Abstract

Optical transmission range and phase matching (PM) conditions for second harmonic generation (SHG) of Er3+:YSGG and CO2 laser in indium doped GaSe:In(0.1, 1.23, 2.32 mass%) are studied in comparison with these in pure and sulfur doped GaSe:S(0.09, 0.5, 2.2, 3 mass%) crystals. No changes in transparency curve are found in GaSe crystals up to 2.32 mass% indium content, but as small change as 0.18° in PM angle for 2.79 µm Er3+:YSGG laser SHG and ~0.06° for 9.58 µm CO2 laser emission line SHG are detected. PM properties of the crystals are evaluated as a function of temperature over the range from -165 to 230 °C. The value of dθ/dT, the change in PM angle with variation of temperature, is found to be very small for GaSe:In crystals. While for SHG of Er3+:YSGG laser, dθ/dT=22″/1°C only, it is as small as -4.9″/1°C for that of CO2 laser radiation. Linear variation of PM angle with temperature increasing is an indicator of absence of crystals structure transformation within temperature range from -165 to 230 °C. Thus, application of GaSe:In solid solutions in high average power nonlinear optical systems seems to be prospective.

© 2008 Optical Society of America

Full Article  |  PDF Article

References

  • View by:
  • |
  • |
  • |

  1. W.  Shi and Yu. J.  Ding, "A monochromatic and high-power terahertz source tunable in the ranges of 2.7-38.4 and 58.2-3540 ?m for variety of potential applications," Appl. Phys. Lett. 84, 1635-1637 (2004).
    [CrossRef]
  2. N. C.  Fernelius, "Properties of gallium selenide single crystal," Prog. Cryst. Growth Charact. 28, 275-353 (1994).
    [CrossRef]
  3. D. R.  Suhre, N. B.  Singh, V.  Balakrishna, N. C.  Fernelius, and F. K.  Hopkins, "Improved crystal quality and harmonic generation in GaSe doped with indium," Opt. Lett. 22, 775-777 (1997).
    [CrossRef] [PubMed]
  4. N. B.  Singh, R.  Narayanan, A. X.  Zhao, V.  Balakrishna, R. H.  Hopkins, D. R.  Suhre, N. C.  Fernelius, F. K.  Hopkins, and D. E.  Zelmon, "Bridgman growth of GaSe crystals for nonlinear optical applications," Mater. Sci. Eng. B 49, 243-246 (1997).
    [CrossRef]
  5. N. B.  Singh, D. R.  Suhre, V.  Balakrishna, M.  Marable, R.  Meyer, N.  Fernelius, F. K.  Hopkins, and D.  Zelmon, "Far-infrared conversion materials: Gallium selenide for far-infrared conversion applications," Prog. Cryst. Growth Charact. Mater. 37, 47-102 (1998).
    [CrossRef]
  6. N. B.  Singh, D. R.  Suhre, W.  Rosch, R.  Meyer, M.  Marable, N. C.  Fernelius, F. K.  Hopkins, D. E.  Zelmon, and R.  Narayanan, "Modified GaSe crystals for mid-IR applications," J. Cryst. Growth 198, 588-592 (1999).
    [CrossRef]
  7. V. G.  Voevodin, O. V.  Voevodina, S. A.  Bereznaya, Z. V.  Korotchenko, A. N.  Morozov, S. Yu.  Sarkisov, N. C.  Fernelius, and J. T.  Goldstein, "Large single crystals of gallium selenide: growing, doping by In and characterization," Opt. Mater. 26, 495-499 (2004).
    [CrossRef]
  8. S.  Das, C.  Ghosh, S.  Gangopadhyay, U.  Chatterjee, G. C.  Bhar, V. G.  Voevodin, and O. G.  Voevodina, "Tunable coherent infrared source from 5-16 ?m based on difference-frequency mixing in an indium-doped GaSe crystal," J. Opt. Soc. Am. B 23, 282-288 (2006).
    [CrossRef]
  9. Ch.-W.  Chen, Yu-K.  Hsu, J. Y.  Huang, and Ch.-Sh.  Chang, "Generation properties of coherent infrared radiation in the optical absorption region of GaSe crystal," Opt. Express 14, 10636-10644 (2006).
    [CrossRef] [PubMed]
  10. S.  Das, C.  Ghosh, O. G.  Voevodina, Yu. M.  Andreev, and S. Yu.  Sarkisov, "Modified GaSe crystal as a parametric frequency converter," Appl. Phys. B 82, 43-46 (2006).
    [CrossRef]
  11. Yu. M.  Andreev, V. V.  Atuchin, G. V.  Lanskii, A. N.  Morozov, L. D.  Pokrovsky, S. Yu.  Sarkisov, and O. V.  Voevodina, "Growth, real structure and applications of GaSe1-xSx crystals," Mater. Sci. Eng. B 128, 205-210 (2006).
    [CrossRef]
  12. G.  Saintonge and J. L.  Brebner, "Infrared spectra of GaxIn1-xSe," Can. J. Phys. 62, 730-736 (1984).
    [CrossRef]
  13. Yu. M.  Andreev, V. G.  Voevodin, A. I.  Gribenyukov, O. Ya.  Zyryanov, I. I.  Ippolitov, A. N.  Morozov, A. V.  Sosnin, and G. S.  Khmel???nitstskii, "An efficient generation of the tunable CO2 laser radiation second harmonic in ZnGeP2," Sov. J. Quant. Electr. 14, 1021-1022 (1984).
    [CrossRef]
  14. E.  Takaoka, and K.  Kato, "Temperature phase-matching properties for harmonic generation in GaSe," Jpn. J. Appl. Phys. 38, 2755-2759 (1999).
    [CrossRef]
  15. E.  Takaoka, and K.  Kato, "90° phase-matched third harmonic generation of CO2 laser frequencies in AgGa1-xInxSe2," Opt. Lett. 24, 902-904 (1999).
    [CrossRef]
  16. P. G.  Schunemann, S. D.  Setzler, and T. M.  Pollak, "Phase-matched crystal growth of AgGaSe2 and AgGa1-xInxSe2," J. Cryst. Growth 211, 257-264 (2000).
    [CrossRef]
  17. G. B.  Abdullaev, L. A.  Kulevskii, A. M.  Prokhorov, A. D.  Savel'ev, E. Yu.  Salaev, and V. V.  Smirnov, "GaSe, a new effective material for nonlinear optics," JETP Lett. 16, 90-92 (1972).
  18. G. B.  Abdullaev, K. R.  Allakhverdiev, L. A.  Kulevskii, A. M.  Prokhorov, E. Yu.  Salaev, A. D.  Savel???ev, and V. V.  Smirnov, "Parametric frequency conversion of IR radiation in GaSe crystal," Sov. J. Quant. Electr. 5, 665-668 (1975).
    [CrossRef]
  19. K. L.  Vodopyanov, and L. A.  Kulevskii, "New dispersion relationships for GaSe in the 0.65-18 ?m spectral region," Opt. Commun. 118, 375-378 (1995).
    [CrossRef]
  20. K. R.  Allakhverdiev, T.  Baykara, A.  Kulibekov Gulubayov, A. A.  Kaya, J.  Goldstein, N.  Fernelius, S.  Hanna, and Z.  Salaeva, "Corrected infrared Sellmeier coefficients for gallium selenide," J. Appl. Phys. 98, 093515-1-6 (2005).
    [CrossRef]
  21. D.  Errandonea, A.  Segura, V.  Munoz, and A.  Chevy, "Effects of pressure and temperature on the dielectric constant: Role of the electronic contribution," Phys. Rev. B 60, 15866-15874 (1999).
    [CrossRef]
  22. G.  Antonioli, D.  Bianchi, and P.  Franzosi, "Temperature variation of refractive index in GaSe," Appl. Opt. 18, 3847-3850 (1979).
    [PubMed]
  23. A. A.  Tikhomirov, Yu. M.  Andreev, G. V.  Lanskii, O. V.  Voevodina, S. Yu.  Sarkisov, "Doped GaSe nonlinear crystals," Proc. SPIE 6258, 64-72 (2006).
  24. D. W.  Fischer, and M. C.  Ohmer, "Temperature dependence of ZnGeP2 birefringence using polarized light interference," J. Appl. Phys. 81, 425-431 (1997).
    [CrossRef]

