Reactively co-sputtered aluminum oxide layers with low background loss and varying Er concentrations have been deposited. Net optical gain of 0.76 dB/cm was obtained for an Er concentration of 0.9×10<sup>20</sup>cm<sup>-3</sup>in a channel waveguide.