Abstract

We demonstrate the self-assembly of solution-processible gold nanoparticles into the nanoholes consisting of patterned substrate through annealing, which facilitates successful fabrication of square lattices of gold nanocylinders with a period of 350 nm, a height of about 200 nm, and an aspect ratio larger than 2.

© 2007 Chinese Optics Letters

PDF Article

References

  • View by:
  • |
  • |

  1. A. Christ, S. G. Tikhodeev, N. A. Gippius, J. Kuhl, and H. Giessen, Phys. Rev. Lett. 91, 183901 (2003).
  2. A. Christ, T. Zentgraf, J. Kuhl, S. G. Tikhodeev, N. A. Gippius, and H. Giessen, Phys. Rev. B 70, 125113 (2004).
  3. D. Nau, R. P. Bertram, K. Buse, T. Zentgraf, J. Kuhl, S. G. Tikhodeev, N. A. Gippius, and H. Giessen, Appl. Phys. B 82, 543 (2006).
  4. H. C. Guo, D. Nau, A. Radke, X. P. Zhang, J. Stodolka, X. L. Yang, S. G. Tikhodeev, N. A. Gippius, and H. Giessen, Appl. Phys. B 81, 271 (2005).
  5. X. Zhang, B. Sun, R. H. Friend, H. Guo, D. Nau, and H. Giessen, Nano Lett. 6, 651 (2006).
  6. N. S. Pesika, A. Radisic, K. J. Stebe, and P. C. Searson, Nano Lett. 6, 1023 (2006).
  7. I. B. Diliansky, A. Shishido, I.-C. Khoo, T. S. Mayer, D. Pena, S. Nishimura, C. D. Keating, and T. E. Mallouk, Appl. Phys. Lett. 79, 3392 (2001).
  8. A. Abdolvand, A. Podlipensky, S. Matthias, F. Syrowatka, U. Gosels, G. Seifert, and H. Graener, Adv. Mater. 15, 2983 (2005).

2006 (3)

D. Nau, R. P. Bertram, K. Buse, T. Zentgraf, J. Kuhl, S. G. Tikhodeev, N. A. Gippius, and H. Giessen, Appl. Phys. B 82, 543 (2006).

X. Zhang, B. Sun, R. H. Friend, H. Guo, D. Nau, and H. Giessen, Nano Lett. 6, 651 (2006).

N. S. Pesika, A. Radisic, K. J. Stebe, and P. C. Searson, Nano Lett. 6, 1023 (2006).

2005 (2)

A. Abdolvand, A. Podlipensky, S. Matthias, F. Syrowatka, U. Gosels, G. Seifert, and H. Graener, Adv. Mater. 15, 2983 (2005).

H. C. Guo, D. Nau, A. Radke, X. P. Zhang, J. Stodolka, X. L. Yang, S. G. Tikhodeev, N. A. Gippius, and H. Giessen, Appl. Phys. B 81, 271 (2005).

2004 (1)

A. Christ, T. Zentgraf, J. Kuhl, S. G. Tikhodeev, N. A. Gippius, and H. Giessen, Phys. Rev. B 70, 125113 (2004).

2003 (1)

A. Christ, S. G. Tikhodeev, N. A. Gippius, J. Kuhl, and H. Giessen, Phys. Rev. Lett. 91, 183901 (2003).

2001 (1)

I. B. Diliansky, A. Shishido, I.-C. Khoo, T. S. Mayer, D. Pena, S. Nishimura, C. D. Keating, and T. E. Mallouk, Appl. Phys. Lett. 79, 3392 (2001).

Adv. Mater. (1)

A. Abdolvand, A. Podlipensky, S. Matthias, F. Syrowatka, U. Gosels, G. Seifert, and H. Graener, Adv. Mater. 15, 2983 (2005).

Appl. Phys. B (2)

D. Nau, R. P. Bertram, K. Buse, T. Zentgraf, J. Kuhl, S. G. Tikhodeev, N. A. Gippius, and H. Giessen, Appl. Phys. B 82, 543 (2006).

H. C. Guo, D. Nau, A. Radke, X. P. Zhang, J. Stodolka, X. L. Yang, S. G. Tikhodeev, N. A. Gippius, and H. Giessen, Appl. Phys. B 81, 271 (2005).

Appl. Phys. Lett. (1)

I. B. Diliansky, A. Shishido, I.-C. Khoo, T. S. Mayer, D. Pena, S. Nishimura, C. D. Keating, and T. E. Mallouk, Appl. Phys. Lett. 79, 3392 (2001).

Nano Lett. (2)

X. Zhang, B. Sun, R. H. Friend, H. Guo, D. Nau, and H. Giessen, Nano Lett. 6, 651 (2006).

N. S. Pesika, A. Radisic, K. J. Stebe, and P. C. Searson, Nano Lett. 6, 1023 (2006).

Phys. Rev. B (1)

A. Christ, T. Zentgraf, J. Kuhl, S. G. Tikhodeev, N. A. Gippius, and H. Giessen, Phys. Rev. B 70, 125113 (2004).

Phys. Rev. Lett. (1)

A. Christ, S. G. Tikhodeev, N. A. Gippius, J. Kuhl, and H. Giessen, Phys. Rev. Lett. 91, 183901 (2003).

Cited By

OSA participates in Crossref's Cited-By Linking service. Citing articles from OSA journals and other participating publishers are listed here.