2006 (5)

S.  Das, C.  Ghosh, S.  Gangopadhyay, U.  Chatterjee, G. C.  Bhar, V. G.  Voevodin, and O. G.  Voevodina, "Tunable coherent infrared source from 5-16 ?m based on difference-frequency mixing in an indium-doped GaSe crystal," J. Opt. Soc. Am. B 23, 282-288 (2006).
[CrossRef]

Ch.-W.  Chen, Yu-K.  Hsu, J. Y.  Huang, and Ch.-Sh.  Chang, "Generation properties of coherent infrared radiation in the optical absorption region of GaSe crystal," Opt. Express 14, 10636-10644 (2006).
[CrossRef] [PubMed]

S.  Das, C.  Ghosh, O. G.  Voevodina, Yu. M.  Andreev, and S. Yu.  Sarkisov, "Modified GaSe crystal as a parametric frequency converter," Appl. Phys. B 82, 43-46 (2006).
[CrossRef]

Yu. M.  Andreev, V. V.  Atuchin, G. V.  Lanskii, A. N.  Morozov, L. D.  Pokrovsky, S. Yu.  Sarkisov, and O. V.  Voevodina, "Growth, real structure and applications of GaSe1-xSx crystals," Mater. Sci. Eng. B 128, 205-210 (2006).
[CrossRef]

A. A.  Tikhomirov, Yu. M.  Andreev, G. V.  Lanskii, O. V.  Voevodina, S. Yu.  Sarkisov, "Doped GaSe nonlinear crystals," Proc. SPIE 6258, 64-72 (2006).

2004 (2)

W.  Shi and Yu. J.  Ding, "A monochromatic and high-power terahertz source tunable in the ranges of 2.7-38.4 and 58.2-3540 ?m for variety of potential applications," Appl. Phys. Lett. 84, 1635-1637 (2004).
[CrossRef]

V. G.  Voevodin, O. V.  Voevodina, S. A.  Bereznaya, Z. V.  Korotchenko, A. N.  Morozov, S. Yu.  Sarkisov, N. C.  Fernelius, and J. T.  Goldstein, "Large single crystals of gallium selenide: growing, doping by In and characterization," Opt. Mater. 26, 495-499 (2004).
[CrossRef]

2000 (1)

P. G.  Schunemann, S. D.  Setzler, and T. M.  Pollak, "Phase-matched crystal growth of AgGaSe2 and AgGa1-xInxSe2," J. Cryst. Growth 211, 257-264 (2000).
[CrossRef]

1999 (4)

N. B.  Singh, D. R.  Suhre, W.  Rosch, R.  Meyer, M.  Marable, N. C.  Fernelius, F. K.  Hopkins, D. E.  Zelmon, and R.  Narayanan, "Modified GaSe crystals for mid-IR applications," J. Cryst. Growth 198, 588-592 (1999).
[CrossRef]

E.  Takaoka, and K.  Kato, "Temperature phase-matching properties for harmonic generation in GaSe," Jpn. J. Appl. Phys. 38, 2755-2759 (1999).
[CrossRef]

E.  Takaoka, and K.  Kato, "90° phase-matched third harmonic generation of CO2 laser frequencies in AgGa1-xInxSe2," Opt. Lett. 24, 902-904 (1999).
[CrossRef]

D.  Errandonea, A.  Segura, V.  Munoz, and A.  Chevy, "Effects of pressure and temperature on the dielectric constant: Role of the electronic contribution," Phys. Rev. B 60, 15866-15874 (1999).
[CrossRef]

1998 (1)

N. B.  Singh, D. R.  Suhre, V.  Balakrishna, M.  Marable, R.  Meyer, N.  Fernelius, F. K.  Hopkins, and D.  Zelmon, "Far-infrared conversion materials: Gallium selenide for far-infrared conversion applications," Prog. Cryst. Growth Charact. Mater. 37, 47-102 (1998).
[CrossRef]

1997 (3)

D. R.  Suhre, N. B.  Singh, V.  Balakrishna, N. C.  Fernelius, and F. K.  Hopkins, "Improved crystal quality and harmonic generation in GaSe doped with indium," Opt. Lett. 22, 775-777 (1997).
[CrossRef] [PubMed]

N. B.  Singh, R.  Narayanan, A. X.  Zhao, V.  Balakrishna, R. H.  Hopkins, D. R.  Suhre, N. C.  Fernelius, F. K.  Hopkins, and D. E.  Zelmon, "Bridgman growth of GaSe crystals for nonlinear optical applications," Mater. Sci. Eng. B 49, 243-246 (1997).
[CrossRef]

D. W.  Fischer, and M. C.  Ohmer, "Temperature dependence of ZnGeP2 birefringence using polarized light interference," J. Appl. Phys. 81, 425-431 (1997).
[CrossRef]

1995 (1)

K. L.  Vodopyanov, and L. A.  Kulevskii, "New dispersion relationships for GaSe in the 0.65-18 ?m spectral region," Opt. Commun. 118, 375-378 (1995).
[CrossRef]

1994 (1)

N. C.  Fernelius, "Properties of gallium selenide single crystal," Prog. Cryst. Growth Charact. 28, 275-353 (1994).
[CrossRef]

1984 (2)

G.  Saintonge and J. L.  Brebner, "Infrared spectra of GaxIn1-xSe," Can. J. Phys. 62, 730-736 (1984).
[CrossRef]

Yu. M.  Andreev, V. G.  Voevodin, A. I.  Gribenyukov, O. Ya.  Zyryanov, I. I.  Ippolitov, A. N.  Morozov, A. V.  Sosnin, and G. S.  Khmel???nitstskii, "An efficient generation of the tunable CO2 laser radiation second harmonic in ZnGeP2," Sov. J. Quant. Electr. 14, 1021-1022 (1984).
[CrossRef]

1979 (1)

1975 (1)

G. B.  Abdullaev, K. R.  Allakhverdiev, L. A.  Kulevskii, A. M.  Prokhorov, E. Yu.  Salaev, A. D.  Savel???ev, and V. V.  Smirnov, "Parametric frequency conversion of IR radiation in GaSe crystal," Sov. J. Quant. Electr. 5, 665-668 (1975).
[CrossRef]

1972 (1)

G. B.  Abdullaev, L. A.  Kulevskii, A. M.  Prokhorov, A. D.  Savel'ev, E. Yu.  Salaev, and V. V.  Smirnov, "GaSe, a new effective material for nonlinear optics," JETP Lett. 16, 90-92 (1972).

