Different up-conversion luminescent spectra of Er^(3+) ions were observed in the oxyfluoride glass-ceramics. The ratio of two fluorides in the original compositions was modified in order to form different nanocrystals. The intensity of up-conversion luminescence increased sharply when the ratio of PbF2 and CdF2 was 40:10. The data of differential thermal analysis and X-ray diffraction were used to explain the optimization fluoride ratio. The intensity of up-conversion luminescence is not only decided by the crystallizability but also mainly related with the stoichiometric proportion of fluoride nanocrystals in the glass-ceramics.

© 2005 Chinese Optics Letters

PDF Article

References

  • View by:
  • |
  • |
  • |

  1. M. Beggionra and I. M. Reaney, Appl. Phys. Lett. 83, 467 (2003).
  2. J. Mendez-Ramos, V. Lavin, I. R. Martin, and V. D. Rodriguez, J. Appl. Phys. 94, 2295 (2003).
  3. P. A. Tick, N. F. Borrelli, L. K. Cornelius, and M. A. Newhouse, J. Appl. Phys. 78, 6367 (1995).
  4. Y. Wang and J. Ohwaki, Appl. Phys. Lett. 63, 3268 (1993).
  5. M. Takahashi, M. Izuki, R. Kanno, and Y. Kawamoto, Appl. Phys. Lett. 83, 3920 (1998).
  6. Y. Kawaomto, R. Kanno, and J. Qiu, J. Mater. Sci. 33, 63 (1998).
  7. S. Xu, Z. Yang, G. Wang, S. Dai, L. Hu, and Z. Jiang, Chin. Opt. Lett. 1, 544 (2003).
  8. L. L. Kukkonen, I. M. Reaney, D. Furniss, M. G. Pellatt, and A. B. Seddon, J. Non-Cryst. Solids 290, 25 (2001).
  9. J. Mendez-Ramos, V. Lavin, I. R. Martin, U. R. Rodriguez-Mendoza, J. Appl. Phys. 89, 5307 (2001).
  10. V. K. Tikhomirov, D. Fruniss, A. B. Seddon, Z. M. Reaney, M. Beggiora, M. Ferrari, M. Montagna, and R. Rolli, Appl. Phys. Lett. 81, 1937 (2002).
  11. L. J. Zhao, X. X. Xu, K. Wang, L. Q. Tang, J. J. Xu, and G. Y. Zhang, Acta Scientiarum Naturalium Universitatis Nankaiensis 35, 60 (2002).

2003 (3)

M. Beggionra and I. M. Reaney, Appl. Phys. Lett. 83, 467 (2003).

J. Mendez-Ramos, V. Lavin, I. R. Martin, and V. D. Rodriguez, J. Appl. Phys. 94, 2295 (2003).

S. Xu, Z. Yang, G. Wang, S. Dai, L. Hu, and Z. Jiang, Chin. Opt. Lett. 1, 544 (2003).

2002 (2)

V. K. Tikhomirov, D. Fruniss, A. B. Seddon, Z. M. Reaney, M. Beggiora, M. Ferrari, M. Montagna, and R. Rolli, Appl. Phys. Lett. 81, 1937 (2002).

L. J. Zhao, X. X. Xu, K. Wang, L. Q. Tang, J. J. Xu, and G. Y. Zhang, Acta Scientiarum Naturalium Universitatis Nankaiensis 35, 60 (2002).

2001 (2)

L. L. Kukkonen, I. M. Reaney, D. Furniss, M. G. Pellatt, and A. B. Seddon, J. Non-Cryst. Solids 290, 25 (2001).

J. Mendez-Ramos, V. Lavin, I. R. Martin, U. R. Rodriguez-Mendoza, J. Appl. Phys. 89, 5307 (2001).

1998 (2)

M. Takahashi, M. Izuki, R. Kanno, and Y. Kawamoto, Appl. Phys. Lett. 83, 3920 (1998).

Y. Kawaomto, R. Kanno, and J. Qiu, J. Mater. Sci. 33, 63 (1998).

1995 (1)

P. A. Tick, N. F. Borrelli, L. K. Cornelius, and M. A. Newhouse, J. Appl. Phys. 78, 6367 (1995).

1993 (1)

Y. Wang and J. Ohwaki, Appl. Phys. Lett. 63, 3268 (1993).

Beggionra, M.

M. Beggionra and I. M. Reaney, Appl. Phys. Lett. 83, 467 (2003).

Beggiora, M.

V. K. Tikhomirov, D. Fruniss, A. B. Seddon, Z. M. Reaney, M. Beggiora, M. Ferrari, M. Montagna, and R. Rolli, Appl. Phys. Lett. 81, 1937 (2002).

Borrelli, N. F.

