Abstract
We present complete experimental determinations of the tunnel barrier parameters (two barrier heights, junction area, dielectric constant, and extrinsic series resistance) as a function of temperature for submicrometer Ni–NiO–Ni thin-film tunnel junctions, showing that when the temperature-invariant parameters are forced to be consistent, good-quality fits are obtained between I–V curves and the Simmons equation for this very-low-barrier system (measured ϕ ≈ 0.20 eV). A splitting of ≈10 meV in the barrier heights due to the different processing histories of the upper and lower electrodes is clearly shown, with the upper interface having a lower barrier, consistent with the increased effect of the image potential at a sharper material interface. It is believed that this is the first barrier height measurement with sufficient resolution for this effect to be seen. A fabrication technique that produces high yields and consistent junction behavior is presented as well as the preliminary results of inelastic tunneling spectroscopy at 4 K that show a prominent peak at ∼59 meV, shifted slightly with respect to the expected transverse optic phonon excitation in bulk NiO but consistent with other surface-sensitive experiments. We discuss the implications of these results for the design of efficient detectors for terahertz and IR radiation.
© 2005 Optical Society of America
Full Article | PDF ArticleMore Like This
Philip C. D. Hobbs, Robert B. Laibowitz, Frank R Libsch, Nancy C. LaBianca, and Punit P. Chiniwalla
Opt. Express 15(25) 16376-16389 (2007)
G. D. Boreman, C. Fumeaux, W. Herrmann, F. K. Kneubühl, and H. Rothuizen
Opt. Lett. 23(24) 1912-1914 (1998)
Haifeng Zhang, Min Zhang, Caihui Feng, Weiyou Chen, Caixia Liu, Jingran Zhou, and Shengping Ruan
Appl. Opt. 51(7) 894-897 (2012)