Abdullaev, G. B.

G. B.  Abdullaev, K. R.  Allakhverdiev, L. A.  Kulevskii, A. M.  Prokhorov, E. Yu.  Salaev, A. D.  Savel???ev, and V. V.  Smirnov, "Parametric frequency conversion of IR radiation in GaSe crystal," Sov. J. Quant. Electr. 5, 665-668 (1975).
[CrossRef]

G. B.  Abdullaev, L. A.  Kulevskii, A. M.  Prokhorov, A. D.  Savel'ev, E. Yu.  Salaev, and V. V.  Smirnov, "GaSe, a new effective material for nonlinear optics," JETP Lett. 16, 90-92 (1972).

Allakhverdiev, K. R.

G. B.  Abdullaev, K. R.  Allakhverdiev, L. A.  Kulevskii, A. M.  Prokhorov, E. Yu.  Salaev, A. D.  Savel???ev, and V. V.  Smirnov, "Parametric frequency conversion of IR radiation in GaSe crystal," Sov. J. Quant. Electr. 5, 665-668 (1975).
[CrossRef]

K. R.  Allakhverdiev, T.  Baykara, A.  Kulibekov Gulubayov, A. A.  Kaya, J.  Goldstein, N.  Fernelius, S.  Hanna, and Z.  Salaeva, "Corrected infrared Sellmeier coefficients for gallium selenide," J. Appl. Phys. 98, 093515-1-6 (2005).
[CrossRef]

Andreev, Yu. M.

S.  Das, C.  Ghosh, O. G.  Voevodina, Yu. M.  Andreev, and S. Yu.  Sarkisov, "Modified GaSe crystal as a parametric frequency converter," Appl. Phys. B 82, 43-46 (2006).
[CrossRef]

Yu. M.  Andreev, V. V.  Atuchin, G. V.  Lanskii, A. N.  Morozov, L. D.  Pokrovsky, S. Yu.  Sarkisov, and O. V.  Voevodina, "Growth, real structure and applications of GaSe1-xSx crystals," Mater. Sci. Eng. B 128, 205-210 (2006).
[CrossRef]

A. A.  Tikhomirov, Yu. M.  Andreev, G. V.  Lanskii, O. V.  Voevodina, S. Yu.  Sarkisov, "Doped GaSe nonlinear crystals," Proc. SPIE 6258, 64-72 (2006).

Yu. M.  Andreev, V. G.  Voevodin, A. I.  Gribenyukov, O. Ya.  Zyryanov, I. I.  Ippolitov, A. N.  Morozov, A. V.  Sosnin, and G. S.  Khmel???nitstskii, "An efficient generation of the tunable CO2 laser radiation second harmonic in ZnGeP2," Sov. J. Quant. Electr. 14, 1021-1022 (1984).
[CrossRef]

Antonioli, G.

Atuchin, V. V.

Yu. M.  Andreev, V. V.  Atuchin, G. V.  Lanskii, A. N.  Morozov, L. D.  Pokrovsky, S. Yu.  Sarkisov, and O. V.  Voevodina, "Growth, real structure and applications of GaSe1-xSx crystals," Mater. Sci. Eng. B 128, 205-210 (2006).
[CrossRef]

Balakrishna, V.

N. B.  Singh, D. R.  Suhre, V.  Balakrishna, M.  Marable, R.  Meyer, N.  Fernelius, F. K.  Hopkins, and D.  Zelmon, "Far-infrared conversion materials: Gallium selenide for far-infrared conversion applications," Prog. Cryst. Growth Charact. Mater. 37, 47-102 (1998).
[CrossRef]

N. B.  Singh, R.  Narayanan, A. X.  Zhao, V.  Balakrishna, R. H.  Hopkins, D. R.  Suhre, N. C.  Fernelius, F. K.  Hopkins, and D. E.  Zelmon, "Bridgman growth of GaSe crystals for nonlinear optical applications," Mater. Sci. Eng. B 49, 243-246 (1997).
[CrossRef]

D. R.  Suhre, N. B.  Singh, V.  Balakrishna, N. C.  Fernelius, and F. K.  Hopkins, "Improved crystal quality and harmonic generation in GaSe doped with indium," Opt. Lett. 22, 775-777 (1997).
[CrossRef] [PubMed]

Baykara, T.

K. R.  Allakhverdiev, T.  Baykara, A.  Kulibekov Gulubayov, A. A.  Kaya, J.  Goldstein, N.  Fernelius, S.  Hanna, and Z.  Salaeva, "Corrected infrared Sellmeier coefficients for gallium selenide," J. Appl. Phys. 98, 093515-1-6 (2005).
[CrossRef]

Bereznaya, S. A.

V. G.  Voevodin, O. V.  Voevodina, S. A.  Bereznaya, Z. V.  Korotchenko, A. N.  Morozov, S. Yu.  Sarkisov, N. C.  Fernelius, and J. T.  Goldstein, "Large single crystals of gallium selenide: growing, doping by In and characterization," Opt. Mater. 26, 495-499 (2004).
[CrossRef]

Bhar, G. C.

Bianchi, D.

Brebner, J. L.

G.  Saintonge and J. L.  Brebner, "Infrared spectra of GaxIn1-xSe," Can. J. Phys. 62, 730-736 (1984).
[CrossRef]

Chang, Ch.-Sh.

Chatterjee, U.

Chen, Ch.-W.

Chevy, A.

D.  Errandonea, A.  Segura, V.  Munoz, and A.  Chevy, "Effects of pressure and temperature on the dielectric constant: Role of the electronic contribution," Phys. Rev. B 60, 15866-15874 (1999).
[CrossRef]

Das, S.

Ding, Yu. J.

W.  Shi and Yu. J.  Ding, "A monochromatic and high-power terahertz source tunable in the ranges of 2.7-38.4 and 58.2-3540 ?m for variety of potential applications," Appl. Phys. Lett. 84, 1635-1637 (2004).
[CrossRef]

Errandonea, D.

D.  Errandonea, A.  Segura, V.  Munoz, and A.  Chevy, "Effects of pressure and temperature on the dielectric constant: Role of the electronic contribution," Phys. Rev. B 60, 15866-15874 (1999).
[CrossRef]

Fernelius, N.

N. B.  Singh, D. R.  Suhre, V.  Balakrishna, M.  Marable, R.  Meyer, N.  Fernelius, F. K.  Hopkins, and D.  Zelmon, "Far-infrared conversion materials: Gallium selenide for far-infrared conversion applications," Prog. Cryst. Growth Charact. Mater. 37, 47-102 (1998).
[CrossRef]

K. R.  Allakhverdiev, T.  Baykara, A.  Kulibekov Gulubayov, A. A.  Kaya, J.  Goldstein, N.  Fernelius, S.  Hanna, and Z.  Salaeva, "Corrected infrared Sellmeier coefficients for gallium selenide," J. Appl. Phys. 98, 093515-1-6 (2005).
[CrossRef]

Fernelius, N. C.

