Abstract

The measurement of the depth of reaction of F₂ into the surface of polyethylene and polypropylene is reported. The roughness of the reacted surface has required the development of a novel three-layer, coated sample and subsequent theoretical analysis and analytical techniques. The results with polypropylene can be confirmed by visible reflectance fringes; however, in polyethylene the three-layer method is, at present, the only easy way to measure the extent of fluorine modification of the polymer surface. The extent of fluorination was found to be proportional to the time of exposure to F₂ gas and to increase with elevation of the sample temperature.

Infrared characterization of surfaces and coatings by internal-reflection spectroscopy

E. D. Palik, J. W. Gibson, R. T. Holm, M. Hass, M. Braunstein, and B. Garcia
Appl. Opt. 17(11) 1776-1785 (1978)

Absorption effects on total-internal-reflection fluorescence spectroscopy

Minoru Toriumi, Masatoshi Yanagimachi, and Hiroshi Masuhara
Appl. Opt. 31(30) 6376-6382 (1992)

Resonant internal-reflection prism spectroscopy using surface, guided, and Fabry-Perot EM waves

A. Hjortsberg, W. P. Chen, and E. Burstein
Appl. Opt. 17(3) 430-434 (1978)

Internal Reflection Spectroscopy: Validity of Effective Thickness Equations

N. J. Harrick and A. I. Carlson
Appl. Opt. 10(1) 19-23 (1971)

Direct studies of liquid flows near solid surfaces by total internal reflection fluorescence cross-correlation spectroscopy

Stoyan Yordanov, Andreas Best, Hans-Jürgen Butt, and Kaloian Koynov
Opt. Express 17(23) 21149-21158 (2009)