UV Induced Thermoluminescence and Photoluminescence Studies of Sm3+ Doped LaAlO3 Phosphor

Not Accessible

Your library or personal account may give you access

Abstract

Behavior is displayed by samarium-doped LaAlO3 phosphor which was synthesized by solid state reaction method. For the synthesis of LaAlO3 with variable concentration of Sm (0.2–2.5 mol%) phosphor was calcinated at 1000 °C and sintered at 1250 °C following intermediate grinding. Synthesized sample was characterized by X-ray diffraction analysis and crystallite size was calculated by Scherer's formula. From photoluminescence (PL) spectra of prepared phosphors show broad excitation peak at 250 nm and emission at 566, 600, and 608 nm is obtained. The phosphor is prepared by high temperature synthesis method. Two peaks are obtained in the thermoluminescence (TL) glow curve for lower concentration of Samarium. Single prominent peak is obtained with further increase in the concentration of dopant. It is characteristic yellow-orange emission for samarium ion. The excitation spectra of LaAlO3:Sm3+ phosphor mainly consists of the charge transfer band (CTB) of Sm3+ located in 220–340 nm centered at 250 nm. The present phosphors can act as single host for yellow-orange-red light emission in display devices. The CIE coordinates were calculated by spectrophotometric method using the spectral energy distribution of the LaAlO3:Sm3+ sample. TL glow curve was recorded for variable concentration of dopant with fixed UV exposer time (20 min) and fixed heating rate (5 °C·s−1). TL glow curve shows broad peak and kinetic parameters are calculated by computerized glow curve deconvolution technique. It is suggested that from TL glow curve analysis prepared phosphor may be useful for TL dosimetric application for UV exposure.

© 2016 IEEE

PDF Article
More Like This
Persistent luminescence properties of Cr3+-Sm3+ activated LaAlO3 perovskite

Yumiko Katayama, Hiroaki Kobayashi, Jumpei Ueda, Bruno Viana, and Setsuhisa Tanabe
Opt. Mater. Express 6(5) 1500-1505 (2016)

Site occupancy and photoluminescence of Sm3+ in KSr4(BO3)3:Sm3+ phosphors

Li Wu, Minyuan Ji, Hongrun Wang, Yongfa Kong, and Yi Zhang
Opt. Mater. Express 4(8) 1535-1544 (2014)

Synthesis and luminescence properties of Ba3Lu(PO4)3:Sm3+ phosphor for white light-emitting diodes

Zaifa Yang, Denghui Xu, and Jiayue Sun
Opt. Express 25(8) A391-A401 (2017)

Cited By

You do not have subscription access to this journal. Cited by links are available to subscribers only. You may subscribe either as an Optica member, or as an authorized user of your institution.

Contact your librarian or system administrator
or
Login to access Optica Member Subscription

Select as filters


Select Topics Cancel
© Copyright 2024 | Optica Publishing Group. All Rights Reserved