Abstract

Various overcoat layers have been developed to protect silver mirrors from tarnish and corrosion. However, the mechanisms by which these protective layers improve mirror durability are not fully understood. Mixed flowing gas exposure was used to investigate the corrosion behavior of plasma beam sputtered silver mirrors with different adhesion layer materials. A small amount of nickel in the adhesion layer had a significant impact on the silver–dielectric interface. Additionally, lateral transport of silver was found to be an important factor in the corrosion process. Better stability at all layer interfaces is suggested to improve mirror durability.

© 2016 Optical Society of America

Development and growth of corrosion features on protected silver mirrors during accelerated environmental exposure

Kelsey A. Folgner, Chung-Tse Chu, Scott D. Sitzman, Sean C. Stuart, Zachary R. Lingley, and James D. Barrie
Appl. Opt. 59(5) A187-A197 (2020)

Control of stress in protected silver mirrors prepared by plasma beam sputtering

James D. Barrie, Peter D. Fuqua, Kelsey A. Folgner, and Chung-Tse Chu
Appl. Opt. 50(9) C135-C140 (2011)

Corrosion characterization of durable silver coatings by electrochemical impedance spectroscopy and accelerated environmental testing

Chung-Tse Chu, Peter D. Fuqua, and James D. Barrie
Appl. Opt. 45(7) 1583-1593 (2006)

Effects of stress, defects, and layer composition on the development of corrosion features on protected silver mirrors

Kelsey A. Folgner, Katherine J. Nelms, Chung-Tse Chu, Diana R. Alaan, Christopher J. Panetta, and James D. Barrie
Appl. Opt. 62(7) B222-B230 (2023)

Correlation of long-duration exposure and accelerated testing of protected silver mirrors

Chung-tse Chu, Diana R. Alaan, Kelsey A. Folgner, James D. Barrie, and Peter D. Fuqua
Appl. Opt. 59(5) A219-A228 (2020)