Abstract
Enhanced electrochemical performance was achieved through a multilayer PANI/Au electrodes. An all-solid-state supercapacitor was fabricated using a polyvinyl alcohol /H3PO4 electrolyte, which was lightweight and exhibited a high areal capacitance of 117 mF/cm2 with great rate capability.