Abstract
In this Letter, we report continuous-wave (CW) lasers with wavelengths beyond 3 µm in homemade Ho3+/Pr3+ co-doped AlF3-based glass fibers. The laser cavity was established through the integration of a dichroic mirror (DM, HR@3–3.1 µm) positioned at the pump end and a partial reflectivity (PR) fiber Bragg grating (FBG) situated at the laser emission end. The FBGs in AlF3-based glass fibers were fabricated by a fs laser direct-writing method, and the resonant wavelengths were 3.009, 3.036, and 3.064 µm, respectively. Under the pump of 1.15 µm laser, a maximum unsaturated output power of 1.014 W was obtained at 3.009 µm with an overall laser efficiency of 11.8% and FWHM bandwidth of 0.88 nm. Furthermore, in order to enhance the optical–thermal stability, the FBG was heat-treated at 200°C for 30 min, and a higher output power of 1081 mW (348 mW without heat treatment) at 3.036 µm was achieved. To the best of our knowledge, this is the first demonstration of 3–3.1 µm lasers by using FBGs in Ho3+/Pr3+ co-doped AlF3-based fibers.
© 2024 Optica Publishing Group
Full Article | PDF ArticleMore Like This
Shunbin Wang, Jiquan Zhang, Niannian Xu, Shijie Jia, Gilberto Brambilla, and Pengfei Wang
Opt. Lett. 45(5) 1216-1219 (2020)
Mo Liu, Jiquan Zhang, Niannian Xu, Xinwei Tian, Shijie Jia, Shunbin Wang, Gilberto Brambilla, and Pengfei Wang
Opt. Lett. 46(10) 2417-2420 (2021)
Niannian Xu, Zhiyong Yang, Jiquan Zhang, Nian Lv, Mo Liu, Ruoning Wang, Zhenrui Li, Shijie Jia, Gilberto Brambilla, Shunbin Wang, and Pengfei Wang
Opt. Lett. 47(3) 597-600 (2022)