P. A. Tick, N. F. Borrelli, L. K. Cornelius, and M. A. Newhouse, J. Appl. Phys. 78, 6367 (1995).

Cornelius, L. K.

P. A. Tick, N. F. Borrelli, L. K. Cornelius, and M. A. Newhouse, J. Appl. Phys. 78, 6367 (1995).

Dai, S.

Ferrari, M.

V. K. Tikhomirov, D. Fruniss, A. B. Seddon, Z. M. Reaney, M. Beggiora, M. Ferrari, M. Montagna, and R. Rolli, Appl. Phys. Lett. 81, 1937 (2002).

Fruniss, D.

V. K. Tikhomirov, D. Fruniss, A. B. Seddon, Z. M. Reaney, M. Beggiora, M. Ferrari, M. Montagna, and R. Rolli, Appl. Phys. Lett. 81, 1937 (2002).

Furniss, D.

L. L. Kukkonen, I. M. Reaney, D. Furniss, M. G. Pellatt, and A. B. Seddon, J. Non-Cryst. Solids 290, 25 (2001).

Hu, L.

Izuki, M.

M. Takahashi, M. Izuki, R. Kanno, and Y. Kawamoto, Appl. Phys. Lett. 83, 3920 (1998).

Jiang, Z.

Kanno, R.

M. Takahashi, M. Izuki, R. Kanno, and Y. Kawamoto, Appl. Phys. Lett. 83, 3920 (1998).

Y. Kawaomto, R. Kanno, and J. Qiu, J. Mater. Sci. 33, 63 (1998).

Kawamoto, Y.

M. Takahashi, M. Izuki, R. Kanno, and Y. Kawamoto, Appl. Phys. Lett. 83, 3920 (1998).

Kawaomto, Y.

Y. Kawaomto, R. Kanno, and J. Qiu, J. Mater. Sci. 33, 63 (1998).

Kukkonen, L. L.

L. L. Kukkonen, I. M. Reaney, D. Furniss, M. G. Pellatt, and A. B. Seddon, J. Non-Cryst. Solids 290, 25 (2001).

Lavin, V.

J. Mendez-Ramos, V. Lavin, I. R. Martin, and V. D. Rodriguez, J. Appl. Phys. 94, 2295 (2003).

Martin, I. R.

J. Mendez-Ramos, V. Lavin, I. R. Martin, and V. D. Rodriguez, J. Appl. Phys. 94, 2295 (2003).

Mendez-Ramos, J.

J. Mendez-Ramos, V. Lavin, I. R. Martin, and V. D. Rodriguez, J. Appl. Phys. 94, 2295 (2003).

J. Mendez-Ramos, V. Lavin, I. R. Martin, U. R. Rodriguez-Mendoza, J. Appl. Phys. 89, 5307 (2001).

Montagna, M.

V. K. Tikhomirov, D. Fruniss, A. B. Seddon, Z. M. Reaney, M. Beggiora, M. Ferrari, M. Montagna, and R. Rolli, Appl. Phys. Lett. 81, 1937 (2002).

Newhouse, M. A.

P. A. Tick, N. F. Borrelli, L. K. Cornelius, and M. A. Newhouse, J. Appl. Phys. 78, 6367 (1995).

Ohwaki, J.

Y. Wang and J. Ohwaki, Appl. Phys. Lett. 63, 3268 (1993).

Pellatt, M. G.

L. L. Kukkonen, I. M. Reaney, D. Furniss, M. G. Pellatt, and A. B. Seddon, J. Non-Cryst. Solids 290, 25 (2001).

Qiu, J.

Y. Kawaomto, R. Kanno, and J. Qiu, J. Mater. Sci. 33, 63 (1998).

Reaney, I. M.

M. Beggionra and I. M. Reaney, Appl. Phys. Lett. 83, 467 (2003).

L. L. Kukkonen, I. M. Reaney, D. Furniss, M. G. Pellatt, and A. B. Seddon, J. Non-Cryst. Solids 290, 25 (2001).

Reaney, Z. M.

V. K. Tikhomirov, D. Fruniss, A. B. Seddon, Z. M. Reaney, M. Beggiora, M. Ferrari, M. Montagna, and R. Rolli, Appl. Phys. Lett. 81, 1937 (2002).

Rodriguez, V. D.

J. Mendez-Ramos, V. Lavin, I. R. Martin, and V. D. Rodriguez, J. Appl. Phys. 94, 2295 (2003).

Rolli, R.

V. K. Tikhomirov, D. Fruniss, A. B. Seddon, Z. M. Reaney, M. Beggiora, M. Ferrari, M. Montagna, and R. Rolli, Appl. Phys. Lett. 81, 1937 (2002).

