Abstract

Sn/Yb codoped silica optical fiber preform is prepared by the modified chemical vapor deposition (MCVD) followed by the solution-doping method. Ultraviolet (UV) optical absorption, photoluminescence (PL) spectra under 978-nm laser diode (LD) pumping, and refractive index change after exposure to 266-nm laser pulses are obtained. There is only a little change in the PL spectra while a positive refractive index change up to 2\times10^{-4} is observed after 30-min exposure to 266-nm laser pulses. The results show that both of the peculiar photosensitivity of Sn-doped silica and the gain property of Yb-doped silica fiber are preserved in the Sn/Yb codoped silica optical fiber preform. The experimental data suggest that the photosensitivity of the fiber preform under high energy density laser irradiation should be mainly due to the bond-breaking of oxygen deficient defects, while under relatively low energy density laser irradiation, the refractive index change probably originates from the photoconversion of optically active defects.

© 2009 Chinese Optics Letters

PDF Article

References

  • View by:
  • |
  • |
  • |

  1. Y. Z. Xu, H. Y. Tam, S. Y. Liu, and M. S. Demokan, IEEE Photon. Technol. Lett. 10, 1253 (1998).
  2. G. A. Ball, W. W. Morey, and P. K. Cheo, IEEE Photon. Technol. Lett. 5, 267 (1993).
  3. G. G. Karapetyan, A. V. Daryan, D. M. Meghavoryan, and N. E. Gevorgyan, Opt. Commun. 205, 421 (2002).
  4. W. H. Loh, L. Dong, and J. E. Caplen, Appl. Phys. Lett. 69, 2151 (1996).
  5. N. Chiodini, A. Paleari, G. Spinolo, A. Chiasera, M. Ferrari, G. Brambilla, and E. R. Taylor, J. Non-Cryst. Solids 311, 217 (2002).
  6. G. Brambilla, V. Pruneri, and L. Reekie, Appl. Phys. Lett. 76, 807 (2000).
  7. G. Brambilla, V. Pruneri, L. Reekie, C. Contardi, D. Milanese, and M. Ferraris, Opt. Lett. 25, 1153 (2000).
  8. N. Chiodini, S. Ghidini, A. Paleari, G. Brambilla, and V. Pruneri, Appl. Phys. Lett. 77, 3701 (2000).
  9. A. Anedda, C. M. Carbonaro, A. Serpi, N. Chiodini, A. Paleari, R. Scotti, G. Spinolo, G. Brambilla, and V. Pruneri, J. Non-Cryst. Solids 280, 287 (2001).
  10. G. Chen, Y. Li, L. Liu, Y. He, L. Xu, and W. Wang, J. Appl. Phys. 96, 6153 (2004).
  11. T. Nakanishi, M. Fujimaki, S. Tokuhiro, K. Nomura, Y. Ohki, and K. Imamura, J. Non-Cryst. Solids 318, 87 (2003).
  12. B. Leconte, W.-X. Xie, M. Douay, P. Bernage, P. Niay, J. F. Bayon, E. Delevaque, and H. Poignant, Appl. Opt. 36, 5923 (1997).

2004 (1)

G. Chen, Y. Li, L. Liu, Y. He, L. Xu, and W. Wang, J. Appl. Phys. 96, 6153 (2004).

2003 (1)

T. Nakanishi, M. Fujimaki, S. Tokuhiro, K. Nomura, Y. Ohki, and K. Imamura, J. Non-Cryst. Solids 318, 87 (2003).

2002 (2)

N. Chiodini, A. Paleari, G. Spinolo, A. Chiasera, M. Ferrari, G. Brambilla, and E. R. Taylor, J. Non-Cryst. Solids 311, 217 (2002).

G. G. Karapetyan, A. V. Daryan, D. M. Meghavoryan, and N. E. Gevorgyan, Opt. Commun. 205, 421 (2002).

2001 (1)

A. Anedda, C. M. Carbonaro, A. Serpi, N. Chiodini, A. Paleari, R. Scotti, G. Spinolo, G. Brambilla, and V. Pruneri, J. Non-Cryst. Solids 280, 287 (2001).

