Abstract
We report a novel type-II photonic crystal fiber Bragg grating for high-temperature applications. The Bragg grating is inscribed in a low-loss in-fiber structure named suspended-core photonic microcell, which is postprocessed from a commercial pure-silica photonic crystal fiber. Grating samples with core diameters of about 4 μm were made by using a focused near-infrared femtosecond laser and a phase mask, and then tested in a tube furnace from room temperature to about 1200 °C. The thermal response of the Bragg resonant wavelength was measure to be about 12 and 16 pm/°C, respectively, at the temperature around 100 °C and 1000 °C. The grating spectrum remained stable in a 10-h isothermal annealing at 1000 °C and started decaying at about 1120 °C with the rate of about 0.02 dB/min. This type of grating possesses flexibilities in both waveguide and grating structure design, exhibits good high-temperature performance, hence would be promising platform for building wavelength-division-multiplexed fiber sensors and tunable devices with a wide working temperature range.
© 2018 IEEE
PDF Article
More Like This
Cited By
You do not have subscription access to this journal. Cited by links are available to subscribers only. You may subscribe either as an Optica member, or as an authorized user of your institution.
Contact your librarian or system administrator
or
Login to access Optica Member Subscription