Abstract
We report experimental demonstration of graphene mode-locked operation of ${{\rm Tm}^{3 + }}\!:\!{{\rm YLiF}_4}$ (YLF) and ${{\rm Tm}^{3 + }}\!:\!{{\rm KY}_3}{{\rm F}_{10}}$ (KYF) lasers near 2.3 µm. To scale up the intracavity pulse energy, the cavity was extended, and double-end pumping was employed with a continuous-wave, tunable ${{\rm Ti}^{3 + }}\!:\!{\rm sapphire}$ laser delivering up to 1 W near 780 nm. The extended ${{\rm Tm}^{3 + }}\!:\!{\rm KYF}$ laser cavity was purged with dry nitrogen to eliminate pulsing instabilities due to atmospheric absorption lines, but this was not needed in the case of the ${{\rm Tm}^{3 + }}\!:\!{\rm YLF}$ laser. Once initiated by graphene, stable uninterrupted mode-locked operation could be maintained with both lasers. With the extended cavity ${{\rm Tm}^{3 + }}\!:\!{\rm YLF}$ laser, 921 fs pulses were generated at a repetition rate of 17.2 MHz at 2304 nm. 739 fs pulses were obtained at the repetition rate of 54 MHz from the ${{\rm Tm}^{3 + }}\!:\!{\rm KYF}$ laser at 2340 nm. The corresponding pulse energy and peak power were 2.4 nJ and 2.6 kW for the ${{\rm Tm}^{3 + }}\!:\!{\rm YLF}$ laser, and 1.2 nJ and 1.6 kW for the ${{\rm Tm}^{3 + }}\!:\!{\rm KYF}$ laser. We foresee that it should be possible to generate shorter pulses at higher pump levels.
© 2020 Optical Society of America
Full Article | PDF ArticleMore Like This
Yagız Morova, Mauro Tonelli, Valentin Petrov, and Alphan Sennaroglu
Opt. Lett. 45(4) 931-934 (2020)
Abdullah Muti, Isınsu Baylam, Mauro Tonelli, and Alphan Sennaroglu
Opt. Lett. 45(15) 4104-4107 (2020)
Liza Basyrova, Pavel Loiko, Jean-Louis Doualan, Abdelmjid Benayad, Alain Braud, Christophe Labbé, and Patrice Camy
Opt. Lett. 46(22) 5739-5742 (2021)