Abstract

We have used an accelerated humidity test consisting of a 24-h cycle between 27–50°C at 95% relative humidity to rate the moisture resistance of typical protective films such as CaF₂, LaF₃, and fluorinated polymers (TFE, FEP) deposited on BaF₂ and NaCl substrates. The test life of BaF₂ specimens was increased from about 4 cycles to over 9, 26, and 42 cycles when protected by CaF₂, TFE, and LaF₃, respectively. Heat treating the as-deposited CaF₂ films further improved specimen life by a factor of 2. The lifetime of NaCI specimens was improved from a fraction of a cycle to 1 and 3 cycles, respectively, by CaF₂ and TFE coatings. No adherent LaF₃ films could be deposited on the salt. Microhardness measurements of the CaF₂ films showed a direct correlation with humidity resistance. The effect of heat treatment was apparently to sinter the fine CaF₂ particles composing the film, thus increasing film density, refractive index, and hardness while reducing moisture permeability. CaF₂ and TFE films function as antireflective, as well as protective layers, on BaF₂ and NaCl.

© 1975 Optical Society of America

Combination Moisture Resistant and Antireflection Plasma Polymerized Thin Films for Optical Coatings

John R. Hollahan, Theodore Wydeven, and Catherine C. Johnson
Appl. Opt. 13(8) 1844-1849 (1974)

Reflectance and durability of Ag mirrors coated with thin layers of Al₂O₃ plus reactively deposited silicon oxide

G. Hass, J. B. Heaney, H. Herzig, J. F. Osantowski, and J. J. Triolo
Appl. Opt. 14(11) 2639-2644 (1975)

Laser Induced Damage in Optical Materials: 6th ASTM Symposium

Alexander J. Glass and Arthur H. Guenther
Appl. Opt. 14(3) 698-715 (1975)

Characterization of optical thin films

H. K. Pulker
Appl. Opt. 18(12) 1969-1977 (1979)

Absorption of thin film materials at 10.6 μm

W. E. K. Gibbs and A. W. Butterfield
Appl. Opt. 14(12) 3043-3046 (1975)