface,” Appl. Phys. Lett. 95(4), 041109 (2009).
[Crossref]

Wang, S. C.

M. H. Lo, P. M. Tu, C. H. Wang, C. W. Hung, S. C. Hsu, Y. J. Cheng, H. C. Kuo, H. W. Zan, S. C. Wang, C. Y. Chang, and S. C. Huang, “High efficiency light emitting diode with anisotropically etched GaN-sapphire interface,” Appl. Phys. Lett. 95(4), 041109 (2009).
[Crossref]

H. W. Huang, C. H. Lin, C. C. Yu, B. D. Lee, C. H. Chiu, C. F. Lai, H. C. Kuo, K. M. Leung, T. C. Lu, and S. C. Wang, “Improvement of light output in GaN-based power chip light-emitting diodes with a nano-rough surface by nanoimprint lithography,” Semicond. Sci. Technol. 23(4), 045022 (2008).
[Crossref]

C. C. Hung-Wen Huang, C. C. Kao, J. T. Chu, H. C. Kuo, S. C. Wang, and C. C. Yu, “Improvement of InGaN-GaN light-emitting diode performance with a nano-roughened p-GaN surface,” IEEE Photon. Technol. Lett. 17(5), 983–985 (2005).
[Crossref]

Weisbuch, C.

T. David, T. Fujii, B. Moran, S. Nakamura, S. P. DenBaars, C. Weisbuch, and H. Benisty, “Photonic crystal laser lift-off GaN light-emitting diodes,” Appl. Phys. Lett. 88(13), 133514 (2006).
[Crossref]

Yang, C. C.

C. C. Yang, C. F. Lin, C. M. Lin, C. C. Chang, K. T. Chen, J. F. Chien, and C. Y. Chang, “Improving light output power of InGaN-based light emitting diodes with pattern-nanoporous p-type GaN:Mg surfaces,” Appl. Phys. Lett. 93(20), 203103 (2008).
[Crossref]

Yang, C. S.

Yao, Y.

S. M. Huang, Y. Yao, C. Jin, Z. Sun, and Z. J. Dong, “Enhancement of the light output of GaN-based light-emitting diodes using surface-textured indium-tin-oxide transparent ohmic contacts,” Displays 29(3), 254–259 (2008).
[Crossref]

Yu, C. C.

H. W. Huang, C. H. Lin, C. C. Yu, B. D. Lee, C. H. Chiu, C. F. Lai, H. C. Kuo, K. M. Leung, T. C. Lu, and S. C. Wang, “Improvement of light output in GaN-based power chip light-emitting diodes with a nano-rough surface by nanoimprint lithography,” Semicond. Sci. Technol. 23(4), 045022 (2008).
[Crossref]

C. C. Hung-Wen Huang, C. C. Kao, J. T. Chu, H. C. Kuo, S. C. Wang, and C. C. Yu, “Improvement of InGaN-GaN light-emitting diode performance with a nano-roughened p-GaN surface,” IEEE Photon. Technol. Lett. 17(5), 983–985 (2005).
[Crossref]

Yu, P.

M.-A. Tsai, P. Yu, C. H. Chiu, H. C. Kuo, T. C. Lu, and S. H. Lin, “Self-assembled two-dimensional surface structures for beam shaping of GaN-based vertical-injection light-emitting diodes,” IEEE Photon. Technol. Lett. 22(1), 12–14 (2010).
[Crossref]

Yu, P. C.

Zan, H. W.

M. H. Lo, P. M. Tu, C. H. Wang, C. W. Hung, S. C. Hsu, Y. J. Cheng, H. C. Kuo, H. W. Zan, S. C. Wang, C. Y. Chang, and S. C. Huang, “High efficiency light emitting diode with anisotropically etched GaN-sapphire interface,” Appl. Phys. Lett. 95(4), 041109 (2009).
[Crossref]

Appl. Phys. Lett. (5)

T. David, T. Fujii, B. Moran, S. Nakamura, S. P. DenBaars, C. Weisbuch, and H. Benisty, “Photonic crystal laser lift-off GaN light-emitting diodes,” Appl. Phys. Lett. 88(13), 133514 (2006).
[Crossref]

C.-H. Chan, C.-H. Hou, S.-Z. Tseng, T.-J. Chen, H.-T. Chien, F.-L. Hsiao, C.-C. Lee, Y.-L. Tsai, and C.-C. Chen, “Improved output power of GaN-based light-emitting diodes grown on a nanopatterned sapphire substrate,” Appl. Phys. Lett. 95(1), 011110 (2009).
[Crossref]

C. C. Yang, C. F. Lin, C. M. Lin, C. C. Chang, K. T. Chen, J. F. Chien, and C. Y. Chang, “Improving light output power of InGaN-based light emitting diodes with pattern-nanoporous p-type GaN:Mg surfaces,” Appl. Phys. Lett. 93(20), 203103 (2008).
[Crossref]

T. Koyama, T. Onuma, H. Masui, A. Chakraborty, B. A. Haskell, S. Keller, U. K. Mishra, H. S. Speck, S. Nakamura, S. P. DenBaars, T. Sota, and S. F. Chichibu, “Prospective emission efficiency and in-plane light polarization of nonpolar m-plane InxGa1-xN/GaN blue light emitting diodes fabricated on freestanding GaN substrates,” Appl. Phys. Lett. 89(9), 091906 (2006).
[Crossref]