V. G.  Voevodin, O. V.  Voevodina, S. A.  Bereznaya, Z. V.  Korotchenko, A. N.  Morozov, S. Yu.  Sarkisov, N. C.  Fernelius, and J. T.  Goldstein, "Large single crystals of gallium selenide: growing, doping by In and characterization," Opt. Mater. 26, 495-499 (2004).
[CrossRef]

N. B.  Singh, D. R.  Suhre, W.  Rosch, R.  Meyer, M.  Marable, N. C.  Fernelius, F. K.  Hopkins, D. E.  Zelmon, and R.  Narayanan, "Modified GaSe crystals for mid-IR applications," J. Cryst. Growth 198, 588-592 (1999).
[CrossRef]

N. B.  Singh, R.  Narayanan, A. X.  Zhao, V.  Balakrishna, R. H.  Hopkins, D. R.  Suhre, N. C.  Fernelius, F. K.  Hopkins, and D. E.  Zelmon, "Bridgman growth of GaSe crystals for nonlinear optical applications," Mater. Sci. Eng. B 49, 243-246 (1997).
[CrossRef]

D. R.  Suhre, N. B.  Singh, V.  Balakrishna, N. C.  Fernelius, and F. K.  Hopkins, "Improved crystal quality and harmonic generation in GaSe doped with indium," Opt. Lett. 22, 775-777 (1997).
[CrossRef] [PubMed]

N. C.  Fernelius, "Properties of gallium selenide single crystal," Prog. Cryst. Growth Charact. 28, 275-353 (1994).
[CrossRef]

Fischer, D. W.

D. W.  Fischer, and M. C.  Ohmer, "Temperature dependence of ZnGeP2 birefringence using polarized light interference," J. Appl. Phys. 81, 425-431 (1997).
[CrossRef]

Franzosi, P.

Gangopadhyay, S.

Ghosh, C.

Goldstein, J.

K. R.  Allakhverdiev, T.  Baykara, A.  Kulibekov Gulubayov, A. A.  Kaya, J.  Goldstein, N.  Fernelius, S.  Hanna, and Z.  Salaeva, "Corrected infrared Sellmeier coefficients for gallium selenide," J. Appl. Phys. 98, 093515-1-6 (2005).
[CrossRef]

Goldstein, J. T.

V. G.  Voevodin, O. V.  Voevodina, S. A.  Bereznaya, Z. V.  Korotchenko, A. N.  Morozov, S. Yu.  Sarkisov, N. C.  Fernelius, and J. T.  Goldstein, "Large single crystals of gallium selenide: growing, doping by In and characterization," Opt. Mater. 26, 495-499 (2004).
[CrossRef]

Gribenyukov, A. I.

Yu. M.  Andreev, V. G.  Voevodin, A. I.  Gribenyukov, O. Ya.  Zyryanov, I. I.  Ippolitov, A. N.  Morozov, A. V.  Sosnin, and G. S.  Khmel???nitstskii, "An efficient generation of the tunable CO2 laser radiation second harmonic in ZnGeP2," Sov. J. Quant. Electr. 14, 1021-1022 (1984).
[CrossRef]

Hanna, S.

K. R.  Allakhverdiev, T.  Baykara, A.  Kulibekov Gulubayov, A. A.  Kaya, J.  Goldstein, N.  Fernelius, S.  Hanna, and Z.  Salaeva, "Corrected infrared Sellmeier coefficients for gallium selenide," J. Appl. Phys. 98, 093515-1-6 (2005).
[CrossRef]

Hopkins, F. K.

N. B.  Singh, D. R.  Suhre, W.  Rosch, R.  Meyer, M.  Marable, N. C.  Fernelius, F. K.  Hopkins, D. E.  Zelmon, and R.  Narayanan, "Modified GaSe crystals for mid-IR applications," J. Cryst. Growth 198, 588-592 (1999).
[CrossRef]

N. B.  Singh, D. R.  Suhre, V.  Balakrishna, M.  Marable, R.  Meyer, N.  Fernelius, F. K.  Hopkins, and D.  Zelmon, "Far-infrared conversion materials: Gallium selenide for far-infrared conversion applications," Prog. Cryst. Growth Charact. Mater. 37, 47-102 (1998).
[CrossRef]

N. B.  Singh, R.  Narayanan, A. X.  Zhao, V.  Balakrishna, R. H.  Hopkins, D. R.  Suhre, N. C.  Fernelius, F. K.  Hopkins, and D. E.  Zelmon, "Bridgman growth of GaSe crystals for nonlinear optical applications," Mater. Sci. Eng. B 49, 243-246 (1997).
[CrossRef]

D. R.  Suhre, N. B.  Singh, V.  Balakrishna, N. C.  Fernelius, and F. K.  Hopkins, "Improved crystal quality and harmonic generation in GaSe doped with indium," Opt. Lett. 22, 775-777 (1997).
[CrossRef] [PubMed]

Hopkins, R. H.

N. B.  Singh, R.  Narayanan, A. X.  Zhao, V.  Balakrishna, R. H.  Hopkins, D. R.  Suhre, N. C.  Fernelius, F. K.  Hopkins, and D. E.  Zelmon, "Bridgman growth of GaSe crystals for nonlinear optical applications," Mater. Sci. Eng. B 49, 243-246 (1997).
[CrossRef]

Hsu, Yu-K.

Huang, J. Y.

Ippolitov, I. I.

Yu. M.  Andreev, V. G.  Voevodin, A. I.  Gribenyukov, O. Ya.  Zyryanov, I. I.  Ippolitov, A. N.  Morozov, A. V.  Sosnin, and G. S.  Khmel???nitstskii, "An efficient generation of the tunable CO2 laser radiation second harmonic in ZnGeP2," Sov. J. Quant. Electr. 14, 1021-1022 (1984).
[CrossRef]

Kato, K.

E.  Takaoka, and K.  Kato, "Temperature phase-matching properties for harmonic generation in GaSe," Jpn. J. Appl. Phys. 38, 2755-2759 (1999).
[CrossRef]

E.  Takaoka, and K.  Kato, "90° phase-matched third harmonic generation of CO2 laser frequencies in AgGa1-xInxSe2," Opt. Lett. 24, 902-904 (1999).
[CrossRef]

Kaya, A. A.

K. R.  Allakhverdiev, T.  Baykara, A.  Kulibekov Gulubayov, A. A.  Kaya, J.  Goldstein, N.  Fernelius, S.  Hanna, and Z.  Salaeva, "Corrected infrared Sellmeier coefficients for gallium selenide," J. Appl. Phys. 98, 093515-1-6 (2005).
[CrossRef]

Khmel???nitstskii, G. S.

Yu. M.  Andreev, V. G.  Voevodin, A. I.  Gribenyukov, O. Ya.  Zyryanov, I. I.  Ippolitov, A. N.  Morozov, A. V.  Sosnin, and G. S.  Khmel???nitstskii, "An efficient generation of the tunable CO2 laser radiation second harmonic in ZnGeP2," Sov. J. Quant. Electr. 14, 1021-1022 (1984).
[CrossRef]

Korotchenko, Z. V.

