Fourier transform infrared (FT-IR) spectra were measured for thermal oxides with different electrical properties grown on 4H-SiC substrates. The peak frequency of the transverse optical (TO) phonon mode was blue-shifted by 5 cm⁻¹ as the oxide-layer thickness decreased to 3 nm. The blue shift of the TO mode indicates interfacial compressive stress in the oxide. Comparison of data for the oxide on a SiC substrate with that for similar oxides on a Si substrate implies that the peak shift of the TO mode at the SiO₂/SiC interface is larger than that of SiO₂/Si, which suggests that the interfacial stress for the oxide on the SiC substrate is larger than that on the Si substrate. For the SiO₂/SiC interfacial region (<3 nm oxide thickness), despite the fact that the blue shift of the TO modes becomes larger while approaching the oxide/SiC interface, the peak frequency of the TO modes red-shifts at the oxide/SiC interface. The peak-frequency shift of the TO mode for the sample without post-oxidation annealing was larger than that for the samples post-annealed in a nitric oxide atmosphere. The channel mobilities are correlated with the degree of shift of the TO mode when the oxide thickness is <3 nm. It appears that the compressive stress at the SiO₂/SiC interface generates silicon suboxide components and weakens the Si-O bonds. As the result, the TO mode was red-shifted and the oxygen deficiency increased to relax the compressive stress in the oxide with <3 nm thickness. Fourier transform infrared spectroscopy measurements provide unique and useful information about stress and inhomogeneity at the oxide/SiC interface.

© 2016 The Author(s)

4H-SiC wafer slicing by using femtosecond laser double-pulses

Eunho Kim, Yasuhiko Shimotsuma, Masaaki Sakakura, and Kiyotaka Miura
Opt. Mater. Express 7(7) 2450-2460 (2017)

Electrical and ultraviolet characterization of 4H-SiC Schottky photodiodes

G. Lioliou, M.C. Mazzillo, A. Sciuto, and A.M. Barnett
Opt. Express 23(17) 21657-21670 (2015)

Fourier transform infrared spectroscopy of size-segregated aerosol deposits on foil substrates

Judith A. Hopey, Kirk A. Fuller, Venkataramanan Krishnaswamy, David Bowdle, and Michael J. Newchurch
Appl. Opt. 47(13) 2266-2274 (2008)

Dependences of photoluminescence from P-implanted epitaxial Ge

L. Ding, Andy Eu-Jin Lim, Jason Tsung-Yang Liow, M. B. Yu, and G.-Q. Lo
Opt. Express 20(8) 8228-8239 (2012)

Temperature and doping dependence of the Raman scattering in 4H-SiC

Yan Peng, Xiaobo Hu, Xiangang Xu, Xiufang Chen, Juan Peng, Jisheng Han, and Sima Dimitrijev
Opt. Mater. Express 6(9) 2725-2733 (2016)