2000 (3)

G. Brambilla, V. Pruneri, L. Reekie, C. Contardi, D. Milanese, and M. Ferraris, Opt. Lett. 25, 1153 (2000).

G. Brambilla, V. Pruneri, and L. Reekie, Appl. Phys. Lett. 76, 807 (2000).

N. Chiodini, S. Ghidini, A. Paleari, G. Brambilla, and V. Pruneri, Appl. Phys. Lett. 77, 3701 (2000).

1998 (1)

Y. Z. Xu, H. Y. Tam, S. Y. Liu, and M. S. Demokan, IEEE Photon. Technol. Lett. 10, 1253 (1998).

1997 (1)

1996 (1)

W. H. Loh, L. Dong, and J. E. Caplen, Appl. Phys. Lett. 69, 2151 (1996).

1993 (1)

G. A. Ball, W. W. Morey, and P. K. Cheo, IEEE Photon. Technol. Lett. 5, 267 (1993).

Anedda, A.

A. Anedda, C. M. Carbonaro, A. Serpi, N. Chiodini, A. Paleari, R. Scotti, G. Spinolo, G. Brambilla, and V. Pruneri, J. Non-Cryst. Solids 280, 287 (2001).

Ball, G. A.

G. A. Ball, W. W. Morey, and P. K. Cheo, IEEE Photon. Technol. Lett. 5, 267 (1993).

Bayon, J. F.

Bernage, P.

Brambilla, G.

N. Chiodini, A. Paleari, G. Spinolo, A. Chiasera, M. Ferrari, G. Brambilla, and E. R. Taylor, J. Non-Cryst. Solids 311, 217 (2002).

A. Anedda, C. M. Carbonaro, A. Serpi, N. Chiodini, A. Paleari, R. Scotti, G. Spinolo, G. Brambilla, and V. Pruneri, J. Non-Cryst. Solids 280, 287 (2001).

G. Brambilla, V. Pruneri, L. Reekie, C. Contardi, D. Milanese, and M. Ferraris, Opt. Lett. 25, 1153 (2000).

N. Chiodini, S. Ghidini, A. Paleari, G. Brambilla, and V. Pruneri, Appl. Phys. Lett. 77, 3701 (2000).

G. Brambilla, V. Pruneri, and L. Reekie, Appl. Phys. Lett. 76, 807 (2000).

Caplen, J. E.

W. H. Loh, L. Dong, and J. E. Caplen, Appl. Phys. Lett. 69, 2151 (1996).

Carbonaro, C. M.

A. Anedda, C. M. Carbonaro, A. Serpi, N. Chiodini, A. Paleari, R. Scotti, G. Spinolo, G. Brambilla, and V. Pruneri, J. Non-Cryst. Solids 280, 287 (2001).

Chen, G.

G. Chen, Y. Li, L. Liu, Y. He, L. Xu, and W. Wang, J. Appl. Phys. 96, 6153 (2004).

Cheo, P. K.

G. A. Ball, W. W. Morey, and P. K. Cheo, IEEE Photon. Technol. Lett. 5, 267 (1993).

Chiasera, A.

N. Chiodini, A. Paleari, G. Spinolo, A. Chiasera, M. Ferrari, G. Brambilla, and E. R. Taylor, J. Non-Cryst. Solids 311, 217 (2002).

Chiodini, N.

N. Chiodini, A. Paleari, G. Spinolo, A. Chiasera, M. Ferrari, G. Brambilla, and E. R. Taylor, J. Non-Cryst. Solids 311, 217 (2002).

A. Anedda, C. M. Carbonaro, A. Serpi, N. Chiodini, A. Paleari, R. Scotti, G. Spinolo, G. Brambilla, and V. Pruneri, J. Non-Cryst. Solids 280, 287 (2001).

N. Chiodini, S. Ghidini, A. Paleari, G. Brambilla, and V. Pruneri, Appl. Phys. Lett. 77, 3701 (2000).

Contardi, C.

Daryan, A. V.

G. G. Karapetyan, A. V. Daryan, D. M. Meghavoryan, and N. E. Gevorgyan, Opt. Commun. 205, 421 (2002).

Delevaque, E.

Demokan, M. S.

Y. Z. Xu, H. Y. Tam, S. Y. Liu, and M. S. Demokan, IEEE Photon. Technol. Lett. 10, 1253 (1998).

Dong, L.

W. H. Loh, L. Dong, and J. E. Caplen, Appl. Phys. Lett. 69, 2151 (1996).

Douay, M.

Ferrari, M.

N. Chiodini, A. Paleari, G. Spinolo, A. Chiasera, M. Ferrari, G. Brambilla, and E. R. Taylor, J. Non-Cryst. Solids 311, 217 (2002).