V. G.  Voevodin, O. V.  Voevodina, S. A.  Bereznaya, Z. V.  Korotchenko, A. N.  Morozov, S. Yu.  Sarkisov, N. C.  Fernelius, and J. T.  Goldstein, "Large single crystals of gallium selenide: growing, doping by In and characterization," Opt. Mater. 26, 495-499 (2004).
[CrossRef]

Kulevskii, L. A.

K. L.  Vodopyanov, and L. A.  Kulevskii, "New dispersion relationships for GaSe in the 0.65-18 ?m spectral region," Opt. Commun. 118, 375-378 (1995).
[CrossRef]

G. B.  Abdullaev, K. R.  Allakhverdiev, L. A.  Kulevskii, A. M.  Prokhorov, E. Yu.  Salaev, A. D.  Savel???ev, and V. V.  Smirnov, "Parametric frequency conversion of IR radiation in GaSe crystal," Sov. J. Quant. Electr. 5, 665-668 (1975).
[CrossRef]

G. B.  Abdullaev, L. A.  Kulevskii, A. M.  Prokhorov, A. D.  Savel'ev, E. Yu.  Salaev, and V. V.  Smirnov, "GaSe, a new effective material for nonlinear optics," JETP Lett. 16, 90-92 (1972).

Kulibekov Gulubayov, A.

K. R.  Allakhverdiev, T.  Baykara, A.  Kulibekov Gulubayov, A. A.  Kaya, J.  Goldstein, N.  Fernelius, S.  Hanna, and Z.  Salaeva, "Corrected infrared Sellmeier coefficients for gallium selenide," J. Appl. Phys. 98, 093515-1-6 (2005).
[CrossRef]

Lanskii, G. V.

Yu. M.  Andreev, V. V.  Atuchin, G. V.  Lanskii, A. N.  Morozov, L. D.  Pokrovsky, S. Yu.  Sarkisov, and O. V.  Voevodina, "Growth, real structure and applications of GaSe1-xSx crystals," Mater. Sci. Eng. B 128, 205-210 (2006).
[CrossRef]

A. A.  Tikhomirov, Yu. M.  Andreev, G. V.  Lanskii, O. V.  Voevodina, S. Yu.  Sarkisov, "Doped GaSe nonlinear crystals," Proc. SPIE 6258, 64-72 (2006).

Marable, M.

N. B.  Singh, D. R.  Suhre, W.  Rosch, R.  Meyer, M.  Marable, N. C.  Fernelius, F. K.  Hopkins, D. E.  Zelmon, and R.  Narayanan, "Modified GaSe crystals for mid-IR applications," J. Cryst. Growth 198, 588-592 (1999).
[CrossRef]

N. B.  Singh, D. R.  Suhre, V.  Balakrishna, M.  Marable, R.  Meyer, N.  Fernelius, F. K.  Hopkins, and D.  Zelmon, "Far-infrared conversion materials: Gallium selenide for far-infrared conversion applications," Prog. Cryst. Growth Charact. Mater. 37, 47-102 (1998).
[CrossRef]

Meyer, R.

N. B.  Singh, D. R.  Suhre, W.  Rosch, R.  Meyer, M.  Marable, N. C.  Fernelius, F. K.  Hopkins, D. E.  Zelmon, and R.  Narayanan, "Modified GaSe crystals for mid-IR applications," J. Cryst. Growth 198, 588-592 (1999).
[CrossRef]

N. B.  Singh, D. R.  Suhre, V.  Balakrishna, M.  Marable, R.  Meyer, N.  Fernelius, F. K.  Hopkins, and D.  Zelmon, "Far-infrared conversion materials: Gallium selenide for far-infrared conversion applications," Prog. Cryst. Growth Charact. Mater. 37, 47-102 (1998).
[CrossRef]

Morozov, A. N.

Yu. M.  Andreev, V. V.  Atuchin, G. V.  Lanskii, A. N.  Morozov, L. D.  Pokrovsky, S. Yu.  Sarkisov, and O. V.  Voevodina, "Growth, real structure and applications of GaSe1-xSx crystals," Mater. Sci. Eng. B 128, 205-210 (2006).
[CrossRef]

V. G.  Voevodin, O. V.  Voevodina, S. A.  Bereznaya, Z. V.  Korotchenko, A. N.  Morozov, S. Yu.  Sarkisov, N. C.  Fernelius, and J. T.  Goldstein, "Large single crystals of gallium selenide: growing, doping by In and characterization," Opt. Mater. 26, 495-499 (2004).
[CrossRef]

Yu. M.  Andreev, V. G.  Voevodin, A. I.  Gribenyukov, O. Ya.  Zyryanov, I. I.  Ippolitov, A. N.  Morozov, A. V.  Sosnin, and G. S.  Khmel???nitstskii, "An efficient generation of the tunable CO2 laser radiation second harmonic in ZnGeP2," Sov. J. Quant. Electr. 14, 1021-1022 (1984).
[CrossRef]

Munoz, V.

D.  Errandonea, A.  Segura, V.  Munoz, and A.  Chevy, "Effects of pressure and temperature on the dielectric constant: Role of the electronic contribution," Phys. Rev. B 60, 15866-15874 (1999).
[CrossRef]

Narayanan, R.

N. B.  Singh, D. R.  Suhre, W.  Rosch, R.  Meyer, M.  Marable, N. C.  Fernelius, F. K.  Hopkins, D. E.  Zelmon, and R.  Narayanan, "Modified GaSe crystals for mid-IR applications," J. Cryst. Growth 198, 588-592 (1999).
[CrossRef]

N. B.  Singh, R.  Narayanan, A. X.  Zhao, V.  Balakrishna, R. H.  Hopkins, D. R.  Suhre, N. C.  Fernelius, F. K.  Hopkins, and D. E.  Zelmon, "Bridgman growth of GaSe crystals for nonlinear optical applications," Mater. Sci. Eng. B 49, 243-246 (1997).
[CrossRef]

Ohmer, M. C.

D. W.  Fischer, and M. C.  Ohmer, "Temperature dependence of ZnGeP2 birefringence using polarized light interference," J. Appl. Phys. 81, 425-431 (1997).
[CrossRef]

Pokrovsky, L. D.

Yu. M.  Andreev, V. V.  Atuchin, G. V.  Lanskii, A. N.  Morozov, L. D.  Pokrovsky, S. Yu.  Sarkisov, and O. V.  Voevodina, "Growth, real structure and applications of GaSe1-xSx crystals," Mater. Sci. Eng. B 128, 205-210 (2006).
[CrossRef]

Pollak, T. M.

P. G.  Schunemann, S. D.  Setzler, and T. M.  Pollak, "Phase-matched crystal growth of AgGaSe2 and AgGa1-xInxSe2," J. Cryst. Growth 211, 257-264 (2000).
[CrossRef]

Prokhorov, A. M.

