Abstract

Concentrations of intrinsic structural defects in synthetic silica glass, AQT, were measured by highly sensitive ESR and photoluminescence measurements. It was revealed that the defects, influential for 193 nm absorption, were less than 10<sup>13</sup>pcs/cm<sup>3<sup>.</sup> </sup>