Thermal barrier coatings (TBC) are used widely on a range of components that operate at high temperatures. We report measurement of the factor that is required to convert the Raman shift to stress for air plasma sprayed yttria (7 wt %) stabilized tetragonal zirconia (ZrO<sub>2</sub>) (YSZ) thermal barrier coatings. The factor is evaluated for the as-coated condition and also following a heat treatment at 1000 °C for 1050 h. Two Raman bands at 608 cm<sup>?1</sup> and 640 cm<sup>?1</sup> have been investigated in a diamond anvil cell under hydrostatic pressure up to ?24 GPa. In the range of zero to ?1.6 GPa, a linear behavior was observed in terms of the shifts of these two Raman bands with a gradient similar to dense bulk tetragonal ZrO<sub>2</sub>. From these measurements the factors to convert wavenumber shift to stress have been derived. The application of these conversion factors to stress measurement in TBC coated test specimens and components is discussed.

PDF Article

Cited By

You do not have subscription access to this journal. Cited by links are available to subscribers only. You may subscribe either as an OSA member, or as an authorized user of your institution.

Contact your librarian or system administrator
Login to access OSA Member Subscription