G. B.  Abdullaev, K. R.  Allakhverdiev, L. A.  Kulevskii, A. M.  Prokhorov, E. Yu.  Salaev, A. D.  Savel???ev, and V. V.  Smirnov, "Parametric frequency conversion of IR radiation in GaSe crystal," Sov. J. Quant. Electr. 5, 665-668 (1975).
[CrossRef]

G. B.  Abdullaev, L. A.  Kulevskii, A. M.  Prokhorov, A. D.  Savel'ev, E. Yu.  Salaev, and V. V.  Smirnov, "GaSe, a new effective material for nonlinear optics," JETP Lett. 16, 90-92 (1972).

Rosch, W.

N. B.  Singh, D. R.  Suhre, W.  Rosch, R.  Meyer, M.  Marable, N. C.  Fernelius, F. K.  Hopkins, D. E.  Zelmon, and R.  Narayanan, "Modified GaSe crystals for mid-IR applications," J. Cryst. Growth 198, 588-592 (1999).
[CrossRef]

Saintonge, G.

G.  Saintonge and J. L.  Brebner, "Infrared spectra of GaxIn1-xSe," Can. J. Phys. 62, 730-736 (1984).
[CrossRef]

Salaev, E. Yu.

G. B.  Abdullaev, K. R.  Allakhverdiev, L. A.  Kulevskii, A. M.  Prokhorov, E. Yu.  Salaev, A. D.  Savel???ev, and V. V.  Smirnov, "Parametric frequency conversion of IR radiation in GaSe crystal," Sov. J. Quant. Electr. 5, 665-668 (1975).
[CrossRef]

G. B.  Abdullaev, L. A.  Kulevskii, A. M.  Prokhorov, A. D.  Savel'ev, E. Yu.  Salaev, and V. V.  Smirnov, "GaSe, a new effective material for nonlinear optics," JETP Lett. 16, 90-92 (1972).

Salaeva, Z.

K. R.  Allakhverdiev, T.  Baykara, A.  Kulibekov Gulubayov, A. A.  Kaya, J.  Goldstein, N.  Fernelius, S.  Hanna, and Z.  Salaeva, "Corrected infrared Sellmeier coefficients for gallium selenide," J. Appl. Phys. 98, 093515-1-6 (2005).
[CrossRef]

Sarkisov, S. Yu.

Yu. M.  Andreev, V. V.  Atuchin, G. V.  Lanskii, A. N.  Morozov, L. D.  Pokrovsky, S. Yu.  Sarkisov, and O. V.  Voevodina, "Growth, real structure and applications of GaSe1-xSx crystals," Mater. Sci. Eng. B 128, 205-210 (2006).
[CrossRef]

S.  Das, C.  Ghosh, O. G.  Voevodina, Yu. M.  Andreev, and S. Yu.  Sarkisov, "Modified GaSe crystal as a parametric frequency converter," Appl. Phys. B 82, 43-46 (2006).
[CrossRef]

A. A.  Tikhomirov, Yu. M.  Andreev, G. V.  Lanskii, O. V.  Voevodina, S. Yu.  Sarkisov, "Doped GaSe nonlinear crystals," Proc. SPIE 6258, 64-72 (2006).

V. G.  Voevodin, O. V.  Voevodina, S. A.  Bereznaya, Z. V.  Korotchenko, A. N.  Morozov, S. Yu.  Sarkisov, N. C.  Fernelius, and J. T.  Goldstein, "Large single crystals of gallium selenide: growing, doping by In and characterization," Opt. Mater. 26, 495-499 (2004).
[CrossRef]

Savel???ev, A. D.

G. B.  Abdullaev, K. R.  Allakhverdiev, L. A.  Kulevskii, A. M.  Prokhorov, E. Yu.  Salaev, A. D.  Savel???ev, and V. V.  Smirnov, "Parametric frequency conversion of IR radiation in GaSe crystal," Sov. J. Quant. Electr. 5, 665-668 (1975).
[CrossRef]

Savel'ev, A. D.

G. B.  Abdullaev, L. A.  Kulevskii, A. M.  Prokhorov, A. D.  Savel'ev, E. Yu.  Salaev, and V. V.  Smirnov, "GaSe, a new effective material for nonlinear optics," JETP Lett. 16, 90-92 (1972).

Schunemann, P. G.

P. G.  Schunemann, S. D.  Setzler, and T. M.  Pollak, "Phase-matched crystal growth of AgGaSe2 and AgGa1-xInxSe2," J. Cryst. Growth 211, 257-264 (2000).
[CrossRef]

Segura, A.

D.  Errandonea, A.  Segura, V.  Munoz, and A.  Chevy, "Effects of pressure and temperature on the dielectric constant: Role of the electronic contribution," Phys. Rev. B 60, 15866-15874 (1999).
[CrossRef]

Setzler, S. D.

P. G.  Schunemann, S. D.  Setzler, and T. M.  Pollak, "Phase-matched crystal growth of AgGaSe2 and AgGa1-xInxSe2," J. Cryst. Growth 211, 257-264 (2000).
[CrossRef]

Shi, W.

W.  Shi and Yu. J.  Ding, "A monochromatic and high-power terahertz source tunable in the ranges of 2.7-38.4 and 58.2-3540 ?m for variety of potential applications," Appl. Phys. Lett. 84, 1635-1637 (2004).
[CrossRef]

Singh, N. B.

N. B.  Singh, D. R.  Suhre, W.  Rosch, R.  Meyer, M.  Marable, N. C.  Fernelius, F. K.  Hopkins, D. E.  Zelmon, and R.  Narayanan, "Modified GaSe crystals for mid-IR applications," J. Cryst. Growth 198, 588-592 (1999).
[CrossRef]

N. B.  Singh, D. R.  Suhre, V.  Balakrishna, M.  Marable, R.  Meyer, N.  Fernelius, F. K.  Hopkins, and D.  Zelmon, "Far-infrared conversion materials: Gallium selenide for far-infrared conversion applications," Prog. Cryst. Growth Charact. Mater. 37, 47-102 (1998).
[CrossRef]

N. B.  Singh, R.  Narayanan, A. X.  Zhao, V.  Balakrishna, R. H.  Hopkins, D. R.  Suhre, N. C.  Fernelius, F. K.  Hopkins, and D. E.  Zelmon, "Bridgman growth of GaSe crystals for nonlinear optical applications," Mater. Sci. Eng. B 49, 243-246 (1997).
[CrossRef]

D. R.  Suhre, N. B.  Singh, V.  Balakrishna, N. C.  Fernelius, and F. K.  Hopkins, "Improved crystal quality and harmonic generation in GaSe doped with indium," Opt. Lett. 22, 775-777 (1997).
[CrossRef] [PubMed]

Smirnov, V. V.

G. B.  Abdullaev, K. R.  Allakhverdiev, L. A.  Kulevskii, A. M.  Prokhorov, E. Yu.  Salaev, A. D.  Savel???ev, and V. V.  Smirnov, "Parametric frequency conversion of IR radiation in GaSe crystal," Sov. J. Quant. Electr. 5, 665-668 (1975).
[CrossRef]

G. B.  Abdullaev, L. A.  Kulevskii, A. M.  Prokhorov, A. D.  Savel'ev, E. Yu.  Salaev, and V. V.  Smirnov, "GaSe, a new effective material for nonlinear optics," JETP Lett. 16, 90-92 (1972).

Sosnin, A. V.

