Raman Spectroscopic Study of the Aging and Nitration of Actinide Processing Anion-Exchange Resins in Concentrated Nitric Acid

Not Accessible

Your library or personal account may give you access

Abstract

Degradation of two types of anion exchange resins, Dowex 11 and Reillex HPQ, from the action of concentrated nitric acid (4 to 12 M) and radiolysis [from depleted uranium as UO2 2+ nitrate species and 239Pu as Pu(IV) nitrate species] was followed as a function of time with Raman vibrational spectroscopy. Elevated temperatures (~ 50 degrees C) were used in the absence of actinide metal loading to simulate longer exposures of the resin to a HNO3 process stream and waste storage conditions. In the absence of actinide loading, only minor changes in the Dowex resin at acid concentrations < 10 M were observed, while at 12 M acid concentration, the emergence of a Raman peak at 1345 cm-1 indicates the addition of nitro functional groups to the resin. Similar studies with the Reillex resin show it to be more resistant to nitric acid attack at all acid concentrations. Incorporation of weakly radioactive depleted uranium as the UO2 2+ nitrate species to the ion-exchange sites of Dowex 11 under differing nitric acid concentrations (6 to 12 M) at room temperature showed no Raman evidence of resin degradation or nitration, even after several hundred days of contact. In contrast, Raman spectra for Dowex 11 in the presence of 239Pu as Pu(IV) nitrate species reveal numerous changes indicating resin alterations, including a new mode at 1345 cm-1 consistent with a Pu(IV)-nitrate catalyzed addition of nitro groups to the resin backbone.

PDF Article
More Like This
Comparative study of multiple thiol-based self-assembled monolayer coatings for the SERS detection of nitrite, nitrate, and perchlorate anions in water

P. Muñoz, C. T. N. Noordam, R. J. M. Egberink, J. Huskens, and S. M. Garcia-Blanco
Appl. Opt. 58(34) 9345-9352 (2019)

Process optimization of buried Ag+–Na+ ion-exchanged waveguides: theory and experiment

Ramu V. Ramaswamy, H. C. Cheng, and Ramakant Srivastava
Appl. Opt. 27(9) 1814-1819 (1988)

Cited By

You do not have subscription access to this journal. Cited by links are available to subscribers only. You may subscribe either as an Optica member, or as an authorized user of your institution.

Contact your librarian or system administrator
or
Login to access Optica Member Subscription

Select as filters


Select Topics Cancel
© Copyright 2024 | Optica Publishing Group. All Rights Reserved