Abstract

The diffusivity of thicker than usual Ti films into LiNbO₃ to create deep waveguides has been investigated as a function of crystal orientation and diffusion ambient for temperatures ranging from 1050 to 1100°C. The diffusion parameters for substrates diffused in water vapor environment are always larger than ones diffused in dry ambient. Differences in the diffusion coefficient for the extraordinary mode as high as 90, 66, and 84% are measured for X-, Y-, and Z-cut crystals, respectively. Smaller but noticeable differences are detected for the ordinary mode. Similar enhancing effects of the water vapor are also obtained for the surface-index change. Severe rough surface finish and surface contouring, revealing an etchedlike appearance, are observed on Z-cut substrates diffused in wet atomosphere. In general, substrates diffused in dry O₂ produced relatively smoother surfaces. No outdiffused modes are excited in Z-cut substrates when diffused in dry oxygen ambient for long times at high temperatures.

© 1986 Optical Society of America

Water vapor effects on optical characteristics in Ti:LiNbO₃ channel waveguides

Toshinori Nozawa, Kazuto Noguchi, Hiroshi Miyazawa, and Kenji Kawano
Appl. Opt. 30(9) 1085-1089 (1991)

Effect of water vapor in a y-cut lithium niobate waveguide

M. Ahmad, K. Chelapathi, and Y. G. K. Patro
Appl. Opt. 35(9) 1489-1491 (1996)

Characterization of index profiles of Zn-diffused LiNbO₃ waveguides

Rubén Nevado and Ginés Lifante
J. Opt. Soc. Am. A 16(10) 2574-2580 (1999)

Mode control of Ti-diffused LiNbO₃ slab optical waveguide

H. Naitoh, M. Nunoshita, and T. Nakayama
Appl. Opt. 16(9) 2546-2549 (1977)

Polarization dependence in Ti-diffused LiNbO₃ directional couplers

Donghua Gu, Ohannes Eknoyan, and Henry F. Taylor
Appl. Opt. 41(1) 74-77 (2002)