Ferraris, M.

Fujimaki, M.

T. Nakanishi, M. Fujimaki, S. Tokuhiro, K. Nomura, Y. Ohki, and K. Imamura, J. Non-Cryst. Solids 318, 87 (2003).

Gevorgyan, N. E.

G. G. Karapetyan, A. V. Daryan, D. M. Meghavoryan, and N. E. Gevorgyan, Opt. Commun. 205, 421 (2002).

Ghidini, S.

N. Chiodini, S. Ghidini, A. Paleari, G. Brambilla, and V. Pruneri, Appl. Phys. Lett. 77, 3701 (2000).

He, Y.

G. Chen, Y. Li, L. Liu, Y. He, L. Xu, and W. Wang, J. Appl. Phys. 96, 6153 (2004).

Imamura, K.

T. Nakanishi, M. Fujimaki, S. Tokuhiro, K. Nomura, Y. Ohki, and K. Imamura, J. Non-Cryst. Solids 318, 87 (2003).

Karapetyan, G. G.

G. G. Karapetyan, A. V. Daryan, D. M. Meghavoryan, and N. E. Gevorgyan, Opt. Commun. 205, 421 (2002).

Leconte, B.

Li, Y.

G. Chen, Y. Li, L. Liu, Y. He, L. Xu, and W. Wang, J. Appl. Phys. 96, 6153 (2004).

Liu, L.

G. Chen, Y. Li, L. Liu, Y. He, L. Xu, and W. Wang, J. Appl. Phys. 96, 6153 (2004).

Liu, S. Y.

Y. Z. Xu, H. Y. Tam, S. Y. Liu, and M. S. Demokan, IEEE Photon. Technol. Lett. 10, 1253 (1998).

Loh, W. H.

W. H. Loh, L. Dong, and J. E. Caplen, Appl. Phys. Lett. 69, 2151 (1996).

Meghavoryan, D. M.

G. G. Karapetyan, A. V. Daryan, D. M. Meghavoryan, and N. E. Gevorgyan, Opt. Commun. 205, 421 (2002).

Milanese, D.

Morey, W. W.

G. A. Ball, W. W. Morey, and P. K. Cheo, IEEE Photon. Technol. Lett. 5, 267 (1993).

Nakanishi, T.

T. Nakanishi, M. Fujimaki, S. Tokuhiro, K. Nomura, Y. Ohki, and K. Imamura, J. Non-Cryst. Solids 318, 87 (2003).

Niay, P.

Nomura, K.

T. Nakanishi, M. Fujimaki, S. Tokuhiro, K. Nomura, Y. Ohki, and K. Imamura, J. Non-Cryst. Solids 318, 87 (2003).

Ohki, Y.

T. Nakanishi, M. Fujimaki, S. Tokuhiro, K. Nomura, Y. Ohki, and K. Imamura, J. Non-Cryst. Solids 318, 87 (2003).

Paleari, A.

N. Chiodini, A. Paleari, G. Spinolo, A. Chiasera, M. Ferrari, G. Brambilla, and E. R. Taylor, J. Non-Cryst. Solids 311, 217 (2002).

A. Anedda, C. M. Carbonaro, A. Serpi, N. Chiodini, A. Paleari, R. Scotti, G. Spinolo, G. Brambilla, and V. Pruneri, J. Non-Cryst. Solids 280, 287 (2001).

N. Chiodini, S. Ghidini, A. Paleari, G. Brambilla, and V. Pruneri, Appl. Phys. Lett. 77, 3701 (2000).

Poignant, H.

Pruneri, V.

A. Anedda, C. M. Carbonaro, A. Serpi, N. Chiodini, A. Paleari, R. Scotti, G. Spinolo, G. Brambilla, and V. Pruneri, J. Non-Cryst. Solids 280, 287 (2001).

G. Brambilla, V. Pruneri, L. Reekie, C. Contardi, D. Milanese, and M. Ferraris, Opt. Lett. 25, 1153 (2000).

N. Chiodini, S. Ghidini, A. Paleari, G. Brambilla, and V. Pruneri, Appl. Phys. Lett. 77, 3701 (2000).

G. Brambilla, V. Pruneri, and L. Reekie, Appl. Phys. Lett. 76, 807 (2000).

Reekie, L.