Seddon, A. B.

V. K. Tikhomirov, D. Fruniss, A. B. Seddon, Z. M. Reaney, M. Beggiora, M. Ferrari, M. Montagna, and R. Rolli, Appl. Phys. Lett. 81, 1937 (2002).

L. L. Kukkonen, I. M. Reaney, D. Furniss, M. G. Pellatt, and A. B. Seddon, J. Non-Cryst. Solids 290, 25 (2001).

Takahashi, M.

M. Takahashi, M. Izuki, R. Kanno, and Y. Kawamoto, Appl. Phys. Lett. 83, 3920 (1998).

Tang, L. Q.

L. J. Zhao, X. X. Xu, K. Wang, L. Q. Tang, J. J. Xu, and G. Y. Zhang, Acta Scientiarum Naturalium Universitatis Nankaiensis 35, 60 (2002).

Tick, P. A.

P. A. Tick, N. F. Borrelli, L. K. Cornelius, and M. A. Newhouse, J. Appl. Phys. 78, 6367 (1995).

Tikhomirov, V. K.

V. K. Tikhomirov, D. Fruniss, A. B. Seddon, Z. M. Reaney, M. Beggiora, M. Ferrari, M. Montagna, and R. Rolli, Appl. Phys. Lett. 81, 1937 (2002).

Wang, G.

Wang, K.

L. J. Zhao, X. X. Xu, K. Wang, L. Q. Tang, J. J. Xu, and G. Y. Zhang, Acta Scientiarum Naturalium Universitatis Nankaiensis 35, 60 (2002).

Wang, Y.

Y. Wang and J. Ohwaki, Appl. Phys. Lett. 63, 3268 (1993).

Xu, J. J.

L. J. Zhao, X. X. Xu, K. Wang, L. Q. Tang, J. J. Xu, and G. Y. Zhang, Acta Scientiarum Naturalium Universitatis Nankaiensis 35, 60 (2002).

Xu, S.

Xu, X. X.

L. J. Zhao, X. X. Xu, K. Wang, L. Q. Tang, J. J. Xu, and G. Y. Zhang, Acta Scientiarum Naturalium Universitatis Nankaiensis 35, 60 (2002).

Yang, Z.

Zhang, G. Y.

L. J. Zhao, X. X. Xu, K. Wang, L. Q. Tang, J. J. Xu, and G. Y. Zhang, Acta Scientiarum Naturalium Universitatis Nankaiensis 35, 60 (2002).

Zhao, L. J.

L. J. Zhao, X. X. Xu, K. Wang, L. Q. Tang, J. J. Xu, and G. Y. Zhang, Acta Scientiarum Naturalium Universitatis Nankaiensis 35, 60 (2002).

Acta Scientiarum Naturalium Universitatis Nankaiensis (1)

L. J. Zhao, X. X. Xu, K. Wang, L. Q. Tang, J. J. Xu, and G. Y. Zhang, Acta Scientiarum Naturalium Universitatis Nankaiensis 35, 60 (2002).

Appl. Phys. Lett. (4)

Y. Wang and J. Ohwaki, Appl. Phys. Lett. 63, 3268 (1993).

M. Takahashi, M. Izuki, R. Kanno, and Y. Kawamoto, Appl. Phys. Lett. 83, 3920 (1998).

M. Beggionra and I. M. Reaney, Appl. Phys. Lett. 83, 467 (2003).

V. K. Tikhomirov, D. Fruniss, A. B. Seddon, Z. M. Reaney, M. Beggiora, M. Ferrari, M. Montagna, and R. Rolli, Appl. Phys. Lett. 81, 1937 (2002).

Chin. Opt. Lett. (1)

J. Appl. Phys. (3)

J. Mendez-Ramos, V. Lavin, I. R. Martin, U. R. Rodriguez-Mendoza, J. Appl. Phys. 89, 5307 (2001).

J. Mendez-Ramos, V. Lavin, I. R. Martin, and V. D. Rodriguez, J. Appl. Phys. 94, 2295 (2003).

P. A. Tick, N. F. Borrelli, L. K. Cornelius, and M. A. Newhouse, J. Appl. Phys. 78, 6367 (1995).

J. Mater. Sci. (1)

Y. Kawaomto, R. Kanno, and J. Qiu, J. Mater. Sci. 33, 63 (1998).

J. Non-Cryst. Solids (1)

L. L. Kukkonen, I. M. Reaney, D. Furniss, M. G. Pellatt, and A. B. Seddon, J. Non-Cryst. Solids 290, 25 (2001).

Cited By

OSA participates in CrossRef's Cited-By Linking service. Citing articles from OSA journals and other participating publishers are listed here.

Alert me when this article is cited.