Abstract
Extreme-ultraviolet lithography requires expensive multilayer-coated Zerodur or ULE optics with extremely tight figure and finish specifications. Therefore it is desirable to develop methods to recover these optics if they are coated with a nonoptimum multilayer films or in the event that the coating deteriorates over time owing to long-term exposure to radiation, corrosion, or surface contamination. We evaluate recoating, reactive-ion etching, and wet-chemical techniques for the recovery of Mo/Si and Mo/Be multilayer films upon Zerodur and ULE test optics. The recoating technique was successfully employed in the recovery of Mo/Si-coated optics but has the drawback of limited applicability. A chlorine-based reactive-ion etch process was successfully used to recover Mo/Si-coated optics, and a particularly large process window was observed when ULE optics were employed; this is an advantageous for large, curved optics. Dilute HCl wet-chemical techniques were developed and successfully demonstrated for the recovery of Mo/Be-coated optics as well as for Mo/Si-coated optics when Mo/Be release layers were employed; however, there are questions about the extendability of the HCl process to large optics and multiple coat and strip cycles. The technique of using carbon barrier layers to protect the optic during removal of Mo/Si in HF:HNO3 also showed promise.
© 2001 Optical Society of America
Full Article | PDF ArticleMore Like This
Paul B. Mirkarimi, Sasa Bajt, and Mark A. Wall
Appl. Opt. 39(10) 1617-1625 (2000)
Eberhard Spiller, Sherry L. Baker, Paul B. Mirkarimi, Victor Sperry, Eric M. Gullikson, and Daniel G. Stearns
Appl. Opt. 42(19) 4049-4058 (2003)
Qingyan Hou, Ming Li, Rongli Cui, Peng Liu, Shuaipeng Yue, and Guangcai Chang
Opt. Express 30(26) 48042-48050 (2022)