G. Brambilla, V. Pruneri, and L. Reekie, Appl. Phys. Lett. 76, 807 (2000).

G. Brambilla, V. Pruneri, L. Reekie, C. Contardi, D. Milanese, and M. Ferraris, Opt. Lett. 25, 1153 (2000).

Scotti, R.

A. Anedda, C. M. Carbonaro, A. Serpi, N. Chiodini, A. Paleari, R. Scotti, G. Spinolo, G. Brambilla, and V. Pruneri, J. Non-Cryst. Solids 280, 287 (2001).

Serpi, A.

A. Anedda, C. M. Carbonaro, A. Serpi, N. Chiodini, A. Paleari, R. Scotti, G. Spinolo, G. Brambilla, and V. Pruneri, J. Non-Cryst. Solids 280, 287 (2001).

Spinolo, G.

N. Chiodini, A. Paleari, G. Spinolo, A. Chiasera, M. Ferrari, G. Brambilla, and E. R. Taylor, J. Non-Cryst. Solids 311, 217 (2002).

A. Anedda, C. M. Carbonaro, A. Serpi, N. Chiodini, A. Paleari, R. Scotti, G. Spinolo, G. Brambilla, and V. Pruneri, J. Non-Cryst. Solids 280, 287 (2001).

Tam, H. Y.

Y. Z. Xu, H. Y. Tam, S. Y. Liu, and M. S. Demokan, IEEE Photon. Technol. Lett. 10, 1253 (1998).

Taylor, E. R.

N. Chiodini, A. Paleari, G. Spinolo, A. Chiasera, M. Ferrari, G. Brambilla, and E. R. Taylor, J. Non-Cryst. Solids 311, 217 (2002).

Tokuhiro, S.

T. Nakanishi, M. Fujimaki, S. Tokuhiro, K. Nomura, Y. Ohki, and K. Imamura, J. Non-Cryst. Solids 318, 87 (2003).

Wang, W.

G. Chen, Y. Li, L. Liu, Y. He, L. Xu, and W. Wang, J. Appl. Phys. 96, 6153 (2004).

Xie, W.-X.

Xu, L.

G. Chen, Y. Li, L. Liu, Y. He, L. Xu, and W. Wang, J. Appl. Phys. 96, 6153 (2004).

Xu, Y. Z.

Y. Z. Xu, H. Y. Tam, S. Y. Liu, and M. S. Demokan, IEEE Photon. Technol. Lett. 10, 1253 (1998).

Appl. Opt. (1)

Appl. Phys. Lett. (3)

W. H. Loh, L. Dong, and J. E. Caplen, Appl. Phys. Lett. 69, 2151 (1996).

G. Brambilla, V. Pruneri, and L. Reekie, Appl. Phys. Lett. 76, 807 (2000).

N. Chiodini, S. Ghidini, A. Paleari, G. Brambilla, and V. Pruneri, Appl. Phys. Lett. 77, 3701 (2000).

IEEE Photon. Technol. Lett. (2)

Y. Z. Xu, H. Y. Tam, S. Y. Liu, and M. S. Demokan, IEEE Photon. Technol. Lett. 10, 1253 (1998).

G. A. Ball, W. W. Morey, and P. K. Cheo, IEEE Photon. Technol. Lett. 5, 267 (1993).

J. Appl. Phys. (1)

G. Chen, Y. Li, L. Liu, Y. He, L. Xu, and W. Wang, J. Appl. Phys. 96, 6153 (2004).

J. Non-Cryst. Solids (3)

T. Nakanishi, M. Fujimaki, S. Tokuhiro, K. Nomura, Y. Ohki, and K. Imamura, J. Non-Cryst. Solids 318, 87 (2003).

A. Anedda, C. M. Carbonaro, A. Serpi, N. Chiodini, A. Paleari, R. Scotti, G. Spinolo, G. Brambilla, and V. Pruneri, J. Non-Cryst. Solids 280, 287 (2001).

N. Chiodini, A. Paleari, G. Spinolo, A. Chiasera, M. Ferrari, G. Brambilla, and E. R. Taylor, J. Non-Cryst. Solids 311, 217 (2002).

Opt. Commun. (1)

G. G. Karapetyan, A. V. Daryan, D. M. Meghavoryan, and N. E. Gevorgyan, Opt. Commun. 205, 421 (2002).

Opt. Lett. (1)

Cited By

OSA participates in CrossRef's Cited-By Linking service. Citing articles from OSA journals and other participating publishers are listed here.