Yu. M.  Andreev, V. G.  Voevodin, A. I.  Gribenyukov, O. Ya.  Zyryanov, I. I.  Ippolitov, A. N.  Morozov, A. V.  Sosnin, and G. S.  Khmel???nitstskii, "An efficient generation of the tunable CO2 laser radiation second harmonic in ZnGeP2," Sov. J. Quant. Electr. 14, 1021-1022 (1984).
[CrossRef]

Suhre, D. R.

N. B.  Singh, D. R.  Suhre, W.  Rosch, R.  Meyer, M.  Marable, N. C.  Fernelius, F. K.  Hopkins, D. E.  Zelmon, and R.  Narayanan, "Modified GaSe crystals for mid-IR applications," J. Cryst. Growth 198, 588-592 (1999).
[CrossRef]

N. B.  Singh, D. R.  Suhre, V.  Balakrishna, M.  Marable, R.  Meyer, N.  Fernelius, F. K.  Hopkins, and D.  Zelmon, "Far-infrared conversion materials: Gallium selenide for far-infrared conversion applications," Prog. Cryst. Growth Charact. Mater. 37, 47-102 (1998).
[CrossRef]

N. B.  Singh, R.  Narayanan, A. X.  Zhao, V.  Balakrishna, R. H.  Hopkins, D. R.  Suhre, N. C.  Fernelius, F. K.  Hopkins, and D. E.  Zelmon, "Bridgman growth of GaSe crystals for nonlinear optical applications," Mater. Sci. Eng. B 49, 243-246 (1997).
[CrossRef]

D. R.  Suhre, N. B.  Singh, V.  Balakrishna, N. C.  Fernelius, and F. K.  Hopkins, "Improved crystal quality and harmonic generation in GaSe doped with indium," Opt. Lett. 22, 775-777 (1997).
[CrossRef] [PubMed]

Takaoka, E.

E.  Takaoka, and K.  Kato, "90° phase-matched third harmonic generation of CO2 laser frequencies in AgGa1-xInxSe2," Opt. Lett. 24, 902-904 (1999).
[CrossRef]

E.  Takaoka, and K.  Kato, "Temperature phase-matching properties for harmonic generation in GaSe," Jpn. J. Appl. Phys. 38, 2755-2759 (1999).
[CrossRef]

Tikhomirov, A. A.

A. A.  Tikhomirov, Yu. M.  Andreev, G. V.  Lanskii, O. V.  Voevodina, S. Yu.  Sarkisov, "Doped GaSe nonlinear crystals," Proc. SPIE 6258, 64-72 (2006).

Vodopyanov, K. L.

K. L.  Vodopyanov, and L. A.  Kulevskii, "New dispersion relationships for GaSe in the 0.65-18 ?m spectral region," Opt. Commun. 118, 375-378 (1995).
[CrossRef]

Voevodin, V. G.

S.  Das, C.  Ghosh, S.  Gangopadhyay, U.  Chatterjee, G. C.  Bhar, V. G.  Voevodin, and O. G.  Voevodina, "Tunable coherent infrared source from 5-16 ?m based on difference-frequency mixing in an indium-doped GaSe crystal," J. Opt. Soc. Am. B 23, 282-288 (2006).
[CrossRef]

V. G.  Voevodin, O. V.  Voevodina, S. A.  Bereznaya, Z. V.  Korotchenko, A. N.  Morozov, S. Yu.  Sarkisov, N. C.  Fernelius, and J. T.  Goldstein, "Large single crystals of gallium selenide: growing, doping by In and characterization," Opt. Mater. 26, 495-499 (2004).
[CrossRef]

Yu. M.  Andreev, V. G.  Voevodin, A. I.  Gribenyukov, O. Ya.  Zyryanov, I. I.  Ippolitov, A. N.  Morozov, A. V.  Sosnin, and G. S.  Khmel???nitstskii, "An efficient generation of the tunable CO2 laser radiation second harmonic in ZnGeP2," Sov. J. Quant. Electr. 14, 1021-1022 (1984).
[CrossRef]

Voevodina, O. G.

Voevodina, O. V.

Yu. M.  Andreev, V. V.  Atuchin, G. V.  Lanskii, A. N.  Morozov, L. D.  Pokrovsky, S. Yu.  Sarkisov, and O. V.  Voevodina, "Growth, real structure and applications of GaSe1-xSx crystals," Mater. Sci. Eng. B 128, 205-210 (2006).
[CrossRef]

A. A.  Tikhomirov, Yu. M.  Andreev, G. V.  Lanskii, O. V.  Voevodina, S. Yu.  Sarkisov, "Doped GaSe nonlinear crystals," Proc. SPIE 6258, 64-72 (2006).

V. G.  Voevodin, O. V.  Voevodina, S. A.  Bereznaya, Z. V.  Korotchenko, A. N.  Morozov, S. Yu.  Sarkisov, N. C.  Fernelius, and J. T.  Goldstein, "Large single crystals of gallium selenide: growing, doping by In and characterization," Opt. Mater. 26, 495-499 (2004).
[CrossRef]

Zelmon, D.

N. B.  Singh, D. R.  Suhre, V.  Balakrishna, M.  Marable, R.  Meyer, N.  Fernelius, F. K.  Hopkins, and D.  Zelmon, "Far-infrared conversion materials: Gallium selenide for far-infrared conversion applications," Prog. Cryst. Growth Charact. Mater. 37, 47-102 (1998).
[CrossRef]

Zelmon, D. E.

N. B.  Singh, D. R.  Suhre, W.  Rosch, R.  Meyer, M.  Marable, N. C.  Fernelius, F. K.  Hopkins, D. E.  Zelmon, and R.  Narayanan, "Modified GaSe crystals for mid-IR applications," J. Cryst. Growth 198, 588-592 (1999).
[CrossRef]

N. B.  Singh, R.  Narayanan, A. X.  Zhao, V.  Balakrishna, R. H.  Hopkins, D. R.  Suhre, N. C.  Fernelius, F. K.  Hopkins, and D. E.  Zelmon, "Bridgman growth of GaSe crystals for nonlinear optical applications," Mater. Sci. Eng. B 49, 243-246 (1997).
[CrossRef]

Zhao, A. X.

N. B.  Singh, R.  Narayanan, A. X.  Zhao, V.  Balakrishna, R. H.  Hopkins, D. R.  Suhre, N. C.  Fernelius, F. K.  Hopkins, and D. E.  Zelmon, "Bridgman growth of GaSe crystals for nonlinear optical applications," Mater. Sci. Eng. B 49, 243-246 (1997).
[CrossRef]

Zyryanov, O. Ya.