M. H. Lo, P. M. Tu, C. H. Wang, C. W. Hung, S. C. Hsu, Y. J. Cheng, H. C. Kuo, H. W. Zan, S. C. Wang, C. Y. Chang, and S. C. Huang, “High efficiency light emitting diode with anisotropically etched GaN-sapphire interface,” Appl. Phys. Lett. 95(4), 041109 (2009).
[Crossref]

Displays (1)

S. M. Huang, Y. Yao, C. Jin, Z. Sun, and Z. J. Dong, “Enhancement of the light output of GaN-based light-emitting diodes using surface-textured indium-tin-oxide transparent ohmic contacts,” Displays 29(3), 254–259 (2008).
[Crossref]

Electrochem. Solid-State Lett. (1)

E.-J. Kang, C. Huh, S.-H. Lee, J.-J. Jung, S.-J. Lee, and S.-J. Park, “Improvement in light-output power of InGaN/GaN LED by formation of nanosize cavities on p-GaN surface,” Electrochem. Solid-State Lett. 8(12), G327 (2005).
[Crossref]

IEEE Electron Device Lett. (1)

C.-C. Kao, Y.-K. Su, C.-L. Lin, and J.-J. Chen, “Efficiency Improvement of GaN-Based LEDs With SiO2 Microrod Array and Textured Sidewalls,” IEEE Electron Device Lett. 31(1), 35–37 (2010).
[Crossref]

IEEE Photon. Technol. Lett. (3)

C. C. Hung-Wen Huang, C. C. Kao, J. T. Chu, H. C. Kuo, S. C. Wang, and C. C. Yu, “Improvement of InGaN-GaN light-emitting diode performance with a nano-roughened p-GaN surface,” IEEE Photon. Technol. Lett. 17(5), 983–985 (2005).
[Crossref]

M.-A. Tsai, P. Yu, C. H. Chiu, H. C. Kuo, T. C. Lu, and S. H. Lin, “Self-assembled two-dimensional surface structures for beam shaping of GaN-based vertical-injection light-emitting diodes,” IEEE Photon. Technol. Lett. 22(1), 12–14 (2010).
[Crossref]

S.-I. Na, G.-Y. Ha, D.-S. Han, S.-S. Kim, J.-Y. Kim, J.-H. Lim, D.-J. Kim, K.-I. Min, and S.-J. Park, “Selective wet etching of p-GaN for efficient GaN-based-light-emitting diodes,” IEEE Photon. Technol. Lett. 18(14), 1512–1514 (2006).
[Crossref]

J. Appl. Phys. (2)

C. Huh, K. S. Lee, E. J. Kang, and S. J. Park, “Improved light-output and electrical performance of InGaN-based, light-emitting diode by microroughening of the p-GaN surface,” J. Appl. Phys. 93(11), 9383 (2003).
[Crossref]

Y. Sun and S. R. Forrest, “Organic light emitting devices with enhanced outcoupling via microlenses fabricated by imprint lithography,” J. Appl. Phys. 100(7), 073106 (2006).
[Crossref]

J. Electrochem. Soc. (1)

H.-Y. Lee, X. Y. Huang, and C.-T. Lee, “Light output enhancement of GaN-based roughened LEDs using bias-assisted photoelectrochemical etching method,” J. Electrochem. Soc. 155(10), H707 (2008).
[Crossref]

Opt. Express (2)

Semicond. Sci. Technol. (1)

H. W. Huang, C. H. Lin, C. C. Yu, B. D. Lee, C. H. Chiu, C. F. Lai, H. C. Kuo, K. M. Leung, T. C. Lu, and S. C. Wang, “Improvement of light output in GaN-based power chip light-emitting diodes with a nano-rough surface by nanoimprint lithography,” Semicond. Sci. Technol. 23(4), 045022 (2008).
[Crossref]

Other (1)

E. Fred, Schubert: Light-Emitting Diodes, (Cambridge University Press, 2003) p. 89.

Cited By

OSA participates in Crossref's Cited-By Linking service. Citing articles from OSA journals and other participating publishers are listed here.

Alert me when this article is cited.


Figures (6)

Fig. 1
Fig. 1

Schematic illustration for texturization of the GaN surface using the CsCl nano-islands as an etch mask.

Fig. 2
Fig. 2

AFM images of the top surface morphology of LED. (a) CsCl islands on p-GaN surface with average size of 450 nm. Nano-roughened p-GaN surface with ICP etching durations of (b) 50, (c) 150 and (d) 250 sec.

Fig. 3
Fig. 3

(a) I-V forward characteristics and (b) leakage current as a function of reverse bias of conventional and ICP-roughened LEDs. The inset shows a SEM cross-section micrograph of p-GaN etched for 250 sec.

Fig. 4
Fig. 4

(a) Light output powers and (b) peak wavelengths and FWHMs of EL peaks for the LEDs without and with ICP etching treatment as a function of the injection current. The inset in (a) shows photos of conventional and roughened LEDs with 150 sec-etched at an injection current of 1 mA.

Fig. 5
Fig. 5

Far-field emission patterns of the conventional and ICP-roughened LEDs at an injection current of 200 mA.

Fig. 6
Fig. 6

Light extraction enhancements of LEDs as a function of the nano-island size under the optimum 150 sec ICP etching at an injection current of 350 mA. The inset shows the typical rough surface with island average size of 650 nm.

Metrics