Yu. M.  Andreev, V. G.  Voevodin, A. I.  Gribenyukov, O. Ya.  Zyryanov, I. I.  Ippolitov, A. N.  Morozov, A. V.  Sosnin, and G. S.  Khmel???nitstskii, "An efficient generation of the tunable CO2 laser radiation second harmonic in ZnGeP2," Sov. J. Quant. Electr. 14, 1021-1022 (1984).
[CrossRef]

Appl. Opt. (1)

Appl. Phys. B (1)

S.  Das, C.  Ghosh, O. G.  Voevodina, Yu. M.  Andreev, and S. Yu.  Sarkisov, "Modified GaSe crystal as a parametric frequency converter," Appl. Phys. B 82, 43-46 (2006).
[CrossRef]

Appl. Phys. Lett. (1)

W.  Shi and Yu. J.  Ding, "A monochromatic and high-power terahertz source tunable in the ranges of 2.7-38.4 and 58.2-3540 ?m for variety of potential applications," Appl. Phys. Lett. 84, 1635-1637 (2004).
[CrossRef]

Can. J. Phys. (1)

G.  Saintonge and J. L.  Brebner, "Infrared spectra of GaxIn1-xSe," Can. J. Phys. 62, 730-736 (1984).
[CrossRef]

J. Appl. Phys. (1)

D. W.  Fischer, and M. C.  Ohmer, "Temperature dependence of ZnGeP2 birefringence using polarized light interference," J. Appl. Phys. 81, 425-431 (1997).
[CrossRef]

J. Cryst. Growth (2)

P. G.  Schunemann, S. D.  Setzler, and T. M.  Pollak, "Phase-matched crystal growth of AgGaSe2 and AgGa1-xInxSe2," J. Cryst. Growth 211, 257-264 (2000).
[CrossRef]

N. B.  Singh, D. R.  Suhre, W.  Rosch, R.  Meyer, M.  Marable, N. C.  Fernelius, F. K.  Hopkins, D. E.  Zelmon, and R.  Narayanan, "Modified GaSe crystals for mid-IR applications," J. Cryst. Growth 198, 588-592 (1999).
[CrossRef]

J. Opt. Soc. Am. B (1)

JETP Lett. (1)

G. B.  Abdullaev, L. A.  Kulevskii, A. M.  Prokhorov, A. D.  Savel'ev, E. Yu.  Salaev, and V. V.  Smirnov, "GaSe, a new effective material for nonlinear optics," JETP Lett. 16, 90-92 (1972).

Jpn. J. Appl. Phys. (1)

E.  Takaoka, and K.  Kato, "Temperature phase-matching properties for harmonic generation in GaSe," Jpn. J. Appl. Phys. 38, 2755-2759 (1999).
[CrossRef]

Mater. Sci. Eng. B (2)

Yu. M.  Andreev, V. V.  Atuchin, G. V.  Lanskii, A. N.  Morozov, L. D.  Pokrovsky, S. Yu.  Sarkisov, and O. V.  Voevodina, "Growth, real structure and applications of GaSe1-xSx crystals," Mater. Sci. Eng. B 128, 205-210 (2006).
[CrossRef]

N. B.  Singh, R.  Narayanan, A. X.  Zhao, V.  Balakrishna, R. H.  Hopkins, D. R.  Suhre, N. C.  Fernelius, F. K.  Hopkins, and D. E.  Zelmon, "Bridgman growth of GaSe crystals for nonlinear optical applications," Mater. Sci. Eng. B 49, 243-246 (1997).
[CrossRef]

Opt. Commun. (1)

K. L.  Vodopyanov, and L. A.  Kulevskii, "New dispersion relationships for GaSe in the 0.65-18 ?m spectral region," Opt. Commun. 118, 375-378 (1995).
[CrossRef]

Opt. Express (1)

Opt. Lett. (2)

Opt. Mater. (1)

V. G.  Voevodin, O. V.  Voevodina, S. A.  Bereznaya, Z. V.  Korotchenko, A. N.  Morozov, S. Yu.  Sarkisov, N. C.  Fernelius, and J. T.  Goldstein, "Large single crystals of gallium selenide: growing, doping by In and characterization," Opt. Mater. 26, 495-499 (2004).
[CrossRef]

Phys. Rev. B (1)

D.  Errandonea, A.  Segura, V.  Munoz, and A.  Chevy, "Effects of pressure and temperature on the dielectric constant: Role of the electronic contribution," Phys. Rev. B 60, 15866-15874 (1999).
[CrossRef]

Proc. SPIE (1)

A. A.  Tikhomirov, Yu. M.  Andreev, G. V.  Lanskii, O. V.  Voevodina, S. Yu.  Sarkisov, "Doped GaSe nonlinear crystals," Proc. SPIE 6258, 64-72 (2006).

Prog. Cryst. Growth Charact. (1)

N. C.  Fernelius, "Properties of gallium selenide single crystal," Prog. Cryst. Growth Charact. 28, 275-353 (1994).
[CrossRef]

Prog. Cryst. Growth Charact. Mater. (1)

N. B.  Singh, D. R.  Suhre, V.  Balakrishna, M.  Marable, R.  Meyer, N.  Fernelius, F. K.  Hopkins, and D.  Zelmon, "Far-infrared conversion materials: Gallium selenide for far-infrared conversion applications," Prog. Cryst. Growth Charact. Mater. 37, 47-102 (1998).
[CrossRef]

Sov. J. Quant. Electr. (2)

G. B.  Abdullaev, K. R.  Allakhverdiev, L. A.  Kulevskii, A. M.  Prokhorov, E. Yu.  Salaev, A. D.  Savel???ev, and V. V.  Smirnov, "Parametric frequency conversion of IR radiation in GaSe crystal," Sov. J. Quant. Electr. 5, 665-668 (1975).
[CrossRef]

Yu. M.  Andreev, V. G.  Voevodin, A. I.  Gribenyukov, O. Ya.  Zyryanov, I. I.  Ippolitov, A. N.  Morozov, A. V.  Sosnin, and G. S.  Khmel???nitstskii, "An efficient generation of the tunable CO2 laser radiation second harmonic in ZnGeP2," Sov. J. Quant. Electr. 14, 1021-1022 (1984).
[CrossRef]

Other (1)

K. R.  Allakhverdiev, T.  Baykara, A.  Kulibekov Gulubayov, A. A.  Kaya, J.  Goldstein, N.  Fernelius, S.  Hanna, and Z.  Salaeva, "Corrected infrared Sellmeier coefficients for gallium selenide," J. Appl. Phys. 98, 093515-1-6 (2005).
[CrossRef]

Cited By

OSA participates in CrossRef's Cited-By Linking service. Citing articles from OSA journals and other participating publishers are listed here.

Alert me when this article is cited.


Figures (3)

Fig. 1.
Fig. 1.

Transmission spectra of pure and doped GaSe crystals. Curve identification is given in the insert.

Fig. 2.
Fig. 2.

Scheme of the experimental setup for CO2 and Er3+:YSGG laser SHG. BS1 and BS2 are removable beam splitters, M1 and M2 is two-mirror optical system for a laser beam alignment, ID1, ID2 and ID3 are iris diaphragms, L1, L2 and L3 are lenses, NLC is a non-linear crystal, F is a block filter and D1 and D2 are detectors, PC is personal computer, OS is oscilloscope.

Fig. 3.
Fig. 3.

External PM angles for SHG under pumping by (a) Er3+:YSGG and (b) 9.58 µm CO2 laser emission line versus temperature. Experimental data of this study are given by circles. Triangles are the PM angles estimated with available literature data for refractive indices. Crystal parameters are shown in the inserts.

Tables (1)

Tables Icon

Table 1. Parameters of pure and doped GaSe crystals and external PM angles for Er3+:YSGG and CO2 laser SHG.

Metrics